Hasil Pencarian  ::  Simpan CSV :: Kembali

"One of the first books new engineers and technicians should read. This new third edition of the perennial best seller preserves the core of the previous editions, focusing on the metallurgical and materials evaluation for failure mode identification. Comprehensive information covering the basic principles and practices are clearly explained."

"Basic principles and practices are clearly explained, with numerous examples featuring commonly used metals, parts, and service environments. This classic first edition has been widely used as a primer for those who need to undertake failure investigations. The updated second edition provides expanded coverage of many important failure analysis concepts and analytical techniques."

"Friction stir welding adalah proses pengelasan solid-state thermomechanical. Sejak penemuannya di TWI pada tahun 1991, proses ini telah diaplikasikan dalam berbagai industri seperti otomotif, aerospace, perkapalan, dan elektronik. Skripsi ini menginvestigasi efek parameter pengelasan micro friction stir welding terhadap temperatur pada aluminium paduan A1100 dengan ketebalan 400 μm. Pada proses pengelasan micro friction stir welding, panas yang dihasilkan gesekan dan efek pengadukan oleh rotasi tool dapat mengakibatkan perubahan pada mikrostruktur dan berakibat pada perubahan sifat mekanik. Ada tiga parameter pengelasan yang dipertimbangkan dalam skripsi ini yaitu, plunge speed, dwell time pertama, dan dwell time kedua. Temperatur aluminium pada saat proses pengelasan FSW diukur. Hasil yang diperoleh menunjukkan bahwa dwell time kedua memiliki pengaruh besar terhadap temperatur lasan sedangkan dwell time pertama kurang berpengaruh.

---

Friction stir welding is a solid-state thermomechanical welding process. Since its invention by TWI in 1991, it has found its application in industries such as automotives, aerospace, shipbuilding, and electronics. In this paper, the effects of welding parameters on the temperature of micro friction stir welding in thin sheet aluminum A1100 alloy with a thickness of 400 μm were investigated. In a micro friction stir welding process, the heat generated by friction and the mixing effect of the tool rotation can cause changes to the microstructure thus changing its mechanical properties. Three welding parameters were considered, plunge speed, first dwell time and second dwell time. The temperature during FSW were measured. The results obtained showed that the second dwell time was a dominant factor affecting the temperature of the weld whereas the first dwell time has very little effect on temperature."

"ABSTRAKTelah dilakukan suatu disain perlakuan panas pada paduan Al-Si untuk meningkatkan kekerasan paduan. Studi XRD terhadap paduan menunjukkan bahwa paduan adalah dua fasa yang diidentifikasi sebagai a-Al dan s-Si. Pada kondisi as cast kedua fasa terdistribusi secara random dengan fraksi volum kira-kira sama dan menghasilkan kekerasan mikro sekitar 56 HRB. Pada perlakuan panas T4 nilai kekerasan ini menurun menjadi - 40 HRB dikarenakan presipitasi fasa B-Si pada batas butir a-Al dan terus turun sampai dibawah nilai -30 HRB setelah perlakuan panas T7 disebabkan pertumbuhan butir kedua fasa. Nilai kekerasan tertinggi { 70 HRB } dicapai pada kondisi perlakuan T6 dimana observasi dengan mikroskop optik menunjukan bahwa strukturmikro paduan terdiri dari fasa halus p-Si tersebar secara merata diantara matrik a-Al yang terisolasi oleh fasa S-Si pada batas butirnya.Studi ini juga menunjukan pada perlakuan panas T6 meskipun menghasilkan material piston dengan kekerasan tinggi tetapi energi bentur material adalah cukup rendah untuk beberapa material yang mendapat perlakuan dengan waktu tahan berbeda. Dana studi ini disimpulkan, perlakuan T6 dengan temperatur 225°C dan waktu tahan 3 jam adalah sebagai parameter pada perlakuan panas yang memberikan kombinasi antara kekerasan material dan energi bentur yang optimal untuk diterapkan pada fabrikasi piston motor."