"The study was conducted to explore the feasibility of using concrete sludge waste (CSW) and coconut fiber to manufacture paving blocks. The CSW were collected from a ready-mix concrete plant, while the coconut fibers were sourced from a coconut husk processing plant. The CSW was sun-dried for two days and only aggregates passing the No. 4 sieve were used to replace natural sand at replacement levels of 25%, 50% and 100% by weight with an aggregate/cement ratio of 1:3. The untreated coconut fibers were manually cut into a fiber length of 5 cm and were used in the paving block mix at proportions of 0%, 1%, 2% and 3% by weight of cement. The compressive strength, flexural strength, absorption and abrasion resistance of the resulting paving block specimens were tested to study whether or not the paving blocks has sufficient mechanical properties that allow them to have a quality classification grade under Indonesian national standards. The results of the study indicate that the paving blocks show sufficient compressive strength and abrasion properties to achieve a quality grade of A and B, respectively. However, the absorption level turned out to be the limiting constraint, where all of the paving block specimens resulted in an absorption level above the maximum allowable level under national standards.

---

Studi ini dilakukan untuk meninjau kelayakan penggunaan limbah adukan beton (CSW) dan serat kelapa untuk memproduksi paving block. CSW diambil dari pabrik beton ready-mix, dijemur selama dua hari dan hanya aggregat yang melewati saring No. 4 digunakan sebagai subtitusi pasir alam pada tingkatan 25%, 50% dan 100% dengan rasio aggregat-semen 1:3. Serat kelapa dipotong secara manual menjadi panjang 5 cm dan digunakan dalam campuran paving block pada proporsi 0%, 1%, 2% dan 3% dari berat semen. Sifat mekanik paving block yang diuji meliputi kuat tekan, kuat lentur, absorpsi dan ketahanan aus. Hasil penelitian menunjukkan bahwa paving block yang dihasilkan menunjukkan kuat tekan dan ketahanan aus yang cukup untuk mencapai kualitas kelas A dan B, berdasarkan SNI 03-0691-1996. Namun, semua spesimen paving block yang dihasilkan menghasilkan absorpsi di atas batas yang ditentukan SNI 03-0691-1996."

"Dalam penelitian ini meninjau penggunaan serbuk kerang sebagai substitusi perekat semen sedangkan agregat halus untuk Campuran mortar dengan bahan limbah berupa Concrete Sludge Waste (CSW) sebagai substitusi pasir. Sifat mekanik Paving block yang diuji dengan total benda uji sebanyak 180 buah. Yang meliputi kuat tekan sebanyak 60 benda uji sesuai SNI 03-0691-1996, kuat lentur sebanyak 60 benda uji sesuai standar ASTM C 78-94, absorpsi sebanyak 60 benda uji sesuai SNI 03-0691-1996.Pengujian kuat tekan hingga umur benda uji 28 hari, dibagi menjadi 4 variasi pengujian sehingga didapat variasi optimum untuk komposisi semen, agregat halus 1:4,5 , yang terdiri dari 98 % semen, 2 % serbuk kerang dan 100 % CSW didapatkan nilai kuat tekan optimum sebesar 10.05 MPa. Pengujian kuat lentur hingga umur benda uji 28 hari dengan variasi yang sama didapatkan kuat lentur optimum sebesar 6.42 MPa. Pengujian absorpsi hingga umur benda uji 56 hari dengan variasi yang sama didapatkan nilai absorpsi sebesar 5.51 %. Dengan nilai yang diharapkan maka paving block dapat diaplikasikan dalam pembuatan bata beton (paving block) kelas pedestrian.This reseach aims to observe the use of shell powder as a substitute of adhesive cement while Concrete Sludge Waste (CSW) as a substitute of sand for paving block. The mechanical properties tested in the laboratory with 180 samples of total samples. Comprising 60 samples for testing of the compressive strength refers to SNI 03-0691-1996, 60 sample for testing of flexural strength refers to C 78-94, 60 samples for testing of absorption refer to SNI 03-0691-1996.

Testing of the compressive strength performed up to 28 days is divided into 4 variations. From this research, variation for composition cement, Aggregate 1:4,5, consist of 98% cement 2% shell powder as an adhesive materials and 100% CSW as an aggregate getting 10.05 MPa as an optimum compressive strength. Testing of the flexural strength performed up to 28 days with the same variation getting 6.42 MPa as an optimum flexural strength. Testing of the absorption performed up to 56 days with the same variation getting 4,84 % as an optimum absorption. With this value, hoped can be applied in the manufacture of concrete bricks (paving blocks) for pedestrian class."

