"ABSTRAKEceng gondok tergolong serat alam yang keberadaannya melimpah di Indonesia. Serat alam ini tersusun atas serat selulosa yang merupakan komponen struktural utama dinding sel tanaman hijau. Untuk mendapatkan serat selulosa dari eceng gondok, dilakukan beberapa perlakuan. Pada penelitian ini dilakukan perlakuan pengekstrakkan serat selulosa secara kimiawi, antara lain proses dewaxing, penghilangan hemiselulosa, delignifikasi, tahap pendapatan selulosa murni, dan tahap pengeringan. Digunakan variasi pelarut, yakni Sodium Chlorite (NaClO2), Hydrocloric Acid (HCl), dan Hydrogen Peroxide (H2O2), yang bertujuan untuk mengetahui pelarut mana yang paling efektif dalam pengekstraksian serat selulosa tanaman eceng gondok. Didapatkan pada penelitian ini bahwa, pelarut NaClO2 dinilai paling efektif untuk ekstraksi serat selulosa. Hal ini berdasarkan dari gugus fungsi serat yang terbentuk pada analisis FTIR (Fourier Transform Infrared), karakteristik termal yang didapat dari analisis TGA (Thermogravimetric Analysis), dan dari kandungan hemiselulosa yang paling sedikit dibandingkan dengan pelarut lainnya dari analisis HPLC (High Pressure Liquid Chromatography).

---

ABSTRACTWater hyacinth, classified as a natural fibres that is abundance in Indonesia. This natural fibre consists of cellulose fibres which is the main structural component of cell wall of green plant. To obtain cellulose fibers, chemical treatment such as dewaxing, removal of hemicelluloce component, delignification, until drying process of cellulose fibre have been made in this research. Variation of solvent is used, Sodium Chlorite (NaClO2), Hydrogen Peroxide (H2O2), and Hydrocloric Acid (HCl) Ammonia, with a purpose to determine which are the most effective solvent in this extraction. From this study, we obtained that the most effective solvent in the extraction of cellulose fibre from water hyacinth plant is NaClO2 solution. It is based on the functional group formed on the analysis of FTIR (Fourier Transform Infrared), thermal characteristic obtained from thermagravimetric analysis, and content of hemicellulose from high pressure liquid chromatography analysis."

"[Selulosa mikrokristal merupakan salah satu turunan selulosa yang biasanya dimanfaatkan dalam industri farmasi sebagai eksipien dalam pembuatan tablet cetak secara langsung. Salah satu tumbuhan gulma yang memiliki kadar selulosa cukup tinggi (sekitar 60%) yaitu eceng gondok. Tujuan dari penelitian ini adalah untuk mendapatkan isolat kapang selulolitik, memperoleh kondisi optimum hidrolisis enzimatis dan membandingkan selulosa mikrokristal yang diperoleh dari eceng gondok dengan Avicel pH 101.Pada penelitian ini, selulosa mikrokristal diperoleh dengan metode hidrolisis enzim selulase.Enzim selulase diperoleh melalui ekstraksi dari kapang selulolitik.Kemudian selulosa mikrokristal hasil hidrolisis diidentifikasi dengan XRD (X-Ray Diffraction) dan SEM (Scanning Electron Microscope) serta dibandingkan dengan Avicel pH 101. Berdasarkan hasil penelitian diperoleh kondisi hidrolisis selulase teroptimal pada jam ke-1 dengan volume enzim sebanyak 2 mL. Berdasarkan perbandingan pola difraktogram dan secara morfologi sudah terlihat adanya kemiripan antara mikrokristalin selulosa hasil hidrolisis dengan mikrokristalin selulosa standar (Avicel pH 101)., Microcrystalline cellulose is one of the cellulose derivatives which normally used in the pharmaceutical industry as an excipient in the manufacturing of tablets. One of the weed plants that have pretty high cellulose( about 60 % ) is water hyacinth . The purpose of this study was to obtain isolates of cellulolytic fungi , obtain optimum of enzimatic hydrolysis conditions and comparing microcrystalline cellulose derived from water hyacinth with Avicel pH 101. In this study , microcrystalline cellulose obtained by the hydrolysis method of cellulase enzymes. Cellulase enzyme obtained through extraction from the mold cellulolitic. The microcrystalline cellulose obtained from hydrolysis was identified by XRD ( X - Ray Diffraction ) and SEM ( Scanning Electron Microscope ) and also compared with Avicel pH 101. Based on experiment result that the optimum condition for cellulase hydrolysis is 1 hour and by 2ml volume. Based on the comparison of diffractogram patterns and morphology, there is similiarity for both microcrystalline cellulose from hydrolysis and Avicel pH 10.]"

