"This book offering advantages in design, efficiency, treatment time, and retention, self-ligating brackets have become a major part of modern orthodontic practice. Self-Ligating Brackets in Orthodontics: Current Concepts and Techniques summarizes all information and clinical studies on these popular systems, integrating them with the authors' practical, hands-on experience. From materials and mechanics, to diagnostic and therapeutic principles, to step-by-step treatment techniques, the book is a visual guide and compendium to this groundbreaking field."

"Pendahuluan: Breket Stainless Steel 17-4 PH merupakan salah satu breket yang paling banyak digunakan dalam bidang Ortodonti dengan jangka waktu yang lama didalam rongga mulut, Penggunaannya yang lama mengakibatkan kerugian bagi kesehatan pengguna karena lepasnya ion nikel dan kromium akibat proses korosi. Oleh karena itu, tujuan dari penelitian ini adalah untuk mengatahui sitotoksisitas breket pada sel gingiva akibat lepasnya ion nikel dan kromium pada saliva buatan. Metode: Penelitian In Vitro dengan 2 kelompok breket Stainless Steel 17-4 PH lokal dan impor yang masing-masing berjumlah 24 buah breket. Tiap kelompok jumlah sampel dibagi tiga berdasarkan lama waktu perendaman breket di dalam saliva buatan selama 16, 28, dan 35 hari. Lepasan ion Cr dan Ni dalam saliva hasil perendaman breket di paparkan ke sel gingiva untuk di lakukan uji sitotoksisitas menggunakan MTT Assay. Terlihat seberapa besar viabilitas sel yang menandakan toksisitas breket. Hasil: Terdapat pola viabilitas sel yang berbeda antara breket Stainless Steel 17-4 PH lokal dan impor, namun secara statistik perbedaan viabilitas sel tersebut tidak signifikan, sehingga tidak terdapat perbedaan sitotoksisitas breket Stainless Steel 17-4 PH lokal dan impor. Kesimpulan: Uji sitotoksisitas pada braket Stainless Steel 17-4 PH lokal memperlihatkan pola viabilitas sel pada perendaman 16 hari lebih tinggi lalu ketika perendaman 28 hari tampak viabilitas sel menurun dan meningkat kembali pada perendaman 35 hari sedangkan uji sitotoksisitas pada braket Stainless Steel 17-4 PH impor memperlihatkan pola viabilitas sel pada perendaman 16 hari lebih rendah bila dibandingkan dengan perendaman 28 hari dan menurun kembali pada perendaman 35 hari namun, nilainya masih diatas nilai viabilitas sel perendaman 16 hari. Perbedaan viabilitas sel antara kelompok breket Stainless Steel 17-4 PH lokal dan impor mungkin disebabkan oleh perbedaan metode pabrikasi dan komposisi yang digunakan antara kedua breket tersebut.

---

Introduction: 17-4 PH Stainless Steel bracket is one of the most widely used brackets in the field of Orthodontics with long periods of time in the oral cavity. Its long use has caused a loss to the health of users due to the release of nickel and chromium ions due to the corrosion process. Therefore, the purpose of this study was to determine bracket cytotoxicity in gingival cells due to the release of nickel ions and chromium in artificial saliva. Methods: In Vitro research with 2 groups of local and imported 17-4 PH Stainless Steel brackets, each 24 brackets. Each group number of samples is divided into three based on immersion period in artificial saliva for 16, 28, and 35 days. Release of Cr and Ni ions in saliva from immersion brackets were exposed to gingival cells for cytotoxicity testing using MTT Assay. It can see how much cell viability indicates toxicity of brackets. Results: There are different cell viability patterns between local and imported 17- 4 PH Stainless Steel brackets, but statistically the cell viability difference is not significant, so there is no difference in cytotoxicity of local and imported 17-4 PH Stainless Steel brackets. Conclusion: Cytotoxicity test on local 17-4 PH Stainless Steel bracket shows cell viability pattern at immersion 16 days higher then when immersion 28 days it appears cell viability decreases and increases again at 35 days immersion while the cytotoxicity test on imported 17-4 PH Stainless Steel bracket showed a pattern of cell viability at 16 days soaking lower than 28 days immersion and decreased again at 35 days immersion, however the value is still above the 16-day immersion cell viability value. Differences in cell viability between groups of 17-4 PH Stainless Steel brackets local and imports maybe due to differences in manufacturing methods and the composition used between the two brackets."

