"Nanophotonics, a novel optical technology, utilizes the local interaction between nanometric particles via optical near fields. The optical near fields are the elementary surface excitations on nanometric particles, i.e. dressed photons that carry material energy. Of the variety of qualitative innovations in optical technology realized by nanophotonics, this books focuses on fabrication. To fabricate nano-scale photonic devices with nanometer-scale controllability in size and position, we developed a self-assembly method for size- and position-controlled ultra-long nanodot chains using a novel effect of near-field optical desorption. A novel deposition and etching scheme under nonresonant conditions is also demonstrated and its origin is reviewed."

"Penelitian ini bertujuan untuk membandingkan perubahan warna permukaan nanofil yang dipoles dengan teknik pemolesan one step dan multi step polish setelah perendaman kopi. 30 sampel, dibagi menjadi 3 perlakuan: dipoles PoGo® (one step), dipoles Sof-Lex® (multi step) dan tidak dipoles. Sampel direndam kopi selama 12 hari. Pengukuran perubahan warna menggunakan vita classic. Setelah perendaman selama 12 hari, seluruh sampel direndam kopi (dipoles Sof-Lex®, PoGo® dan tidak poles) menunjukkan perubahan warna. Perubahan warna pada nanofil dipoles Sof-Lex® lebih kecil dibanding PoGo® namun tidak bermakna. Dapat disimpulkan multi-step polish menghasilkan perubahan warna lebih kecil dibanding one step polish namun tidak bermakna.

---

This research aims to compare color change on nanofiller polished by one step and multi step polish techniques after being immersed in coffee. 30 samples treated into 3 types, polished by PoGo® (one step), Polished by Sof-Lex® (multi step) and unpolished. Samples were immersed in coffee in 12 days. Colour change was measured by using vita classic. After 12 days of immersion, all sample groups (polished by PoGo®, polished by Sof-Lex®, and unpolished) immersed in coffee, reveal color change. Color change on nanocomposite polished by Sof-Lex® is less than the one polished by PoGo®. It can be concluded multi step polish produces less color change compare to one step polish but the difference is not significant"

"This book provides a comprehensive overview of contemporary basic research, emerging technology, and commercial and industrial applications associated with the electrophoretic deposition of nanomaterials. This presentation of the subject includes an historical survey, the underlying theory of electrophoresis, dielectrophoresis, and the colloidal deposition of materials. This is followed by an assessment of the experimental equipment and procedures for electrophoretic and dielectrophoretic aggregation, manipulation, and deposition of nanoparticles, nanotubes, and other nanomaterials. Additional chapters explore the specific science and technology of electrophoretic film formation, using widely studied and application-driven nanomaterials, such as carbon nanotubes, luminescent nanocrystals, and nano-ceramics. The concluding chapters explore industrial applications and procedures associated with electrophoretic deposition of nanomaterials."