"Eceng gondok merupakan gulma perairan, namun memiliki kadar selulosa cukup tinggi. Selulosa eceng gondok merupakan sumber potensial bahan baku alternatif pembuatan carboxymethyl cellulose (CMC) pengganti kayu. Selulosa eceng gondok dicampurkan dalam campuran pelarut isopropanol-etanol. Kemudian dilanjutkan dengan mereaksikan selulosa eceng gondok dengan NaOH dan ClCH2COONa. Proses netralisasi dilakukan dengan menggunakan asam asetat dan etanol 96 % serta pengeringan dalam oven. Karakterisasi CMC optimum yang dihasilkan memiliki derajat substitusi (DS) 1,65 dan tingkat kemurnian 93,16 % pada kondisi konsentrasi NaOH 10 %, dengan komposisi media reaksi Isopropanol-Etanol 80 ml:20 ml.

---

Water hyacinth is an aquatic weed, but has a high cellulose content. Water hyacinth cellulose is a potential source for alternative materials of carboxymethyl cellulose (CMC) as wood substitutes. Water hyacinth cellulose mixed in a solvent mixture of isopropanol-ethanol. Then reacting cellulose with NaOH and ClCH2COONa. Neutralization process using acetic acid and 96% ethanol and drying in the oven. Optimum characterization of the resulting CMC has a degree of substitution (DS) of 1.65 and a purity level of 93.16% on condition 10% NaOH concentration and the composition of the reaction media is Ethanol Isopropanol 20 ml: 80 ml."

"Eceng gondok (Eichhornia crassipes) merupakan salah satu tanaman yang dianggap sebagai gulma yang dapat merusak ekosistem. Untuk mengurangi efek negatif dan meningkatkan nilai tambah dari eceng gondok, tanaman ini digunakan sebagai salah satu sumber alternatif dalam pembuatan Carboxymethyl Cellulose (CMC) karena memiliki kandungan selulosa yang cukup tinggi. Proses pembuatan CMC meliputi beberapa tahapan yang dilakukan secara berurutan, yaitu alkalisasi, karboksimetilasi, netralisasi, purifikasi dan pengeringan. Dua tahap pertama dilakukan dengan mereaksikan serat selulosa eceng gondok yang telah diisolasi sebelumnya dengan NaOH dan ClCH2COOH dalam suatu media reaksi. Pada penelitian ini digunakan campuran pelarut isobutil-isopropil alkohol. Kemudian, proses netralisasi dilakukan dengan menggunakan asam asetat, purifikasi dengan ethanol 96%, dan pengeringan dilakukan dengan memanaskan dalam oven pada suhu 60°C. Variasi variabel yang dilakukan pada penelitian ini, diantaranya konsentrasi NaOH sebesar 5%, 10%, 20%, 30% dan 35%, serta perbandingan komposisi media reaksi isobutil-isopropil alkohol sebesar 20 ml:80 ml, 50 ml:50 ml, dan 80 ml:20 ml. Suhu reaksi karboksimetilasi yang ditetapkan ialah sebesar 55°C. CMC yang dihasilkan dikarakterisasi dengan pengukuran nilai Derajat Subtitusi (DS), kemurnian serta analisis gugus fungsional dengan menggunakan FTIR. Berdasarkan hasil penelitian didapatkan CMC dengan nilai DS tertinggi sebesar 2,33 ada pada kondisi komposisi campuran isobutil-isopropil alkohol 20 ml:80 ml dan konsentrasi NaOH 10% serta rendemen 138,37%, dan kemurnian 94,02%.