"Latar Belakang: Prosedur bonding braket dengan teknik transiluminasi menjadi salah satu alternatif teknik penyinaran pada segmen posterior gigi yang dinilai memiliki akses dan pandangan yang terbatas. Hingga saat ini, masih terdapat perbedaan pendapat mengenai tingkat keberhasilan bonding braket dengan teknik ini. Belum ada standarisasi mengenai arah penyinaran, waktu penyinaran dan besar intensitas light-curing unit dalam bonding braket dengan teknik transiluminasi. Penelitian ini bertujuan untuk mengetahui perbedaan nilai kuat rekat geser pada polimerisasi bahan adhesif dengan teknik transiluminasi pada prosedur bonding braket logam gigi premolar terhadap berbagai intensitas light-curing unit LED. Metode: Dua puluh empat gigi premolar dibagi secara acak kedalam 3 kelompok menggunakan light-curing unit LED dengan intensitas 1000, 1300 dan 3200 mW/cm2. Waktu penyinaran disesuaikan dengan petunjuk teknis alat. Penyinaran braket dilakukan dari arah oklusal dan lingual gigi premolar pada semua kelompok. Spesimen direndam dalam larutan akuades setelah bonding kemudian disimpan didalam inkubator dengan suhu 37°C selama 24 jam. Uji kuat rekat geser dilakukan menggunakan mesin uji universal dengan beban automatic 5kN dan crosshead speed 0.5 mm/menit. Hasil: Nilai rerata kuat rekat geser braket logam pada kelompok LED intensitas 1000, 1300 dan 3200 mW/cm2 secara berurutan adalah 9,33±2.12 MPa, 13,34±2.66 MPa, dan 9,82±2,13 MPa. Kelompok 2 (intensitas 1300 mW/cm2) memiliki nilai kuat rekat tertinggi dibandingkan kelompok lainnya. Uji statistik menunjukan terdapat perbedaan bermakna antara nilai kuat rekat geser braket logam pada LED intensitas 1300 mW/cm2 dengan intensitas 1000 mW/cm2 dan 3200 mW/cm2. Rendahnya nilai kuat rekat geser pada kelompok 3 (intensitas 3200 mW/cm2) pada penelitian ini disebabkan oleh kurangnya pemeliharaan light-curing unit yang digunakan sehingga mempengaruhi output intensitas cahaya. Kesimpulan: Teknik transiluminasi dengan kombinasi arah penyinaran merupakan teknik penyinaran yang efektif dan dapat diterima secara klinis pada prosedur bonding braket premolar. Ketiga intensitas yang digunakan memenuhi nilai kuat geser klinis sehingga klinisi dapat menggunakan ketiga pilihan intensitas LED tersebut. Pemeriksaan dan perawatan berkala pada light-curing unit diperlukan untuk menjaga kualitas dari perangkat yang digunakan.

---

Introduction: Transillumination is an alternative technique to light-curing the posterior segment of the tooth which is considered to have limited access and vision in bracket bonding procedure. However, the effectiveness of this technique is still arguable. There is still no standardization regarding the curing direction, times and light intensity of the curing unit in the bonding bracket with the transillumination technique. This study aims to determine the differences of shear bond strength of orthodontic stainless steel braket using transillumination technique with various LED curing intensity in posterior teeth.

Methods: Twenty four premolars were divided into 3 groups using a LED curing unit with various light intensity of 1000, 1300 and 3200 mW/cm2. The curing time was adjusted to the technical instructions of the curing unit. The curing direction was performed from the occlusal and lingual surface of the premolars in all groups. The specimens were placed in distilled water after bonding and then stored in an incubator at 37°C for 24 hours prior to testing. The shear bond strength test was carried out with an universal testing machine at an automatic load 5kN and crosshead speed of 0.5 mm/min.

