"Penelitian ini menampilkan model rheologi beton berkinerja tinggi (High Performance Concrete) dengan kuat tekan 60 MPa pada umur awal beton. Dua buah balok yang digunakan berukuran 150mm x 150mm x 600mm berdasarkan ASTM C78-94. Pengamatan dilakukan selama 24 jam di awal atau pada saat sebelum curing menggunakan Vibrating Wire Embedded Strain Gages.Model rheologi didekati dengan menggunakan data regangan susut rata-rata dari kedua balok tersebut, serta beberapa parameter rheologi diperoleh dengan menggunakan trial and error. Model rheologi beton berkinerja tinggi pada umur awal beton dibagi menjadi lima rheologi yang terdiri dari Solidifying Liquid - Kelvin Voigt Niken - Kelvin Voigt Niken - Kelvin Voigt Niken - Kelvin Voigt Niken.

---

This study presents rheological model of high performance concrete with 60 MPa compressive strength of concrete at early age. The size of these two beams is 150 mm x 150 mm x 600 mm according to ASTM C78-94. Observations were made during 24 hours at the beginning or at the time before curing using vibrating wire embeded strain gages. Rheological models approximated using shrinkage strain data is the average of the two beams, as well as some rheological parameters obtained by using trial and error. Rheological models of high performance concrete at early age concrete is divided into five rheological model, consists of Solidifying Liquid - Kelvin Voigt Niken - Kelvin Voigt Niken - Kelvin Voigt Niken - Kelvin Voigt Niken."

"Penelitian ini membahas mengenai model rheologi yang terjadi pada umur awal beton yang diakibatkan oleh regangan susut yang terjadi, serta bagaimana pengaruh penambahan fly ash terhadap model rheologi pada umur awal beton. Model rheologi merupakan suatu konsep abstrak yang telah diformulasikan untuk mendeksripsikan perilaku material. Penelitian dilakukan secara eksperimental menggunakan prisma beton 60 MPa berukuran 15 cm x 15 cm x 60 cm berdasakan ASTM C78-94 pada posisi vertikal dan diamati regangan susutnya dengan menggunakan Vibrating Wire Embedded Strain Gage (VWESG) sesaat setelah beton dicor hingga beton berumur 24 jam. Hasil penelitian menunjukkan bahwa beton berkinerja tinggi dengan menggunakan fly ash pada umur awal (0 - 24 jam) dapat dimodelkan dengan model rheologi yang terdiri dari lima model yaitu Solidifying Liquid (0 - 1,1 jam), Solidifying Liquid (1,1 - 1,6 jam), Kelvin-Voigt (1,6 - 6,3 jam), Kelvin-Voigt (6,3 - 10,3 jam), dan Kelvin-Voigt (10,3 - 24 jam).

---

This research discusses rheological models in early age concrete caused by shrinkage strain and the influence of fly ash on the rheological model of early age concrete. Rheological model is an abstract concept that has been formulated to describe material behavior. Three shrinkage specimens made of 60 MPa concrete prism type specimens size of 15 cm x 15 cm x 60 cm and observed by Vibrating Wire Embedded Strain Gage (VWESG) right after the fresh concrete is placed to the mold until the specimens age is 24 hours. The result of this research shows that high-performance concrete using fly ash at early ages (0-24 hours) can be modeled by five rheological models which are Solidifying Liquid (0 - 1,1 hours), Solidifying Liquid (1,1 - 1,6 hours), Kelvin-Voigt (1,6 - 6,3 hours), Kelvin-Voigt (6,3 - 10,3 hours), dan Kelvin-Voigt (10,3 - 24 hours)."