"Pada proses pengadukan beton, akan menghasilkan limbah beton yang mengering pada tempat adukan dan air sisa dari adukan beton. Dari hasil limbah adukan beton tersebut, timbullah ide penelitian untuk memanfaatkan kembali limbah tersebut sebagai campuran paving block. Paving block tersebut dicampur bahan tambahan berupa serat ijuk. Parameter yang diuji adalah kuat tekan, kuat lentur dan penyerapan. Dari hasil penelitian, paving block tersebut memiliki kuat tekan serta kuat lentur yang rendah dan penyerapan yang tinggi. Dengan menambahkan serat ijuk ke dalam campuran, kuat tekan dan kuat lentur paving block tersebut dapat meningkat.

---

In the process of concrete mixing, concrete sludge waste will be produced from dry concrete and remaining water in place of concrete mixing. There is an idea to recycle concrete sludge waste as the material for paving block. That paving block will be added with palm fiber. The parameters that will be tested are compressive strength, flexural strength and absorption. As the results of research, the paving block has low compressive strength and flexural strength. But its absorption is high. By adding palm fiber into the mix, compressive strength and flexural strength of paving block can be increased."

"ABSTRAKPenelitian yang dilakukan ini membahas tentang timbulan dan komposisi limbah padat yang dihasilkan oleh Apartemen Margonda Residence 3. Metode yang digunakan untuk teknis pengabilan sampah adalah metode SNI 19-3964-1994 mengenai Metode Pengambilan dan Pengukuran Contoh Timbulan Dan Komposisi Sampah Perkotaan. Hasil penelitian adalah alternatif sistem teknis operasional, yang dimulai dari pewadahan hingga pembuangan akhir. Timbulan sampah yang dihasilkan oleh apartemen adalah 0.213 kg/orang/hari dan 1.7 L/orang/hari. Komposisi yang terdapat pada gedung Apartemen Margonda Residence 3 setelah melakukan sampling selama 8 hari adalah sampah organik sebesar 552.881, sampah plastik 17.819, sampah kertas 15.356, sampah pampers dan pembalut 5.085, sampah kaca 3.440 sampah logam 1.570, sampah tekstil sebesar 1.010, sampah B3 0.163 dan sampah lainnya seperti karet, sterofoam, kayu sebesar 2.768. Komposisi yang terdapat pada area parkir dan jalan pada apartemen adalah sampah kertas sebesar 43.091, sampah plastik sebesar 46.136, sampah logam 3.981, sampah kaca 2.576, sampah tekstil 1.639, sampah B3 1.405 dan sampah lainnya 1.171. Perencana pemanfaatan limbah pada anorganik pada apartemen adalah dengan menerapkan sistem bank sampah dan untuk sampah organik dengan melakukan pengomposan agar dapat meminimalisasi timbulan sampah yang dihasilkan.

---

ABSTRACTThis research discusses about solid waste generation and composition at Margonda Residence Apartmen 3. The method which being used is SNI 19 3964 1994 on Methods Of Sample Collection and Measurement Of The Compositian and Urban Waste. The result of study alternative are technical operational system, which start from lug to landfill. Generation of solid waste generated apartement is 0,213 kg person day and 1,7 L person day. The composition of solid waste in Margonda Residence 3 Apartment after sampling for eight days is organic waste 552,881 , plastic 17,819 , paper 15,356 , garbage diapers and sanitary napkins 5,085 , glas 3,440 , metal 1,570 , garbage textiles by 1010 , 0163 B3 and other debris such as rubber, Styrofoam, wood amounted to 2,768 . The composition contained in the parking area and the road to the apartment is a waste of paper 43,091 , plastic 46,136 , metals 3,981 , 2,576 glass , 1,639 textile trash, B3 1,405 and 1,171 more. Planning inorganic waste utilization in the apartment is to implement the system of waste banks and for organic waste by composting in order to minimize the generation of waste generated."