Results: The average value of the shear bond strength of stainless steel brackets in the LED groups with intensities of 1000, 1300 and 3200 mW/cm2 respectively were 9.33±2.12 MPa, 13.34±2.66 MPa, and 9.82±2.13 MPa. The group 2 (intensity of 1300 mW/cm2) had the highest shear bond strength value compared to other groups. There was a significant difference statistically between the shear bond strength of stainless steel brackets on LED intensity of 1300 mW/cm2 with an intensity of 1000 mW/cm2 and 3200 mW/cm2. The lower shear bond strength value of the group 3 (intensity of 3200 mW/cm2) in this study occured due to the lack of maintenance of the curing unit used which affects the light intensity output.

Conslusion: The transillumination technique with a combination of curing directions from occlusal and lingual surface of posterior teeth is an effective and clinically acceptable light curing technique for orthodontic bracket bonding procedures. The three light intensities of LED curing unit used meet the clinical shear bond strength values, therefore clinicians can use all the options above. Regular inspection and maintenance of the light-curing unit is necessary to maintain the quality of the device used."

"Pendahuluan: Kehadiran jenis braket sistem self-ligating pasif menambah variasi jenis braket yang digunakan dalam perawatan ortodonti saat ini, sehingga timbul pertanyaan mengenai efektifitasnya terhadap perawatan ortodonti. Salah satu parameter yang menentukan efektifitas tersebut adalah durasi waktu perawatan yang dibutuhkan untuk memperbaiki maloklusi, misalnya kecepatan penutupan ruang secara en-masse menggunakan elastomeric chain. Tujuan: Mengetahui efektifitas perawatan ortodonti yang dilakukan menggunakan sistem braket self-ligating pasif dan sistem braket konvensional selama tahap penutupan ruang secara en-masse. Metode: Penelitian prospective randomized controlled clinical trial dengan teknik split mouth ini dilakukan selama 11 bulan. Sebelas subyek (3 pria dan 8 wanita usia minimal 15 tahun) dengan pencabutan premolar satu rahang atas dan akan memasuki tahap space closure diikutsertakan dalam penelitian ini. Setiap subyek dipasangkan braket konvensional di satu sisi rahang dan self-ligating pasif di sisi lainnya, dimana penentuannya dilakukan secara random, kemudian diberikan gaya sebesar 150 g dengan powerchain pada kawat SS .019 x .025. Pengukuran jarak penutupan ruang dan kehilangan penjangkaran dilakukan pada T0, T1 (4 minggu), dan T2 (8 minggu). Hasil: Terdapat perbedaan rata-rata kecepatan penutupan ruang yang signifikan antara kelompok sistem braket self-ligating pasif dan kelompok sistem braket konvensional (p=0,010) dimana kelompok braket self-ligating pasif memiliki kecepatan yang lebih besar dibandingkan kelompok braket konvensional, namun tidak terdapat perbedaan rata-rata kehilangan penjangkaran yang signifikan secara statistik antara kedua kelompok tersebut. Kesimpulan: Sistem braket self-ligating pasif memiliki efektifitas yang lebih baik karena dapat mempercepat durasi waktu perawatan ortodonti.

---

Introduction: The presences of passive self - ligating bracket system add variety of bracket type used in today's orthodontic treatment, so that raised question in regard to the effectiveness of the treatment. One of the parameters that determines the effectiveness of the treatment is the time required to fix malocclusion, e.g. rate of en - masse closing space using elastomeric chain.

Objectives: To study the effectiveness of orthodontic treatment using passive self - ligating system and conventional system during space closure stages.

Methods: Prospective randomized controlled clinical trial with a split mouth technique was carried out for 11 months. Eleven subjects (3 men and 8 women with age minimum of 15 year old) with the extraction of the first premolars, where it will enter the space closure stage were included in this study. Each subject was bonded with conventional bracket on one side of the arch and with passive self - ligating on the other side which was determined randomly, was given a force of 150 g with power chain on .019 x .025 SS wire. The measurement of space closure and loss of anchorage were performed at T0, T1 (4 weeks), and T2 (8 weeks).

Result: There was significant differences of the average rate of closing space between passive self - ligating system and conventional system group (p = 0.010), for which a group of passive self - ligating system has a greater speed compare than conventional group, though there was no difference in loss of anchorage between the two groups.

Conclusion: The passive self - ligating system is more effective because it can reduce the duration of orthodontic treatment."