"[ABSTRAKPenelitian susut dan rangkak di daerah tropis lembab ini dilakukan pada beton berkinerja tinggi fc’ 60 MPa dengan campuran tanpa abu terbang (TAT) dan dengan abu terbang (DAT). Spesimen susut berukuran 150х150х600 mm3 (3 buah) dan spesimen rangkak 200х600х2700 mm3 (1 buah). Pemberian beban dilakukan dengan cara pratekan sebesar 0.3 fc’ pada umur 15 hari, tulangan sebatas emberian beban tersebut. Ruang dikondisikan pada temperature 28±3OC dan kelembaban 72±5%.Model dibuat berdasar pengamatan 800 hari dan 1000 hari. Data diolah dengan metode outlying ASTM E178-02 untuk nilai ekstrim dengan tingkat signifikansi 5%.Tujuan penelitian ini adalah menghasilkan model rheologi susut dan rangkak beton berkinerja tinggi di daerah tropis lembab.Model rheologi susut sampai jangka waktu 1000 hari adalah (H|N)-(H|N), sedangkan untuk rangkak (H|N)- (StV|N). Faktor koreksi susut untuk rasio air terhadap semen (w/cm) 0.26, 0.30, 0.34, dan 0.38 dalam jangka pendek (7-15 hari) berturut-turut adalah 1, 1.1, 2.1 dan 2.3, serta untuk jangka panjang 1, 1.13, 1.54 dan 1.65. Faktor koreksi jumlah semen sama dengan faktor koreksi ACI 209R Tropis lembab menyebabkan suhu maximum 24 jam pertama untuk skala penuh dapatmencapai 2 kali suhu maximum di daerah non tropis lembab. Pencapaian suhu maximum tersebut setengah waktu pencapaian suhu maximum di daerah non tropis.Laju regangan susut di daerah tropis lembab pada jangka pendek TAT adalah 1.1 dan jangka panjang 4.1 kali laju regangan ACI 209R dan bila dengan abu terbang 1.6 dan 2.4. Laju rangkak kedua campuran terhadap ACI adalah 0.8 untuk jangka pendek dan 1.8 untuk jangka panjang. Regangan susut jangka panjang terhadap ACI 209 untukTAT 1.7 dan DAT 1.4; sedang rangkak 1.3 dan 1.;

