Arvinda Widyana
"Katalis heterogen dengan support silika berpori yang disintesis dengan teknik co-Micelle/Emulsion Templating (co-MET) memiliki porositas yang seragam. Penggunaan polimer kationik, 2–(Acryloyloxy)–N,N,N–Trimethylethanaminium Chloride dalam teknik co-MET berfungsi untuk menstabilkan emulsi dan membentuk struktur mesopori.
Dalam penelitian ini FeCl3 dan HSO3CF3 diimpregnasikan pada silika makro/mesopori yang dihasilkan kemudian dikarakterisasi menggunakan SEM, EDS, FTIR, dan XRD. Data SEM menunjukkan bahwa pori yang dihasilkan pada silika semakin meningkat seiring bertambahnya konsentrasi polimer kationik. Pada FTIR, impregnasi FeCl3 dan HSO3CF3 berhasil dengan adanya peak pada 1036 cm-1 (ikatan Si-O-Fe), 462 cm-1 (vibrasi Fe-Cl) dan 615 cm-1 (ikatan C-S).
Uji katalitik reaksi antara benzaldehid dan etanol menunjukkan bahwa katalis HSO3CF3-silika makro/mesopori dengan konsentrasi 5% polimer kationik memiliki hasil yang lebih baik dibandingkan katalis dengan konsentrasi polimer kationik 0,5%, 1%, 2,5% dan 10%.

Heterogeneous catalysts with porous silica support whichwere synthesized by co-Micelle/Emulsion Templating (co-MET) techniques have uniform porosity. The use of cationic polymers, 2-(Acryloyloxy)-N,N,N-trimethylethanaminium chloride in co-MET technique serves to stabilize the emulsion and form mesoporous structure.
In this study, FeCl3 and HSO3CF3 were impregnated into macro/mesoporous silica and then were characterizated using SEM, EDS, FTIR, and XRD. SEM data show that the silica pores generated in increases with increasing concentrations of cationic polymer. On FTIR spectrum, impregnation of FeCl3 and HSO3CF3 proven by the peak at 1036 cm-1 (Si-O-Fe bond), 462 cm-1 (vibrations of Fe-Cl) and 615 cm-1(C-S bond).
Catalytic reaction between benzaldehid and ethanol shows that HSO3CF3-Silica macro/mesoporous catalyst with a 5% concentration of cationic polymer has the best result than those with cationic polymer concentration of 0,5%, 1%, 2,5% and 10%.
"
Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2013
S52440
UI - Skripsi Membership  Universitas Indonesia Library
cover
Pandapotan, David Chandra
"Dalam penelitian ini, SiO2 berpori disintesis dari prekursor tetraetil ortosilikat (TEOS) melalui teknik co-micelle emulsion templating (co-MET) untuk digunakan sebagai padatan pendukung katalis asam Lewis AlCl3. Teknik co-MET dilakukan dengan memvariasikan jenis template (PEG 4000 dan akrilamida) dan persen PEG (2,5%, 5%, 10%, 15% dan 20%). Padatan pendukung yang terbentuk dikarakterisasi dengan FTIR, SEM-EDS, danXRD sedangkan katalis asam dikarakterisasi dengan SEM-EDS dan FTIR untuk membuktikan terjadinya imobilisasi asam tersebut.
Dari karakterisasi menggunakan SEM-EDS, terlihat bahwa template PEG 5% memberikan pori-pori yang seragam dan teratur dengan ukuran makro. Katalis yang terbentuk digunakan pada reaksi antara benzaldehida dan metanol dengan memvariasikan jenis padatan pendukung, waktu reaksi, dan suhu reaksi.
Hasil produk dianalisis dengan kromatografi gas untuk mengetahui persen konversi , persen yield, dan persen selektivitas, kemudian GC-MS untuk mengetahui jenis dan komposisi produk yang dihasilkan. Kondisi optimum diperoleh pada suhu reaksi 50oC selama 8 jam yang menghasilkan persen konversi sebesar 68,41%, persen yield sebesar 33,09%, dan selektivitas sebesar 81,94%. Produk utama yang dihasilkan adalah benzaldehid dimetil asetal.

In this study, porous silica was synthesized from tetraethyl ortoslicate (TEOS) precursor through co-micelle emulsion templating (co-MET) technique to be used as a solid support of the Lewis acid AlCl3. Co-MET technique was conducted by varying template type (PEG 4000 and acrylamide) and percentage of PEG (2,5%, 5%, 10%, 15% dan 20%). The forming solid supporst were then characterized by FTIR, SEM-EDS and XRD while the acid catalysts were characterized by SEM-EDS and FTIR to verify acid immobilization.