"Latar Belakang: Deformasi slot braket Stainless Steel akan mempengaruhi gaya yang diaplikasikan kepada gigi sehingga menghambat pergerakan gigi dan memperlama waktu perawatan ortodonti.Tujuan: Mengetahui deformasi slot braket dari lima merek braket yaitu 3M, Biom, Versadent, Ormco dan Shinye akibat gaya torque kawat Beta Titanium 0.021x0.025 inci dengan sudut puntir 45° dan besar gaya torque dengan sudut puntir 30° dan 45°. Penelitian juga bertujuan untuk membandingkan deformasi dan besar gaya torque antara kelima merek braket.Metode Penelitian: 50 braket Stainless Steel Edgewise dari lima kelompok merek braket (n=10) dilem ke akrilik. Masing-masing braket dilakukan dua tahapan pengukuran yaitu pengukuran deformasi braket dengan menghitung rerata tinggi slot braket dengan mikroskop stereoskopi sebelum dan sesudah uji torque dan pengukuran besar gaya torque dengan alat uji torque.Hasil: Analisa statistik menunjukkan terdapat deformasi slot braket pada kelima merek braket dengan deformasi permanen secara klinis pada braket Biom (2,79 μm) dan Shinye (2,29 μm). Besar gaya torque pada kelima braket dari yang paling besar yaitu 3M, Ormco, Versadent, Shinye dan Biom. Perbandingan deformasi slot braket dan besar gaya torque antara kelima braket adalah terdapat perbedaan deformasi slot braket antara kelima merek braket kecuali antara 3M dan Ormco dan Biom dan Shinye dan terdapat perbedaan besar gaya torque antara kelima braket dengan sudut puntir 30° (kecuali 3M dan Ormco) dan 45°.Kesimpulan: Komposisi logam dan proses pembuatan braket merupakan faktor yang mempengaruhi terjadinya deformasi slot braket dan besar gaya torque. Proses pembuatan dengan metode MIM dan komposisi logam AISI 303 dan 17-4 PH menurunkan risiko deformasi.

---

Background: Stainless Steel bracket slot deformation will affect force applied to teeth can impede tooth movement and prolong orthodontic treatment time.Objective: To determine slot deformation of five different bracket brands namely, 3M, Biom, Versadent, Ormco and Shinye due to torque of Beta Titanium wire 0.021 x 0.025 inch with torsional angle of 45° and the amount of torque with torsional angle of 30° and 45°. The research also aims to compare the deformation and amount of torque between all five brackets brands.Methods: 50 Stainless Steel Edgewise bracket from five bracket group brands (n=10) is attached onto on acrylic. Bracket slot measurement are carried out in two stages, firstly deformation measurement by calculating average bracket slot height with stereoscopy microscope before and after application of torque and secondly, measurement of torque with a torque measurement apparatus.Results: Statistical analysis shows that there are slot deformations on the five bracket brands with clinical permanent deformation on Biom (2,79 μm) and Shinye (2,29 μm). The amount of torque on the five bracket brands from the highest is 3M, Ormco, Versadent, Shinye and Biom. From correlation assessment between bracket slot deformation and amount of torque in the five brands, a difference is found in the deformation in the five brands except between 3M and Ormco and Biom and Shinye. There is a difference in the amount of torque between the five brands with torsional angle of 30° (except 3M and Ormco) and 45°.Conclusion: Metal compositions and manufacturing process are the factors that influence the occurrence of deformation bracket slot and the amount of torque. Manufacturing process using MIM and metal compositions of AISI 303 and 17-4 PH reduce the risk of deformation."