"Instalasi pengolahan air minum dalam prosesnya akan menghasilkan limbah yang berupa lumpur. Berdasarkan Peraturan Pemerintah no. 16 tahun 2005 tentang Pengembangan Sistem Penyediaan Air Minum pasal 9 ayat 3 bahwa limbah akhir dari proses pengolahan air baku menjadi air minum wajib diolah terlebih dahulu sebelum dibuang ke sumber air baku dan daerah terbuka. Instalasi Pengolahan Air Minum Cibinong merupakan salah satu instalasi yang belum melakukan pengolahan limbah dari proses pengolahan air karena limbah yang dihasilkan langsung dibuang ke sungai Ciliwung. Jumlah timbulan debit lumpur dengan aliran kontinyu IPAM Cibinong I sebesar 394,35 m3/hari dan IPAM Cibinong II sebesar 187,44 m3/hari. Tujuan dari penelitian ini untuk merencanakan instalasi pengolahan lumpur guna mentaati peraturan yang berlaku. Berdasarkan neraca massa dapat diketahui unit penghasil lumpur yang signifikan adalah unit sedimentasi, dikarenakan massa lumpur yang dihasilkan cukup besar. Akan direncanakan unit pengolahan lumpur yang terdiri dari proses thickening, chemical conditioning, dan dewatering. Pemilihan unit tahap dewatering pengolahan tersebut berdasarkan analisa SWOT dan metode decision matrix, kemudian diperoleh mechanical dewatering dengan menggunakan centrifuge. Berdasarkan luas lahan, timbulan cake lumpur, dan kebutuhan polimer dipilih instalasi pengolahan lumpur yang terdiri dari 2 buah bak ekualisasi. Dimana 1 bak ekualisasi mengumpulkan lumpur dari unit flokulasi dan air pencucian filter, selanjutnya menuju chemical conditioner, recovery basin¸ dan gravity thickener. Sedangkan bak ekualisasi lainnya mengumpulkan lumpur dari unit sedimentasi menuju gravity thickener kemudian menuju centrifuge.

---

Water treatment plant produced sludge in a large quantity. Based on Government Regulation No. 16, 2005 in which under item 3 of the article 9, it is stipulated that the waste produced from any processing must be treated before it is discharged into water sources and open areas. The sludge generated from WTP Cibinong I and II is directly discharge into stream Ciliwung. The sludge generation of WTP Cibinong I in continuous flow is 394,35 m3/day and WTP Cibinong II is 187,44 m3/day.

The aim of this study is to plan for sludge treatment plant in order to comply with applicable regulations. Based on the mass balance, sedimentation is a unit which significantly produced sludge in large quantity. Sludge treatment plant will be planned consists of thickening process, chemical conditioning, and dewatering. The selection of dewatering processing unit is based on SWOT analysis and decision matrix method, with this tools it can be concluded that centrifuge will be used.

Based on land area, sludge generation, and need of polymer, will be selected sludge treatment plant which has 2 equalization basins. One equalization basin will collect the sludge from flocculation unit and backwash water and towards to chemical conditioner, recovery basin, and will be mixed in gravity thickener with outflow from other equalization basin which collects sludge from sedimentation. After that, it will toward to mechanical dewatering centrifuge."

"Limbah sisa adukan beton dan limbah kaca seringkali menjadi sampah dan berpotensi merusak lingkungan karena sifatnya yang sulit terurai. Padahal kedua bahan tersebut mempunyai potensi untuk dimanfaatkan, salah satunya sebagai pengganti agregat dan semen pada paving block. Tujuan penelitian ini adalah mengetahui seberapa besar pengaruh penambahan limbah adukan beton dan serbuk kaca terhadap sifat-sifat mekanik paving block. Pembuatan paving block dibuat dari limbah adukan beton, semenPC type I, dan serbuk kaca yang berasal dari sisa botol heinkein dan anker bir. Benda uji penelitian dibuat dengan perbandingan komposisi semen dan agregat 1:4,5 dengan 4 perlakuan subtitusi serbuk kaca yaitu 0%, 10%, 20%, dan 30% dari berat semen. Pengujian kuat tekan dan kuat lentur dilakukan pada hari ke-7,14,28 sedangkan pengujian penyerapan air dilakukan pada hari ke-14, 28, 49 dan 56.Dari hasil pengujian, didapatkan bahwa penambahan serbuk kaca 10% dari berat semen mempunyai komposisi terbaik untuk menghasilkan kekuatan yang optimum. Dimana kuat tekan paving block pada umur 28 hari mencapai 13,625 Mpa dan mengalami peningkatan sebesar 25,86% dari paving block tanpa mengunakan campuran serbuk kaca.

