"Qualitative analysis by using x ray diffraction technique at addition Zr elements to forming of phase in u - Zr alloys. U - Zr alloys represent one of type of uranium alloys which is used as fuel like fuel of training of radioisotope of General Atomic (TRIGA) in the form of U-ZrH, experiment Breeder Reactor (EBR) , integral of fast Reactor (IFR) and others. Making of U - Zr fuel conducted by melting U matal and Zr in arc furnace at variation of Zr content of 2,6,10 and 14% (U - 2Zr,U-6Zr,10Zr and U-14Zr)..."

"Telah dilakukan penelitian tentang analisa tegangan sisa baja rol-temps. Pengujian tegangan sisa dilakukan dengan teknik difraksi sinar- dimana proses pengerolan ini merupakan proses rol-temps. Dalam proses desain dan produksi suatu produk sering terjadi kegagalan dari material tersebut baik sebelum dan saat digunakan. Hal ini karena adanya tegangan sisa yang tidak terhitungkan sebelumnya. Namun tegangan sisa ini tidak selalu merugikan, karena tergantung arahnya beban yang dikenakan. Secara umum adanya tegangan sisa ini lebih sering merugikan. Hasil penelitian menunjukkan bahwa besarnya tegangan sisa juga dipengaruhi perubahan struktur akibat adanya transformasi fasa, walaupun besarnya tegangan sisa akibat rolling pra-tempa relatif kecil Dengan panas anil 700 °C dan waktu tahan 25 menit terlihat penurunan tegangan sisa Puncak-puncak difraksi yang dilaku rol lebih lebar daripada yang tidak dirol. Hal ini menunjukkan regangannya tidak homogen. Dari analisa penghalusan GSAS dapat menggambarkan ketidak homogenan regangan."

"Dual Energy Subtraction (DES) merupakan teknik pencitraan yang memanfaatkan kalsium untuk melemahkan energi foton yang lebih rendah dalam sinar-X yang menghasilkan dua gambar terpisah yaitu jaringan lunak pada dada dan tulang rusuk. Dalam memperoleh citra dari teknik Dual Energy Subtraction (DES) menggunakan radiografi digital dapat dibagi menjadi dua teknik terpisah yaitu single exposure dan double exposure. Studi ini menggunakan fantom Rando yang merepresentasikan anatomi thoraks dengan proyeksi Posterior-Anterior (PA). Dilakukan studi dengan menggunakan double exposure dengan memberikan variasi kombinasi tegangan kVp. Pada pengolahan data subtraksi citra didapatkan hasil yang signifikan pada variasi kombinasi tegangan sebesar 120 kVp dengan 60 kVp. Parameter Signal Difference to Noise Ratio (SDNR) dikalkulasi sebagai parameter kualitas citra yang akan diuji pada studi ini. Pada pengolahan data citra pada fantom Rando anatomi thoraks, nilai SDNR tertinggi pada variasi kombinasi tegangan 120 kVp dengan 60 kVp. Pada hubungan antara SDNR dengan dosis berpengaruh dalam optimasi dosis. Studi ini menunjukkan perlunya penelitian lebih lanjut untuk teknik single exposure dan variasi kombinasi faktor eksposi lain untuk menjadi perbandingan kedua teknik dan keperluan optimasi

---

Dual Energy Subtraction (DES) is an imaging technique that utilizes calcium to attenuate the lower energy photons in X-rays which produce two separate images of soft tissue in the chest and ribs. In obtaining images from the technique Dual Energy Subtraction (DES) using digital radiography it can be divided into two separate techniques, namely single exposure and double exposure. This study uses a Rando phantom which represents the thoracic anatomy with a Posterior-Anterior (PA) projection. Study was double exposure carried out by providing variations in the combination of kVp voltages. In image subtraction data processing, significant results were obtained at the variation of the voltage combination of 120 kVp to 60 kVp. The Signal Difference to Noise Ratio (SDNR) parameter is calculated as the image quality parameter to be tested in this study. In image data processing on the thoracic anatomical Rando phantom, the highest SDNR is at the variation of the voltage combination 120 kVp with 60 kVp. The relationship between SDNR and dose has an effect on dose optimization. This study shows the need for further research on techniques for single exposure and various combinations of other exposure factors to be a comparison of the two techniques and optimization needs"

