"Tesis ini meneliti mengenai pengaruh asam stearat terhadap basal spasi organoclay dan sifat-sifat dari nanokomposit karet alam/organoclay terekspansi serta pengaruh organoclay terekspansi terhadap sifat dan morfologi dari nanokompositnya. Nanokomposit karet alam/organoclay terekspansi dibuat dengan cara pelelehan kompon. Hasil penelitian menunjukkan bahwa peningkatan dosis asam stearat dapat meningkatkan basal spasi organoclay sehingga organoclay terekspansi dapat terdispersi dengan merata di dalam matriks karet alam, menghasilkan nanokomposit dengan sifat mekanik dan swelling yang meningkat.

---

This thesis are to studies the effect of stearic acid on organoclay d-spacing and properties of natural rubber/expanded organoclay and the effect of expanded organoclays on properties and morphology of its nanocomposites. Natural rubber/expanded organoclay nanocomposites was prepared by using melt compounding technique. The result showed that the increasing of stearic acid doses could increase the d-spacing of organoclay so that expanded organoclay can disperse uniformly in natural rubber matrix, produces nanocomposites with increasing of mechanical and swelling properties."

"Film nanokomposit polimer biodegradable telah dibuat. Clay Tapanuli termodifikasi heksadesiltrimetilamonium bromida (C16) dan oktadesiltrimetilamonium bromida (C18) digunakan sebagai nanofiller. Penelitian ini terdiri atas pemurnian clay, sintesis organoclay dan pembuatan film nanokomposit dengan metode solvent casting. Penelitian ini untuk mempelajari pengaruh jumlah organoclay dan panjang rantai alkil surfaktan terhadap sifat mekanik bahan bionanokomposit. Pergeseran puncak d001 pada difraktogram menunjukkan kenaikan basal spacing sebesar 0,35 nm dan 0,48 nm masingmasing oleh surfaktan C16 dan C18. Difraktogram XRD nanokomposit selulosa asetat dan poli(vinil alkohol) juga menunjukkan adanya struktur dispersi campuran interkalasi dan eksfoliasi. Hasil ini mendukung hasil uji mekanik film nanokomposit dimana kuat tarik dan modulus elastisitas meningkat. Hasil uji tarik film nanokomposit menunjukkan adanya pengaruh penambahan organoclay dan panjang rantai alkil surfaktan terhadap perubahan nilai kuat tarik, modulus tarikdan regangansaatpatah film nanokomposit dimana peningkatan sifat mekanik nanokomposit selulosa asetat lebih tingi dibandingkan nanokomposit poli(vinilalkohol). Citra FE-SEM film nanokomposit pada permukaan patahan memperlihatkan pori-pori yang tidak teratur dan elastisitas film nanokomposit poli(vinilalkohol) yang lebih panjang dibandingkan film nanokomposit selulosa asetat.

---

Nanocomposite films of biodegradable polymers were prepared. The Tapanuly clay modified by heksadecyltrimethylammonium bromide (C16) and Octadecyltrimethylammonium bromide (C18) were used as nanofillers. This experiment were consisted of namely clay purification, organoclay synthesis, and nanocomposite film preparation by a solvent casting methode. The aim of this work was to study the effect of organoclay content and the surfactant alkyl chain length to the mechanical properties of bionanocomposite materials. The shifting of d001 peaks on the difractogram showed that the basal spacing increased by 0.35 nm and 0.48 nm by C16 and C18 surfactants respectively. The XRD difraction also showed the results of cellulose acetate nanocomposite and poly(vinyl alcohol) nanocomposite had a mixed structure of intercalated and exfoliated structure.

These results supported the mechanical testing results of the nanocomposite films that of the tensile strentgh and modulus elasticity was enhanced. The mechanical testing result showed that the organoclay content and surfactant alkyl chain length influenced the tensile strength, modulus elasticity, and strain at break of the nanocomposite films that of the increasing of cellulose acetate nanocomposite mechanical properties was higher than poly(vinyl alcohol) nanocomposite. FESEM images on the fracture surface of the nanocomposite films showed irregular pores on the cellulose acetate nanocomposite films and the longer elasticity of poly(vinyl alcohol) nanocomposite compared to the cellulose acetate nanocomposite films."

