"Penelitian ini membuat karbon aktif dari limbah kulit kopi karena sampai saat ini pemanfaatan limbah kulit kopi belum maksimum. Aktivasi yang digunakan adalah aktivasi kimia menggunakan Kalium Karbonat karena berdasarkan penelitian-penelitian sebelumnya, luas permukaan yang dihasilkan dapat bersaing dengan activating agent lain. Variasi yang dilakukan adalah variasi rasio massa activating agent/massa bahan baku 1/1, 3/2, dan 2/1 dan variasi suhu 600°C, 700°C, dan 800°C. Luas permukaan diperoleh dari konversi bilangan iod dengan hasil tertinggi adalah 891 m2/gram yang didapatkan dari suhu aktivasi 800°C dan rasio impregnasi 3/2. Sebagai pembanding, luas permukaan yang diperoleh dari aktivasi fisika menggunakan CO2 adalah 176 m2/gram.

---

This research aims to produce activated carbon from coffee shell waste due to utilization of coffee shell waste that far from maximum. Activation that will be used in this research is chemical activation using Potassium Carbonate because in previous researches show that surface area obtained by this activating agent can compete with other activating agent. The variation in this research is impregnation ratio and temperature. The impregnation ratio is 1/1, 3/2, and 2/1 while the temperature variation is 600°C, 700°C, and 800°C. The surface area is obtained by conversion of iod number with the highest result is 891 m2/gram which produced at temperature 800°C and impregnation ratio 3/2. Physical activation using CO2 is done for comparison and obtains surface area 176 m2/gram."

"Pada penelitian ini dilakukan produksi karbon aktif berbahan baku jerami padi dengan karbonisasi dan dilanjutkan dengan aktivasi kimia menggunakan K2CO3. Penelitian ini bertujuan untuk menganalisis pengaruh lama waktu dan suhu aktivasi pada tahap aktivasi kimia terhadap luas permukaan karbon aktif. Proses aktivasi dilakukan pada variasi suhu 700°C, 800°C, 900°C dan lama waktu aktivasi divariasikan selama 60 menit, 90 menit, dan 120 menit. Hasil yang diperoleh menunjukkan bahwa peningkatan suhu dan lama waktu aktivasi menyebabkan luas permukaan terus mengalami peningkatan hingga suhu aktivasi 900oC dan lama waktu selama 90 menit. Luas permukaan karbon aktif tertinggi sebesar 1.003 m2/g diperoleh dengan aktivasi pada suhu 900oC dan lama waktu selama 90 menit. Activated carbon from rice straw waste is produced in this research with carbonization and followed by chemical activation using potassium carbonate. This research aims to analyze the effect of duration and temperature in activation process. The activation process is held in 700°C, 800°C, 900°C of temperature and 60, 90 and 120 minutes of duration. It shows that surface area is increased by the increasing of activation temperature and duration except the activated carbon with 900°C of activation temperature and 120 minutes of activation duration. Highest surface area is 1,003 m2/g from activated carbon with 900°C of activation temperature and 90 minutes of activation duration."

"Penelitian ini membahas produksi karbon aktif berbahan baku bambu dengan metode aktivasi menggunakan larutan KOH pada suasana gas nitrogen untuk mengontrol pembentukan pori karbon aktif. Aktivasi kimia dilakukan dengan rasio massa KOH : massa karbon yaitu 3:1 pada suhu 600°C, 700°C, dan 800°C selama 30 menit dan 60 menit. Sebagai pembanding dilakukan aktivasi fisika tanpa penambahan activating agent pada suhu 700°C selama 60 menit. Luas permukaan paling tinggi sebesar 802,60 mg/g (sekitar 824,83 m2/g) diperoleh dari aktivasi kimia selama 30 menit pada suhu 800°C, sedangkan luas permukaan paling rendah sebesar 283,39 mg/g (sekitar 291,23 m2/g) diperoleh dari aktivasi fisika.