---

Residual concrete sludge waste and glass waste is often a waste and potentially damaging to the environment because it is difficult to unravel. Yet, both materials have the potential to be used, as a substitute for aggregate and cement on paving block for example. The purpose of this study was to determine how much impact from the addition of waste concrete and glass powder on the mechanical properties of paving block. Paving blocks were made ​​of concrete waste, Portland Cement type I, and glass powder taken from the rest of heinkein and Anker beer bottles. Research specimens were made ​​with cement and aggregate composition ratio of 1:4,5 and different amount of substitution using glass powder. Glass powder ratios are as follow: 0%, 10%, 20%, and 30% of cement weight. Compressive and flexural strength testing were performed on day 7, 14, 28 while the water absorption test were performed on day 14, 28, 49 and 56.

From the test results, it was found that the specimen with the addition of glass powder by 10% of cement weight has the best composition resulted in producing optimum power. Compressive strength of paving blocks at day 28 reached 13.625 MPa, produced an increase by 25,86% compared to the paving block without using mixture of glass powder."

"Berdasarkan data Dinas Kebersihan DKI Jakarta (2009), timbulan limbah padat DKI Jakarta yang dihasilkan sebesar 6.594 ton/hari. Kantor Pusat PT. Pertamina, yang meliputi Pertamina Pusat dan Gedung Kwarnas, memiliki TPS sebagai fasilitas pemilahan limbah padat. Namun, kegiatan tersebut kurang berjalan dengan baik karena semua limbah padat tercampur kembali dan langsung diangkut ke TPST Bantargebang. Oleh karena itu, diperlukan upaya pengurangan timbulan limbah padat dari sumber melalui perumusan Standard Operating Procedure (SOP) pengelolaan limbah padat dalam bentuk flowchart yang berlandaskan konsep Green Building.Hasil sampling menunjukkan bahwa rata-rata timbulan Gedung Utama sebesar 3,36 L/orang/hari, Gedung Annex sebesar 2,26 L/orang/hari, dan Gedung Kwarnas sebesar 4,55 L/orang/hari. Hanya Gedung Perwira yang mempunyai nilai rata-rata timbulan sesuai standar SNI 3242:2008 (0,5-0,75 L/orang/hari), yaitu sebesar 0,64 L/orang/hari. Analisa hasil sampling dan kuesioner menunjukkan bahwa SOP yang efektif untuk diterapkan pada area tersebut meliputi pewadahan, pengumpulan, pemindahan, pengangkutan, pengolahan, dan pembuangan akhir.Terdapat dua rencana upaya pengolahan limbah padat, yaitu penerapan bank sampah dan pengomposan. Target penerapan bank sampah Pertamina Pusat dan Gedung Kwarnas masing-masing sebesar 35 % dari limbah padat anorganik. Sedangkan target pengomposan Pertamina Pusat dan Gedung Kwarnas pada hari Selasa dan Kamis masing-masing sebesar 30% serta Jumat sebesar 45% dari limbah padat organik. Dengan adanya upaya pengelolaan limbah padat tersebut, diharapkan timbulan limbah padat pada Pertamina Pusat yang diangkut ke TPST Bantargebang diperkirakan berkurang sekitar 32,4% dan Gedung Kwarnas sekitar 34,1% dari total timbulan limbah padat.Based on data from Cleansing Office DKI Jakarta (2009), waste generation in DKI Jakarta is about 6.594 ton/day. Head Office of PT. Pertamina, which includes Pertamina Pusat and Kwarnas Building, have TPS as solid waste sorting facility. However, such activities do not work well because all wastes are mixed again and instantly transported to TPST Bantargebang. Therefore, reduction of solid waste from the source is required by formulating a Standard Operating Procedure (SOP) of solid waste in form of flowchart based on the concept of Green Building.

Based on the results of measurements, the rate of generation of Utama Building is 3,36 L/person/day, Annex Building is 2,26 L/person/day, and Kwarnas Building is 4,55 L/person/day. There is only one building in Head Office of PT. Pertamina, which is Perwira Building, that has a proper rate of generation (0,64 L/person/day) with SNI 3242:2008 (0,5-0,75 L/person/day). Further analysis of sampling and questionnaire results, indicate that the effective SOP that can be applied on that area, includes storage, collection, transfer, transportation, treatment, and final disposal.