From SEM- EDS analysis, it is shown that PEG 5% template gave uniform, ordered and interconnected macropore. The catalyst was then used for benzaldehyde and methanol reaction by varying the kind of catalyst support, reaction time and reaction temperature.
The resulting products were analyzed by GC to determine the percentage of conversion, yield and selectivity, and analyzed by GC-MS to determine structure and composition of the products. The optimum condition is obtained over reaction temperature of 50oC and reaction time of 8 hours which gave benzaldehyde conversion of 68,4%, yield of 33,09%, and selectivity of 81,94%. The main product of the reaction is benzaldehyde dimethyl acetal.
"
Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2013
S52801
UI - Skripsi Membership  Universitas Indonesia Library
cover
Lauditta Indahdewi
"Sintesis silika berpori dilakukan melalui teknik co-micelle emulsion templating (co-MET) untuk digunakan sebagai pendukung katalis AlCl3. Teknik co-MET menggunakan dua template polimer, yaitu PEG 4000 dan poliakrilamida. Konsentrasi PEG divariasikan pada 2,5%, 5%, dan 10%. Silika makro/mesopori dikarakterisasi dengan BET, FTIR, SEM-EDS, dan XRD sedangkan silika yang telah diimpregnasi oleh AlCl3 dikarakterisasi dengan SEM-EDS dan FTIR untuk membuktikan terjadinya impregnasi AlCl3 pada permukaan silika. Dari karakterisasi menggunakan SEM-EDS, terlihat bahwa silika dengan template PEG 5% memberikan pori-pori yang seragam dan teratur. Silika tersebut digunakan sebagai katalis untuk reaksi esterifikasi antara gliserol dan asam lemak, yaitu asam oktanoat dan dekanoat dengan memvariasikan jenis padatan pendukung, waktu reaksi, dan suhu reaksi.
Hasil produk esterifikasi dianalisis dengan HT-GC dan HPLC untuk mengetahui besar persen konversi, kemudian HTGC-MS untuk mengetahui jenis dan komposisi produk yang dihasilkan. Kondisi optimum diperoleh pada reaksi gliserol dan asam dekanoat menggunakan katalis AlCl3 yang terimpregnasi pada SiO2 makro/mesopori dengan konsentrasi PEG 5% dengan suhu 100°C selama 6 jam yang menghasilkan persen konversi sebesar 97,6%. Produk utama yang dihasilkan adalah tricaprin sebesar 30,19% dari total keseluruhan produk.

Synthesis micro/mesoporous silica through co-micelle emulsion templating (co-MET) technique to be used as a support catalyst AlCl3. co-MET technique was conducted by two polymer templates, which is PEG 4000 and polyacrylamide. Concentrations of PEG are varying 2.5%, 5%, and 10%. The forming catalyst support was characterized by BET, FTIR, SEM-EDS, and XRD while the modified catalysts were characterized by SEM-EDS and FTIR to verify impregnation of AlCl3 on silica surface. From SEM-EDS analysis, it is shown that PEG 5% template gave uniform, ordered and interconnected macrospores. The synthesized catalyst was used for esterification reaction, between glycerol and fatty acid, which is octanoic acid and decanoic acid with varying solid support catalyst, reaction time and temperature.
The resulting products were analyzed by HT-GC and HPLC to determine the percentage of conversion, and analyzed by HTGC-MS to determine structure and composition of the products. The optimum condition is obtained over reaction between glycerol and decanoid acid using catalyst AlCl3/silica with concentration of PEG of 5% with temperature of 100°C and reaction time 6 hours which is gave 97.6% of fatty acid conversion. The main product of the reaction is tricaprin which is gave 30.19% from all total products.