"Latar Belakang: Salah satu faktor yang menentukan keberhasilan restorasi proksimal resin komposit adalah adaptasi yang rapat tepi restorasi dan dinding gingiva kavitas. Restorasi resin komposit akan mengalami kontraksi saat polimerisasi sehingga terdapat celah antara tepi restorasi dan kavitas. Celah ini dapat menimbulkan kebocoran mikro sehingga menyebabkan bakteri, cairan, molekul, dan ion masuk kedalamnya. Penelitian ini bertujuan untuk menganalisis perbedaan tingkat kebocoran mikro dinding gingiva restorasi proksimal resin komposit nanohibrid antara teknik inkremental, bulk-fill yang diaktivasi sonik, dan tanpa aktivasi sonik.Metode: Kavitas kelas II dipreparasi pada tiga puluh gigi premolar rahang atas dan bawah, kemudian dibagi menjadi tiga kelompok. Kelompok pertama ditumpat dengan RK bulk-fill yang diaktivasi sonik, kelompok kedua dengan RK bulk-fill tanpa aktivasi sonik, dan kelompok ketiga dengan RK yang diletakkan secara inkremental. Selanjutnya spesimen direndam dalam air distilasi selama 24 jam dan kemudian dilakukan uji thermocycling, yang diikuti perendaman dalam metilen biru 1% selama 24 jam. Gigi selanjutnya dibelah longitudinal dan dilakukan pengamatan menggunakan mikroskop stereo pembesaran 25x dan dinilai dalam skala ordinal (0-3). Analisis statistik dilakukan dengan uji Kolmogorov-Smirnov.Hasil: Tidak terdapat perbedaan bermakna secara statistik di antara tiga kelompok.Kesimpulan: Tidak ada satupun dari kelompok RK bulk-fill yang diaktivasi sonik, bulk-fill tanpa aktivasi sonik dan yang diletakkan secara inkremental yang dapat menghilangkan kebocoran mikro pada dinding gingiva kavitas kelas II.Kata kunci: kebocoran mikro, teknik peletakan resin komposit, kontraksi

---

Background One of the factor that determine the success of proximal composite restoration is a good marginal adaptation at the interface area Composite resin will undergo contraction during polimerization which may result gap formation between the wall cavity and restoration. The gap can cause a microleakage and resulting a passage for bacteria fluid molecules and ions The purpose of this study is to analize the microleakage of gingival wall nanohybrid composite restoration that filled using sonic activated bulk bulk without sonic activation and incremental techniques.

Methods Standardized class II cavities were prepared on 30 extracted human upper and lower human teeth and randomly assigned to three groups The first group were filled with sonicactivated bulk fill composite resin the second group were filled with bulk fill composite resin without sonic activation and the third group were filled incrementally. The specimens were stored in distilled water for 24 hours and then subjected to thermocycling followed by immersion in 1 methylene blue dye for 24 hours. The teeth were sectioned longitudinally and evaluated for microleakage under 25x magnification stereomicroscope and scored in ordinal scale 0 3 Statistical analysis was performed with the Kolmogorov Smirnov test.

Results There was no statistically significant difference among the three groups Conclusion None of the the techniques was capable of eliminating the microleakage on gingival wall cavity preparations."

"Pendahuluan: Berbagai pilihan produk braket dan kawat ortodonti tersedia di pasaransehingga para ortodontis harus lebih cermat dalam melakukan seleksi terhadap produkbraket dan kawat yang digunakan. Ukuran tinggi slot braket dan dan diameter kawatortodonti yang tercantum pada label kemasan dapat berbeda dengan ukuran hasilpengukuran. Hal ini dapat mempengaruhi hasil pergerakan gigi yang terjadi selamaperawatan ortodonti. Tujuan dari penelitian ini adalah untuk mengetahui ukuran tinggislot braket dan diameter kawat sebenernya dari produk 3M/Unitek, Ormco, danDentaurum serta menganalisis perbedaannya dengan ukuran yang tertera pada kemasan.Metode: Sampel penelitian terdiri dari 30 braket gigi insisif atas slot 0.022 inci dan 45kawat ukuran 0,019 x 0,025 inci yang terdiri dari merk 3M/Unitek, Ormco, danDentaurum. Pengukuran tinggi slot braket dan diameter kawat ortodonti dilakukanmenggunakan Mikroskop Stereoskop Discovery V12 (Carl Zeiss Microimaging GmbH,Jerman) disertai perangkat komputer dan AxioCam.Hasil: Nilai rerata ukuran tinggi slot braket Ormco hasil pengukuran adalah 0,488 mm,3M/Unitek adalah 0,491 mm, Dentaurum adalah 0,538 mm. Nilai rerata ukurandiameter kawat Ormco berupa tinggi kawat hasil pengukuran adalah 0,413 mm danlebar kawat hasil pengukuran adalah 0,496 mm, nilai rerata ukuran diameter kawat3M/Unitek berupa tinggi kawat hasil pengukuran adalah 0,413 mm dan lebar kawathasil pengukuran adalah 0,500 mm, nilai rerata ukuran diameter kawat Dentaurumberupa tinggi kawat hasil pengukuran adalah 0,419 mm dan lebar kawat hasilpengukuran adalah 0,510 mm.Kesimpulan: Terdapat perbedaan bermakna rerata ukuran tinggi slot braket dandiameter berupa tinggi dan lebar kawat ortodonti produk 3M/Unitek, Ormco, danDentaurum pada hasil pengukuran dengan ukuran pada kemasan.

