"Pada penelitian ini dilakukan produksi karbon aktif berbahan baku jerami padi dengan karbonisasi dan dilanjutkan dengan aktivasi kimia menggunakan K2CO3. Penelitian ini bertujuan untuk menganalisis pengaruh lama waktu dan suhu aktivasi pada tahap aktivasi kimia terhadap luas permukaan karbon aktif. Proses aktivasi dilakukan pada variasi suhu 700°C, 800°C, 900°C dan lama waktu aktivasi divariasikan selama 60 menit, 90 menit, dan 120 menit. Hasil yang diperoleh menunjukkan bahwa peningkatan suhu dan lama waktu aktivasi menyebabkan luas permukaan terus mengalami peningkatan hingga suhu aktivasi 900oC dan lama waktu selama 90 menit. Luas permukaan karbon aktif tertinggi sebesar 1.003 m2/g diperoleh dengan aktivasi pada suhu 900oC dan lama waktu selama 90 menit. Activated carbon from rice straw waste is produced in this research with carbonization and followed by chemical activation using potassium carbonate. This research aims to analyze the effect of duration and temperature in activation process. The activation process is held in 700°C, 800°C, 900°C of temperature and 60, 90 and 120 minutes of duration. It shows that surface area is increased by the increasing of activation temperature and duration except the activated carbon with 900°C of activation temperature and 120 minutes of activation duration. Highest surface area is 1,003 m2/g from activated carbon with 900°C of activation temperature and 90 minutes of activation duration."

"Penelitian ini membuat karbon aktif dari limbah kulit kopi karena sampai saat ini pemanfaatan limbah kulit kopi belum maksimum. Aktivasi yang digunakan adalah aktivasi kimia menggunakan Kalium Karbonat karena berdasarkan penelitian-penelitian sebelumnya, luas permukaan yang dihasilkan dapat bersaing dengan activating agent lain. Variasi yang dilakukan adalah variasi rasio massa activating agent/massa bahan baku 1/1, 3/2, dan 2/1 dan variasi suhu 600°C, 700°C, dan 800°C. Luas permukaan diperoleh dari konversi bilangan iod dengan hasil tertinggi adalah 891 m2/gram yang didapatkan dari suhu aktivasi 800°C dan rasio impregnasi 3/2. Sebagai pembanding, luas permukaan yang diperoleh dari aktivasi fisika menggunakan CO2 adalah 176 m2/gram.

---

This research aims to produce activated carbon from coffee shell waste due to utilization of coffee shell waste that far from maximum. Activation that will be used in this research is chemical activation using Potassium Carbonate because in previous researches show that surface area obtained by this activating agent can compete with other activating agent. The variation in this research is impregnation ratio and temperature. The impregnation ratio is 1/1, 3/2, and 2/1 while the temperature variation is 600°C, 700°C, and 800°C. The surface area is obtained by conversion of iod number with the highest result is 891 m2/gram which produced at temperature 800°C and impregnation ratio 3/2. Physical activation using CO2 is done for comparison and obtains surface area 176 m2/gram."

"Penelitian ini membahas produksi karbon aktif berbahan baku bambu dengan metode aktivasi menggunakan larutan KOH pada suasana gas nitrogen untuk mengontrol pembentukan pori karbon aktif. Aktivasi kimia dilakukan dengan rasio massa KOH : massa karbon yaitu 3:1 pada suhu 600°C, 700°C, dan 800°C selama 30 menit dan 60 menit. Sebagai pembanding dilakukan aktivasi fisika tanpa penambahan activating agent pada suhu 700°C selama 60 menit. Luas permukaan paling tinggi sebesar 802,60 mg/g (sekitar 824,83 m2/g) diperoleh dari aktivasi kimia selama 30 menit pada suhu 800°C, sedangkan luas permukaan paling rendah sebesar 283,39 mg/g (sekitar 291,23 m2/g) diperoleh dari aktivasi fisika.