There are two plans for solid waste treatment, namely waste bank and composting. The reduction target of waste bank application in Pertamina Pusat and Kwarnas Building is 35% from inorganic wastes. While the reduction target of composting in Pertamina Pusat and Kwarnas Building on Tuesday and Thursday is 30% and 45% from organic wastes on Friday. Through this waste management plan, it is expected that the generation of solid waste in Pertamina Pusat which is transported to TPST Bantargebang will be reduced about 32,4% and Kwarnas Building about 34,1% from total waste generation."

"Tesis ini membahas mengenai analisis strategi pengolahan sampah Kota Bandung. Tujuan penelitian ini adalah untuk melihat faktor-faktor apa saja yang mempengaruhi keberhasilan pengelolaan sampah melalui bank sampah khususnya Bank Sampah Resik dengan menggunakan metoda analisis SWOT. Penelitian ini menggunakan pendekatan post positivis dengan teknik pengumpulan data secara mix method. Berdasarkan hasil penelitian ini ditemukan bahwa faktor yang mempengaruhi keberhasilan pengelolaan sampah melalui Bank Sampah Resik adalah faktor kelembagaan yang baik, jaringan yang baik serta kapabilitas personil yang tinggi. Sedangkan strategi yang perlu diambil berdasarkan hasil analisis SWOT adalah strategi mendukung pertumbuhan yang agresif.

---

This thesis studying about analyzing of waste management strategy of Bandung. The purpose of this research are to see the factors that influence the success of waste management through Bank Sampah especially Bank Sampah Resik with SWOT method. This research using post positivism approach with mix method data collecting technique.

According the result of this research, the factors which influence the success of waste management strategy that using Bank Sampah Resik are good corporate governance, good network, and high capability of Bank Sampah Resik servant. Meanwhile the strategic that need to do based on SWOT analyze is growth oriented strategic."

"Penelitian bertujuan mengkaji kuantitas. Kualitas, kelayakan ekologis dan ekonomis pembuatan nata de pina limbah cair nanas (LCN). Penelitian menggunakan rancangan acak lengkap (RAL) dengan 3 perlakuan yaitu (A) LCN tanpa penambahan nutrisi; (B) LCN dengan penambahan nutrisi dan (C) LCN penyimpanan 6 bulan dengan penambahan nutrisi. Produk nata meliputi berat, tebal, warna, kecerahan. Kandungan serat dan sisa limbah dianalisis dengan Anova. Analisis deskriptif untuk kelayakan ekologis dan ekonomi. Hasil penelitian terdapat perbedaan yang sangat nyata perlakuan fermentasi LCN. Ketebalan nata berturut-turut dari dari tinggi kerendah perlakuan B 1,58 cm A 1,24 cm, dan C 0,88 cm. Berat nata B 889 gr, A 616,4 gr, dan C 477, 8 gr. Kadar serat C 9,3%, B 7,6% dan A 6,9% dengan kualitas warna, kecerahan, dan serat, sesuai standar untuk makanan. Pembuatan nata de pina mengurangi volume LCN 46,2-89,1% (Sig. 0,001). Berdasarkan baku mutu limbah, biological oxygen demand (BOD), chemical oxygen demand (COD) dan total suspended solid (TSS) di bawah ambang batas yang dipersyaratkan kecuali pH. Secara ekonomi pembuatan nata depina layak (BC ratio 4,7). Secara keseluruhan pembuatan nata de pina dari LCN menghasilkan nata yang baik serta layak secara ekologis dan ekonomis.