---

Introduction: A wide selection of orthodontic brackets and wire products are available so

orthodontists must be more careful in selecting the bracket and wire products used. The

height of the bracket slot and the diameter of the orthodontic wire indicated on the

packaging label may differ from the result of the real measurement. This can affect

tooth movement that occurs during orthodontic treatment. The purpose of this study was

to determine the size of the bracket slot height and wire diameter of the 3M/Unitek,

Ormco, and Dentaurum products and to analyze the difference with the sizes listed on

the packaging.

Method: The research sample consisted of 30 incisor brackets which have 0.559 mm

(0.022 inch) slot and 45 wires which have 0,48 x 0,64 mm (0.019 x 0.025 inch)

diameter consisting of the 3M/Unitek, Ormco, and Dentaurum brands. The

measurement of the bracket slot height and the diameter of the orthodontic wire was

carried out using the Discovery V12 Stereoscopic Microscope (Carl Zeiss

Microimaging GmbH, Germany) along with a computer and an AxioCam.

Results: The mean value of the measured Ormco bracket slot height measurement is

0.488 mm, 3M/Unitek is 0.491 mm, Dentaurum is 0.538 mm. The average value of the

Ormco wire diameter in measured wire height is 0.413 mm and the measured wire

width is 0.496 mm, the mean value of 3M/Unitek wire diameter in measured wire height

is 0.413 mm and the measured wire width is 0.500 mm, the mean value the diameter of

the Dentaurum wire in measured wire height is 0.419 mm and the measured wire width

is 0.510 mm.

Conclusions: There is a significant difference in the mean diameter size in the form of

height and width of the orthodontic wire of 3M/Unitek, Ormco, and Dentaurum

products measured by the size on the packaging."

"Latar Belakang: Resorpsi akar gigi eksternal orthodontically induced inflammatory root resorption/OIIRR memiliki etiologi yang bersifat multifaktorial, salah satunya adalah sistem braket ortodontik. Perkembangan sistem braket di antaranya sistem braket pre-adjusted edgewise appliance PEA dan self-ligating SL pasif. OIIRR hanya dapat dideteksi oleh pemeriksaan radiograf pada tahap lanjut, sehingga dipertimbangkan untuk menggunakan dentin sialoprotein DSP sebagai penanda OIIRR. Tujuan: Analisis OIIRR ditinjau dari perbedaan konsentrasi DSP tahap awal perawatan ortodontik cekat menggunakan sistem braket SL pasif dan PEA. Metode: Dua kelompok eksperimental SL pasif dan PEA serta satu kelompok kontrol terlibat, terdiri dari enam pasien setiap kelompok. Kriteria subjek yaitu iregularitas Little 4-9 mm pada anterior maksila, tanpa karies aktif dan penyakit periodontal. Sampel cairan krevikular gingiva GCF subjek diambil sebelum, serta 3 dan 12 minggu setelah perawatan ortodontik. Konsentrasi DSP sampel GCF kemudian diperiksa menggunakan enzyme-linked immunoabsorbent assay. Hasil: Kedua sistem braket menunjukkan peningkatan konsentrasi DSP yang tidak bermakna p>0.060 pada perawatan ortodontik selama 3 dan 12 minggu. Tidak terdapat perbedaan konsentrasi DSP yang bermakna antar sistem braket pada perawatan ortodontik selama 3 dan 12 minggu p>0.211 . Kesimpulan: Perawatan ortodontik selama 3 dan 12 minggu menggunakan sistem braket SL pasif dan PEA menunjukkan peningkatan konsentrasi DSP yang tidak bermakna.