---

This research is about production of activated carbon made from raw bamboo with activation method using KOH as activating agent in an atmosphere of nitrogen gas to control pores formed in the activated carbon. Chemical activation was done with mass ratio of activating agent : carbon is 3:1 on 600°C, 700°C, and 800°C for 30 minutes and 60 minutes, and physical activation was done without using activating agent on 700°C for 60 minutes. The highest surface area, 802,60 mg/g (about 824,83 m2/g), was obtained by KOH activation on 800°C for 30 minutes, and the lowest, 283,39 mg/g (about 291,23 m2/g), was obtained by physical activation."

"Adsorpsi umumnya dapat digunakan untuk penghilangan bau, warna, gas beracun, dan sebagainya. Adsorben yang umum dan banyak digunakan adalah karbon aktif. Penelitian ini bertujuan untuk menghasilkan karbon aktif dari bambu betung sebagai bahan baku. Pemilihan bambu betung ini dikarenakan bambu betung merupakan tanaman yang sangat banyak ditemukan di Indonesia dan jumlahnya cukup berlimpah. Selain itu, bambu betung kaya akan kandungan karbon sehingga memiliki kriteria untuk dijadikan bahan baku pembuatan karbon aktif. Penelitian ini menggunakan gas CO2 sebagai aktivator dengan melakukan variasi temperatur aktivasi, 800°C, 850°C, 900°C dan variasi laju alir gas CO2 200 mL/menit, 300 mL/menit, 400 mL/menit. Aktivasi dilakukan selama 1 jam. Bilangan iod tertinggi sebesar 475,25 mg/g diperoleh dengan melakukan variasi temperatur aktivasi 900°C dan laju alir CO2 400 ml/menit. Sebagai pembanding, pada penelitian ini juga dilakukan pengujian bilangan iod terhadap karbon bambu sebelum aktivasi. Bilangan iod untuk karbon ini adalah 190,12 mg/g.

---

Adsorption generally can be used for removal of odors, colors, toxic gases, etc. Adsorbent that common used is activated carbon. This research purpose to produce activated carbon from betung bamboo as raw material. The selection of betung bamboo as raw material because betung bamboo is a plant that very common in Indonesia and is quite abundant. In addition, betung bamboo has rich carbon content so that it has the criteria to be used as raw materials for activated carbon. This research using CO2 as an activator by varying the activation temperature, 800°C, 850°C, 900°C and variations of flow rate 200 mL/min, 300 mL/min, 400 mL/min. Activation is done for 1 hour. Highest iodine number is 475,25 mg/g by varying the activation temperature 900°C and CO2 flow rate is 400 mL/min. In comparing, this research also test for iodine number of carbon before activation. Iodine number for this sample is 190,12 mg/g."

"Adsorpsi dapat digunakan untuk menangani permasalahan limbah industri di Indonesia Karbon aktif merupakan adsorben yang sangat baik untuk proses adsorpsi Hasil uji analisis ultimate menunjukkan tandan kosong kelapa sawit mengandung 48 79 karbon sehingga memiliki potensi sebagai bahan baku karbon aktif Pembuatan karbon aktif berbahan baku tandan kosong kelapa sawit telah dilakukan dengan activating agent KOH di bawah aliran nitrogen murni selama 15 menit dan menghasilkan luas area 807 54 gram Foo dan Hameed 2010 Tujuan dari penelitian ini adalah menghasilkan karbon aktif dengan luas permukaan yang lebih besar dari 807 54 gram dengan variasi activating agent yang digunakan dan waktu aktivasi sehingga akan diketahui kombinasi activating agent dan waktu aktivasi terbaik terhadap pembentukan luas permukaan karbon aktif Activating agent yang akan digunakan adalah dan sedangkan waktu aktivasi yang digunakan adalah 60 menit dan 120 menit Aktivasi dilakukan pada suhu 700 dengan mengalirkan gas dengan laju 300 ml menit.