"
Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2014
S55979
UI - Skripsi Membership  Universitas Indonesia Library
cover
Davis Rozano Besthari
"Telah dibuat fotokatalis magnetik berupa komposit Fe3O4/TiO2 dan Fe3O4/SiO2/TiO2 dengan metode Heteroaglomerasi. Komposit Fe3O4/TiO2 (F/T) dengan rasio massa 1:1, Fe3O4/SiO2/TiO2 (F/S/T) dengan rasio massa 3:1:4, dan Fe3O4/SiO2/TiO2 (F/S/T) dengan rasio massa 2:1:3 berturut-turut memiliki kandungan silika (SiO2) sebesar 0%, 12,5%, dan 16,65%. Karakterisasi komposit dilakukan menggunakan Spektroskopi Transformasi Fourier Infra Merah (FTIR),Difraksi Sinar-X (XRD), dan Vibrating Sample Magnetometer (VSM). Spektrum FTIR komposit-komposit tersebut menunjukkan keberadaan puncak serapan yang bersesuaian dengan puncak serapan konstituen penyusunnya. Pola difraksi Sinar-X ketiga komposit menunjukkan keberadaan fasa kristal magnetit dari Fe3O4 yang bersifat superparamagnetik serta anatase dan rutil dari TiO2 yang bersifat fotoaktif. Kurva histeresis dan besaran-besaran kemagnetan hasil pengukuran menggunakan VSM menunjukkan komposit-komposit tersebut berkelakuan superparamagnetik. Pengaruh kandungan silika (SiO2) pada komposit diamati dengan membandingkan kemampuannya mengurangi konsentrasi larutan berair dari Methylene Blue. Hasil pengamatan menunjukkan bahwa peningkatan kandungan silika (SiO2) pada komposit meningkatkan kemampuan adsorpsi komposit.

Fe3O4/TiO2 and Fe3O4/SiO2/TiO2 composites were prepared by Heteroaglomeration Method. Fe3O4/TiO2 (F/T) with mass ratio 1:1, Fe3O4/SiO2/TiO2 (F/S/T) with mass ratio 3:1:4, and Fe3O4/SiO2/TiO2 (F/S/T) with mass ratio 2:1:3 have silica (SiO2) content of 0%, 12,5%, and 16,65% respectively. All prepared composites were characterized by Fourier Transformation Infra Red (FTIR) Spectroscopy, X-Ray Diffraction (XRD), and Vibrating Sample Magetometer (VSM). FTIR spectrum of all composites showed absorption peaks associate with they constituent. X-Ray Diffraction patterns showed that magnetite crystal phase of Fe3O4 which is superparamagnetic and rutil & anatase of TiO2 which is photoactive were exist in all composites. The values of various magnetic parameters from magnetization hysteresis loop of all composites showed that they were superparamagnetic. The influence of silica (SiO2) in the composites was observed by compare their ability to reduce the concentration of aqueous solution of Methylene Blue. The result showed that the more silica (SiO2) content in the composites, the more they adsorption capacity."
Depok: Fakultas Teknik Universitas Indonesia, 2013
S45791
UI - Skripsi Membership  Universitas Indonesia Library
cover
Lintannisa Rahmatia
"Sintesis dan Aplikasi Nanokomposit Berbasis Selulosa Corn Cob - TiO2/ZnO sebagai Katalis pada Konversi Glukosa Menjadi 5-Hidroksimetilfurfural dan Asam Levuinat Selulosa dapat diisolasi dari limbah corn cob tongkol jagung yang akan digunakan untuk sintesis nanokomposit berbasis selulosa yang dimodifikasi dengan nanopartikel anorganik TiO2/ZnO sehingga memiliki sifat unggul yang berasal dari gabungan sifat keduanya. Metode yang digunakan untuk isolasi selulosa adalah perlakuan alkali dan hidrolisis asam. Hasil isolasi dan sintesis tersebut dikarakterisasi dengan menggunakan instrumen FTIR, XRD, TEM dan SEM. Rendemen selulosa hasil isolasi diperoleh sebesar 57,51. TiO2 dan ZnO hasil sintesis berukuran nano dengan struktur masing-masing berupa anatase dan heksagonal wurtzite. Nanokomposit selulosa ndash; TiO2/ZnO dapat diaplikasikan sebagai katalis pada konversi glukosa menjadi 5-Hidroksimetilfurfural dan produk sampingnya yaitu asam levulinat dengan uji kuantitatif nya menggunakan HPLC. Kondisi optimum pembentukan 5-Hidroksimetilfurfural dari konversi glukosa adalah pada suhu 180oC selama 210 menit, dengan komposisi glukosa sebanyak 30 mg dan katalis 15 mg. Laju reaksi konversi glukosa menjadi 5-hidroksimetilfurfural mengikuti reaksi orde 1 dengan energi aktivasi yang diperoleh dengan perhitungan Arhenius adalah sebesar 37,61 kJ/mol untuk reaksi penguraian glukosa menjadi produk, 29,28 kJ/mol untuk reaksi pembentukan HMF dan 22,12 kJ/mol untuk reaksi pembentukan LA,

