"Pada penelitian ini baja tahan karat SS304 di las dengan las resistansi titik dengan dua kondisi yaitu kondisi normal (tanpa pickling) dan di pickling. Pengaruh kuat arus terhadap peningkatan kekuatan tarik geser dan diameter nugget di investigasi. Struktur makro dan mikro yang terbentuk pada area lasan juga di investgasi. Hasilnya mengindikasikan peningkatan arus akan meningkatkan kekuatan tarik geser dan diameter nugget. Penghilangan lapisan oksida sebelum pengelasan resistansi titik kurang efisien.

---

In this study, stainless steel SS 304 were welded by resistance spot welding with two initial conditions which are normal condition (without pickling) and pickling. The influence of weld current to improve tensile shear strength and the diameter of nuggets was investigated. Macrostructure and microstructure formed in weld areas were also investigated. The results obtained indicate that the enhancement of weld current will increase tensile shear strength and the diameter of nuggets. However, removing the oxide layer before resistance spot welding carried out were seen less efficient."

"Baja tahan karat Austenitik tipe 304 merupakan jenis yang terluas pemakaiannya, yaitu sekitar 65 -70 % dari total kebutuhan baja tahan karat. Baja ini mempunyai sifat yang sangat reaktif pada temperatur di atas 500 _C, sehingga menimbulkan korosi batas butir ( intergranular corrosion ) pada temperature sensitization ( 500 ? 800 _C ) sesuai dengan beberapa kondisi, antara lain a). proses pengelasan b). perlakuan panas dan c). kondisi lapangan. Hasil pengelasan baja tahan karat austenitik dipengaruhi banyak faktor, antara lain jenis logam pengisi, persiapan material sebelum di las, perlakuan sebelum dan sesudah di las, gas pelindung yang digunakan dan lain-lain. Penelitian ini bertujuan mempelajari pengaruh media pendingin terhadap struktur mikro dan sifat mekanis pengelasan austenitik tipe 304 dengan FCAW dan dengan media pendingin udara, air dan perlakuan preheating serta gas pelindung CO2 dan gas pelindung campuran (CO2 + Argon ). Hasil penelitian enam sampel yang diuji dengan parameter media pendingin yang berbeda dan gas pelindung yang juga berbeda, diperoleh kekuatan tarik dan kekerasan yang bervariasi, mulai dari kekuatan tarik 605 MPa sampai dengan 648 MPa dan kekerasan vickers di HAZ dari 220 HV sampai dengan 268 HV. Hasil pengelasan optimum terdapat pada Sampel B ( media pendingin air dan gas pelindung CO2 ). Pembentukan krom karbida di HAZ, paling banyak terdapat pada Sampel D ( krom 29, 42 wt% ) dan paling sedikit pada Sampel A ( krom 12,25 wt% )

---

Austenitic stainless steel type 304 is the most widely used type, which is about 65 -70% of the total demand for stainless steel. This steel has very reactive properties at temperatures above 500 _C, causing intergranular corrosion at temperature sensitization ( 500 ? 800 _C ) in accordance with several conditions, including a). welding process b). heat treatment and c). field conditions. The results of welding of austenitic stainless steel are influenced by many factors, including the type of filler metal, preparation of the material before welding, treatment before and after welding, the shielding gas used and others. This study aims to study the effect of the cooling medium on the microstructure and mechanical properties of type 304 austenitic welding with FCAW and with air cooling, water and preheating treatment as well as CO2 shielding gas and mixed shielding gas (CO2 + Argon). The results of the six samples tested with different cooling media parameters and different shielding gases, obtained varying tensile strengths and hardness, ranging from tensile strength of 605 MPa to 648 MPa and Vickers hardness in HAZ from 220 HV to 268 HV. The optimum welding results were found in Sample B (water cooling media and CO2 protective gas). The formation of chromium carbide in HAZ was most abundant in Sample D (chrome 29.42 wt% ) and the least in Sample A (chromium 12.25 wt% )."