---

ABSTRACTThe research of shrinkage and creep in humid tropical weather area was done in highperformance concrete HPC fc of 6The research of shrinkage and creep in humid tropical weather area was done in highperformance concrete (HPC) fc’ of 60 MPa mixed with composition without fly ash called TAT and within fly ash called DAT. Three shrinkage specimens are 150х150х600 mm3 and one creep specimen is 200х600х2700 mm3. Loading was applied by prestressing of 0.3 fc’in 15th day, the reinforcement was limited by that prestressing. Room was set in 28 ± 3oC temperature and 72 ± 5% humidity. Rheological models were created based on 800 days and 1000 daysobservation. Datas were processed by using ASTM E178-02 outlying methode for extreme value with 5% significant level.The objective of this research is to create rheological models of shrinkage and creep of high performance concrete in humid tropical weather.Shrinkage rheological model until the age of 1000 days is (H|N)-(H|N), while for creep is (H|N)- (StV|N). Shrinkage correction factors for water ratio to cement (w/cm) of 0.26, 0.30, 0.34, and 0.38 (7-15 days) are 1, 1.1, 2.1 and 2.3 respectively, and for long term are 1, 1.13, 1.54 dan 1.65. Correction factors of cement amount was similar with correction factor of ACI 209R.Humid tropical area caused maximum temperature in first 24 hours could reach 2 times of maximum temperature in non humid tropical area (full scale). The maximum temperature achievement was much faster, that was a half of maximum temperature achievement in non humid tropical area. Reffered to ACI 209 R, the rate of shrinkagein humid tropical area in short term is 1.1 and for long term is 4.1 times rate ACI 209R for TAT, 1.6 and 2.4 for DAT. Creep rate of the both mixture was compared with ACI 209R: 0.8 for short term and 1.8 for long term. Long term shrinkage strain of TAT and DAT was 1.7 and 1.4 times ACI 209R, while for creep was 1.3 and 1.0 MPa mixed with composition without fly ashcalled TAT and within fly ash called DAT Three shrinkage specimens are150 150 600 mm3 and one creep specimen is 200 600 2700 mm3 Loading wasapplied by prestressing of 0 3 fc in 15th day the reinforcement was limited by thatprestressing Room was set in 28 3oC temperature and 72 5 humidity Rheological models were created based on 800 days and 1000 daysobservation Datas were processed by using ASTM E178 02 outlying methode forextreme value with 5 significant level The objective of this research is to create rheological models of shrinkage and creepof high performance concrete in humid tropical weather Shrinkage rheological model until the age of 1000 days is H N H N while forcreep is H N StV N Shrinkage correction factors for water ratio to cement w cm of 0 26 0 30 0 34 and 0 38 7 15 days are 1 1 1 2 1 and 2 3 respectively and for long term are 1 1 13 1 54 dan 1 65 Correction factors of cement amount wassimilar with correction factor of ACI 209R Humid tropical area caused maximum temperature in first 24 hours could reach 2times of maximum temperature in non humid tropical area full scale The maximumtemperature achievement was much faster that was a half of maximum temperatureachievement in non humid tropical area Reffered to ACI 209 R the rate of shrinkagein humid tropical area in short term is 1 1 and for long term is 4 1 times rate ACI209R for TAT 1 6 and 2 4 for DAT Creep rate of the both mixture was comparedwith ACI 209R 0 8 for short term and 1 8 for long term Long term shrinkage strainof TAT and DAT was 1 7 and 1 4 times ACI 209R while for creep was 1 3 and 1 , The research of shrinkage and creep in humid tropical weather area was done in highperformance concrete HPC fc of 6The research of shrinkage and creep in humid tropical weather area was done in highperformance concrete (HPC) fc’ of 60 MPa mixed with composition without fly ash called TAT and within fly ash called DAT. Three shrinkage specimens are 150х150х600 mm3 and one creep specimen is 200х600х2700 mm3. Loading was applied by prestressing of 0.3 fc’in 15th day, the reinforcement was limited by that prestressing. Room was set in 28 ± 3oC temperature and 72 ± 5% humidity. Rheological models were created based on 800 days and 1000 daysobservation. Datas were processed by using ASTM E178-02 outlying methode for extreme value with 5% significant level.The objective of this research is to create rheological models of shrinkage and creep of high performance concrete in humid tropical weather.Shrinkage rheological model until the age of 1000 days is (H|N)-(H|N), while for creep is (H|N)- (StV|N). Shrinkage correction factors for water ratio to cement (w/cm) of 0.26, 0.30, 0.34, and 0.38 (7-15 days) are 1, 1.1, 2.1 and 2.3 respectively, and for long term are 1, 1.13, 1.54 dan 1.65. Correction factors of cement amount was similar with correction factor of ACI 209R.Humid tropical area caused maximum temperature in first 24 hours could reach 2 times of maximum temperature in non humid tropical area (full scale). The maximum temperature achievement was much faster, that was a half of maximum temperature achievement in non humid tropical area. Reffered to ACI 209 R, the rate of shrinkagein humid tropical area in short term is 1.1 and for long term is 4.1 times rate ACI 209R for TAT, 1.6 and 2.4 for DAT. Creep rate of the both mixture was compared with ACI 209R: 0.8 for short term and 1.8 for long term. Long term shrinkage strain of TAT and DAT was 1.7 and 1.4 times ACI 209R, while for creep was 1.3 and 1.0 MPa mixed with composition without fly ashcalled TAT and within fly ash called DAT Three shrinkage specimens are150 150 600 mm3 and one creep specimen is 200 600 2700 mm3 Loading wasapplied by prestressing of 0 3 fc in 15th day the reinforcement was limited by thatprestressing Room was set in 28 3oC temperature and 72 5 humidity Rheological models were created based on 800 days and 1000 daysobservation Datas were processed by using ASTM E178 02 outlying methode forextreme value with 5 significant level The objective of this research is to create rheological models of shrinkage and creepof high performance concrete in humid tropical weather Shrinkage rheological model until the age of 1000 days is H N H N while forcreep is H N StV N Shrinkage correction factors for water ratio to cement w cm of 0 26 0 30 0 34 and 0 38 7 15 days are 1 1 1 2 1 and 2 3 respectively and for long term are 1 1 13 1 54 dan 1 65 Correction factors of cement amount wassimilar with correction factor of ACI 209R Humid tropical area caused maximum temperature in first 24 hours could reach 2times of maximum temperature in non humid tropical area full scale The maximumtemperature achievement was much faster that was a half of maximum temperatureachievement in non humid tropical area Reffered to ACI 209 R the rate of shrinkagein humid tropical area in short term is 1 1 and for long term is 4 1 times rate ACI209R for TAT 1 6 and 2 4 for DAT Creep rate of the both mixture was comparedwith ACI 209R 0 8 for short term and 1 8 for long term Long term shrinkage strainof TAT and DAT was 1 7 and 1 4 times ACI 209R while for creep was 1 3 and 1 ]"