---

This research is about production of activated carbon made from raw bamboo with activation method using KOH as activating agent in an atmosphere of nitrogen gas to control pores formed in the activated carbon. Chemical activation was done with mass ratio of activating agent : carbon is 3:1 on 600°C, 700°C, and 800°C for 30 minutes and 60 minutes, and physical activation was done without using activating agent on 700°C for 60 minutes. The highest surface area, 802,60 mg/g (about 824,83 m2/g), was obtained by KOH activation on 800°C for 30 minutes, and the lowest, 283,39 mg/g (about 291,23 m2/g), was obtained by physical activation."

"Optimasi adalah disiplin ilmu yang digunakan untuk mencari nilai optimal dalam suatu fungsi. Ilmu ini banyak digunakan untuk mengurangi biaya dan waktu dalam meneliti suatu eksperimen agar diperoleh hasil yang terbaik. Penelitian ini bertujuan untuk memperoleh kondisi proses optimal untuk memaksimalkan luas permukaan dan yield. Bahan baku yang digunakan adalah ampas kopi, tempurung kelapa, dan polyethylene terephthalate (PET). Metode aktivasi yang digunakan adalah aktivasi fisika-kimia dengan senyawa aktivasi KOH, NaOH, H3PO4, dan K2CO3. Penentuan kondisi optimal dilakukan dengan metode respons permukaan (RSM) tipe Box-Behnken Design (BBD). Model yang diperoleh dianalisis menggunakan uji ANOVA dan uji residual. Hasil RSM berupa plot kontur dan permukaan yang digunakan untuk megetahui wilayah kondisi optimum serta analisa pengaruh faktor terhadap respons. Nilai kondisi optimum ditentukan menggunakan Response Optimizer dan diperoleh hasil bahwa sintesis karbon aktif dari ampas kopi dengan senyawa KOH, NaOH, H3PO4, dan K2CO3 terjadi ketika rasio impregnasi 1,00-1,37, suhu aktivasi 600-800°C, dan waktu aktivasi 60-120 menit. Sintesis optimal dari tempurung kelapa terjadi ketika rasio impregnasi 1,00-3,00, suhu aktivasi 647-808°C, dan waktu aktivasi 70-120 menit. Sintesis optimal dari PET terjadi ketika rasio impregnasi 1,00-2,80, suhu aktivasi 700-800°C, dan waktu aktivasi 109-120 menit.

---

Optimization is a discipline to obtain the best value of a function. This study is used to minimize research cost and time. This research is done to achieve the optimum condition of process conditions for maximum surface area and yield of activated carbon. The precursors used in this research are waste coffee, coconut shell, and polyethylene terephthalate (PET). The type of activation method used is physical-chemical activation with KOH, NaOH, H3PO4, and K2CO3 as activating agents. To determine the optimum condition, this research use Response Surface Method (RSM) with Box-Behnken Design (BBD). The resulting model is tested using ANOVA analysis and the residual test. When the model passes the test, plot contours and surfaces achieved can be analyzed to determine the optimum area and the behavior of factors and responses. Response Optimizer option is used to determine the optimum value. Results show that synthesis of activated carbon using waste coffee and activating agents KOH, NaOH, H3PO4, and K2CO3 are optimized when impregnation ratio is 1.00-1.37, temperature is 600-800°C, and activation time 60-120 minutes. Synthesis from coconut shell is optimized when impregnation ratio is 1.00-3.00, temperature is 647-808°C, and activation time 70-120 minutes. Synthesis from PET is optimized when impregnation ratio is 1.00-2.80, temperature is 700-800°C, and activation time 109-120 minutes."

"Pada penelitian pembuatan karbon aktif dari bambu ini digunakan metode aktivasi kimia dengan menggunakan variasi activating agent, yakni H3PO4 dan KOH dengan rasio massa activating agent/massa karbon 1/1, 2/1, dan 3/1. Aktivasi dilakukan pada temperatur 700oC selama 1 jam. Luas permukaan tertinggi yang direpresentasikan dengan bilangan iodin sebesar 772,08 mg/g diperoleh dengan aktivasi menggunakan H3PO4 dengan rasio massa activating agent/massa karbon 3/1, sedangkan aktivasi menggunakan KOH diperoleh bilangan iodin tertinggi sebesar 744,92 mg/g dengan rasio massa activating agent/massa karbon 3/1. Sebagai pembanding, juga dilakukan pembuatan karbon aktif dengan metode aktivasi fisika dan diperoleh bilangan iodin karbon aktif sebesar 283,38 mg/g.