---

Adsorption can be used to handle indrustial waste problem in Indonesia Activated carbon is an excellent adsorbent for adsorption process The results of ultimate analysis showed oil palm empty fruit bunch contains 48 79 of carbon so it has the potential as the raw material of activated carbon Preparation of activated carbon made from palm empty fruit bunch has been carried out with KOH activator under a stream of pure nitrogen for 15 minutes and resulted in 807 54 gram of surface area Foo and Hameed 2010 The purpose of this research is to produce activated carbon with a surface area which is more than 807 54 gram by using the variation of activating agent and activation time to know the best combination of activating agent and activation time for the formation of the surface area Acivating agents used in this research were and while the activation times were 60 and 120 minutes Activation proceed at 700 under flow of 300 ml min"

"Peningkatan konsentrasi CO2 di atmosfer memberikan dampak kenaikan suhu dan perubahan iklim. Adsorpsi dengan adsorben merupakan pemisahan CO2 yang memiliki konsumsi energi dan biaya yang rendah. Karbon aktif dipilih sebagai adsorben karena memiliki kapasitas adsorpsi CO2 yang lebih baik pada tekanan atmosfer dan suhu yang tinggi. Ranting tanaman teh dapat dimanfaatkan sebagai bahan baku pembuatan karbon aktif karena memiliki kandungan karbon yang tinggi yaitu 53%. Penelitian ini dilakukan untuk mendapatkan pengaruh pembuatan karbon aktif dari ranting teh melalui karbonisasi 400°C selama 1 jam menggunakan gas N2, dan aktivasi fisika pada suhu aktivasi yang divariasikan, yaitu 600, 700, dan 800°C selama 4 menit dengan pemanfaatan alat APS (arc plasma sintering), terhadap pembentukan pori, luas permukaan, pembentukan gugus fungsi, serta struktur dan ukuran kristal. Karakterisasi karbon aktif didapatkan melalui SEM, BET, FTIR, dan XRD. Kemudian, melalui alat TPD-CO2, jumlah kapasitas adsorpsi CO2 pada karbon aktif dari ranting teh dapat terukur. Melalui proses karbonisasi dan aktivasi fisika, didapatkan karbon aktif dengan luas permukaan 86,668 m2/g dan kapasitas adsorpsi 2,057 mmol/g yang optimal pada suhu aktivasi fisika 800°C.

---

Increasing CO2 concentrations in the atmosphere have an impact on rising temperatures and climate change. Adsorption with adsorbents is a CO2 separation that has low energy consumption and costs. Activated carbon was chosen as an adsorbent because it has better CO2 adsorption capacity at atmospheric pressure and high temperature. Tea plant twigs can be used as raw material for making active carbon because they have a high carbon content, namely 53%. This research was conducted to obtain the effect of making activated carbon from tea twigs through carbonization at 400°C for 1 hour using N2 gas, and physical activation at varied activation temperatures, namely 600, 700, and 800°C for 4 minutes using the APS (arc plasma sintering), on pore formation, surface area, formation of functional groups, as well as crystal structure and size. Characterization of activated carbon was obtained through SEM, BET, FTIR, and XRD. Then, using the TPD-CO2, the amount of CO2 adsorption capacity on activated carbon from tea twigs can be measured. Through the carbonization and physical activation process, activated carbon was obtained with a surface area of 86,668 m2/g and an adsorption capacity of 2,057 mmol/g which was optimal at a physical activation temperature of 800°C."

"Penelitian ini merupakan salah satu bentuk pemanfaatan limbah agrikultur yang melimpah di Indonesia sehingga limbah ini akan mendapatkan peningkatan nilai guna. Tujuan penelitian ini adalah untuk mendapatkan karbon aktif fisik dan mengetahui kondisi optimum pembuatan karbon aktif. Bahan baku pembuatan karbon aktif ini adalah bagas tebu yang merupakan limbah pabrik gula. Beberapa metode yang sudah pernah dilakukan terhadap bahan baku ini dalam pembuatan karbon aktif adalah aktivasi thermal N2 dan kimia dengan berbagai activating agent, tetapi aktivasi dengan aliran gas karbon dioksida belum pernah dilakukan. Penelitian ini menghasilkan sembilan sampel karbon aktif dengan variasi laju alir karbon dioksida 300, 400, dan 500 cc/mnt dan variasi waktu aktivasi 30, 60, dan 120 menit dengan temperatur 900oC. Kondisi operasi optimum pada variabel penelitian ini didapatkan pada laju alir 500 cc/mnt selama 120 menit dengan mendapatkan luas permukaan karbon aktif yang direpresentasikan dengan daya serap iod sebesar 769.5 mg/g. Hubungan variabel yang ditemukan adalah semakin besar laju alir gas karbon dioksida dan/atau semakin lama waktu aktivasi akan memperbesar luas permukaan karbon aktif. Luas permukaan karbon aktif ini lebih besar daripada karbon aktif aktivasi thermal N2, tetapi lebih kecil dari aktivasi kimia KOH.