"Penelitian yang dilakukan akhir-akhir ini mengenai susut sebatas susut pada beton arah horizontal. Tes susut ASTM C157/ C157M-08 adalah tes susut pada arah horizontal. Sedangkan pada keadaan dilapangan, tidak semua beton ada pada kondisi horizontal, dapat diambil contoh yaitu kolom pada bangunan. Penulis ingin melihat apakah ada pengaruh dari perubahan letak beton tersebut terhadap susut beton dengan meneliti susut beton pada arah vertikal. Penelitian yang dilakukan adalah beton berkinerja tinggi menggunakan Ordinary Portland Cement (OPC), silikafume, dan High Range Water Reducing (HRWR) yaitu sika viscocrete 10. Untuk uji kuat tekan beton, benda uji akan dibuat dalam silinder kecil berdiameter 100mm dan tinggi 200mm yang dites pada hari 3,7,14,dan 28 hari. Uji modulus elastisitas menggunakan silinder besar berdiameter 150mm dan tinggi 300mm. Sedangkan untuk pengujian susut menggunakan balok berukuran 150mm x 150mm x 600mm berdasarkan ASTM C78-94 karena sebagian besar elemen struktur menderita lentur. Hasil penelitian menunjukkan bahwa susut yang terjadi pada arah vertikal lebih kecil dibandingkan susut yang terjadi pada arah horizontal dan lebih kecil dibandingkan susut menurut ACI 209R-92.

---

Research carried out recently about the extent of shrinkage in concrete shrinkage horizontal direction. Shrinkage test ASTM C157 / C157M-08 is a test shrinkage in the horizontal direction. While the state of the field, not all concrete there is in the horizontal condition, the sample can be taken on the building columns. The author would like to see if there is the influence of changes in the location of the concrete to the shrinkage of concrete by examining the concrete shrinkage in the vertical direction. The research conducted is of high-performance concrete using Ordinary Portland Cement (OPC), silikafume, and High Range Water Reducing (HRWR) is Sika Viscocrete 10. For concrete compressive strength test, the test object will be created in a small cylinder of 100mm diameter and 200mm high to be tested on day 3,7,14, and 28 days. Modulus of elasticity test using a cylinder of 150mm diameter and 300mm high. As for the shrinkage test using a beam size of 150mm x 150mm x 600mm according to ASTM C78-94 because most of the structural elements suffer from flexure. The results showed that the shrinkage that occurs in the vertical direction is smaller than the shrinkage that occurs in the horizontal direction and smaller than the shrinkage according to ACI 209R-92."

"Penelitian yang dilakukan akhir-akhir ini mengenai susut sebatas susut pada beton arah horizontal. Padahal pada kenyataannya, banyak elemen struktur beton yang berada pada posisi selain horizontal, seperti kolom. Oleh karena itu, dilakukan suatu penelitian terhadap campuran beton berkinerja tinggi yang menggunakan fly ash, yang selanjutnya akan diamati perilaku susutnya pada arah vertikal untuk mengetahui apakah ada pengaruh berat sendiri beton dan penggunaan fly ash terhadap susut yang terjadi, serta membandingkan dengan perhitungan regangan susut berdasarkan ACI 209R-92. Untuk pengujian susut, benda uji akan dibuat dalam balok ukuran 15 cm x 15 cm x 60 cm dan diuji dengan menggunakan Vibrating Wire Embedded Strain Gage (VWESG) sesaat setelah beton dicor hingga beton berumur 110 hari. Pengujian tekan dan modulus elastisitas juga dilakukan untuk mengetahui karekteristik kuat tekan dan modulus elastisits beton yang diteliti. Benda uji tekan akan dibuat dalam silinder dengan diameter 10 cm dn tinggi 20 cm yang dites pada hari ke 3, 7, 14, dan 28. Sedangkan benda uji modulus elastisitas akan dibuat dalam silinder silinder dengan diameter 15 cm dn tinggi 15 cm yang dites pada hari ke-28. Hasil penelitian menunjukkan bahwa berat sendiri beton dan penggunaan fly ash tidak berpengaruh terhadap susut yang terjadi. Regangan susut yang terjadi hampir sama dengan regangan susut berdasarkan ACI209-92.