---

This research aims to produce activated carbon from bamboo as the raw materials. In this research controlled by the activation method using variation of activating agent, H3PO4 and KOH with a mass ratio of activating agent/carbon mass are 1/1, 2/1, and 3/1. It also performed at 700°C activation temperature for 1 hour. The highest iodine number of 772.08 mg/g obtained by activation using H3PO4 with a mass ratio of activating agent/carbon mass 3/1, whereas activation with KOH obtained the highest iodine number of 744.92 mg/g with a mass ratio of activating agent/carbon mass 3/1. For comparison, the study was also carried out the manufacture of activated carbon by physical activation method and the iodine number of activated carbon obtained at 283.38 mg/g."

"Dalam penelitian ini dilakukan pembuatan karbon aktif yang berbahan baku dari cangkang sawit dan melihat pengaruh aktivasi kimia dan fisika terhadap sifat karbon aktif yang dihasilkan. Karbonisasi dilakukan pada suhu 400oC. Pada aktivasi kimia digunakan aktivator H3PO4 4M , sedangkan pada aktivasi fisika digunakan aliran gas N2 dan gas CO2 yang laju alirnya divariasikan ( 100 mL/menit, 200 mL/menit, 300 mL/menit dan 400 mL/menit). Karakterisasi karbon aktif yang dipelajari dalam penelitian ini adalah rendemen, kadar air, kadar zat mudah menguap, kadar abu dan bilangan iodin. Hasil penelitian menunjukkan bahwa karbon aktif terbaik berdasarkan daya jerap iodinnya adalah karbon yang mengalami aktivasi kimia (perendaman H3PO4) dan aktivasi fisika dengan menggunakan gas N2 dengan laju alir sebesar 100 mL/menit dilanjutkan gas CO2 dengan laju alir sebesar 200 mL/menit. Karbon ini memiliki bilangan iodin sebesar 678,15 mg/g dengan rendemen sebesar 63,02%, kadar air 14,11%, kadar zat mudah menguap 28,57%, dan kadar abu 4,17%.

---

In this research be held the making of activated carbon by using palm empty bunches (PEB) as the primery ingredients and to see the effect of chemical and physical activation towards the condition of activated carbon produced. Carbonization is done in the temperature of 400oC. In the chemical activation H3PO4 4M is used as activator, meanwhile, in physical activation N2 and CO2 gases is used while varying the speed of flow (100 mL/min, 200 mL/min, 300 mL/min and 400 mL/min). The characteristic of activated carbon that will be studied in this research is yield, humidity, volatile matter, percentage of ash and iodin number.

The result shows that the best activated carbon is based on the iodin number is the carbon that have been through the chemical activation ( H3PO4 soaking) and physical activation by using N2 gas with the speed of flow 200 ml/min. This carbon has the iodin number for 678.15 mg/g with yield 63.02%, water content 14.11%, volatile matter 28.57%, and ash content 4.17%."

"Pada penelitian ini dilakukan produksi karbon aktif untuk keperluan medis dengan bahan baku kulit kacang menggunakan K2CO3 sebagai activating agent. Pengaruh suhu dan durasi aktivasi terhadap luas permukaan dan daya adsorpsi karbon aktif dianalisis. Proses aktivasi dilakukan pada variasi suhu 600°C, 700°C, 800°C dan durasi aktivasi pada variasi 60, 90, dan 120 menit. Luas permukaan karbon aktif yang direpresentasikan dengan Bilangan iodin dan daya adsorpsi terhadap methylene bluetertinggi adalah sebesar 1095 m2/g dan 299 mg/gdiperoleh pada suhu aktivasi 800°C selama 120 menit. Dibandingkan dengan indeks standar dari Depkes Indonesia dan United States Pharmacopeia, medicinal activated carbon dari kulit kacang ini mampu memenuhi standar kualitas Bilangan iodin dan daya adsorpsi terhadap methylene blue untuk digunakan dalam dunia medis.