---

Water hyacinth (Eichhornia crassipes) is a plant that is considered as a weed that can damage ecosystems. In order to reduce the negative effects and to increase the added value of water hyacinth, this plant is used as one of the alternative sources in producing carboxymethyl cellulose (CMC) as it has fairly high cellulose content. CMC producing process includes several stages that are performed sequentially, i.e. alkalization, carboxymethylation, neutralization, purification and drying. The first two stages performed by reacting cellulose fibers that has been previously isolated by NaOH and sodium monochloroacetate (ClCH2COONa) in a solvent medium.

This research uses a mixture of isobutyl-isopropyl alcohol as solvent. Then, the neutralization process is done by using acetic acid, purified with 96% ethanol, and drying stage is done by heating in an oven at a temperature of 60°C. Variations variables in this research, including NaOH concentration of 5%, 10%, 20%, 30% and 35%, and the ratio of composition-isobutyl isopropyl alcohol solvent at 20 ml:80 ml, 50 ml:50 ml, and 80 ml:20 ml.

Carboxymethylation reaction temperature is set at 55°C. CMC produced are characterized by measuring the value of (Degree of Substituion) DS, purity and functional group analysis using FTIR. Based on the results, the CMC with the highest DS value of 2.33 is at the condition of mixed composition isobutylisopropyl alcohol 20 ml: 80 ml and the concentration of NaOH 10%, yield of 138.37%, and purity of 94,02%."

"Hidrogel didefinisikan sebagai suatu struktur polimer tiga dimensi yang dapat dibentuk dari polimer alam atau sintetik dan mampu mempertahankan sejumlah besar air. Hidrogel dapat dibuat melalui dua cara yaitu penyilangan fisik (physical cross-linking) dan penyilangan kimia (chemical cross-linking). Struktur yang stabil dan pembengkakan efektif dari hidrogel bisa didapatkan melalui proses penyilangan kimia. Pada penelitian ini akan dibuat hidrogel berbasis polimer alam yang besifat tidak beracun. Hidrogel disintesis dengan menggunakan turunan selulosa yaitu berupa Natrium Karboksimetil Selulosa (NaCMC/CMC) dan asam sitrat sebagai agen pengikat silang. Selulosa yang digunakan berasal dari tanaman eceng gondok, yang telah diketahui sebagai salah satu sumber serat selulosa yang potensial dalam pembuatan CMC. Efek dari kondisi preparasi, seperti konsentrasi asam sitrat yang digunakan serta waktu reaksi saat proses sintesis ditinjau melalui hasil karakterisasi hidrogel. Variasi variabel yang dilakukan pada penelitian ini diantaranya konsentrasi asam sitrat sebesar 5, 10, 15% dan komposisi campuran media reaksi isobutil-isopropil alkohol sebesar 2:8, 5:5, dan 8:2 dengan tujuan untuk mendapatkan nilai DS yang berbeda-beda. Berdasarkan hasil penelitian, swelling ratio hidrogel paling tinggi didapatkan saat komposisi media reaksi isopropil-isobutil alkohol 8:2 dan konsentrasi asam sitrat sebesar 10% . Hal ini didukung dengan ditemukannya ikatan ester pada hasil uji gugus fungsi dengan menggunakan FTIR (Fourier Transform Infrared) dan terbentuknya pori-pori kecil dan besar pada permukaan hidrogel berdasarkan hasil pengamatan mikroskopis hidrogel dengan menggunakan SEM (Scanning Electron Microscope).

---

Hydrogels are defined as a three-dimensional polymer structure that can be formed from natural or synthetic polymers and are able to retain large amounts of water. Hydrogels can be made in two ways, i.e. physical cross-linking and chemical cross-linking. The stable structure and effective swelling of the hydrogel can be obtained through the chemical cross-linking process. In this study, hydrogel will be made of natural polymer that is non-toxic. Hydrogels synthesized by using cellulose or its derivatives (Carboxymethyl Cellulose (CMC)) through chemical crosslinking process with citric acid acts as crosslinking agent. Cellulose is derived from water hyacinth plant, which has been known as one of the potential sources of cellulosic fibers in producing CMC. Effects of preparation condition, such as citric acid concentration and variation in the value of the degree of substitution of CMC, are reviewed through the hydrogel characterization results. Variations of variables in this research include the concentration of citric acid of 5, 10, and 15% and the ratio of composition isobutyl-isopropyl alcohol solvent at 2:8, 5:5, and 8:2 in order to get the different value of degree of substitution of CMC. Based on the results, the hydrogel with the highest swelling ratio is at the condition of mixed composition isobutyl-isopropyl alcohol 2:8 and the concentration of citric acid at 10%. This is supported by the invention of the ester bond in the test results of functional groups using FTIR (Fourier Transform Infrared) and the formation of small and large pores on the surface of hydrogels based on hydrogel microscopic observation using SEM (Scanning Electron Microscope)."

