Hasil Pencarian  ::  Simpan CSV :: Kembali

"Fenomena pembalikan polarisasi pada material film tipis BST akan dipelajari dengan menggunakan pendekatan seperti pada material ferroelektrik Bulk. Pendekatan statis dan dinamis akan dilakukan dengan menggunakan persamaan energi bebas Landau - Devonshire (LD) dan persamaan Landau - Kalathikov (LK) untuk memperlihatkan hasil minimum dan maximum dari arus pembalikan polarisasi. Dengan menggunakan pendekatan respon medan listrik yang bersifat sinusoidal akan diperlihatkan pula loop histerisis dengan memvariasikan frekuensi dan amplitudo dari medan listrik yang diberikan.

---

Switching phenomenon in BST Thin film will be considered by approaching of Bulk ferroelectric material. Static and dynamic approach will be formulated by combination of Landau - Devinshire (LD) and Landau - Kalathikov (LK) equation for determined maximum and minimum of switching current. Hysterisis loop was developed using sinusoidal electrical field response by variation in frequency and amplitude of electrical field."

"Telah dilakukan analisis data XRD pada suhu ruang dengan penghalusan parameter metode Rietveld pada material ferroelektrik KH2PO4. Dihasilkan nilai indikator R-pola (.pp = 26,82 % ; R-pola dengan pemberat (Rw,) = 33,77 % dan R-Bragg (RB) = 16,26 %. Dalam analisis ini diperoleh 20 parameter yang mencakup Latar Belakang (6), Posisi Atom (4), Faktor Skala (1), Pergeseran Titik Nol (1), Bentuk Puncak -- U,V,W (3), Koefisien Puncak FWHM (3), Faktor Suhu (1) dan Orientasi yang Disukai (1). Posisi atom yang diperoleh digunakan until perhitungan nilai polarisasi listrik spontan (P5) yang menghasilkan harga PS 0,043 coulomb meter-2 (hasil eksperimen 0,0475 coulomb meter-2 (Landolt dan Borstein, 1975)."

"ABSTRAK Telah berhasil dihitung nilai polarisasi spontan Ps bulk dan lapisan tipis PZT beserta PZT doping Vanadium PVZT (Soft Doping). Lapisan tipis PZT dan PVZT dibuat dengan metode pelapis putar (Spin Coating) dengan variasi doping Vanadium pada dua macam substrat yaitu Pt(200)/Si(100) dan Corning. Hasil penelitian manunjukkan bahwa nilai parameter kisi kristal PZT bulk, yaitu: a = 4,0323 ? dan c = 4,1838 ?, dengan nilai polarisasi spontan Ps = 0,5545 C/m2, hasil ini tidak jauh berbeda dengan nilai parameter kisi pada ICDD, yaitu: a = 4,036 ? dan c = 4,146 ?. Pemberian doping Vanadium yang semakin besar akan merubah struktur kristal PZT (parameter kisi) menjadi mendekati kubus. Dengan berubahnya parameter kisi kristal mengakibatkan perubahan nilai polarisasi spontan Ps. Peningkatan doping Vanadium (V) akan menghasilkan nilai Ps yang semakin membesar. Hal ini sesuai dengan karakteristik soft doping. Kata Kunci : PZT, PVZT, bulk, spin coating, lapisan tipis, Vanadium, polarisasi spontan Ps"