"ABSTRAKGas CO adalah gas yang berbahaya, tidak hanya karena bersifat racun tetapi juga dikarenakan karakteristiknya yang tidak berbau, berwana dan tidak berasa. Pendeteksian secara konvensional tidak memadai untuk diaplikasikan di industri yang membutuhkan kecepatan dan ketepatan pendeteksian. Pengembangan sensor gas mengarah pada bahan metal-oksida semikonduktor seng oksida ZnO . Untuk meningkatkan performa sensor, reduksi ukuran dan proses pendopingan telah menjadi alternatif yang mumpuni. Dopan dengan sifat katalitik, yaitu serium CeO2 , dipilih dalam penelitian ini. Nanopartikel CeO2 disintesis melalui metode presipitasi dengan presipitator NH4OH. Proses optimasi ukuran nanopartikel CeO2 dilakukan dengan memvariasikan temperatur kalsinasi, yaitu 300 oC, 400 oC, 500 oC, 600 oC dan 700 oC . Karakterisasi CeO2 hasil sintesis dilakukan dengan menggunakan FTIR, XRD, PSA, dan TEM. Hasil FTIR mengidentifikasikan bahwa seluruh hasil sintesis mengandung gugus CeO2. Dari hasil karakteriasi XRD dapat diketahui ukuran kristalinitas CeO2 secara berurutan dari temperatur kalsinasi terkecil, yakni 5,3 nm, 5,7 nm, 6,5 nm, 9,9 nm, dan 12,3 nm. Selanjutnya nanopartikel CeO2 dengan ukuran terkecil, yakni hasil kalsinasi dengan temperatur 300 oC, dikarakterisasi lebih lanjut dengan menggunakan PSA dan TEM untuk memastikan sebaran ukurannya. Dari hasil PSA dan TEM diperoleh ukurannya adalah 113 nm dan 4 nm. CeO2 digunakan sebagai dopan dalam pembuatan lapisan tipis dengan memvariasikan konsentrasinya, yakni 0 wt , 4 wt , dan 8 wt . Pada penelitian ini digunakan tiga jenis metode deposisi yakni ultrasonic spray pyrolysis USP , dip-coating, dan spin-coating. Proses pendeposisian lapisan tipis ZnO yang didoping CeO2 dilakukan di atas substrat kaca terlapis emas. Selanjutnya hasil deposisi akan dianalisis morfologi kristalnya dengan menggunakan SEM, komposisi dengan EDS dan performa sensor dengan rangkaian alat deteksi. Morfologi lapisan tipis hasil deposisi dengan metode ultrasonic spray pyrolysis USP dan dip-coating menghasilkan bentuk partikel bulat sementara metode spin-coating menghasilkan bentuk nanowire. Performa sensor diuji dengan mengalirkan gas CO ke ruang uji dengan konsentrasi 100 ppm. Nilai sensitivitas sensor tertinggi bernilai 41 yang diperoleh pada sensor gas lapisan tipis ZnO yang didoping 4 CeO2 hasil deposisi dengan menggunakan metode dip-coating. Waktu respon dan waktu pulih tercepat adalah 5,5 detik dan 7 detik yang diperoleh pada sensor gas lapisan tipis ZnO yang didoping 8 CeO2 hasil deposisi dengan menggunakan metode dip-coating.

---

ABSTRACTCarbon monoxide is a dangerous air pollution gas, not only due to its high toxicity but also because of its chemical characteristics exposure to CO occurs without the awareness of an individual. This gas is odorless, tasteless and colorless. Conventional detection is inadequate to apply in industries that require speed and accuracy of detection. The development of gas sensors leads to a metal oxide material of zinc oxide ZnO semiconductors. To improve sensor performance, reduction of size and preparation process has become a viable alternative. Dopants with catalytic properties, ie cerium CeO2 , were selected in this study. The CeO2 nanoparticles were synthesized by precipitation methods with NH4OH precipitators. The process of optimizing the size of CeO2 nanoparticles is done by varying the calcination temperature, 300 oC, 400 oC, 500 oC, 600 oC, and 700 oC. The synthesis of CeO2 characterization was performed using FTIR, XRD, PSA, and TEM. The FTIR results identify that all synthesis products contain the CeO2 group. The XRD result shows that the crystallite size of the cerium oxide increased from 5.3 nm to 12.3 nm as the calcining temperature increased from 300 to 700 oC. Furthermore, CeO2 nanoparticles that calcined at 300 C, are further characterized by using PSA and TEM to confirm the size distribution. From the results of PSA and TEM obtained size is 113 nm and 4 nm. CeO2 was used as a dopant in the manufacture of the thin films with different CeO2 Zn ratios, various concentrations were 0 2 and 6 wt . Ultrasonic spray pyrolysis USP , dip coating, and spin coating are used as the deposition method. The thin films deposited on top of a glass substrate with gold interdigitated electrode for electrical measurements . Furthermore, the deposition results will be analyzed by using SEM, EDS and sensor performance. In order to investigate gas sensing properties, the films deposited on top of glass substrates with gold interdigitated electrodes was heated at various temperature 150 oC, 200 oC, and 250 oC in chamber gas to collect resistance data. The volume of gas CO 100 ppm to be injected was controlled by the duration. The highest sensitivity sensor value is 41 obtained in the 4 CeO2 doped ZnO by dip coating method. Response time and recovery time is 5.5 seconds and 7 seconds is obtained in ZnO layer sensor which is doped 8 CeO2 with deposition using the dip coating method."