---

This research is a form of utilization of agricultural industry wastes so that the waste can gain significant enhancement of value. Purposes of this research is to get the physical condition of activated carbon and knowing the optimum condition to make the activated carbon. The agricultural industry waste that is used in the research is sugarcane bagasse that is waste of sugar industry. Researches that has been done with sugarcane bagasse is using physics activation of N2 and chemical activation using various activating agent, but the method in this research is activation using carbon dioxide gas flow that hasn't been done with this raw material.

The target is this research manufacture nine samples that are consists of variation of carbon dioxide gas flow 300, 400, and 500 cc/minute and activation time 30, 60, and 120 minutes at temperature 900oC. The optimum operating condition reached at 500 cc/minute gas flow and 120 minutes activation time that give an activated carbon with surface area that is represented by iod adsorption 769.5 mg/g. Correlation between this two free variables are the more fast carbon dioxide gas flow and/or more long activation time makes the larger activated carbon surface area. Surface area of the activated carbon in this research is bigger than physics activation of N2, but smaller than chemical activation using KOH."

"Pada penelitian pembuatan karbon aktif dari bambu ini digunakan metode aktivasi kimia dengan menggunakan variasi activating agent, yakni H3PO4 dan KOH dengan rasio massa activating agent/massa karbon 1/1, 2/1, dan 3/1. Aktivasi dilakukan pada temperatur 700oC selama 1 jam. Luas permukaan tertinggi yang direpresentasikan dengan bilangan iodin sebesar 772,08 mg/g diperoleh dengan aktivasi menggunakan H3PO4 dengan rasio massa activating agent/massa karbon 3/1, sedangkan aktivasi menggunakan KOH diperoleh bilangan iodin tertinggi sebesar 744,92 mg/g dengan rasio massa activating agent/massa karbon 3/1. Sebagai pembanding, juga dilakukan pembuatan karbon aktif dengan metode aktivasi fisika dan diperoleh bilangan iodin karbon aktif sebesar 283,38 mg/g.

---

This research aims to produce activated carbon from bamboo as the raw materials. In this research controlled by the activation method using variation of activating agent, H3PO4 and KOH with a mass ratio of activating agent/carbon mass are 1/1, 2/1, and 3/1. It also performed at 700°C activation temperature for 1 hour. The highest iodine number of 772.08 mg/g obtained by activation using H3PO4 with a mass ratio of activating agent/carbon mass 3/1, whereas activation with KOH obtained the highest iodine number of 744.92 mg/g with a mass ratio of activating agent/carbon mass 3/1. For comparison, the study was also carried out the manufacture of activated carbon by physical activation method and the iodine number of activated carbon obtained at 283.38 mg/g."