---

This research aims to produce activated carbon for medicinal use from peanut shell using K2CO3 as an activating agent. The influence of the activation temperature and activation time on the surface area and Methylene Blue adsorpsion capacity was studied. The activation temperature was varied at 600°C, 700°C, and 800°C, and activation time was varied at 60, 90, and 120 minutes. The highest surface area represented by Iodine number and adsorptive capacity of methylene blue was 1095 m2/g and 299 mg/g, obtained by activation temperature of 800°C and activation time of 120 minutes. Compared with the quality index of Depkes Indonesia and United States Pharmacopeia standards, this peanut shellbased medicinal activated carbon fulfiled Iodine number and adsorptive power of methylene blue quality to be used for medicinal use"

"Tempurung kelapa dipilih menjadi bahan dasar adsorben pada masker dalam menyerap gas CO2 karen memiliki kandungan selulosa sebesar 26,60 , kandungan hemiselulosa 27,70 dan kandungan lignin sebesar 29,40 serta produksinya yang tinggi 61 juta ton atau 33,94 dari produksi dunia. Metode aktivasi tempurung kelapa dilakukan secara fisika menggunakan CO2 pada suhu 850 0C, dan secara kimia dengan ZnCl2 pada suhu 80 0C dilanjutkan dengan pirolisis menggunakan N2 pada suhu 650 0C. Karakterisasi yang digunakan adalah BET untuk mengetahui luas permukaan karbon aktif.Melalui uji BET didapatkan luas permukaan karbon teraktivasi kimia sebesar 432,26 m2/g dan yang teraktivasi fisika sebesar 323,57 m2/g. Selanjutnya kapasitas adsorpsi masker karbon aktif diuji pada ruang kompartemen dengan mengalirkan campuran gas CO2 dan udara selama satu jam, lalu mengukur perbedaan konsentrasi CO2 masukan dan keluaran dengan CO2 detector.Berdasarkan hasil uji adsorpsi polutan, didapatkan bahwa variasi terbaik adalah masker dengan massa karbon aktif 6 gram, teraktivasi kimia, dan dengan menggunakan perekat TEOS yang mampu mengadsorpsi polutan CO2 sebesar 76,52 . Masker yang dibuat pada penelitian ini memliki waktu jenuh selama empat jam pada kondisi konsentrasi CO2 yang tinggi.

---

Adsorbent in mask to absorb CO2 gas because it has cellulose content of 26.60 , hemicellulose content 27.70 and lignin content of 29.40 and its production is 61 million ton or 33.94 of world production. The method of coconut shell activation was done physically using CO2 at 850 0C, and chemically with ZnCl2 at 80 0C followed by pyrolysis using N2 at 650 0C. The characterization used is BET to measure surface area of activated carbon.

Through BET test, it was found that the chemical activated carbon surface area is 432.26 m2 g and the physical activation is 323.57 m2 g. Furthermore, the adsorption capacity of the activated carbon mask is tested in the compartment chamber by flowing a mixture of CO2 and air for an hour, then measuring the CO2 input and output CO2 difference using CO2 detector.

Based on the results of adsorption test, it was found that the best variation is a mask with 6 gram active carbon mass, chemical activated, and by using TEOS as adhesive capable of adsorbing CO2 pollutant by 76.52 . Mask made in this research has saturated time for four hours under high CO2 concentration conditions."