"Salah satu turunan selulosa, selulosa mikrokristal, merupakan bahan penting dalam pembuatan sediaan farmasi, yaitu sebagai eksipien dalam pembuatan tablet secara cetak langsung. Tumbuhan gulma eceng gondok memiliki kadar selulosa yang cukup tinggi yaitu sekitar 60 . Tujuan dari penelitian ini adalah untuk mendapatkan serbuk selulosa mikrokristal dari eceng gondok dan identitasnya melalui spektrofotometri inframerah dan penentuan titik lebur, serta karakteristik fisika dan kimianya dan membandingkan hasilnya dengan Avicel PH 101 sebagai standar. Pada penelitian ini, selulosa mikrokristal diperoleh melalui hidrolisis enzimatis dengan enzim selulase. Identitas dari selulosa mikrokristal diperoleh melalui spektrum inframerah yang mirip dengan standar serta suhu lebur dalam rentang 247-250 C. Selulosa mikrokristal yang diperoleh berupa serbuk sedikit kasar, tidak berbau dan berasa serta berwarna sedikit kekuningan dibandingkan standar. Karakteristik selulosa mikrokristal yang diperoleh meliputi tidak terbentuk warna biru dengan larutan iodin, distribusi ukuran partikel sebesar 741 nm, pH 7,49, kadar abu 0,203 , kadar air 3,685 , susut pengeringan 3,8741 , serta kerapatan partikel, laju alir dan sudut istirahat yang memenuhi persyaratan sesuai literatur. Berdasarkan perbandingan pola difraktogram dengan difraksi sinar-X dan secara morfologi dengan SEM Scanning Electron Microscope sudah terlihat kemiripan antara selulosa mikrokristal hasil hidrolisis dengan standar.

---

One of the cellulose derivatives, microcrystalline cellulose is normally used in the pharmaceutical industry as an excipient in the manufacturing of tablets. Water hyacinth is a weed plant that has high cellulose content for about 60 . The purpose of this study was to obtain microcrystalline cellulose powder from water hyacinth and the identity by infrared spectrophotometry and melting point determination and the physical and chemical characteristics were compared to Avicel PH 101 as standard. In this study, microcrystalline cellulose obtained by enzymatic hydrolysis with cellulase enzymes. The identities were obtained from infrared spectrum which similar as standard and melting point chars between 247 250 C. The powder was moderately fine, odorless, tasteless and yellowish compared to standard. The characteristics were obtained, including not giving blue coloured with iodine solution, particle size distribution for 741 nm, pH 7,49, ash contents 0,203 , moisture content 3,685 , loss on drying 3,8741 also the density, flow rate and angle of repose fulfilled the requirements based on the literature. Based on the comparison of diffractogram patterns by X ray Diffraction and morphology by SEM Scanning Electron Microscope , there is similarity for both microcrystalline cellulose from hydrolysis and standard."