"One basic problematic aspect in x-ray diffraction phase analysis is microabsorption effect which may arise from the sizeof the crystallite phases. Complication of the problem may intensify in sintered ceramic materials where milling of thesamples is not simple. We report the Rietveld x-ray diffraction phase analysis of MgO-􀁡-Al2O3 powder mixtures withphase content ratio of 1:1 by weight and MgO-Y2O3 sintered ceramic composites with Y2O3 contents of 10%, 20% and30% by weight. The mixtures were pre-sintered at 1000􀂰C for 2 hours and then milled while the composites weresintered at 1550􀂰C for 3 hours. The phase composition analysis was done using Rietica, a non-commercial Rietveldmethod-based software. Relative and absolute phase compositions were examined and results showed that there was asignificant amount of phase composition bias resulted from the examination. For the powder mixture, milling can reducemicroabsorption effect and hence the calculation bias. For the ceramic composite where milling is almost impossible,additional of Y2O3 caused smaller crystallite size of MgO, so that composition bias is smaller in composites with higherY2O3 content. A mathematical model is proposed to provide more acceptable phase composition results."

"Pada penelitian ini, mullite yang disintesis dari aluminum nitrat hidrat [(Al(NO3)3.9H2O] dan sol silika sekam padi dikenakan pada perlakuan sintering dengan suhu 900, 1000, 1100, 1200, dan 1300°C, kemudian dikarakterisasi dengan difraksi sinar-x (XRD) dilanjutkan dengan penghalusan menggunakan metode Rietveld, dan analisis termal diferensial (DTA). Hasil penelitian menunjukkan bahwa dalam sampel yang disintering pada suhu 900°C, tidak ditemukan fasa mullite, tetapi fasa kristobalit dan alumina terdeteksi dengan jelas. Pembentukan mullite baru terjadi pada suhu 1000°C dan bertumbuh dengan peningkatan suhu ditandai dengan kenaikan persen berat (wt%) dari 62,62 menjadi 92,29%, disertai penurunan persen berat kristobalit dari 22,42 menjadi 1,25% dan penurunan persen berat alumina dari 77,58 menjadi 6,46%. Hasil penghalusan menunjukkan korelasi yang baik antara unit sel hasil perhitungan dan hasil pengamatan, dengan dimensi unit sel adalah a = 7,545 nm, b = 7,689 nm dan c = 2,884 nm untuk mullite, a = b = 0,5531 nm, dan c = 0,6923 nm untuk kristobalit, dan a = b = 0,5026 nm, dan c = 1,2808 nm untuk alumina. Hasil analisis dengan DTA menunjukkan bahwa dalam sampel yang tidak disintering, hanya terdapat alumina dan silika, sementara dalam sampel yang disintering terdapat mullite, alumina, dan kristobalit.

---

In this study, mullite synthesized from aluminum nitrate hydrate [(Al(NO3)3.9H2O] and silica sol from rice husk was subjected to sintering treatment at temperatures of 900, 1000, 1100, 1200, and 1300°C, and characterized using x-ray diffraction (XRD), followed by Rietveld refinement, and differential thermal analysis (DTA). The results indicated that in the sample sintered at 900°C, no mullite phase was identified, but crystoballite and alumina were well detected. The formation of mullite started at temperature of 1000°C and continued to grow at higher temperatures, resulted in increased weight percentage (wt%) from 62.62 to 92.29%, while crystoballite and alumina decreased from 22.42 to 1.25% and from 77.58 to 6.46 % respectively. A good correlation was found between the calculated and observed unit cells. For mullite phase, the unit cell dimensions are a = 7.545 nm, b =.689 nm and c = 2.884 nm, for crystoballite a =b = 0.5531 nm and c = 0.6923 nm, and for alumina a = b = 0.5026 nm, and c = 1.2808 nm. The DTA analyses revealed that in the untreated sample, only alumina and silica were detected, while in the sintered samples we found the existence of mullite, alumina, and crystoballite."

"Telah dilakukan pengukuran faktor keluaran (OF) pada berkas sinar-X 6 MV dan 10 MV untuk lapangan terbuka dan dengan menggunakan filter wedge. Lapangan radiasi dibentuk dengan menggunakan MLC. Hasil pengukuran menunjukkan hasil keduanya berbeda. Selain itu dilakukan pula pengukuran pengaruh bentuk lapangan radiasi terhadap intensitas. Dipilih 3 bentuk lapangan yang disesuaikan dengan keperluan klinis dengan luas lapangan dasar 15 x 15 cm2. Pengaruh lapangan pada intensitas yang diakibatkan oleh faktor hamburan dinyatakan sebagai rasio bacaan elektrometer. Untuk lapangan 1 dan 2 berbentuk khusus dengan luas lapangan bervariasi hingga luas 220 cm2. Sedangkan untuk lapangan 3 berbentuk persegi empat panjang yang ditutup blok MLC pada pertengahan lapangan. Luas lapangan juga dibuat bervariasi mulai 75 cm2 hingga 225 cm2. Tidak diperoleh korelasi tertentu antara perubahan lapangan dengan intensitas. Selanjutnya hasil pengukuran dibandingkan dengan kalkulasi hamburan Clarkson dan hasilnya tidak jauh berbeda terutama untuk lapangan kecil. Dilakukan pula pengukuran tambahan untuk mengetahui perbedaan intensitas pada tepi lapangan yang dibentuk dengan MLC dan blok. Hasilnya menunjukkan perbedaan yang tidak signifikan.