"Pengelasan Tungsten Inert Gas TIG merupakan pengelasan yang menggunakan elektroda non konsumabel, sehingga dapat dilakukan tanpa logam pengisi. Pengelasan TIG secara umum dilakukan untuk pengelasan stainless steel 304. Material Stainless Steel 304 merupakan material yang umum digunakan di bidang industri perminyakan dan manufaktur. Arus merupakan parameter yang paling umum diubah untuk mencari karakteristik yang berbeda. Namun pengubahan frekuensi masih sangat jarang digunakan dan masihsedikit penelitian yang membahas pengaruh frekuensi terhadap hasil pengelasan. Dalam penelitian ini akan dibahas mengenai pengaruh frekuensi terhadap geometri manik hasil pengelasan pelat SS 304 dengan dimensi 100 mm x 50 mm x 3 mm. Pengelasan dilakukan secara otomatis menggunakan peralatan Power TIG 2200 AC/DC Pulse Welding Machine Gekamac dengan besar arus sebesar 90, 93, 95, 97, dan 100 A dan variasi frekuensi pengelasan sebesar 50-250 Hz dengan jarak 50 Hz. Karakterisasi hasil pengelasan dilakukan melalui makrografi dengan jangka sorong digital ketelitian 0,01 mm dan perangkat lunak Dinolight. Hasilnya adalah pengaruh kenaikan frekuensi terhadap geometri manik las sebanding dengan penurunan arus pengelasan. Bagian yang berbeda hanya geometri lebar manik las bagian tengah.

---

Tungsten Inert Gas TIG welding procedure is done using non consumable electrodes. This method is widely used for welding stainless steel SS 304 components in petroleum and manufacturing industry. Most of the available studies are conducted to observe the influence of various current inputs to the produced weld. Welding frequency, however, has not been discussed significantly regarding to its effect on the result of TIG weld. This research mainly discusses about the effect of welding frequency to bead geometry of welded SS 304 plates. Initial specimens were shaped into 100 mm x 50 mm x 3 mm dimension using hand jigsaw. The welding procedures were done automatically using Power TIG 2200 AC DC Pulse Welding Machine Gekamac instrument with variations on welding current and frequency of 90, 93, 95, 97, 100 A and 50 250 Hz with 50 Hz step, respectively. Characterizations of produced welds were done by macrography using digital caliper and Dinolight software. The result is effect for higher frequency to bead geometry are the same with effect of lower current."

"Aplikasi pengelasan dengan material yang berbeda mendapatkan keuntungan dari segi ekonomis. Pada penelitian ini digunakan material antara baja tahan karat austenitik dan baja karbon rendah SS 400 dengan jenis kawat las yang berbeda yaitu ER 309 dan ER 316 dengan metode GMAW. Hal ini bertujuan untuk melihat pengaruh dari sifat mekanis material. Untuk mengidentifikasi fase penyusun pada sambungan las tak sejenis dilakukan melalui mikroskop optik (OM), dan untuk menguji kekerasan dilakukan menggunakan micro Vickers untuk mendapatkan sifat mekanik lasan yang terdiri dari logam dasar (BM), daerah terpengaruh panas (HAZ), dan logam las (WM). Dari hasil percobaan didapatkan bahwa nilai kekerasan tertinggi ada pada daerah WM dan HAZ sebab memiliki butir yang lebih halus dibandingkan dengan logam induk. Butir yang halus ini akan membuat semakin banyak batas butir sehingga memiliki kekerasan yang lebih tinggi. Struktur mikro yang didapat pada BM dan HAZ SS 316 memiliki fasa austenit sedangkan BM dan HAZ SS 400 memiliki fasa ferit dan perlit. Pada daerah logam las (WM) dengan kawat las ER 309 memiliki kekerasan tertinggi sebesar 258 Hv dibandingkan dengan nilai kekerasan logam las menggunakan kawat las ER 316, 253 Hv, hal ini disebabkan karena adanya kandungan Cr yang lebih tinggi pada ER 309 (23,5%), dibandingkan dengan menggunakan kawat las ER 316 (19,25%).