"Preparasi nanokomposit masterbatch pati/organoclay digunakan sebagai bahan pencampur pembuatan plastik kemasan yang bersifat biodegradable. Masterbatch tersusun atas pati singkong (tapioka), organoclay (montmorillonite), dan bahan aditif (plasticizer dan compatibilizer). Proses sintesis dengan metode melt compounding (pencampuran lelehan) yang dilakukan menggunakan alat Rheomix mixer. Untuk mendapatkan masterbatch optimum, struktur dan morfologi dari masterbatch diamati menggunakan Scanning Electron Microscope (SEM), X-Ray Diffraction (XRD) dan Differential Scanning Calorimetry (DSC). Bahan aditif gliserol monostearat (GMS) dan gum rosin (GR) dapat mempengaruhi perbedaan pembentukan thermoplastic starch (TPS) yang menjadi matriks dari masterbatch. Penggunaan GMS sebagai aditif dengan konsentrasi pati sebesar 36% (wt) menunjukkan morfologi permukaan yang paling homogen, pati mengalami destrukturasi menjadi TPS secara merata, menghasilkan penurunan basal spacing menjadi 2,04 nm dan terbentuk struktur interkalasi. Penggunaan GR sebagai aditif dengan konsentrasi pati yang sama, menunjukkan morfologi permukaan yang kurang homogen, tidak semua pati mengalami destrukturasi dan peningkatan basal spacing organoclay sebesar 3,89 nm serta terbentuk struktur eksfoliasi. Selain itu, peningkatan konsentrasi pati juga memberikan pengaruh terhadap morfologi masterbatch. Semakin banyak konsentrasi pati, morfologi dari masterbatch semakin tidak homogen.

---

Preparation of nanocomposite masterbatch starch / organoclay were used as biodegradable mixed materials on the manufacturing of plastic packaging. Masterbatch consist of cassava starch, organoclay (montmorillonite), and additives (plasticizer and compatibilizer). The synthesis process by melt compounding using a Rheomix mixer. To obtain optimum structure and morphology of the masterbatch were observed using Scanning Electron Microscope (SEM), X-Ray Diffraction (XRD) and Differential Scanning Calorimetry (DSC). The Additives glycerol monostearate (GMS) and gum rosin (GR) can influenced the differences in the homogeneous of thermoplastic starch (TPS) as a matrix of the masterbatch. The using of GMS as an additive with a 36% (wt) concentration of starch showed the most homogeneous surface morphology, destructuring of starch into TPS homogeneously, the basal spacing of organoclay was decreased into 2.04 nm and obtain intercalated structure. The using of GR as an additive with the same concentration of starch, showed a less homogeneous surface morphology, destructuring of starch into TPS is not homogeneous, increased basal spacing to 3.89 nm and obtain exfoliated structure. Furthermore, the increased starch concentrations was also influence on the morphology of masterbatch. Increased of starch concentration caused the non homogeneous morphology of the masterbatch."

"Data XRD dari nanokomposit Ti-Si-N telah dianalisis menggunakan program GSAS berbasis metode Rietveld untuk mengidentifikasa fasa-fasa pembentuk serta komposisinya dan mencari pengaruhnya terhadap kekerasan material tersebut. Telah ditemukan fasa-fasa baru dalam sampel tersebut, disamping fasa-fasa nanokomposit nc-TiN/a-Si3N4 & a-/nc-TiSi2 yang telah banyak dikenal. Dari fasa-fasa kristal yang diperoleh, setelah dilakukan perhitungan fraksi fasa amorf Si3N4 dan TiSi2 maka diperoleh bahwa kekerasan optimal terjadi pada kandungan a-Si3N4 8 wt.%.

---

Phase composition analysis using rietveld methode and it?s influence to the hardness of Ti-Si-N nanocomposites. XRD data of nanocomposites Ti-Si-N have been analysed using GSAS based on Rietveld Method in order to identify phases and their composition as well as its influence on the hardness of these nanocomposites. Several new phases have been found in the sample beside the nc-TiN/a-Si3N4& a-/nc-TiSi2 that have been known widely. From the obtained crystalline phase, after the calculation of amorf Si3N4 and TiSi2 phase fraction, it is found that the optimum hardness can be reached when the fraction of a-Si3N4 phase around 8 wt.%."