"Aligned Carbon Nanotube (ACNT) adalah salah satu jenis nanomaterial yang memiliki sifat luar biasa dan dapat digunakan untuk berbagai aplikasi di masa depan. LPG adalah salah satu sumber karbon yang dapat menghasilkan ACNT dengan metode Water Asssisted Chemical Vapour Deposition (WA-CVD). Penelitian ini mempelajari bagaimana kinerja dari substrat kuarsa dan bagaimana pengaruh suhu pertumbuhan dan waktu reaksi terhadap kualitas ACNT yang dihasilkan. Penelitian ini menghasilkan nanokarbon dengan yield yang cukup tinggi yaitu mencapai 2,70 mg/cm2. Hasil dari variasi waktu 100 menit dan 120 menit, didapatkan morfologi CNT yang dihasilkan pada waktu reaksi 100 menit lebih merata. Selanjutnya, uji pengaruh suhu terhadap hasil CNT menghasilkan produk pada suhu 800oC sebagai suhu optimum dimana yield dari nanokarbon adalah 2,22 mg/cm2 dan morfologi yang lebih merata dengan diameter 38 nm dilihat dari karakterisasi TEM, SEM-EDX, dan mapping. Sementara itu, keberadaan dari pengotor seperti karbon amorf dan CNT yang terenkapsulasi oleh katalis pada suhu 850oC didapatkan karena trade-off suhu tinggi dimana laju pelarutan karbon dalam katalis melebihi laju difusi dari karbon. Sedangkan sintesis dengan suhu 750oC hanya menghasilkan Carbon Nanofibers (CNF). Dengan hasil ini, dapat dikatakan bahwa orientasi dari CNT yang dihasilkan belum aligned atau dengan kata lain belum terbentuk ACNT. Meskipun demikian, orientasi dan morfologi paling merata didapatkan pada waktu reaksi 100 menit dengan 800oC. Perlakuan terhadap katalis menjadi suatu permasalahan belum didapatkannya ACNT. Selain itu, kinerja steam juga menjadi suatu masalah yang belum teratasi sehingga ACNT belum didapatkan. Waktu reaksi juga harus diturunkan untuk mendapatkan aligned dan penurunan waktu reaksi tidak akan jadi masalah untuk yield karena substrat kuarsa mampu menghasilkan yield yang tinggi.

---

Aligned Carbon Nanotube (ACNT) is a nanomaterial with extraordinary properties and has very wide future applications. LPG is one of carbon source to produce ACNT through Water Assisted Chemical Vapour Deposition (WA-CVD) method. This research investigates performance of quartz substrate and effects of growth temperature and reaction time on the quality of ACNT. The synthesis in this research produced nanocarbon with high yield reaching 2.70 mg/cm2. At the varied reaction time (100 and 120 minutes), morphology of ACNT produced at 100 minutes is more uniform. Afterwards, growth temperature effect shows that 800oC is the optimum where the yield is reaching 2.22 mg/cm2 and more uniform morphology with diameter 38 nm characterized by TEM, SEM-EDX, and mapping. However, existence of polluter such as amorphous carbon and encapsulated CNT by the catalyst was obtained as trade-off of high temperature at 850oC where dissolution rate of carbon to catalyst is higher than diffusion rate of carbon. Meanwhile, at 750oC only Carbon Nanofiber (CNF) can be produced. Therefore, this research could not produced aligned structured of CNT. Yet, good orientation and morphology of CNT were produced at 100 minutes synthesis and at 800oC. Catalyst pretreatment is one of root cause of not producing ACNT. Besides that, the performance of steam could be another source of the problem. Reaction time has to be reduced until below 100 minutes to get aligned carbon nanotube. The reduced reaction time could still produced high yield since quartz substrate could bear high yield of nanocarbons including ACNT."

"This thesis explores four interesting topics within plasmonics, extraordinary optical transmission, negative refractive index metamaterials, plasmonic devices for controlling SPPs, and field enhancement phenomena near metal nanoparticles."