---

Welding applications with different materials have an economic advantage. In this study, materials between austenitic stainless steel and SS 400 low carbon steel were used with different types of welding wire, namely ER 309 and ER 316 with the GTAW method. It aims to see the effect on the mechanical properties of the welded joints. To identify the constituent phases of dissimilar welded joints, an optical microscope (OM) was carried out, and the hardness testing, micro Vickers was used to obtaining the mechanical properties of the weldment, which consists of base metal (BM), heat affected zone (HAZ), and weld metal (WM). The experimental results show that the highest hardness values are in the WM and HAZ regions because they have finer grains than the parent metal. These fine grains will create more grain boundaries so that they have higher hardness. The microstructure obtained in BM and HAZ SS 316 has an austenite phase, while BM and HAZ SS 400 have ferrite and pearlite phases. In the weld metal (WM) area with ER 309, the highest hardness is 258 Hv compared to the hardness value of welding metal using ER 316, 253 Hv. This is due to the higher Cr content in ER 309 (23.5 %) than ER 316 (19.25%)."

"Stainless Steel merupakan logam yang banyak digunakan untuk keperluan industri karena stainless steel memiliki ketahanan korosi yang baik dan tahan terhadap temperatur tinggi. Pada umumnya, penggunaan stainless steel membutuhkan teknik penyambungan yang salah satunya adalah pengelasan. Pemilihan parameter yang tepat sangat dibutuhkan untuk mendapatkan hasil pengelasan yang optimal. Pada penelitian ini dilakukan percobaan untuk mengetahui hubungan kuat arus, heat time, dan hold time terhadap kekuatan tarik yang dihasilkan dengan menggunakan teknik pengelasan RSW. Mesin las yang digunakan adalah WIMTOUCH 1800 tipe JPC 35. Kuat arus yang digunakan adalah 7000 A, 7700 A, dan 8400 A; heat time yang digunakan adalah 5 cycle, 10 cycle, dan 15 cycle; dan hold time yang digunakan adalah 5 cycle, 10 cycle, dan 15 cycle. Karakterisasi hasil las dilakukan melalui analisis diameter weld nugget dengan menggunakan mikroskop digital dan pengujian kekuatan tarik. Dari hasil penelitian yang didapatkan, diketahui bahwa semakin besar kuat arus dan heat time maka diameter weld nugget yang dihasilkan akan semakin besar sedangkan trendline dari hold time pada penelitian ini tidak dapat terlihat. Nilai kekuatan tarik maksimum yang didapatkan adalah 11,3 kN dengan parameter pengelasan arus 7700 A, heat time 15 cycle, dan hold time 10 cycle.

---

Stainless Steel is a metal that is widely used for industrial purposes because stainless steel has good corrosion resistance and resistance to high temperatures. In general, the use of stainless steel requires a technique of connection one of which is welding. Selection of appropriate parameters is needed to obtain optimal welding results. In this experiment, the experiment was conducted to find out the relationship of current strength, heat time, and hold time to the tensile strength produced by using RSW welding technique. The welding machine used is WIMTOUCH 1800 type JPC 35. The current strength used is 7000 A, 7700 A, and 8400 A the heat time used is 5 cycles, 10 cycles, and 15 cycles and hold time used is 5 cycles, 10 cycles, and 15 cycles. The characterization of the welding results is done by analyzing the diameter of the weld nugget by using digital microscope and tensile strength test. From the results obtained, it is known that the greater the current strength and heat time then the diameter of the weld nugget generated will be greater while the trendline of hold time in this study can not be seen. The maximum tensile strength value obtained is 11.3 kN with welding parameters 7700 A, heat time 15 cycles, and hold time 10 cycles. "