"Sintesis membran selulosa asetat dilakukan melalui dua tahap yang meliputi: sintesis organoclay dan sintesis membran. Sedangkan, sintesis organoclay terdiri dari tiga tahapan yaitu purifikasi karbonat, sintesis Na-Bentonit dan sintesis organoclay-ODTMABr. Na-Bentonit dengan kapasitas tukar kation (KTK) 48,749 meq/100 gram bentonit yang diinterkalasi dengan 1 KTK surfaktan ODTMABr menghasilkan Organoclay Terinterkalasi (OCT). Pengaruh interkalasi diamati oleh XRD low angle yang menunjukkan adanya kenaikan nilai basal spacing dari Na-Bentonit ke OCT, baik tanpa maupun dengan purifikasi karbonat, masing-masing dari 15,31 Å ke 20,07 Å dan 15,66 Å ke 19,94 Å. Selulosa asetat (CA) dimodifikasi dengan penambahan nanofiller organoclay-ODTMABr (OCT-C18) dengan metode solvent casting. Karakterisasi yang dilakukan adalah XRD, FTIR, SEM, dan EDX. Pengamatan pengaruh komposisi berat OCT-C18 yang ditambahkan ke dalam larutan selulosa asetat menunjukkan bahwa membran dengan komposisi 7% wt memiliki warna yang paling keruh, secara fisik terasa paling lentur, dan tidak mudah robek.

---

Synthesis of cellulose acetate membranes through two stages which include organoclay synthesis and membrane synthesis. Meanwhile, organoclay synthesis consists of three phases that include carbonate purification, synthesis of Na-Bentonite and organoclay-ODTMABr synthesis. Na-bentonite by cation exchange capacity (CEC) 48.749 meq/100 grams of bentonite which intercalated with 1 CEC ODTMABr surfactant produce organoclay intercalated (OCT). Effect of intercalation was observed by low angle XRD which shows an increase value of basal spacing of Na-Bentonite to OCT, either without or with carbonate purification, respectively from 15.31 Å to 20.07 Å and 15.66 Å to 19.94 Å Å. Cellulose acetate (CA) modified with adding organoclay-ODTMABr (OCT-C18) nanofillers with a solvent casting method. XRD, FTIR, SEM, and EDX characterization was performed. Parameters measured influence of weight percent of OCT-C18 is added to a solution of cellulose acetate. Membrane with a composition of 7 wt% has the most opaque colors, the highest physical resilient, and the strongest (not easily torn)."

"Nanokomposit selulosa asetat telah disintesis dengan menggunakan nanofiller organoclay yang dimodifikasi dengan TiO2. Bentonit Tapanuli yang sebelumnya dikenai proses purifikasi dan penyeragaman kation dimodifikasi dengan ditambahkan TiO2 dengan persen berat yakni 0%, 1%, 3%, 5%, dan 10% terhadap total komposit. Analisis FTIR menunjukkan interkalasi surfaktan telah berhasil dilakukan dengan adanya pita serapan baru dari HDTMABr pada 2636 cm-1 dan 2569 cm-1. Pembuatan nanokomposit dilakukan dengan menggunakan aseton sebagai pelarut dan metode solvent casting sebagai teknik untuk pembuatan film nanokomposit. Aplikasi nanokomposit berupa uji fotodegradasi pada penyinaran sinar matahari langsung, lampu UV, dan tanpa penyinaran selama tiga puluh hari. Diketahui, semakin banyak TiO2 semakin besar komposit yang terdegradasi. Persen penurunan berat hasil uji aplikasi pada penyinaran lampu UV sebesar 4,02% , 13,45%, 18,66%, 22,35%, 27,86%, pada penyinaran langsung sebesar 2,15%, 8,49%, 13,85%, 14,70%, 15,02%, dan pada tanpa penyinaran sebesar 0,16%, 0,16%, 0,18%, 0,20%, 0,26%. Modifikasi nanokomposit dengan penambahan TiO2 sebagai agen fotokatalitik menambahkan sifat baru berupa kemampuan fotodegradas.

---

Nanocomposite cellulose acetate has been synthesized using organoclay nanofiller modified with TiO2. Tapanuli Bentonite were previously subjected to processes of purification and unification of cations then modified with TiO2 that was added as much 0%, 1%, 3%, 5%, 10% weight of the total composite. FTIR analysis showed intercalation with surfactant was successfully carried out in the presence of HDTMABr, indicated by new absorption band at 2636 cm-1 and 2569 cm-1. Fabrication of nanocomposite film was carried out using acetone as solvent and through solvent casting method.