"Pada pemerosesan industri tekstil banyak menggunakan air, zat pewarna juga bahan kimia campuran yang berdampak pada timbulnya limbah cair tekstil [1]. Salah satu komponen limbah berbahaya yang terkandung dalam limbah cair tekstil adalah logam-logam berat seperti kadmium (Cd), timbal (Pb), tembaga (Cu), dan seng (Zn) [1]. Contoh langkah untuk mencegah pencemaran logam berat cair adalah menggunakan material mesopori silika seperti SBA-15 karena memiliki luas permukaan, diameter, serta volume pori yang besar serta struktur heksagonal teratur sehingga dapat diaplikasikan sebagai adsorben logam berat. Pada penelitian ini, dilakukan analisis studi kepustakaan sintesis mesopori SBA-15 dengan metode sol-gel serta fungsionalisasi CPTMS yang telah berhasil dilakukan dan dilanjutkan menganalisis kemampuan serapannya pada logam berat kadmium (Cd), tembaga (Cu), seng (Zn), dan timbal (Pb). Tipikalnya, menyintesis SBA-15 dilakukan menggunakan Tetraethyl Orthosilicate (TEOS) sebagai prekursor dan Triblock Copolymer Pluronic 123 (P-123) sebagai surfaktan. Kemudian, hasil produk SBA-15 dilakukan fungsionalisasi CPTMS dengan metode post grafting. Hasil karakterisasi memperlihatkan, pada perhitungan BET dibanding sampel SBA-15 murni, sampel SBA-15 CPTMS mengalami penurunan parameter diameter pori dari 29,203 menjadi 28,521 Å, volume pori dari 265,161 menjadi 199,694 cm3/gr dan luas permukaan spesifik dari 831,996 menjadi 711,061 m2/gr, pada pengujian SAXS, sampel SBA-15 CPTMS tidak terdapat perbedaan signifikan dengan SBA-15 dengan tetap memperlihatkan puncak bidang (100), bidang (110) dan bidang 200, pada pengamatan TEM, sampel SBA-15 CPTMS tetap mempertahankan bentuk heksagonalnya, dan pada pengujian FTIR, terlihat adanya gugus klorida (-Cl) pada gelombang 500 cm 1 yang menunjukkan proses fungsionalisasi CPTMS berhasil dilakukan. Sementara, hasil pengujian serapan logam berat dengan AAS memperlihatkan fungsionalisasi CPTMS tidak memiliki selektivitas yang baik pada logam berat kadmium (Cd) dan seng (Zn) karena penurunan nilai persentase penyerapan. Namun, perhitungan kapasitas adsorpsi memperlihatkan bahwa diseluruh sampel pengujian logam berat terjadi peningkatan kapasitas adsoprsi sampel SBA-15 CPTMS bila dibandingkan dengan SBA-15 murni.

---

In the textile industry, production process is widely used water, dyes and chemicals that have an impact on the emergence of textile liquid waste [1]. Examples of hazardous waste components contained in textile liquid waste are heavy metals mainly derived from colouring agents such as cadmium (Cd), lead (Pb), copper (Cu), and zinc (Zn) [1]. Efforts that can be made to prevent the water pollution containing liquid heavy metals is to use silica mesoporous materials such as SBA-15 because it has a large surface area, pore diameter, pore volume and ordered hexagonal structure so that it can be applied as heavy metals adsorbents. In this research, an analysis of the literature review of SBA-15 mesoporous materials synthesis using sol-gel method and CPTMS functionalization has been successfully carried out and continued by analysing its adsorption ability in heavy metals such as cadmium (Cd), copper (Cu), zinc (Zn), and lead (Pb). Typically, synthesizing SBA-15 is carried out using Tetraethyl Orthosilicate (TEOS) as a precursor and Triblock Copolymer Pluronic 123 (P-123) as a surfactant. Then, the results of the SBA-15 product were carried out CPTMS functionalization with the post grafting method. The characterization results show, in the BET calculation compared to pure SBA-15 samples, SBA-15 CPTMS samples decreased pore diameter parameters from 29,203 to 28,521 Å, pore volume from 265,161 to 199,694 cm3/gr and specific surface area from 831,996 to 711,061 m2/gr, in the SAXS test, the SBA-15 CPTMS sample was not significantly different from the SBA-15 while still showing peak plane (100), plane (110) and plane (200), on TEM observations, SBA-15 CPTMS samples remained maintaining its hexagon shape, and in the FTIR test, a chloride group (-Cl) in the 500 cm-1 wave showed a successful CPTMS functionalization. Meanwhile, the results of heavy metal adsorption testing with AAS showed that CPTMS functionalization did not have good selectivity on cadmium (Cd) and zinc (Zn) heavy metals due to a decrease in the percentage of adsorption. However, the adsorption capacity calculation shows that throughout the heavy metal test sample there is an increase in the adsorption capacity of the SBA-15 CPTMS sample when compared to the pure SBA-15."