"Pada penelitian ini dilakukan pengelasan pipa orbital dengan pengelasan Tungsten Inert Gas (TIG) arus pulsa tanpa logam pengisi (autogenous) pada pipa baja tahan karat tipe 304. Dimensi dari material uji adalah diameter luar 114 mm dan ketebalan 3 mm. Tujuan dari penelitian ini untuk mengetahui pengaruh parameter arus pulsa, posisi las dan siklus kerja terhadap karakteristik geometri las, sifat mekanik dan struktur mikro. Variasi parameter dalam penelitian ini yaitu arus konstan, arus pulsa dan siklus kerja. Arus rata-rata dari setiap parameter dibuat sama yaitu 100 ampere, namun pada arus pulsa terdapat variasi arus puncak, arus dasar, waktu arus puncak dan waktu arus dasar. Kecepatan pengelasan yang digunakan adalah 1,4 mm/detik. Hasil penelitian ini menunjukkan bahwa pada pengelasan dengan variasi arus pulsa menghasilkan lebar manik las yang lebih besar dari pada pengelasan dengan arus konstan. Hasil lebar manik las berbanding lurus dengan peningkatan arus pulsa. Terjadi penurunan kekuatan tarik sebesar 23,95 % pada parameter 65-B posisi las 0⁰ dan kenaikan kekuatan tarik sebesar 16,09 % pada parameter 65-A posisi las 180⁰ terhadap kekuatan tarik logam dasar. Pada kekerasan mikro dengan metode vickers, terjadi penurunan kekerasan terbesar pada daerah HAZ dan daerah las sebesar 20,50 % dan 7,22 % pada parameter 50-C. 

---

Orbital pipe welding was carried out in this research by pulse current Tungsten Inert Gas (TIG) welding without metal filler (autogenous) of 304 stainless steel pipes. The dimensions of the specimens were 114 mm outside diameter and the thickness of 3 mm. The purpose of this study was to determine the effect of pulse current parameters, weld position and duty cycle on the characteristics of weld geometry, mechanical properties and microstructure. Variation of parameters in this study were constant current, pulse current and duty cycle. The average current of each parameter was the same 100 ampere, but in the pulse current there were variations in peak current, base current, peak current time and base current time. The welding speed used was 1.4 mm/second. The results of this study indicate that in the welding with variations in pulse currents it produces a larger weld bead width than the welding with a constant current. The width of the weld bead was directly proportional to the increase in pulse current. There was a decrease in tensile strength of 23.95% in the parameter 65-B weld position 0⁰ and an increase in tensile strength of 16.09% in parameter 65-A weld position 180⁰ against the tensile strength of the base metal. In the micro hardness with vickers method, the greatest hardness occurred in the HAZ region and the weld area by 20.50% and 7.22% in the 50-C parameter."

"Peningkatan penggunaan pengelasan dengan dua material yang berbeda selalu di gunakan pada dunia industri, pengelasan dengan dua material yang berbeda terus meningkat penggunaannya. Tujuannya untuk mendapatkan spesifikasi yang baik namun tetap menekan biaya yang digunakan. Material yang sering digunakan dalam dissimilar welding adalah stainless steel 304 dan structure steel 400. Kedua material ini memiliki kelebihan masing-masing. Untuk memperoleh hasil pengelasan yang baik, diperlukan pemilihan parameter yang tepat agar tidak timbul permasalahan seperti distorsi pada pengelasan. Distorsi merupakan sebuah proses perubahan bentuk pada material akibat pengelasan.Penelitian ini bertujuan untuk mengetahui pengaruh kuat arus dan kecepatan pengelasan terhadap kekuatan material pada dissimilar Gas Metal Arc Welding (GMAW). Kecepatan yang di gunakan bervariasi antara lain 3, hingga 3,25 mm/s. Hasil pengelasan yang telah di dapatkan dari variasi kecepatan dan variasi ampere kemudian dilakukan pengujian microstructur. Dari hasil yang di dapatkan, bahwa terjadi perubahan dari masing-masing microhardness di masing-masing daerah pengelasan.