"Surface Mechanical Attritition Treatment adalah salah satu proses fabrikasi nano materialdengan cara memberikan deformasi mekanis strain-induced pada permukaan material.Penelitian ini memberi perlakuan SMAT pada stainless steel AISI 304 yang merupakanaustenitic stainless steel. Deformasi yang diperlakukan pada permukaan material akanmenghasilkan gradien regangan di seluruh bagian material. Perbedaan regangan dan strainrate mempengaruhi struktur yang terjadi. Semakin tinggi regangan yang diberikan (semakindekat dengan permukaan) menghasilkan butir yang lebih halus hingga skala nanometer. Dansebaliknya, semakin rendah regangan yang dialami maka akan dihasilkan butir yang kasar..Proses SMAT pada baja juga dapat menghasilkan transformasi fasa dari austenit kemartensit. Analisis XRD menunjukkan peningkatan kandungan martensit pada lapisan yangterkena regangan tinggi. Pengamatan TEM menunjukkan transformasi martensit terjadidengan dua mekanisme yaitu dari austenit yang berstruktur kristal FCC () menjadi martensityang berstruktur kristal HCP (ε) dan dari austenit yang berstruktur kristal FCC () menjadimartensit yang berstruktur kristal BCC (α’). Transformasi ini mengikuti arah dan hubungankristalografi Kurdjumov-Sachs (K-S) orientation yaitu 〈1-10〉γ//〈112-0〉ε//〈11-1〉α. Sementarapada bagian yang terkena regangan lebih rendah tetap mengandung fasa austenit.Kombinasi dari butir halus dan kasar serta austenit dan martensit pada material yang samamemungkinkan untuk mendapatkan material yang kuat sekaligus tangguh. Butir halus danfasa martensit pada permukaan akan meningkatkan kekerasan material, sementara butir kasardan fasa austenit pada bagian lebih dalam akan mempertahankan keuletan material.

---

Surface Mechanical Attritition Treatment is one of nano material fabrication method which

done by applying strain-induced mechanical deformation on the surface. This research treated

stainless steel AISI 304 which is austenitic stainless steel type, with SMAT. The deformation

cause strain gradient through out the sample. Strain level differences give effect to material

structure. Higher strain which happen closely to the surface region, result in finer grain up to

nano scale, while lower strain cause more coarse grain.

SMAT on stainless steel also could cause phase transformation from austenite to martensite.

XRD analysis showed increase of martensite content on higher strain-affected layer. TEM

observations showed martensite transformation by two mechanism, austenite with FCC

crystal structure () to martensite with HCP crystal structure (ε) and austenite with FCC

crystal structure () to martensite with BCC crystal structure (α’). This transformation are

following crystalographic orientation relationship of Kurdjumov-Sachs (K-S), 〈1-10〉γ//〈112-

0〉ε//〈11-1〉α. While on the other region that less-affected by strain still contain austenite

phase.

Combination of fine grain-coarse grain and austenite-martensite phase on the same material

could result in higher properties material since it could has high strenght and high toughness.

Fine grain and martensite phase on the surface will increase the hardness of material, while

coarse grain and austenite phase on deeper layer will increase the ductility of material."

"Nanofluida adalah jenis fluida yang sedang dikembangkan yang memiliki sifat konduktivitas yang lebih tinggi dibandingkan dengan air. Penelitian lebih lanjut diperlukan agar fluida baru ini dapat diaplikasikan secara efektif dan efisien. Tujuan dilakukannya pcnelilian ini adalah mempelajari pengamh penambahan partikel nano pada air terhadap nilai koefisien gesek jika Huida ini dialirkan pada pipa lurus. Penelitian dilakukan dengan cara mengalirkan fluida air dan nanofluida A1103 dcngan menvariasikan kecepatan aliran pada pipa lums berukuran 4 mm, 8 mm, dan 17 mm yang kemudian diukur nilai perbedaan tekanan dan debilnya. Hasil penelitian menunjukkan bahwa nilai koefisien gesek aliran nanofluida A1203 sedikit lebih kecil dibandingkan dengan aliran air pada aliran turbulen.

---

Nanofluid is a kind of the fluid that is being developed which has higher conductivity rather than the water. It needs advance research in studying the effects of the adding the nano particle to water, due to the friction coefficient when this fluid flows in straight pipe. This research done by flowing the water and nanofluid A1203 , with variation of flow velocity in different straight pipe which has diameter 4 mm, 8 mm, and I 7 mm then measure the head loss and capacity. The results showed that the friction coefficient of nanofluid al203 flow less than the water at the turbulent flow."