"Dalam penelitian ini dilakukan pembuatan karbon aktif yang berbahan baku dari cangkang sawit dan melihat pengaruh aktivasi kimia dan fisika terhadap sifat karbon aktif yang dihasilkan. Karbonisasi dilakukan pada suhu 400oC. Pada aktivasi kimia digunakan aktivator H3PO4 4M , sedangkan pada aktivasi fisika digunakan aliran gas N2 dan gas CO2 yang laju alirnya divariasikan ( 100 mL/menit, 200 mL/menit, 300 mL/menit dan 400 mL/menit). Karakterisasi karbon aktif yang dipelajari dalam penelitian ini adalah rendemen, kadar air, kadar zat mudah menguap, kadar abu dan bilangan iodin. Hasil penelitian menunjukkan bahwa karbon aktif terbaik berdasarkan daya jerap iodinnya adalah karbon yang mengalami aktivasi kimia (perendaman H3PO4) dan aktivasi fisika dengan menggunakan gas N2 dengan laju alir sebesar 100 mL/menit dilanjutkan gas CO2 dengan laju alir sebesar 200 mL/menit. Karbon ini memiliki bilangan iodin sebesar 678,15 mg/g dengan rendemen sebesar 63,02%, kadar air 14,11%, kadar zat mudah menguap 28,57%, dan kadar abu 4,17%.

---

In this research be held the making of activated carbon by using palm empty bunches (PEB) as the primery ingredients and to see the effect of chemical and physical activation towards the condition of activated carbon produced. Carbonization is done in the temperature of 400oC. In the chemical activation H3PO4 4M is used as activator, meanwhile, in physical activation N2 and CO2 gases is used while varying the speed of flow (100 mL/min, 200 mL/min, 300 mL/min and 400 mL/min). The characteristic of activated carbon that will be studied in this research is yield, humidity, volatile matter, percentage of ash and iodin number.

The result shows that the best activated carbon is based on the iodin number is the carbon that have been through the chemical activation ( H3PO4 soaking) and physical activation by using N2 gas with the speed of flow 200 ml/min. This carbon has the iodin number for 678.15 mg/g with yield 63.02%, water content 14.11%, volatile matter 28.57%, and ash content 4.17%."

"Pada penelitian ini, ingin dilihat pengaruh akivasi kimia dan fisika pada pembuatan karbon aktif berbahan baku sekam padi. Aktivasi kimia dilakukan dengan mengimpregnasi arang sekam dengan KOH dengan rasio massa arang sekam dan KOH 1:4 (berat kering). Dan aktivasi fisika dilakukan dengan mengalirkan gas N2 100 mL/ min dan gas CO2 yang divariasikan 100, 200, 300, dan 400 mL/min pada suhu 800°C selama 1 jam. Bilangan iod tertinggi didapatkan dari karbon yang diaktivasi kimia fisika dengan laju N2 100 mL/min dan CO2 100 mL/min yaitu sebesar 793,04 mg/g, sedangkan bilangan iod terendah didapatkan pada karbon ayang diaktivasi kimia fisika yang dialirkan N2 100 mL/min saja 583,26 mg/g. Sebagai pembanding, juga dilakukan pembuatan karbon aktif dengan metode aktivasi fisika saja dan kimia saja. Untuk karbon yang diaktivasi fisika saja dan kimia saja diperoleh bilangan iodin karbon aktif sebesar 421,09 mg/g dan 496,09 mg/g. Karbon aktif yang memiliki bilangan iod tertinggi memiliki kadar air 13,062 %, kadar abu 8,588 %, dan bagian yang hilang pada pemanasan 950°C 23,123 %.

---

The main purpose of this study is want to see the influence of chemical and physical activation in producing activated carbon made from rice husk. The chemical activation was done by KOH impregnation on rice husk that had been carbonized with a mass ratio of rice husk charcoal and KOH 1:4 (dry weight). And physical activation was done by flewing N2 gas 100 mL / min and CO2 with flow rate varied 100, 200, 300, and 400 mL / min at a temperature of 800°C for 1 h. The highest iodine number of activated carbon obtained from chemical physics at a rate of N2 100 mL / min and CO2 100 mL / min, that is 793,04 mg / g, while the lowest iodine number obtained on activated carbon yang physical chemistry N2 flow 100 mL / min only 583.26 mg / g. For comparison, also made the activated carbon made by physical activation only method and chemistry only. For activated carbon that made by physical and chemical activation only just acquired iodine number at 421,09 mg / g and 496,09 mg / g. Activated carbon that has the highest iodine number has 13,062% moisture content, ash content 8,588%, and the missing parts on heating 950°C 23,123%."