---

In industrial world, research and develompent of welding with two different materials is always improving. The purpose of this research is to get an ideal specification without increasing the industrial cost. Materials that is often used in dissimilar welding is stainless steel 304 dan structure steel. These two materials have advantages each. To get a good result in welding, chosing the right parameters is a must, in order to avoid trouble like distortsion in the welding process. Distorsion is an effect caused by welding that changes the material form.

This research purposes is to observe the effect of strong current in electricity and the welding speed to the strenth of materials in dissimilar Gas Metal Arc Welding (GMAW) process. The speed that was used in this research varies from 3 mm/s to 3.25 mm/s. The welding results from speed and current parameters was tested to see the material microstructure. From those results, we got a conclusion, that a microhardness deformation occured in each welded areas."

"Pengelasan memiliki peran penting dalam berbagai aplikasi kehidupan sehari-hari, seperti struktural jembatan dan komponen engineering. Selain itu, baja tahan karat austenitik 316L memiliki keunggulan dalam mengatasi korosi dan permasalahan weld decay sehingga seringkali digunakan di berbagai industri. Selama proses pengelasan suatu material transfer panas dan penggunaan elektroda tungsten yang tidak tepat dapat mempengaruhi sifat mekanis produk. Oleh karena itu, penelitian dilakukan untuk mengusulkan penggunaan metode Tungsten Inert Gas (TIG) autogenous dengan variasi sudut ujung elektroda tungsten untuk mengoptimalkan hasil lasan baja tahan karat 316L. Studi ini mencakup pengaruh geometri manik las, karakterisasi mikrostruktur, dan profil kekerasan. Hasil penelitian menunjukkan bahwa sudut ujung elektroda tungsten memengaruhi lebar dan kedalaman manik las, serta rasio W/D. Meskipun belum mencapai rentang nilai yang dianggap aman terhadap kegagalan retak solidifikasi, sudut ujung elektroda 90º hingga 180º menunjukkan potensi untuk mencapai rentang tersebut. Pengaruh mikrostruktur menunjukkan pengaruh sudut ujung terhadap arah pertumbuhan dendrit, dan profil kekerasan yang merata pada sudut ujung 90º. Penelitian ini memberikan wawasan tentang pengaruh sudut ujung elektroda tungsten dan variasinya terhadap hasil lasan baja tahan karat 316L, dengan harapan memberikan kontribusi pada pemahaman dan pengembangan proses pengelasan yang optimal.

---

Welding plays an important role in various daily life applications, such as bridge structures and engineering components. In addition, 316L austenitic stainless steel has the advantage of overcoming corrosion and weld decay problems so it is often used in various industries. During the welding process of a material heat transfer and improper use of tungsten electrodes can affect the mechanical properties of the product. Therefore, a study was conducted to propose the use of autogenous Tungsten Inert Gas (TIG) method with varying tungsten electrode tip angle to optimize the weld yield of 316L stainless steel. The study includes the influence of weld bead geometry, microstructure characterization, and hardness profile. The results show that the tungsten electrode tip angle affects the width and depth of the weld bead, as well as the W/D ratio. Although it has not yet reached the range of values considered safe against solidification crack failure, tip angles of 90º to 180º show the potential to reach that range. The influence of microstructure shows the effect of tip angle on the direction of dendrite growth, and an even hardness profile at a tip angle of 90º. This research provides insight into the effect of tungsten electrode tip angle and its variations on 316L stainless steel weld yields, with the hope of contributing to the understanding and development of optimized welding processes."