---

Background: The etiology of orthodontically induced inflammatory root resorption OIIRR is considered to be multifactorial, one of them is bracket system. Passive self ligating SL and preadjusted edgewise appliance PEA bracket systems are most frequently used in recent time. Dentin sialoprotein DSP in gingival crevicular fluid GCF could be suitable for monitoring OIIRR at initial stage.

Aim: Analyzing differences of DSP concentration related to OIIRR after initial orthodontic treatment using passive SL and PEA bracket system.

Methods: Two experimental orthodontic groups passive SL or PEA and one control group, with six patients on each group, were participated in this study. The inclusion criteria Little's irregularity index on maxillary anterior teeth ranging from 4 9 mm, no active dental caries and periodontitis. GCF collection was done at baseline, also at 3 and 12 weeks of orthodontic treatment. DSP concentration in GCF was assessed by enzyme linked immunoabsorbent assay.

Results: Both bracket systems showed insignificant increase of DSP concentration p 0.060 during 3 and 12 weeks of orthodontic treatment. There is no significant difference of DSP concentration between both bracket systems during experimental period p 0.211.

Conclusion: Three and twelve weeks of orthodontic treatment using passive SL and PEA bracket system showed insignificant increase in DSP concentration."

"Fabrikasi mikro telah digunakan untuk berbagai aplikasi di bidang engineering seperti micro gear, micro heat exchanger serta dapat diaplikasikan di bidang biologi dan kedokteran seperti micro needle, micro fluidic, dan bracket orthodontics. Penelitian yang dilakukan yaitu modifikasi permukaan pada material steel SKD 61 dengan metode etching untuk mendapatkan surface roughness kontur kedalaman mesh braket ortodontik menggunakan larutan FeCl3 sebagai etchant dengan berbagai variasi pola pocket lingkaran, pocket persegi channel heksagonal hasil maskless photolithography untuk mengetahui feasibility pembuatan mold braket ortodontik yang sesuai dengan kontur gigi dengan metode etching.Pada penelitian ini didapatkan bahwa secara keseluruhan nilai Ra tiap kenaikan waktu mengalami peningkatan, dengan range nilai Ra pocket yaitu 0,36 m - 0,74 m dan nilai Ra optimum 0,51 m sedangkan untuk channel dengan nilai Ra optimum 0, 63 m hampir mendekati Ra ideal pada braket ortodontik yaitu 0,53 m. Kedalaman optimum pada pocket yaitu 175,4 m dan channel 107,7 m mendekati kedalaman ideal pada braket ortodontik yaitu sebesar 150 m. Untuk nilai MRR dan SMRR tidak memiliki tren yang jelas karena naik dan turun setiap perubahan waktu. Surface yang terbentuk memiliki tren hasil pemakanan yang cenderung menghasilkan bentuk U dengan kondisi tidak mengerucut dibagian atas feasible untuk injection molding namun belum memiliki spesifikasi kontur dan kekasaran yang optimum sehingga metode etching memiliki potensi untuk di aplikasikan ke mold braket ortodontik.

---

Micro fabrication has been used for many application at engineering such as micro gear, micro heat exchanger, also nowadays can be applied at biological or medic such as micro needle, micro fluidic and bracket orthodontics. The objective of research to modify the surface on steel SKD 61 material to get optimum surface roughness contour of mesh using FeCl3 as enchat with various pattern circle pocket, square pocket hexagonal channel of maskless photolithography to know the feasibility of mold bracket orthodontics fabrication that appropiate with teeth contour.From this research, the range of pocket Ra value 0,36 m 0,74 m and optimum Ra value is 0,51 m, then for channel has optimum Ra value 0,63 approxiamtely close to Ra value that needed on bracket orthodontics 0,53 m. The depth of pocket has optimum value 175,4 m, then channel has optimum value 107,7 m close to optimum depth value of bracket orthodontics 150 m. MRR and SMRR value not showing trend of increasing or decreasing specificly. Surface characteristic after etching process disposed to make U shape which has no conical shape on the upper side feasible for injection molding but don rsquo t have spesification of optimum value contour surface roughness, so etching method has potential to be applied on mold bracket otrthodontics."