---

Research in shirinkage of concrete carried out recently is merely about shrinkage in horizontal direction. Whereas in reality, many structural elements site in vertical direction, such as column. Therefore, this research carry out shrinkage of high performance concrete using fly ash in vertical direction which is used to find out if there is influence of its own weight and the use of fly ash in concrete shrinkage. In addition, this research is also compared with prediction of shrinkage based on ACI 209R-92.

The shrinkage specimens will be made of beam type specimens size of 15 cm x 15 cm x 60 cm and evaluated by Vibrating Wire Embedded Strain Gage (VWESG) right after the fresh concrete is placed to the mold until the specimens age is approximately 110 days. The compressive strength dan elastic modulus test will also be evaluated to find out the characteristics of compressive strength and elastic modulus of concrete specimens.

The compressive strength specimens will be made of cylinder type specimen size of 10 cm diameter and 20 cm height and tested on 3, 7, 14, and 28 days of concrete specimens age. Whereas the elastic modulus specimens will be made of cylinder type specimen size of 15 cm diameter and 23 cm height and tested on 28 days of concrete specimens age.

The result of this research shows that concrete's own weight and the use of fly ash do not influence the shrinkage of concrete. The shrinkage that occured is almost the same with the one according to ACI 209R-92."

"Pada saat ini beton siap pakai (ready mix) sedang marak digunakan untuk membuat konstruksi bangunan, namun pada penerapannya sering terjadi kelebihan supply dan sisanya terkadang dibuang di sembarang tempat, sehingga dapat mengurangi kesuburan tanah dan merusak keseimbangan ekosistem. Salah satu cara untuk mengatasinya adalah mendaur ulang limbah beton. Namun, pemanfaatan limbah sebagai agregat daur ulang tersebut perlu dikaji lebih mendalam, dengan melakukan pengujian secara eksperimental dan analisis terhadap karakteristik yang dimiliki. Metoda dan prosedur pelaksanaan pengujian agregat daur ulang tersebut dilakukan dengan mengacu pada standar ASTM. Beton dibuat dengan agregat alam maupun campuran antara agregat alam dan agregat daur ulang dengan komposisi tertentu. Kekuatan beton yang akan dipakai adalah 25 MPa. Kemudian dilakukan pengujian terhadap kuat lentur pada umur 28 hari dan susut selama 56 hari. Berdasarkan hasil studi eksperimental, agregat daur ulang mengandung mortar. Kandungan mortar tersebut mengakibatkan absorpsi agregat menjadi lebih besar, lebih poros atau berpori, sehingga kekerasannya berkurang. Beberapa perbedaan kualitas, sifat-sifat fisik dan kimia agregat daur ulang tersebut menyebabkan perbedaan sifat-sifat material beton yang dihasilkan. Persentase penurunan kuat lentur beton agregat daur ulang dengan komposisi 25 % agregat kasar daur ulang dan 0 % agregat halus daur ulang adalah 1.26 %, sedangkan beton agregat daur ulang dengan komposisi 0 % agregat kasar daur ulang dan 25 % agregat halus daur ulang adalah 6.33 %. Ini menunjukkan bahwa penggunaan agregat kasar daur ulang dengan persentase 25 % lebih baik dari pada penggunaan agregat halus daur ulang dengan persentase 25 % untuk pengujian kuat lentur beton. Pada pengujian susut, nilai persentase pertambahan susut beton agregat daur ulang dengan komposisi 0 % agregat kasar daur ulang dan 25 % agregat halus daur ulang adalah 10.53 %, sedangkan dengan komposisi 25 % agregat kasar daur ulang dan 0 % agregat halus daur ulang adalah 5.26%. Ini menunjukkan bahwa penggunaan agregat kasar daur ulang dengan persentase 25 % lebih baik dari pada penggunaan agregat halus daur ulang dengan persentase 25 % untuk pengujian susut.

---

Now ready mix is very well known to make construction of building, but the usage often more supply that throw in anywhere, so it will decrease the fertilizer of soil and destroy the ecosystem. To against that, the solution is to recycled aggregate. We need research chemical properties of the materials and then to be analyzed to understand the difference between natural and recycled aggregates. The method and procedure for testing of the recycled aggregate materials are in accordance with the ASTM standard.

