Hasil Pencarian  ::  Simpan CSV :: Kembali

"Micro alloying in High Strength Low Alloy (HSM) steel is very important role to improve the qualityof those steel formation of precipitation of carbonitride such as Nb(CN) in those niobium containingsteel has a significant influenced on strength. Mechanism of strength improvement due to the existing ofmicro alloy the precipitated in hot finishing deformation not fully studied The previous investigated userelationship between deformation and density of dislocation. HSLA steel containing 0.037% Nb was usedin this research and deformation was performed using compressive plane stress, the relationship between5 % fraction precipitate, t@__¢, and maximum stress achieved at a temperature of 9009 C under strain rare ofI sec'l were evaluated. Analysis data results shows that the relationship between 5% fraction and densityof dislocation can be described as, tg,? .,p"'5."

"During thermo-mechanical treatment process of High Strength Low Alley Steel, strengthening isoccurred during finishing deformation due to pre precipitation hardening formed after roughing. UsingHSLA steel containing 0.031% Nb, strengthening of this steel during finishing deformation at temperatureof 900?C under strain of 0.5 is evaluated in terms of stress at 0.05% strain. Data results shows thatthe strengthening of this steel due to roughing deformation can be described into empirical model as afunction activation energy (QM) and roughing deformation temperature."

"ABSTRAKBaja HSLA atau baja paduan rendah kekuatan tinggi memiliki keunggulan karena kekuatan dan keuletannya yang tinggi serta mampu las yang baik. Mekanisme penguatan pada baja ini diperoleh melalui penghalusan butir selama transformasi austenit menjadi ferit.Untuk mengetahui perilaku pertumbuhan butir ferit selama transformasi , maka dilakukan pemanasan ulang (austenisasi) pada temperatur 1200°C selama 2 jam, lalu didinginkan di udara hingga menca.pai temperatur 750, 800 dan 850°C dan ditahan selam 20, 40 dan 60 menit pada temperatur tersebut setelah itu d icelup dalam air.Ukuran butir jerit yang dihasilkan selama transformasi isotennal pada temperature 750°C lebih kecil dibandingkan hasil transformasi pada temperature 800 d an 850°C. Laju pertumbuhan butir ferit sangat besar pada temperature 850°C laju pertumbuhan pada temperature 750 d an 800°C."

"Skripsi ini membahas pengaruh temperatur pemanasan dan waktu tahan terhadap pertumbuhan butir austenit prior baja HSLA 0,111% Nb setelah di-reheating. Benda uji yang digunakan yaitu baja HSLA 0,111%Nb hasil sand casting yang dipanaskan pada suhu 1000ºC, 1100ºC, dan 1200ºC dengan waktu tahan 20 menit, 50menit, dan 80 menit. Hasil penelitian menunjukan semakin tinggi suhu pemanasan dan semakin lamanya waktu tahan yang diberikan maka ukuran butir akan semakin besar dan tingkat kenaikan ukuran butirnya akan semakin tinggi. Selain itu juga didapatkan persamaan untuk memprediksi hubungan antara besar butir austenit prior terhadap temperatur pemanasan dan waktu tahan dengan bentuk d=9,398x10-15.

---

This thesis discusses the influence of heating temperature and holding time through austenite prior grain growth of 0,111% Nb HSLA steel after reheating. The specimen was reheating at 1000ºC, 1100ºC, and 1200ºC, then hold for 20 minutes, 50 minutes, and 80 minutes. The result showed that the higher temperature and the longer holding time, the austenite grain size is bigger and the increasing of grain size is higher. It is also obtained an equation to predict the relation between austenite prior grain size to heating temperature and holding time in the form of d= 9,398x10-15."

"Dewasa ini, baja HSLA semakin banyak dibutuhkan untuk berbagai aplikasi karena memiliki Sifat mekanis yang lebih baik, yakni kekuatan yang tinggi. Kekuatan yang tinggi tersebut dihasilkan dengan menambahkan unsur-unsur paduan mikro yang meningkatkan kemampuan melalui mekanisme pengenalan presipitat dan juga penghalusan butir ferit. Pada penelitian ini diamati besar butir austenit prior yang dipengaruhi oleh peningkatan temperatur, karena hal itu sangat penting untuk menghasilkan butir ferit yang halus setelah canai panas.Baja HSL/4 dengan kandungan 0, 029% Nb as-casr, digunakan sebagai benda uji dalam penelitian ini. Proses pemanasan dilakukan secara isorthermal pada temperatur 900 sampai 1300°C dengan waktu tahan 1 jam.Pertumbuhan butir austenir prior terjadi lebih cepat pada temperatur diatas 1200°C. Hal ini disebabkan oleh karena pada temperatur tersebut, presipitat Nb(C]\0 dalam baja itu telah larut seluruhnya, sehingga tidak lagi menahan pertumbuhan butir. Peningkatan pertumbuhan bulir tersebur diawali dengan pengkasaran butir yang terjadi pada temperatur sekitar ll-42°C. Energi aktivasi pertumbuhan butir dari baja HSLA 0, 029% Nb dengan pemanasan isothermal adalah -134,58 k.l/m0/ dengan nilai n = -1,07 dan A = J, 19.1'03?. Pertumbuhan butir pada baja HSLA as-chast lebih besar daripada baja HSLA as-1-oHea1 dengan waktu tahan pemanasan yang berbeda Pertumbuhan butir pada baja HSLA-Nb lebih besar daripada pertumbuhan butir baja HSLA-Ti."

"High Strength Low Alloy Steel is highly used in marine environment. Highly aggressive attack from cl- ions plus continuously exposure from oxygen worse its condition. Reheated micro alloyed steel is deformed in 30%, 40% , and 50% rolling deformation, resulting varieties corrosion rate depend on its deformation when it is exposed in chloride environment. Austenite prior grain diameter in its sample also varieties. Effect of strain induced Nb (CN) precipitation also give varieties result on its ferrite grain diameter. Approaching in corrosion rate is from its corrosion thermodynamic especially in free energy theory. Where grain boundaries free energy is high, so if number of grain boundaries increased it is also increasing free energy of sample. Analysis is in observation effect of grain diameter and number of grain boundaries on its corrosion rate. Knowing that giving varieties increase deformation will decreasing its ferrite and austenite grain diameter. Method that is used to represents marine environment is salt spray method using 3.5% Sodium Chloride. Experiments is held in 48 hours and it is repeat 3 times. Another approach that is using is, approaching in free energy theory where it is connect with its potential after deformation. Corrosion rate results is match with free energy theory, where with the increasing of deformation degree so the corrosion rate will be increase. It is match with its free energy number when the grain size is decrease, number of corrosion potential will show the corrosion resistance it is low."