Nanocomposite application in photodegradation test was carried out under direct sunlight radiation, UV light, and without irradiation for thirty days. It's found that the greater the presence amount of TiO2 in the composites, the more weight loss occured due to photodegredation. Percent weight loss in the UV light irradiation are 4,02% , 13,45%, 18,66%, 22,35%, 27,86%, while under direct irradiation, the weight loss was 2,15%, 8,49%, 13,85%, 14,70%, 15,02%, and while without light irradiation was 0,16%, 0,16%, 0,18%, 0,20%, 0,26%. Modification of nanocomposite with the addition of photocatalytic TiO2 as photocatalytic agent has shown the ability of self photodegradation of nanocomposit."

"ABSTRAKPengembangan plastik yang mudah terdekomposisi saat ini sudah banyak di lakukan, terutama dengan menggunakan bahan dasar polimer seperti poly(vinyl alcohol) yang dimodifikasi menjadi komposit. Bio-nanokomposit dibuat dengan metoda solvent casting dari poly(vinyl alcohol) sebagai matriks dan organoclay sebagai nanofiller. Penelitian ini bertujuan mempelajari karakteristik dan sifat mekanik material nanokomposit poly(vinyl alcohol) / organoclay terinterkalasi heksadesiltrimetilamonium bromida (C16). Penelitian ini dilakukan melalui dua tahap yaitu pembuatan organoclay dengan C16; serta sintesis dan karakterisasi nanokomposit poly(vinyl alcohol) / organoclay ? C16. Proses interkalasi terlihat dari pergeseran puncak bentonite dan organoclay yaitu dari 2θ = 6o ke 2θ = 4,9o, dengan nilai basal spacing dari 15,1 Å menjadi 19,7 Å. Kuat tarik tertinggi dimiliki oleh poly(vinyl alcohol) murni dengan nilai 58,02 MPa dan terendah pada nanokomposit poly(vinyl alcohol) / organoclay ? C16 7% dengan nilai 41,33 MPa. Laju transmisi uap air tertinggi dimiliki oleh nanokomposit poly(vinyl alcohol) / organoclay ? C16 7% dengan nilai 0,35 gr/m2/jam dan terendah pada poly(vinyl alcohol) murni dengan nilai 0,62 gr/m2/jam. Nanokomposit poly(vinyl alcohol) / organoclay ? C16 3% memiliki sifat dekomposisi paling baik dan dan sifat dekomposisi yang paling rendah yaitu pada poly(vinyl alcohol) murni.

---

ABSTRACTEasy decomposed plastic development is now being popular, especially with polymer based material such as modified poly(vinyl alcohol) into composites. The bio-nanocomposite made by solvent casting method of poly(vinyl alcohol) as matrix and organoclay as nanofilter. This research aims to study the characteristics and mechanical properties of nanocomposite poly(vinyl alcohol) / hexadecyltrimethylammonium bromide (C16) intercalated organoclay. This study was conducted in two stages, the process of organoclay with C16; as well as the synthesis and characterization of nanocomposite poly(vinyl alcohol) / organoclay - C16. Intercalation process can be seen from the peak shift of bentonite and organoclay that 2θ = 6 ° to 2θ = 4.9 °, with a basal spacing of 15.1 Å to 19.7 Å. The highest tensile strength possessed by pure poly(vinyl alcohol) with a value of 58.02 MPa and the lowest is in the nanocomposite poly(vinyl alcohol) / organoclay - C16 7% by value 41.33 MPa. The highest water vapor transmission rate is owned by nanocomposite poly(vinyl alcohol) / organoclay - C16 7% with a value of 0.35 g/m2/h and the lowest is in the pure poly(vinyl alcohol) with a value of 0.62 g/m2/hr. Nanocomposite poly(vinyl alcohol) / organoclay - C16 3% has the nicest also the most low decomposition propertie, and the nature decomposition is on pure poly(vinylalcohol).;;;"