"Selulosa mikrokristal merupakan eksipien yang umum digunakan dalam pembuatan sediaan farmasetika terutama sediaan tablet. Selulosa mikrokristal telah berhasil dibuat dari tumbuhan gulma eceng gondok Eichhornia crassipes melalui proses hidrolisis enzimatis. Penelitian ini bertujuan meningkatkan kuantitas selulosa mikrokristal yang dihasilkan dengan memanfaatkan inhibitor ? -glukosidase yang diekstraksi dari lumut kerak, memperoleh kondisi optimum hidrolisis enzimatis meliputi optimasi pH dan waktu, serta mendapatkan identitas dan sifat fisikokimianya yang dibandingkan dengan selulosa mikrokristal standar, Avicel PH-101. Penelitian diawali dengan peremajaan kapang Trichoderma reesei, kemudian enzim selulase yang diekstraksi dari Trichoderma reesei bersama dengan inhibitor ? -glukosidase yang diekstraksi dari lumut kerak digunakan untuk hidrolisis enzimatis selulosa pada ? -selulosa hasil delignifikasi dari serbuk eceng gondok untuk memperoleh selulosa mikrokristal. Selulosa mikrokristal hasil hidrolisis enzimatis diidentifikasi, dikarakterisasi, dan dibandingkan dengan Avicel PH-101. Identitas dari selulosa mikrokristal diperoleh melalui spektrum inframerah yang mirip dengan standar. Selulosa mikrokristal yang diperoleh berupa serbuk sedikit kasar, tidak berbau dan berasa serta berwarna sedikit kekuningan dibandingkan standar. Karakteristik selulosa mikrokristal yang diperoleh meliputi terbentuk warna biru dengan larutan iodin, distribusi ukuran partikel sebesar 2,01 ? m, pH 7,03, kadar abu 0,23 , kadar air 3,42, susut pengeringan 3,16, kerapatan partikel passable, serta laju alir dan sudut istirahat yang memenuhi persyaratan. Berdasarkan perbandingan pola difraktogram dengan difraksi sinar-X dan secara morfologi dengan SEM Scanning Electron Microscope sudah terlihat kemiripan antara selulosa mikrokristal hasil hidrolisis dengan standar.

---

Microcrystalline cellulose is an excipient commonly used in the manufacture of pharmaceutical preparations, especially tablet preparations. Microcrystalline cellulose has been successfully made from water hyacinth Eichhornia crassipes through enzymatic hydrolysis process. This study aims to increase the quantity of microcrystalline cellulose produced by utilizing glucosidase inhibitors extracted from lichen, obtaining the optimum conditions of enzymatic hydrolysis including pH and time optimization, and obtaining its identity and physical properties compared to commercial microcrystalline cellulose, Avicel PH 101. The study began with the rejuvenation of Trichoderma reesei, then the cellulase enzyme extracted from Trichoderma reesei together with the glucosidase inhibitor extracted from the lichen were used for enzymatic hydrolysis of cellulose from delignification of the water hyacinth powder to obtain microcrystalline cellulose. Microcrystalline cellulose from enzymatic hydrolysis results were identified, characterized, and compared with Avicel PH 101. The identity of microcrystalline cellulose was obtained through an infrared spectrum similar to the standard. Microcrystalline cellulose obtained in the form of a slightly coarse powder, odorless and tasteless and slightly yellowish than standard. Characteristics of microcrystalline cellulose obtained include blue violet color with iodine solution, particle size distribution of 2.01 m, pH 7.03, ash 0.23, moisture content 3.42, drying shrinkage 3.16 , passable particle density, as well as flow rate and angle of repose that met the requirements. Based on the comparison of difractogram pattern with X ray diffraction and morphology with SEM Scanning Electron Microscope a similarity was able to be seen between microcrystalline cellulose of hydrolysis result with standard."

"Limbah dari pengolahan tahu dan tempe mempunyai kadar COD yang tinggi sekitar 7,000 ? 12,000 mg/L. Dampak lingkungan yang ditimbulkan akibat tercemarnya air di sekitar pabrik tahu dapat mempengaruhi kualitas air sungai yang dapat mengganggu ekosistem perairan. Parameter kualitas air dapat diukur dengan nilai Chemical Oxygen Demand (COD). Diperlukan peningkatkan kualitas air agar kadar COD dapat sesuai dengan standar baku mutu (COD 150 mg/L). Salah satu cara menjaga kualitas air yang dapat digunakan adalah adsorpsi menggunakan karbon aktif. Penelitian ini dilakukan dalam beberapa tahapan, yakni proses persiapan bahan eceng gondok, dehidrasi pada suhu 120 °C selama 12 jam, karbonisasi tanpa udara pada suhu 400 °C selama 70 menit, penyaringan ukuran 100 mesh, dan aktivasi kimiawi menggunakan KOH dengan variasi konsentrasi 2 M, 3 M, 4 M, dan 5 M. Nilai bilangan iod yang menyatakan luas permukaan karbon aktif terbesar adalah dengan menggunakan aktivator KOH 5 M, yakni 469,790 mg/g. Selanjutnya, dilakukan pengujian karakterisasi karbon aktif dengan analisis SEM-EDX yang menghasilkan morfologi luas permukaan karbon akibat pengaruh konsentrasi zat pengaktif. Setelah itu, sampel karbon aktif dipilih yang terbaik dengan luas permukaan optimum dan dilakukan uji kinerja adsorpsi untuk penurunan COD terhadap air limbah tahu dengan mengaduk 1 g karbon aktif dengan 100 mL air sampel dengan variasi waktu kontak 30, 60, 90, 120, dan 150 menit. Waktu kontak yang paling optimum dalam penelitian ini adalah dengan pemberian adsorben karbon aktif selama 150 menit dengan penurunan COD sebesar 57,96%.