---

This research aims to study the quantity, quality, ecological and economic feasibility of nata de pina production (NP) from pineapple liquid waste (PLW). The design of the study employs complete random design (CRD) with three treatments: PLW without nutrients addition (A), PLW nutrients addition (B), and PLW stored for six months with nutrients addition (C). The nata de pina?s production factors measured were weight, thickness, fiber content, color, brightness, and residual waste. The highest weight was reached in treatment B (899 grams), followed by treatment A (616.4 grams), and C (477.8 grams). The thickness of NP of the height and low as in treatment B (1.58 cm) followed by treatment A (1.24 cm) and C (0.88 cm), respectively. The highest fiber content was found in treatment C (9.3%) followed by treatment B (7.6%) and A (6.9%), respectively. Th e fiber content, along with color quality and brightness fit with food standards. The production of NP may reduce the volume of the PLW from 46.2% to 89.1% (p=0.001). Based on the standard value of biological oxygen demand (BOD), chemical oxygen demand (COD), total suspended solid (TSS) below to the required threshold except pH. The production of NP is economically feasible to 4.7 BC ratio. The overal manufacture of nata de pina from PLW produces better and feasible product ecologically and economically."

"Air lindi sampah merupakan salah satu konsekuensi dari adanya aktivitas landfilling di TPA yang mengandung senyawa organik dan anorganik serta beberapa bakteri patogen yang tinggi. Karakteristik air lindi dengan nilai COD tinggi dan rasio BOD/COD yang rendah menunjukkan air lindi bersifat non-biodegradable sehingga pengolahan air lindi secara biologis kurang sesuai. Proses Fenton merupakan salah satu metode oksidasi yang menghasilkan radikal hidroksil (•OH) untuk mendegradasi polutan organik dan meningkatkan nilai biodegradabilitas pada air lindi. Pada penelitian ini akan dikaji potensi kombinasi proses Fenton heterogen menggunakan katalis daur ulang dengan proses biologis untuk mengolah air lindi dari TPST Bantar Gebang. Proses Fenton akan memanfaatkan penggunaaan limbah padat yaitu abu terbang dan lumpur aluminium. Ada tiga tahapan utama pada penelitian ini yaitu screening katalis dari dua sumber limbah berbeda, eksperimen parametrik proses Fenton serta kombinasi hybrid proses Fenton dengan pengolahan biologis. Hasil penelitian menunjukkan abu terbang dapat dijadikan sebagai katalis proses Fenton hetrogen untuk mengolah air lindi. Hasil optimum dengan penyisihan COD 42,95% dan penyisihan DOC 42,99% dengan rasio biodegradabilitas DOC/TC 0,99 (fully biodegradable) didapatkan dengan kondisi operasional proses Fenton dengan konsentrasi katalis 2 g/L; rasio H2O2 1x; dan pH 3. Hasil proses Fenton sebagai pre-treatment pengolahan biologis menunjukkan air lindi yang diolah dengan proses Fenton dapat menaikkan biodegradabilitas pada air lindi. Pengolahan hybrid proses Fenton dengan pengolah biologis lumpur aktif menunjukkan penyisihan COD 65,23% lebih tinggi dan konsentrasi akhir DOC 538 mg/L lebih rendah daripada air lindi tanpa pengolahan pendahuluan dengan penyisihan COD 47% dan konsentrasi DOC pada akhir proses 887 mg/L......Landfill leachate is one of the consequences of landfilling activities in landfills which contain high levels of organic and inorganic compounds and several pathogenic bacteria. The characteristics of leachate with a high COD value and a low BOD/COD ratio indicate that leachate is non-biodegradable so that biological treatment of leachate is not suitable. The Fenton process is an oxidation method that produces hydroxyl radicals (•OH) to degrade organic pollutants and increase the biodegradability of leachate. In this study, the potential for a combination of heterogeneous Fenton processes using recycled catalysts and biological processes to treat leachate from Bantar Gebang TPST will be studied. The Fenton process will utilize the use of solid waste, namely fly ash and aluminum sludge. There are three main stages in this research, namely screening catalysts from two different waste sources, parametric experiments with the Fenton process and a hybrid combination of the Fenton process with biological treatment. The results showed that fly ash can be used as a catalyst for the heterogeneous Fenton process to treat leachate. Optimum results with 42.95% COD removal and 42.99% DOC removal with a DOC/TC biodegradability ratio of 0.99 (fully biodegradable) were obtained with Fenton process operating conditions with a catalyst concentration of 2 g/L; ratio H2O2 1x; and pH 3. The results of the Fenton process as a pre- treatment for biological treatment show that leachate treated with the Fenton process can increase the biodegradability of leachate. Fenton process hybrid treatment with activated sludge biological processor showed 65.23% higher COD removal and 538 mg/L lower final DOC concentration than leachate without pre-treatment with 47% COD removal and 887 mg/L final DOC concentration at the end of the process."