Concretes are made from normal aggregate and mix both normal and recycled aggregate. Concrete strength is 25 MPa. After that, test of flexural strength in 28th day old and shrinkage during 56 days.

Based on the experimental works, recycled aggregates contain mortar. The existence of mortar content in recycled aggregates affects to the accretion of absorption of aggregate, more porous, less hardness. Some of the difference of qualities, physical and chemical properties of recycled aggregates cause the difference of properties of the resulted concrete materials. The difference properties consist of the reduction of flexural strength and increase of shrinkage.

The reduction of percentage recycled aggregate concrete of composition 25 % coarse recycled aggregate and 0 % fine recycled aggregate was 1.26 %, while recycled aggregate concrete of composition 0 % coarse recycled aggregate and 25 % fine recycled aggregate was 6.33 %. This indicate that usage recycled coarse aggregate was prefer than recycled fine aggregate for flexural strength. For shrinkage, percentage accretion value of composition 0 % coarse recycled aggregate and 25 % fine recycled aggregate was 10.53 %, while 25 % coarse recycled aggregate with 0 % fine recycled aggregate was 5.26%. This indicate that usage of coarse aggregate of recycle with percentage 25 % was better the than usage of fine aggregate of recycle with percentage 25 % for the examination of length change."

"Industri konstruksi di Indonesia saat ini terus berkembang, sehingga konsumsi akan material pun kian bertambah. Salah satu material yang sangat banyak digunakan dan terus bertambah permintaannya pada konstruksi adalah semen, khususnya semen tipe 1 (Ordinary Portland Cement). Padahal dari tahun ke tahunnya produksi klinker, yaitu campuran utama pembuat semen, semakin menurun seiring bahan baku yang berkurang. Permasalahan ini coba dipecahkan oleh produsen semen dengan membuat berbagai semen dengan campuran bahan-bahan baru, seperti semen pozzolan, semen dengan silica fume, semen komposit dan lainnya.Portland Composite Cement (PCC) salah satu dari semen tadi merupakan produk yang saat ini telah beredar dan banyak digunakan. PCC dianggap memiliki karakter yang mirip, bahkan lebih baik dibandingkan dengan OPC. Akan tetapi, pada penggunaanya mix design untuk PCC masih sama dengan OPC. Selain itu, belum diketahui pasti karakteristik beton yang dihasilkan dengan menggunakan PCC.Penulisan ini bertujuan untuk mengetahui salah satu karakteristik beton dengan semen PCC yaitu kuat lentur (modulus of rupture) dan susut, dimana mix design yang digunakan tetap menggunakan aturan ACI yang berlaku bagi beton dengan OPC. Jika benar PCC mempunyai kualitas yang lebih baik dibanding OPC, seharusnya kuat lentur (modulus of rupture) juga lebih baik. Kekuatan lentur atau tarik beton akan dipengaruhi oleh perubahan volume, yang dapat mengakibatkan retak. Penggunaan material tambahan seperti fly ash, pozolan dan lainnya, akan mempengaruhi terhadap perubahan susut beton, dimana penggunaan fly ash seharusnya akan mengurangi penyusutan.Dari penelitian ini didapatkan bahwa kuat lentur beton PCC mengalami kenaikan yang lebih lambat dibanding beton OPC, trend yang dihasilkan berupa grafik logaritma yang setelah lewat 28 hari lambat laun menjadi asimtotis. Nilai kuat lentur beton PCC pada umur 28 hari dan setelahnya, lebih tinggi dibanding beton normal. Penggunaan PCC tidak terlalu berpengaruhi terhadap nilai susut beton dibanding beton normal.

---

Indonesia construction industry growing fast, that is why the needs for construction material keep growing. One of them is cement that used a lot for many construction applications and its demand increase from time to time, especially for Ordinary Portland Cement (OPC). On the other side, clinker productivity had been decreasing every year. To solve this problem, cement producer making many variation of composite cement, such as, pozzolan cement, cement with silica fume, PCC, etc.Portland Composite Cement (PCC) is one of the product that used by many people and project. PCC have similar characteristic and even better quality than OPC. Even PCC used the same way with OPC, but the true characteristic of PCC not known yet.This research has objective to study flexural strength and shrinkage of concrete using PCC. If PCC has better quality, its flexural strength should be better than OPC. Flexural strength influenced by volume alteration that cause concrete crack. Fly ash in PCC has property that influencing concrete volume alteration. Fly ash should be able to reduce concrete shrinkage.The research shows that PCC concrete flexural strength increasing slower than OPC concrete. The graph of PCC concrete flexural strength increasing on logarithmic equation those after 28 days by degrees become asymptotic. The PCC concrete flexural strength after 28 days is higher than OPC concrete. Using PCC in concrete does not give significant effect for the concrete shrinkages."