"Tujuan penelitian ini adalah melihat pengaruh aplikasi nano filled coating agent terhadap kekuatan tarik diametral semen ionomer kaca yang terkontaminasi saliva buatan. Spesimen direndam didalam aquabides selama 1 jam, 1 hari dan 1 minggu dengan suhu 37oC. Uji analisis statistik menggunakan t test tidak berpasangan.Hasil penelitian didapatkan pada perendaman 1 jam p= 0.051 dan 1 hari p=0,528 (P>0,05), sedangkan pada 1 minggu p=0.030 (p<0,05). Dapat disimpulkan bahwa aplikasi nano filled coating agent pada semen ionomer kaca yang terkontaminasi saliva buatan, sampai 1 hari dapat memberikan perubahan yang tidak bermakna pada nilai kekuatan tarik diametral.

---

The purpose of this study is to see the influence of nano-filled coating agent applications for diametral tensile strength of GIC contaminated with artificial saliva. Specimens were stored in aquabides for 1 hour, 1 day and 1 week at 37 °C. Test analysis using non-paired t test.

The results obtained at 1 hour immersion p = 0051 and 1 day p = 0.528 (P> 0.05), whereas at 1 week p = 0030 (p <0.05). It can be concluded that the application of nano-filled coating agent on GIC contaminated with artificial saliva, until one day may provide a non-significant change in DTS values​​."

"Nanopartikel hybrid oksida besi/oksida tembaga/oksida seng telah disintesis dengan menggunakan metode sol-gel untuk tiga variasi molar. Seluruh sampel dikarakterisasi dengan spektroskopi X-Ray Diffraction, Field Emission Scanning Electron Microscopy, Vibrating Sample Magnetometer, Energy Dispersive X-Ray, Ultraviolet-visible Reflectance dan Fourier-Transform Infrared. Nanopartikel hybrid yang dihasilkan menunjukkan karakteristik feromagnetik dengan morfologi yang merupakan gabungan spherical-like dari oksida besi dan oksida seng dan clews-like dari oksida tembaga. Keempat unsur penyusunan nanopartikel hybrid hadir dalam bentuk ikatan Zn-O, Fe-O dan Cu-O dengan kehadiran fase dan struktur tunggal dari inverse cubic spinel magnetite, hexagonal wurtzite oksida seng dan monoclinic oksida tembaga. Celah energi nanopartikel hybrid cenderung turun dengan berkurangnya rasio molar oksida seng yang berhubungan dengan peningkatan kuantitas oksida besi dan oksida tembaga. Kondisi optimum aktivitas fotokatalitik nanopartikel hybrid dalam mendegradasi methylene blue dengan pemaparan cahaya ultraviolet diperoleh pada kondisi basa untuk pH 13. Nanopartikel hybrid dengan rasio molar 1:1:5 mampu menghasilkan degradasi maksimum dengan laju degradasi yang lebih tinggi dibandingkan nanopartikel oksida seng. Hole ditemukan sebagai spesies yang berperan aktif dalam aktivitas fotokatalitik nanopartikel hybrid dalam mendegradasi methylene blue.Iron oxide/cuprix oxide/zinc oxide hybrid nanoparticles with three variation of molar ratio have been synthesized using sol-gel methods. All samples were characterized by X-Ray Diffraction, Field Emission Scanning Electron Microscopy, Vibrating Sample Magnetometer, Energy Dispersive X-Ray, Ultraviolet-visible Reflectance and Fourier-Transform Infrared Spectroscopies. The resulting hybrid nanoparticles show ferromagnetic behaviour and have combination of spherical-like of iron oxide and zinc oxide morphologies with clews-like of cuprix oxide morphology. The four elements of the hybrid nanoparticles present in the form of Zn-O, Fe-O and Cu-O bonds and form individual crystal structures and phases of cubic inverse spinel of iron oxide, hexagonal wurtziteof zinc oxide and monoclinic of cuprix oxide. Energy gap of the hybrid nanoparticles tend to shift to lower energy that associates with increasing quantity of iron oxide and cuprix oxide with decreasing zinc oxide molar ratio. Optimum condition for photocatalytic activity of the hybrid nanoparticles in degrading methylene blue under ultraviolet light irradiation is obtained under alkaline conditions for pH 13. Hybrid nanoparticles with a molar ratio of 1:1:5 is able to produce the maximum degradation with higher degradation rate than zinc oxide nanoparticles. Hole found as species that plays an active role in photocatalytic activity of the hybrid nanoparticles to degrade methylene blue."