"ABSTRAKPengelasan logam yang berbeda atau Dissimilar Metal Welding (DMW) adalah proses yang unik dan kompleks karena di setiap zona di daerah pengelasan logam yang berbeda memiliki struktur dan karakteristik yang unik. Struktur yang terbentuk pada masing-masing zona memiliki efek yang signifikan pada sifat-sifat logam las. Dalam penelitian ini, tujuan utamanya adalah untuk menyelidiki evolusi struktur mikro dan mode distribusi sifat mekanik dari pengelasan pelat baja HY80 dan baja tahan karat tipe dupleks 2205 yang dilas dengan menggunakan las manual Shielded Metal Arc Weld (SMAW). Struktur mikro dari setiap zona logam las diamati. Pelat spesimen dilas dengan menggunakan logam pengisi AWS A5.22 DW 309L (E309L) dan AWS A5.22 DW2209 (E2209). Ditemukan bahwa elektroda AWS A5.22 DW 309L memberikan keseimbangan antara fase austenit dan ferit di zona logam inti las yang berbeda dari sambungan baja Dupleks SS2205 dan HY80. Hasilnya menunjukkan bahwa distribusi kekerasan dari sambungan yang berbeda dari proses pengelasan ini dipengaruhi oleh evolusi struktur mikro, di mana kekerasan tertinggi diperoleh pada daerah HAZ. Nilai puncak kekerasan pada daerah HAZ logam dasar HY 80 ditemukan di daerah dekat garis fusi. Struktur mikro logam induk baja Dupleks SS 2205 menunjukkan butiran halus dengan struktur ferit dan austenit, dimana ferit ditunjukan dengan warna gelap dan austenit dengan warna terang. Pada bagian tertentu ditemukan sejumlah inklusi terak sebagai bintik hitam. Struktur mikro dari logam las menunjukkan butiran kasar austenit bersama dengan beberapa inklusi terak sebagai bintik hitam. Zona yang terkena panas dari pelat baja HY80 menunjukkan butiran kasar austenit dan ferit, sedangkan zona yang terkena pan as dari DSS 2205 menunjukkan garis fusi tipis dengan butiran kasar ferit sebagai zona gelap dan butiran kasar austenit sebagai zona terang. Tingkat variasi dalam kandungan ferit logam las juga diamati. Secara keseluruhan hasil pengelasan dengan menggunakan elektroda E 2209.

---

ABSTRACTDissimilar Metal Welding (DMW) is a unique and complex process because in each zone in different metal welding areas it has unique structure and characteristics. The structure formed in each zone has a significant effect on the properties of weld metal. In this study, the main objective was to investigate the evolution of microstructure and mechanical distribution modes of welding of HY80 steel plates and duplex 2205 stainless steel welded using Shielded Metal Arc Weld (SMAW) manual welding. The microstructure of each weld metal zone is observed. The specimen plate is welded using AWS A5.22 DW 309L and AWS A5.22 DW 2209 filler metal. It was found that AWS A5.22 DW 309L electrodes provide a balance between the austenite and ferrite phases in the weld metal zone which is different from the DSS and HY80 steel connections. The results show that the hardness distribution of the joints is different from this welding process, where the highest hardness is obtained in the HAZ region. Value of peak hardness in the HAZ region of base metal HY 80 is found in the area near the fusion line. The microstructure of base metal DSS 2205 shows fine grains with ferrite structures, with dark colors and bright austenites. In certain parts a number of inclusions of slag are found as black spots. The microstructure of the weld metal shows austenite coarse grains along with some inclusions of slag as black spots. The heat-affected zone of the HY80 steel plate shows coarse austenite and ferrite grains, while the heat-affected zone of DSS 2205 shows a thin fusion line with coarse grains of ferrite as a dark zone and coarse austenitic grains as a bright zone. There is a observed degree of variation in weld metal ferrite content. "