Synthesis and Application Nanocomposite Based Corn Cob Cellulose TiO2 ZnO as Catalyst in Glucose Conversion to 5 Hydroxymethylefurfural and Levulinic Acid Cellulose can be isolated from corn cob waste to be used for the synthesis of cellulose based nanocomposites modified with inorganic TiO2 ZnO nanoparticles so as to have superior properties derived from their combined properties. The methods used for cellulosic isolation are alkaline treatment and acid hydrolysis. The isolation and synthesis results were characterized using FTIR, XRD, TEM and SEM instruments. The yield of isolated cellulose was obtained at 57,51. TiO2 and ZnO of nano sized synthesis with their respective structures in the form of anatase and hexagonal wurtzite. Nanocomposite cellulose TiO2 ZnO can be applied as a catalyst on conversion of glucose to 5 Hydroxymethylfurfural and its byproducts of levulinic acid with its quantitative test using HPLC. The optimum conditions of 5 Hydroxymethylfurfural formation of glucose conversion were at 180 C for 210 min, with a glucose composition of 30 mg and a catalyst of 15 mg. The rate of glucose conversion reaction to 5 hydroxymethylfurfural follows the reaction of order 1 with the activation energy obtained by Arhenius calculation is 37.61 kJ mol for the decomposition reaction of glucose into product, 29.28 kJ mol for HMF forming reaction and 22.12 kJ mol for LA forming reaction."
Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2018
T49887
UI - Tesis Membership  Universitas Indonesia Library
cover
Jonbi
"ABSTRAK
Penggunaan beton bertulang sebagai pelat lantai pada pabrik aki, khususnya di ruang formation dan container charge masih banyak dijumpai kendala: terkelupasnya permukaan beton, timbulnya lubang-lubang pada lantai. Selain mengganggu aktivitas kegiatan produksi juga akan mencemari lingkungan. Pada ruang formation dan container charge beban yang bekerja cukup berat yakni beban forklift (± 2ton), bahan yang digunakan mengandung H SO dengan konsentrasi 20% dan beberapa bagian temperatur proses 60oC - 70°C.
Masalah yang ada : mencari bahan alternatif yang dapat digunakan sebagai pelapis permukaan beton. Berdasarkan informasi produk kimia konstruksi, epoxy semen dan epoxy pasir silika dapat digunakan. Namun pemakaian jumlah filler semen dan pasir silika masih mengunakan cara coba-coba. Untuk itu dilakukan penelitian tentang sifat mekanik dan kimia komposit epoxy semen dan epoxy pasir silika dengan perubahan fraksi filler. Penelitian dengan melakukan pengujian terhadap tekan, impak, ketahanan terhadap H SO
Foto mikrostruktur dan pengamatan lapangan. Kemudian dianalisa dengan perhitungan modulus young secara teoritis model kubus, tabung, dan partikulit. Analisa kerapatan massa dan persyaratan komposit. Hasil penelitian menunjukan kedua komposit dapat digunakan untuk pelapis lantai pabrik aki. Hasil uji yang paling baik untuk epoxy semen pada perubahan fraksi filler 40%. Untuk epoxy pasir silika pada fraksi filler 20%. Hasil perhitungan modulus young pada kedua komposit yang dipilih model Partikulit, karena hasil perhitungan lebih kecil dari hasil uji dan model lainnya, sehingga lebih aman.