"Industri konstruksi di Indonesia saat ini terus berkembang, sehingga konsumsi akan material pun kian bertambah. Salah satu material yang sangat banyak digunakan dan terus bertambah permintaannya pada konstruksi adalah semen, khususnya semen tipe 1 (Ordinary Portland Cement). Padahal dari tahun ke tahunnya produksi klinker, yaitu campuran utama pembuat semen, semakin menurun seiring bahan baku yang berkurang. Permasalahan ini coba dipecahkan oleh produsen semen dengan membuat berbagai semen dengan campuran bahan-bahan baru, seperti semen pozzolan, semen dengan silica fume, semen komposit dan lainnya. Portland Composite Cement (PCC) salah satu dari semen tadi merupakan produk yang saat ini telah beredar dan banyak digunakan. PCC dianggap memiliki karakter yang mirip, bahkan lebih baik dibandingkan dengan OPC. Akan tetapi, pada penggunaanya mix design untuk PCC masih sama dengan OPC. Selain itu, belum diketahui pasti karakteristik beton yang dihasilkan dengan menggunakan PCC.Penulisan ini bertujuan untuk mengetahui salah satu karakteristik beton dengan semen PCC yaitu kuat lentur (modulus of rupture) dan susut, dimana mix design yang digunakan tetap menggunakan aturan ACI yang berlaku bagi beton dengan OPC. Jika benar PCC mempunyai kualitas yang lebih baik dibanding OPC, seharusnya kuat lentur (modulus of rupture) juga lebih baik. Kekuatan lentur atau tarik beton akan dipengaruhi oleh perubahan volume, yang dapat mengakibatkan retak. Penggunaan material tambahan seperti fly ash, pozolan dan lainnya, akan mempengaruhi terhadap perubahan susut beton, dimana penggunaan fly ash seharusnya akan mengurangi penyusutan. Dari penelitian ini didapatkan bahwa kuat lentur beton PCC mengalami kenaikan yang lebih lambat dibanding beton OPC, trend yang dihasilkan berupa grafik logaritma yang setelah lewat 28 hari lambat laun menjadi asimtotis. Nilai kuat lentur beton PCC pada umur 28 hari dan setelahnya, lebih tinggi dibanding beton normal. Penggunaan PCC tidak terlalu berpengaruhi terhadap nilai susut beton dibanding beton normal.

---

Indonesia construction industry growing fast, that is why the needs for construction material keep growing. One of them is cement that used a lot for many construction applications and its demand increase from time to time, especially for Ordinary Portland Cement (OPC). On the other side, clinker productivity had been decreasing every year. To solve this problem, cement producer making many variation of composite cement, such as, pozzolan cement, cement with silica fume, PCC, etc. Portland Composite Cement (PCC) is one of the product that used by many people and project. PCC have similar characteristic and even better quality than OPC. Even PCC used the same way with OPC, but the true characteristic of PCC not known yet.

This research has objective to study flexural strength and shrinkage of concrete using PCC. If PCC has better quality, its flexural strength should be better than OPC. Flexural strength influenced by volume alteration that cause concrete crack. Fly ash in PCC has property that influencing concrete volume alteration. Fly ash should be able to reduce concrete shrinkage. The research shows that PCC concrete flexural strength increasing slower than OPC concrete. The graph of PCC concrete flexural strength increasing on logarithmic equation those after 28 days by degrees become asymptotic. The PCC concrete flexural strength after 28 days is higher than OPC concrete. Using PCC in concrete does not give significant effect for the concrete shrinkages."