"Meningkatnya limbah plastik di Indonesia menjadi salah satu masalah di Indonesia. Tujuan dari penelitian ini adalah membuat membran plastik nanokomposit yang memiliki kemampuan terdekomposisi di alam. Sintesis selulosa asetat murni dan nanokomposit SA/OCT-C16 dengan variasi komposisi organoclay 1 wt%, 3 wt%, 5 wt%, dan 7 wt% telah berhasil dibuat dengan metode solvent casting. Struktur bentonit tetap sama meskipun telah mengalami reaksi pertukaran kation hingga menjadi organoclay. Hal tersebut dapat dilihat dengan adanya pita serapan khas bentonit berupa deformasi SI-O-Si pada bilangan gelombang 500-400 cm-1 dan adanya pita serapan khas dari karbon CH2 yang berasal dari surfaktan heksadesiltrimetil amonium bromida (HDTMA-Br) pada bilangan gelombang 2930 cm-1 dan 2842 cm-1. Difraktogram organoclay menunjukkan peningkatan nilai basal spacing dari 15,19 Å menjadi 20,14 Å. Hasil uji tarik menunjukkan bahwa nanokomposit dengan komposisi organoclay 1 wt% memiliki kuat tarik tertinggi yaitu 44,56 MPa dengan kenaikan sebesar 16% dibandingkan dengan selulosa asetat murni. Hasil uji dekomposisi menunjukkan bahwa selulosa asetat mempunyai kemampuan terdekomposisi paling tinggi, yaitu sebanyak 37% sedangkan nanokomposit dengan 1 wt% organoclay terdekomposisi sebanyak 25% selama 60 hari penguburan. Secara umum massa terdekomposisi nanokomposit lebih tinggi daripada massa terdekomposisi plastik komersial.

---

This research is based on the increasing problem of plastic waste in Indonesia. The focus of this research is to produce a nanocomposite plastic membranes that have the ability to decompose in nature better than commercial plastic. Synthesis of cellulose acetate and nanocomposite SA/OCT-C16 with variation in composition of 1 wt%, 3 wt%, 5 wt%, and 7 wt% of organoclay has been successfully created with a solvent casting method. Bentonite structure remain visible although it has undergone a cation exchange reaction to be an organoclay.

It can be seen with their typical absorption bands of bentonite on the form of the deformation of the Si-O-Si at wave number 500-400 cm-1 and the typical absorption band of carbon CH2 derived surfactant hexadecyltrimethylammonium bromide (HDTMA-Br) at wave number 2930 cm-1 and 2842 cm-1. Difractogram on organoclay show the increase of the value of basal spacing of organoclay from 15,19 Å up to 20,14 Å.

The tensile strength test shows that nanocomposite with 1 wt% composition of organoclay has the graetest tensile strength that is equal 44.56 MPa with an increase of 16% compared to pure cellulose acetate. The result of decomposition test shows that pure cellulose acetate has the ability to decompose the highest, which is about 37% whereas nanocomposite with 1 wt% of organoclay only able to decompose as much as 25% during 60 days of burial. In general, the mass of decomposed nanocomposite is higher than the mass of commercial plastic decomposes."

"Nanokomposit Perak, Titanium dioksida, dan Mangan (II,III) oksida (Ag/TiO2/Mn3O4) dengan berbagai rasio molar telah disintesis menggunakan metode hidrotermal. Pengukuran difraksi sinar-X (XRD) mengkonfirmasi struktur nanokomposit Ag/TiO2/Mn3O4 yang terdiri dari struktur kubik Ag, TiO2 anatase, dan Mn3O4 tetragonal. Rasio komposisi unsur nanokomposit Ag/TiO2/Mn3O4 diselidiki dengan fluoresensi sinar-X (XRF). Efek sinergis Ag, TiO2 dan Mn3O4 dapat meningkatkan efisiensi nanokomposit sebagai fotokatalis. Peningkatan efisiensi ditunjukkan dengan melebarnya rentang absorbansi pada hasil pengukuran UV-Vis Diffuse Reflectance. Pengukuran adsorpsi-desorpsi nitrogen menunjukkan bahwa penambahan geraham TiO2 mengakibatkan penurunan luas permukaan spesifik nanokomposit Ag/TiO2/Mn3O4, sedangkan hasil sebaliknya diberikan dengan penambahan geraham Mn3O4. Pada uji fotokatalitik, hasil terbaik ditunjukkan oleh nanokomposit Ag/TiO2/Mn3O4 dengan dominasi Mn3O4 untuk radiasi UV dan cahaya tampak. Pada kondisi optimum, nanokomposit Ag/TiO2/Mn3O4 mampu mendegradasi metilen biru hingga 91% dengan penyinaran selama 2 jam. Uji scavenger mengidentifikasi lubang sebagai spesies yang berkontribusi paling besar pada proses fotokatalitik ini. Uji reusabilitas dan stabilitas pada nanokomposit Ag/TiO2/Mn3O4 menunjukkan hasil positif.