"Tujuan dari studi ini adalah mengevaluasi perubahan-perubahan dalam struktur mikro dan sifat mekanis dari baja tahan karat 304L dan 3l6L dibawah pengelasan perbaikan berulang. Perubahan-perubahan dari kedua material tersebut kemudian diperbandingkan satu sama lain. Pengelasan dan pengelasan perbaikan dilaksanakan dengan GTAW. Proses pengelasan GTAW dilaksanakan menggunakan logam pengisi ER308L untuk baja tahan karat 304L dan ER3l6L untuk baja tahan karat 316L. Spesimen dari logam dasar dan kondisi berbeda dari perbaikan GTAW dipelajari dengan melihat perubahan struktur mikro, komposisi kimia dari fase-fase, ukuran butir dalam daerah terpengaruh panas dan efek terhadap sifat mekanis. Struktur miko diinvestigasi menggunakan mikroskop optik dan scanning electron microscopy (SEM). Komposisi kimia dari base material ditentukan dengat optical emission specffometer. Komposisi kimia dari inti las, daerah terpengaruh panas dan logam induk ditentukan dengan XRF Analyzer. Komposisi kimia dari fase-fase ditentukan dengan Energt Dispersive X' ray Analysis (EDAX). Pengujian mekanik yang dilakukan uji tarik, kekuatan impak Charpy-V, dan uji keras mito Vickers. Permttkaan patahan diamati dengan foto makro dan detail morfologi permukaan patahan pada awal dan tengah atau ujung permukaan patahan diinvestigasi dengan scanning electron microscopy (SEM). Kekerasan dari daerah terpengaruh panas menunrn sesuai dengan peningkatan jumlah perbaikan. Secara umum peningkatan dalam kekuatan tarik (UTS) terjadi dalam pengelasan. Pada perbaikan pertama suatu penurunan bertahap dalam kekuatan Tarik (UTS) terjadi tetapi nilai kekuatan tarik (UTS) tidak kurang dat', base metal. Pengxangan signifikan dalam kekuatan impak charpy-V dengan jumlah perbaikan las diamati dengan lokasi takikan di daerah terpengaruh panas. Perubahan-perubahan yang sama terhadap struktur miko dan sifat mekanis terjadi pada kedua tipe baja tahan karat tersebut. Perbedaannya adalah untuk kekuatan tarik dan kekuatan impak pada hasil pengelasan baja tahan karat 304L lebih baik daripada 316L.

---

The purpose of this study is to evaluate changes in the micro structural and mechanical properties of stainless steel 304L and 3l6L under repeated repair welding. The changes of both of material then will be in comparation to each other. The welding and the repair welding were conducted by gas tungsten arc welding (GTAW). The GTAW welding process w.rs performed using ER308L filler metals for stainless steel 304L and ER3I6L filler metals for stainless steel 316L. Specimen of the base metal and different conditions of gas tungsten arc welding repairs were studied by looking in the micro structural changes, the chemical composition of the phases, the grarn size (in the heat affected zone) and the effect on the mechanical properties. The microstructure was investigated using optical microscopy (OM) and scanning electron microscopy (SEM). The chemical composition of the base material was determined using optical emission spectrometer. The chemical composition of weld metal, heat affected zone and base metal was determined using XRF Analyzer. The chemical composition of the phases was determined using energy dispersive X-ray Analysis (EDAX). Mechanical testing consist of tensile tests, Charpy-V impact resistance and Vickers hardness tests were conducted. Detail of fracture surface morphologies in beginning and centre or end of fracture was investigated using scanning electron microscopy (SEM). Hardness of the heat affected zone decreased as the number of repairs increased. Generally an increase in the ultimate tensile strength (UTS) occuned with welding. At the first repair, a gradual decrease in UTS occurred but the values of UTS were not less than values of the base metal. Signif,rcant reduction in Charpy-V impact resistance with the number of weld repairs were observed when the notch location was in the HAZ. T"be similar changes in the micro structural and mechanical properties occured in both of type of stainless steel. The difference were for the values ofUTS and Charpy-V impact resistance of welding specimen of stainless steel 304L more tlan values of stainless steel 316L."