---

Waste from processing and tofu has a high COD levels of around 7,000 to 12,000 mg/L. The environmental impact caused by contamination of water around the plant out can affect the quality of river water can disrupt aquatic ecosystems. Water quality parameters can be measured by the value of Chemical Oxygen Demand (COD). Water quality improvement is required in order to be able to COD levels in accordance with quality standards (COD 150 mg/L). One way to maintain the quality of water that can be used is adsorption using activated carbon. This research was conducted in several stages, namely the process of preparation of materials hyacinth, dehydrated at 120 °C for 12 hours, carbonization without air at a temperature of 400 °C for 70 minutes, filtering size of 100 mesh, and the activation of chemically using KOH with various concentrations 2 M, 3 M, 4 M and 5 M. Values iodine number is declared the largest surface area of activated carbon is to use 5 M KOH activator, namely 469,790 mg/g. Furthermore, activated carbon characterization testing performed by SEM-EDX analysis that generates a surface area morphology of carbon due to the influence of the concentration of activators. After that, the sample activated carbon have the best surface area is optimized and tested the performance of adsorption for COD reduction of the waste water out by stirring 1 g of activated carbon with 100 mL of water samples with a variation of contact time 30, 60, 90, 120, and 150 minute. The most optimum contact time in this research is the provision of an activated carbon adsorbent for 150 minutes with a COD reduction about 57.96%."

"Selulosa mikrokristal merupakan turunan selulosa yang umum digunakan sebagai eksipien dalam sediaan tablet cetak langsung. Potensi kandungan selulosa yang cukup tinggi pada eceng gondok sekitar 60 memungkinkan untuk digunakan dalam pembuatan selulosa mikrokristal. Penelitian ini bertujuan untuk memperoleh isolat kapang selulolitik, memperoleh kondisi optimum hidrolisis enzimatis meliputi optimasi pH, suhu, waktu, dan konsentrasi enzim, dan membandingkan karakteristik selulosa mikrokristal yang didapatkan dari eceng gondok dengan selulosa mikrokristal standar, Avicel pH101.Penelitian ini diawali dengan isolasi kapang selulolitik, kemudian enzim selulase yang diekstraksi dari kapang selulolitik digunakan untuk hidrolisis enzimatis selulosa pada ?-selulosa hasil delignifikasi dari serbuk eceng gondok untuk memperoleh selulosa mikrokristal. Selulosa mikrokristal hasil hidrolisis enzimatis dikarakterisasi dengan XRD X-Ray Diffraction dibandingkan dengan Avicel 101.Hasil penelitian didapatkan isolat kapang selulolitik yang optimal yaitu isolat hijau tanah dan diperoleh kondisi hidrolisis yang optimal yakni pada suhu 30 C, pH 5, dan durasi 1 jam dengan volume enzim 5 mL. Berdasarkan pola difraktogram terlihat adanya kemiripan sifat kristalin antara selulosa mikrokristal hasil hidrolisis enzimatis dengan standar selulosa mikrokristal Avicel pH101.