"
1996
T-Pdf
UI - Tesis Membership  Universitas Indonesia Library
cover
Muhammad Alwi Rifqi
"Material komposit sangatlah populer dalam beberapa dekade terakhir karena massanya yang ringan dan harganya yang relatif murah disertai dengan kekuatan mekanik yang tinggi. Penelitian ini memiliki tujuan untuk membandingkan sifat mekanik dan kerusakan yang terjadi dari komposit sandwich dengan inti honeycomb polipropilen dan kulit epoksi/serat karbon yang difabrikasi dengan CPA (Cold-Press Adhesive) dan VARI (Vacuum-Assisted Resin Infusion). Terdapat empat pengujian yang dilakukan dalam penelitian ini, yaitu uji densitas, uji tarik, uji tekan, dan uji lentur. Pengamatan kerusakan dilakukan sebelum dan sesudah pengujian dilakukan. Kedua komposit sandwich memiliki nilai densitas yang rendah, yaitu; (0,42 ± 0,03) g/cm3 dan (0,56 ± 0,04) g/cm3 masing-masing untuk komposit sandwich yang dibuat dengan teknik fabrikasi Cold-Press Adhesive (CPA) dan VARI. Komposit sandwich CPA dan VARI mempunyai kekuatan mekanik yang relatif sama, yaitu (14,79 ± 6,11) MPa dan (13,09 ± 2,53) MPa untuk kuat lentur; (1,87 ± 0,17) MPa dan (1,5 ± 0,17) MPa untuk kuat tekan; dan (0,36 ± 0,06) MPa dan (0,33 ± 0,04) MPa untuk kuat tarik. Kerusakan pada inti terjadi pada sampel setelah pengujian lentur dan tekan, sedangkan kerusakan pada kulit terjadi pada sampel setelah pengujian lentur dan tarik. 

Composite materials are so popular in the last few decades as lightweight and relatively cheap with high mechanical properties. The purpose of this research was to compare the mechanical properties and failures of sandwich composites with polypropylene honeycomb as core and epoxy/carbon fiber as skin fabricated with CPA (Cold-Press Adhesive) and VARI (Vacuum-Assisted Resin Infusion). Four testing methods were used in this research, namely density measurement, tensile, compressive, and bending tests. Failure observation was conducted before and after mechanical tests. Densities of the two sandwich composites were (0,42 ± 0,03) g/cm3 and (0,56 ± 0,04) g/cm3 for CPA and VARI consecutively. Sandwich composites fabricated with CPA and VARI had a relatively similar mechanical strength values; in the amount of (14,79 ± 6,11) MPa and (13,09 ± 2,53) MPa for bending strengths, (1,87 ± 0,17) MPa and (1,5 ± 0,17) MPa for compressive strengths, and (0,36 ± 0,06) MPa and (0,33 ± 0,04) MPa for tensile strengths. Failure of the core was occurred in the bending and compressive test samples, meanwhile failure of the skin was occurred in the bending and tensile test samples."
Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2022
S-pdf
UI - Skripsi Membership  Universitas Indonesia Library
cover
Reza Prima Naufal
"Komposit sandwich adalah material yang banyak diaplikasikan dalam berbagai industri, struktur bangunan, dan moda transportasi. Komposit sandwich memiliki kekuatan yang tinggi, massa yang ringan, dan dapat dibentuk dengan mudah. Tujuan penelitian ini adalah membandingkan sifat mekanik (sifat tarik, sifat lengkung, dan sifat tekan) komposit sandwich dengan inti busa PU dan kulit epoksi diperkuat woven roving fiberglass, yang difabrikasi dengan teknik cold press-adhesif (ADS) dan VARI (vacuum assisted resin infusion). Pengukuran densitas, pengujian tarik, lentur dan tekan dilakukan dalam penelitian ini. Pengamatan permukaan sampel dilakukan untuk mengetahui kerusakan yang terjadi pada sampel setelah pengujian mekanik. Densitas komposit sandwich memiliki nilai yang relatif sama, yaitu sebesar (0,25 ± 0,01) g/cm3 untuk komposit VARI dan sebesar (0,27 ± 0,01) g/cm3 untuk komposit ADS. Kuat tarik sampel ADS, (1,96 ± 0,28) MPa, memiliki nilai yang lebih tinggi dibandingkan kuat tarik sampel VR; sedangkan kuat lengkung sampel VR, (11,70 ± 1,98) MPa, memiliki nilai yang lebih tinggi. Kuat tekan kedua sampel memiliki nilai yang relatif sama yaitu (1,36 ± 0,45) MPa untuk sampel VR dan (1,32 ± 0,02) MPa untuk sampel ADS. Kerusakan yang terjadi pada komposit sandwich berupa kerusakan pada inti busa PU, dan delaminasi pada kulit dari komposit sandwich.