---

A measurement has been performed to know the output factors of 6 MV and 10 MV X-ray beam in regular field with and without wedge filters. Radiation field were shaped by using MLC. Both measurement shows different result. The relation between intensity and form of radiation field has also been done. 3 irregular shapes which 15x15 cm2 field was used as a base field size for clinical application were chosen. The influence of field size to intensity that caused by the scatter factor were stated as electrometer reading ratio.The first and second field has a special shape with a vary field size up to 220 cm2. While the third field formed rectangular covered by the MLC block in the center field. And the field size also vary from 75 cm2 to 225 cm2. The result shows no certainty corellation between field size and the intensity. Beyond calculation were made between the measurement result and Clarkson’s scatter factors, and it shows no different result especially in small field. An extra measurement has also been done to find out the difference between intensity in the edge of field using the MLC and regular block. No significant difference were shows in result."

"EDXRF memungkinkan analisis cepat dan tidak merusak baik untuk analisis kuantitatif maupun analisis kualitatif. Analisis XRF kuantitatif dilakukan dengan menggunakan prosedur komparatif, dimana sampel yang tidak diketahui untuk dianalisis dibandingkan dengan sampel yang bertindak sebagai referensi standar. Sebelum melakukan pengukuran, prosedur kalibrasi harus dilakukan. Persiapan spesimen standar untuk kalibrasi harus dilakukan dengan sangat hati-hati dan dengan cara yang sama seperti sampel yang tidak diketahui yang akan diuji. Untuk mendapatkan proses kalibrasi yang tepat, seseorang perlu memahami prinsip-prinsip tentang sinar-X, pengetahuan dasar tentang pengaturan khusus instrumen, dan beberapa teori tentang metode pengujian. Sifat fisik sampel dan beberapa pengaturan khusus instrumen, seperti sumber sinar-X, voltase daya tabung yang diterapkan, atau waktu pengukuran, dapat memengaruhi jumlah elemen yang diukur dengan pemindaian XRF. Proses kalibrasi akan membentuk kurva kalibrasi yang akan digunakan alat untuk menghitung analisis unsur. Jika terjadi kesalahan selama proses kalibrasi, kesalahan tersebut dapat memengaruhi pengukuran sampel yang tidak diketahui nantinya. Tesis ini dilakukan untuk meningkatkan akurasi mesin EDXRF yang tersedia di lab ST dengan memodifikasi kondisi pengujian dan mengubah energi mesin, untuk menghasilkan kondisi pengukuran terbaik meskipun dengan keterbatasan mesin. Dengan demikian, tugas akhir ini bertujuan untuk mendapatkan kondisi yang dapat menghasilkan pengukuran yang paling akurat pada baja.

---

EDXRF enables quick and non destructive analysis for both quantitative analysis or qualitative analysis. Quantitative XRF analysis is accomplished using a comparative procedure, where the unknown samples to be analyzed are compared with samples that act as standard references. Before conducting the measurement, a calibration procedure must be performed. The preparation of the standard specimens for calibration must be carried out with great care and in the same manner as the unknown sample that will be tested. In order to obtain a proper calibration process, one needs to understand the principles regarding X-rays, basic knowledge regarding the instrument-specific settings, and several theories regarding the methods of testing. Physical properties of the sample and several instrument-specific settings, such as the X-ray source, applied voltage of the tube power, or measurement time, can affect the element counts measured by scanning XRF. The calibration process will form a calibration curve, which the instrument will use to calculate the elemental analysis. If errors occur during the calibration process, they can affect the measurement of the unknown sample later. This thesis is conducted to improve the accuracy of an EDXRF machine that is available at the ST lab by modifying the test conditions and altering the machine energy, to generate the best measurement condition despite the limitations of the machine. By doing so, this bachelor's thesis aims to obtain conditions that could produce the most accurate measurements on steel."