"Penelitian ini merupakan salah satu bentuk pemanfaatan limbah agrikultur yang melimpah di Indonesia sehingga limbah ini akan mendapatkan peningkatan nilai guna. Tujuan penelitian ini adalah untuk mendapatkan karbon aktif fisik dan mengetahui kondisi optimum pembuatan karbon aktif. Bahan baku pembuatan karbon aktif ini adalah bagas tebu yang merupakan limbah pabrik gula. Beberapa metode yang sudah pernah dilakukan terhadap bahan baku ini dalam pembuatan karbon aktif adalah aktivasi thermal N2 dan kimia dengan berbagai activating agent, tetapi aktivasi dengan aliran gas karbon dioksida belum pernah dilakukan. Penelitian ini menghasilkan sembilan sampel karbon aktif dengan variasi laju alir karbon dioksida 300, 400, dan 500 cc/mnt dan variasi waktu aktivasi 30, 60, dan 120 menit dengan temperatur 900oC. Kondisi operasi optimum pada variabel penelitian ini didapatkan pada laju alir 500 cc/mnt selama 120 menit dengan mendapatkan luas permukaan karbon aktif yang direpresentasikan dengan daya serap iod sebesar 769.5 mg/g. Hubungan variabel yang ditemukan adalah semakin besar laju alir gas karbon dioksida dan/atau semakin lama waktu aktivasi akan memperbesar luas permukaan karbon aktif. Luas permukaan karbon aktif ini lebih besar daripada karbon aktif aktivasi thermal N2, tetapi lebih kecil dari aktivasi kimia KOH.

---

This research is a form of utilization of agricultural industry wastes so that the waste can gain significant enhancement of value. Purposes of this research is to get the physical condition of activated carbon and knowing the optimum condition to make the activated carbon. The agricultural industry waste that is used in the research is sugarcane bagasse that is waste of sugar industry. Researches that has been done with sugarcane bagasse is using physics activation of N2 and chemical activation using various activating agent, but the method in this research is activation using carbon dioxide gas flow that hasn't been done with this raw material.

The target is this research manufacture nine samples that are consists of variation of carbon dioxide gas flow 300, 400, and 500 cc/minute and activation time 30, 60, and 120 minutes at temperature 900oC. The optimum operating condition reached at 500 cc/minute gas flow and 120 minutes activation time that give an activated carbon with surface area that is represented by iod adsorption 769.5 mg/g. Correlation between this two free variables are the more fast carbon dioxide gas flow and/or more long activation time makes the larger activated carbon surface area. Surface area of the activated carbon in this research is bigger than physics activation of N2, but smaller than chemical activation using KOH."

"Saat ini energi dianggap sebagai kebutuhan utama di dunia. Sayangnya, energi dari bahan bakar fosil menghasilkan karbon dioksida dalam jumlah besar sehingga meningkatkan efek rumah kaca di dunia ini. Untuk mengatasi masalah ini, banyak negara berkembang telah mengkonversi bahan bakar fosil ke gas alam. Selanjutnya, gas alam masih mengandung zat pengotor, sehingga pemurnian gas alam dari zat pengotor sangat penting. Penelitian ini akan membangun simulasi pemurnian yang dicapai dengan dua simulasi yang berbeda. Pada simulasi pertama komponen akan terdiri dari metana, nitrogen dan karbon dioksida dengan persentase komposisi 80% metana dan 10% dari karbon dioksida dan nitrogen masing-masing. Simulasi kedua akan terjadi tanpa nitrogen dan dengan persentase 80% metana dan 20% dari karbon dioksida. Hasil penelitian menunjukkan bahwa karbon dioksida dapat terserap awal 50%. Di sisi lain metana tidak dapat dimurnikan dengan baik ketika ada nitrogen ada dalam proses adsorpsi.

---

Nowadays energy is considered as primary requirement in the world. Unfortunately, the energy from fossil fuel emits large number of carbon dioxide increasing the greenhouse effect in this world. In order to overcome this problem, many develop countries are converting fossil fuel into natural gas. Furthermore, natural gas is still occupied with impurities, therefore purification of Natural gas from impurities are very important.

This study observed the purification simulation process which attained with two different run. The first run components were consists of methane, nitrogen and carbon dioxide with percentage composition 80% of methane and 10% of carbon dioxide and 10 % nitrogen respectively. The second run occurred without nitrogen and with percentage 80% of methane and 20% of carbon dioxide. Result show that carbon dioxide can be adsorbed nearly 50 %. On the other hand methane cannot be well purified when there is nitrogen exist in the adsorption process."