---

Microcrystalline cellulose is a cellulose derivate which usually used as a pharmaceutical excipient in the manufacturing of direct compression tablet. High potency of cellulose in water hyacinth about 60 might be used in manufacturing of microcrystalline cellulose. The research aimed to obtain the best cellulolytic fungi, to obtain the optimal conditions of enzymatic hydrolysis including optimization of pH, temperature, duration and enzyme concentration, and comparing microcrystalline cellulose characteristics obtained from water hyacinth with microcrystalline cellulose standard, Avicel pH101.

This research began with isolation of cellulolytic fungus, then cellulase enzymes extracted from cellulolytic fungi was used for enzymatic hydrolysis of cellulose in cellulose resulting from delignification of the water hyacinth powder to obtain microcrystalline cellulose. Microcrystalline cellulose produced by enzymatic hydrolysis was characterized by XRD X Ray Diffraction compared with Avicel 101.

The results showed optimal cellulolitic isolat of isolate hijau tanah and obtained optimal hydrolysis conditions at 30 C, pH 5, and 1 hours in 5 mL enzyme volume. Based on the pattern of diffraction there was a similarity between microcrystalline cellulose of enzymatic hydrolysis result compared with Avicel pH101."

"Tujuan dari penelitian adalah untuk menghasilkan selulosa mikrokristal melalui hidrolisis α- selulosa serbuk eceng gondok dan membandingkan karakteristiknya dengan pembanding (Avicel PH 101). α-selulosa eceng gondok disiapkan melalui biodelignifikasi menggunakan kapang pelapuk putih Trametes versicolor. Selulase dari rayap Macrotermes gilvus dimurnikan dengan fraksinasi ammonium sulfat, dialisis, dan kromatografi kolom.Hasil hidrolisis ditingkatkan dengan mengoptimalkan suhu, pH, dan waktu hidrolisis. Identifikasi dilakukan dengan menggunakan Scanning Electron Microscope-Energy Dispersive X-Ray (SEM-EDX) dan Fourier-Transform Infrared Spectroscopy (FTIR), diikuti oleh karakterisasi selulosa mikrokristal menggunakan Particle Size Analyzer (PSA) dan pola difraksi menggunakan Differential Scanning Calorimetry (DSC) dibandingkan dengan Avicel PH 101.Hasil penelitian menunjukkan rendemen α-selulosa dari biodelignifikasi adalah 40% b/b terhadap serbuk eceng gondok. Selulase murni dari Macrotermes gilvus menunjukkan aktivitas tinggi 11,743 U/mL membentuk area zona bening 49 mm dengan indeks selulolitik 7,16. Hidrolisis optimum dengan selulase dicapai pada 50⁰C, pH 6,0, selama 2 jam, dengan yield 90,89% MCC.Hasil karakterisasi menunjukkan karakteristik selulosa mikrokristal mirip dengan referensi. MCC dari eceng gondok telah menunjukkan karakteristik mirip dengan referensi dan mungkin berpotensi untuk dikembangkan lebih lanjut.

---

The purpose of this research is to produce microcrystalline cellulose by hydrolysis of α-cellulose water hyacinth powder and compare its characteristics with a comparison (Avicel PH 101). α-cellulose water hyacinth is prepared through biodelignification using white rot mold Trametes versicolor. Cellulase from termite Macrotermes gilvus was purified by fractionation of ammonium sulfate, dialysis, and column chromatography.

The hydrolysis yield is improved by optimizing temperature, pH, and hydrolysis time. Identification was carried out using Scanning Electron Microscope-Energy Dispersive X-Ray (SEM-EDX) and Fourier-Transform Infrared Spectroscopy (FTIR), followed by microcrystalline cellulose characterization using Particle Size Analyzer (PSA) and diffraction patterns using Differential Scanning Calorimetry (DSC) compared with Avicel PH 101.

The results showed the yield of α-cellulose from biodelignification was 40% w/w on water hyacinth powder. Pure cellulase from Macrotermes gilvus showed high activity of 11.743 U/mL forming a 49 mm clear zone area with a cellulolytic index of 7.16. Optimum hydrolysis with cellulase was achieved at 50⁰C, pH 6.0, for 2 hours, with a yield of 90.89% MCC.

The characterization results showed that microcrystalline cellulose characteristics were similar to references. MCC from water hyacinth has shown characteristics similar to references and may be potential for further development."