"Pada saat ini beton siap pakai sedang marak digunakan pada konstruksi bangunan. Seiring dengan perkembangan teknologi, beton siap pakai juga berkembang menggunakan material fly ash yang dapat digunakan sebagai bahan pereduksi semen. Fly ash merupakan limbah hasil pembakaran batubara pada Pembangkit Listrik Tenaga Uap (PLTU). Selain ekonomis, penggunaan fly ash pada beton siap pakai juga dapat meningkatkan kekuatan beton pada usia lanjut dan menurunkan susut yang terjadi bahkan dapat mengurangi emisi gas CO2 yang dihasilkan dari produksi semen. Namun, berdasarkan pengalaman dilapangan menunjukkan bahwa penggunaan abu terbang banyak menimbulkan keretakan pada beton struktural yang mengindikasikan terjadinya susut beton yang lebih besar dari beton normal. Hal ini berkebalikan dengan pernyataan sebelumya. Beton yang diteliti merupakan beton siap pakai yang menggunakan fly ash. Kekuatan beton yang akan dipakai adalah fc - 10 - 50 MPa dengan persentase fly ash yang digunakan 9% - 20%. Kemudian dilakukan pengujian susut selama lebih kurang 28 hari. Berdasarkan, pengujian, diketahui bahwa besarnya persentase fly ash terhadap jumlah semen, perbandingan air semen, nilai slump, banyaknya air dari tiap-tiap sampel, dan kondisi luar seperti suhu dan kelembaban sangat mempengaruhi persentase susut beton. Dari penelitian ini diperoleh bahwa beton siap pakai yang menggunakan fly ash dengan persentase terhadap jumlah semen antara 9% - 20% memiliki persentase susut atau strain dari beton yang lebih kecil daripada beton normal pada usia 28 hari yang persentasenya bisa mencapai 0.035% - 0.041%.

---

Now ready mix concrete is very well known on construction of building. Along with technological development, ready mix concrete was also developed using fly ash material that can be used as ingredients in cement kilns. Fly ash is a coal combustion waste on the Steam Power Plant (Power Plant). Besides economic value, use of fly ash in ready mix concrete can also increase strength in the elderly and reduce shrinkage that occurs, even can reduce CO2 emissions resulting from cement production. However, based on field experience shows that the use of fly ash causes a lot of cracks in structural concrete that indicate the occurrence of concrete shrinkage greater than normal concrete. This contrasts with the previous statement. Concrete under study is a ready mix concrete using fly ash. Concrete strength will be used is fc' 10 MPa - 50 MPa with the percentage of fly ash used in 9% - 20%. Then do the test more or less shrinkage during 28 days.

Based testing, found that the percentages of fly ash on the amount of cement, water cement ratio, slump, amount of water from each sample, and external conditions such as temperature and humidity affect the percentage shrinkage of concrete. From this study found that the ready mix concrete using fly ash with a percentage of total cement between 9% - 20% have a percentage of shrinkage or strain of concrete is smaller than normal concrete at the age of 28 days that the rates can reach 0035% - 0041%."

"Saat ini telah terjadi penambangan sumber daya alam bahan baku beton secara berlebihan. Dilihat dari sisi lain, banyak terdapat limbah beton yang hanya menjadi limbah di tempat pembuangannya. Penelitian ini akan menggunakan agregat kasar daur ulang sebagai agregat pada beton. Komposisi benda uji terdiri dari 0%, 20%, 40%, dan 60% agregat kasar daur ulang dari limbah beton mutu K350-K400. Pengujian meliputi, yaitu pengujian kuat tekan, kuat lentur, dan susut pada beton. Kuat tekan dan kuat lentur beton dengan komposisi 20% agregat kasar daur ulang meningkat 14,961% dan 12,5% dari kuat beton normal pada umur 28 hari. Susut beton dengan komposisi 60% agregat kasar daur ulang mempunyai nilai susut tertinggi dibandingkan dengan campuran lainnya.

---

Nowadays, there is a natural resource mining of concrete forming materials excessively. On the other hand, there are a lot of concrete waste in concrete waste dumps. This study will use recycled coarse aggregate as aggregate in concrete. The composition of the test object consisting of 0%, 20%, 40%, and 60% recycled coarse aggregate from concrete waste K350-K400. Testing includes, compressive strength test, flexural strength, and shrinkage in concrete. Compressive strength and flexural strength of concrete with 20% recycled coarse aggregate increased by 14.961% and 12.5% of the normal concrete at 28 days. Shrinkage of concrete with a composition of 60% recycled coarse aggregate has the highest shrinkage value compared to other mixtures."