Sandwich composites are widely applicated materials in various industries, building structure, and transportation. Sandwich composites have high strength value, lightweight, and can be fabricated easily. The purpose of this research was to compare the mechanical properties (tensile, flexural, and compressive strengths) of sandwich composite with polyurethane foam as a core and woven roving fiberglass reinforced epoxy as skins, which were fabricated using cold press-adhesive (ADS) and VARI (vacuum assisted resin infusion). Density measurement, tensile, flexural, and compressive tests were carried out in this research. Sample surface observation was carried out to determine the damage that occurred to the samples after mechanical tests. The densities of both composites had relatively the same values, (0,25 ± 0,01) g/cm3 for VR sandwich composite and (0,27 ± 0,01) g/cm3 for ADS sandwich composite. The tensile strength of ADS sandwich composite, (1,96 ± 0,28) MPa, had a higher value than that the VR sandwich composite sample, while the flexural strength of VR sandwich composite, (11,70 ± 1,98) MPa, had a higher value than that the ADS sandwich composite. Compressive strength of both sandwich composites had relatively the same values (1,36 ± 0,45) MPa for VR sandwich composite and (1,32 ± 0,02) MPa for ADS sandwich composite. The damage occurred in the PU foam core, and delamination occurred in the skin of the sandwich composites."
Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2022
S-pdf
UI - Skripsi Membership  Universitas Indonesia Library
cover
Reza Mohammad Aditya
"Metode fabrikasi material komposit paduan Al 6061 dengan penambahan partikel mikro SiC dipilih menggunakan metode pengecoran aduk karena mampu mendistribusikan partikel penguat SiC dan memiliki nilai ekonomis yang baik. Material ini kemudian diharapkan memiliki sifat mekanis yang baik dengan densitas yang relatif rendah.
Pada penelitian ini dilakukan variasi penambahan volume fraksi dari partikel miro SiC sebesar 2%, 4%, 6%, 8%, dan 10% untuk mengetahui nilai optimal dari penambahan partikel penguat. Penambahan Mg sebesar 10 wt.% dilakukan untuk meningkatkan kemampubasahan dan penambahan Sr dan TiB dilakukan untuk meningkatkan sifat mekanis dari material komposit. Kemudian didapatkan nilai kekuatan tarik, elongasi, dan kekerasan memiliki nilai maksimal pada penambahan partikel penguat SiC sebesar 10 wt.% dengan nilai masing-masing 230 MPa, 6,5%, dan 62,2 HRB. Sedangkan nilai kekuatan impak memiliki nilai optimum pada penambahan partikel penguat sebesar 4% dengan nilai 0.0294 Joule/mm2. Kemudian juga didapatkan bahwa persentase porositas terus meningkat seiring dengan peningkatan volume fraksi dari partikel penguat.

Manufacturing of composite material Aluminum Alloy (Al-Mg-Si) with the addition of micro SiC particles reinforcement chosen using stir casting method because it can be able to evenly distribute the SiC particles reinforcement and has a good economic value. Then this addition of SiC particles predicted will improved the mechanical properties and density of the materials.
In this study, the addition of micro particles volume fraction in the amount of SiC 2%, 4%, 6%, 8%, and 10% were used in order to know the optimum volume fraction. The addition of Mg 10 wt.% were used as wetting agent to increase the wettability between matrix and reinforce and the addition of AlSr and TiB were used to increase the mechanical properties. As a result, the ultimate tensile strength, elongation, and hardness value has a maximum value in addition of micro particles volume fraction in the amount of SiC 10 wt.%with the value up to 230 MPa, 6,5%, dan 62,2 HRB. However, the impact value and hardness value has a optimum value in addition of micro particles volume fraction in the amoung of SiC 4% with the value 0.0294 Joule/mm2. The percentages of porosity were increased along with the increase of micro particles volume fraction.
"
Depok: Fakultas Teknik Universitas Indonesia, 2016
S65316
UI - Skripsi Membership  Universitas Indonesia Library
cover
Dena Wulandari
"Film komposit PVA-TiO2 telah berhasil dipreparasi dan dideposisi di atas substrat PCB dengan elektroda berstruktur interdigital dari film Cu/Ag dengan metode dip-coating. Film dikarakterisasi dengan RCL meter di dalam chamber yang kondisi kelembabannya diatur menggunakan larutan jenuh garam. Penambahan TiO2 dapat memperbesar sensitivitas film terhadap kelembaban secara signifikan. Konsentrasi TiO2 50% memberikan sifat sensing RH yang optimal. Mekanisme deteksi molekul air dari masing-masing komponen penyusun film yang menyumbangkan perubahan impedansinya akan didiskusikan. Pengaruh dari frekuensi triger, efek penuaan dan reprodusibilitas preparasi dan fabrikasi sensor juga telah diteliti."
2006
SAIN-11-3-2006-20
Artikel Jurnal  Universitas Indonesia Library