---

Silver, Titanium dioxide, and Manganese (II,III) oxide (Ag/TiO2/Mn3O4) nanocomposites with various molar ratios have been synthesized using the hydrothermal method. X-ray diffraction (XRD) measurements confirmed the structure of the Ag/TiO2/Mn3O4 nanocomposite consisting of a cubic structure of Ag, TiO2 anatase, and tetragonal Mn3O4. The elemental composition ratio of Ag/TiO2/Mn3O4 nanocomposite was investigated by X-ray fluorescence (XRF). The synergistic effect of Ag, TiO2 and Mn3O4 can increase the efficiency of nanocomposites as photocatalysts. The increase in efficiency is indicated by the widening of the absorbance range on the measurement results of UV-Vis Diffuse Reflectance. The nitrogen adsorption-desorption measurements showed that the addition of TiO2 molars resulted in a decrease in the specific surface area of ​​the Ag/TiO2/Mn3O4 nanocomposite, while the opposite result was given by the addition of Mn3O4 molars. In the photocatalytic test, the best results were shown by the Ag/TiO2/Mn3O4 nanocomposite with the dominance of Mn3O4 for UV radiation and visible light. Under optimum conditions, Ag/TiO2/Mn3O4 nanocomposite was able to degrade methylene blue up to 91% with irradiation for 2 hours. The scavenger test identified pits as the species that contributed most to this photocatalytic process. Reusability and stability tests on Ag/TiO2/Mn3O4 nanocomposites showed positive results."

"Membran selulosa asetat / organoclay-HDTMABr dibuat melalui dua tahap sintesis, yaitu sintesis organoclay dan sintesis membran. Sintesis organoclay meliputi tiga tahap, yaitu purifikasi karbonat, preparasi Na-Bentonit, dan sintesis organoclay-HDTMABr. Organoclay-HDTMABr disintesis menggunakan Na-Bentonit dan HDTMABr sebanyak 1 KTK dengan metode ultrasonik, dimana Na-Bentonit yang digunakan memiliki kapasitas tukar kation (KTK) sebesar 48,749 meq/100 gram bentonit. Pengujian XRD pada sampel organoclay menunjukkan interkalasi HDTMABr dapat meningkatkan basal spacing organoclay menjadi 18,80 Å dan 19,04 Å pada masing-masing sintesa dengan purifikasi dan tanpa purifikasi karbonat. Telah dilakukan variasi komposisi organoclay-HDTMABr 1 KTK (OCT-C16) yang ditambahkan pada biokomposit sebagai nanofiller. Hasil sintesis pada penelitian ini dikarakterisasi menggunakan FTIR. Dari kelima variasi komposisi OCT-C16 (0%, 1%, 3%, 5%, dan 7%) yang ditambahkan, variasi 7% OCT-C16 menghasilkan produk membran biokomposit yang paling keruh, paling lentur, dan tidak mudah robek.

---

Cellulose acetate / organoclay-HDTMABr membranes ware prepared ​​through two stages of synthesis, namely : the organoclay synthesis and membrane synthesis. Organoclay synthesis involved three stages : purification of carbonate, preparation of Na-bentonite, and synthesis of organoclay-HDTMABr. Organoclay-HDTMABr was synthesized with the amount of 1 CEC Na-Bentonite and HDTMABr using an ultrasonic method. The Na-Bentonite had a cation exchange capacity (CEC) of 48.749 meq/100 grams of bentonite. XRD measdurement result showed HDTMABr increased the basal spacing of organoclay to 18,80 Å and 19,04 Å for organoclay with carbonate purification and without carbonate purification respetively. The HDTMABr-organoclay (OCT-C16) was added to cellulose acetate as nanofiller with different compositions. The biocomposites obtained in this study, with the clay loading of 0%, 1%, 3%, 5%, and 7% were characterized by FTIR. It was observed that the addition of 7 % OCT-C16 into cellulose acetate membranes produced the most flexible, the most opaque, and most difficult torn membrane."