"Pada penelitain kali ini telah dirancang sebuah rangkaian Sawyer-Tower untuk bahan ferroelektrik dengan rangkaian kompensasi dan menggunakan tegangan tingi. Sistem yang digunakan terdiri dari Function Generator dengan output gelombang segitiga, Power Amplifier, Transformator tegangan tinggi (5000V),Frekuensi Counter, dan rangkaian Sawyer Tower yang memiliki rangkaian kompensasi sederhana serta pemrograman dengan meggunakan National Instrumen LabView 2010 yang akan menampilkan grafik histerisis dari bahan ferroelektrik. Dengan sistem ini telah berhasil memeperoleh PE loop dan penyimpanan data dalam bentuk ms.exel

---

In this instrumentation research it has been designed a Sawyer-Tower circuit for ferroelectric materials by using a voltage compensation circuit and high voltage. The system used consists of a function generator to provide a triangle wave output, power amplifier, high voltage transformer (5000V), frequency counter, and Sawyer-Tower circuit which has a simple compensation circuit and programming utilized the National Instruments LabVIEW 2010. The result of the program is the showcase hysteresis of ferroelectric materials . This system has been managed to obtain the P-E loop and data storage in the form of .xls, .txt, .word"

"ABSTRAKBatasan rasio komposisi Cu : Mg yang mengalami fenomena rapid hardening pada paduan Al-Cu-Mg masih belum diketahui secara pasti. Selain itu juga, pengaruh komposisi Cu dan Mg pada rentang yang lebar terhadap respons penuaan belum pernah diamati dengan rinci. Penelitian ini mengamati pengaruh variasi komposisi Cu dan Mg pada fenomena rapid hardening dan respons penuaan pada paduan Al-Cu-Mg. Karakterisasi meliputi pengujian kekerasan Vickers dan pengamatan mikrostruktur dengan menggunakan mikroskop optik, SEM/EDS (Scanning Electron Microscopy/Energy Dispersive Spectroscopy), dan TEM (Transmission Electron Microscopy). Hasil menunjukkan bahwa peningkatan komposisi Cu dan Mg memperkecil ukuran butir dan meningkatkan fraksi volume partikel intermetalik yang terbentuk. Pada rentang komposisi Cu (1.1-3.0 at.%) dan Mg (1.7-3.5 at.%) yang lebar, pada paduan Al-Cu-Mg, batas rasio terjadinya fenomena rapid hardening belum dapat ditentukan dengan tepat. Komposisi dimana terjadi fenomena rapid hardening pada penuaan temperatur 170 oC ternyata fluktuatif. Pada saat rapid hardening (waktu penuaan 60 detik), loop dislokasi merupakan satu-satunya mikrostruktur yang ditemukan, sementara pada saat kekerasan puncak, ditemukan presipitat fasa S.

---

ABSTRACTThe range of Cu : Mg ratio in Al-Cu-Mg alloy which undergoes rapid hardening has not been clearly understood. The ageing response on this alloy with wide Cu : Mg ratio has not been fully evaluated. This study observed the effect of Cu : Mg ratio on rapid hardening and ageing response of Al-Cu-Mg alloys. Characterization included Vickers Hardness Testing and Microstructural Observation by using Optical Microscope, SEM/EDS (Scanning Electron Microscopy/Energy Dispersive Spectroscopy), and TEM (Transmission Electron Microscopy). The results showed that the higher the Cu and Mg content, the smaller the grain size and the higher the volume fraction of intermetallic particles. Within the range of 1.1-3.0 at.% Cu and 1.7-3.5 at.% Mg, the Cu : Mg ratio at which rapid hardening occurred, was not able to define. The data was fluctuative at the ageing temperature of 170 oC. After rapid hardening (for 60 seconds of ageing), dislocation loops were observed. While at the peak hardness, the microstructure was strengthened by S precipitates."