Hasil Pencarian  ::  Simpan CSV :: Kembali

"Penelitian ini dilakukan untuk mendapatkan rancangan reaktor katalis terstruktur pelat sejajar yang digunakan untuk memproduksi nanokarbon dan hidrogen melalui reaksi dekomposisi katalitik metana. Katalis yang digunakan adalah katalis multimetal Ni-Cu-Al 3:2:1. Pada reaktor katalis terstruktur pelat sejajar ini dilakukan pengujian untuk 20 menit dan 355 menit reaksi. Pada 20 menit reaksi, konversi metana tertinggi yang didapat adalah 70,16% dengan kemurnian hidrogen 74,29% dan yield karbon 2,58 gram. Pada 355 menit reaksi, didapatkan bahwa konversi metana mengalami penurunan dari 76,15% hingga 46,06% dan naik kembali pada menit ke-235 sebesar 59,90% kemudian cenderung stabil setelah menit ke-235. Pada 6 jam reaksi uji stabilitas, yield karbon yang dihasilkan 17,25 gram.

---

The purpose of this research is to construct plate catalyst structured to produce nanocarbon and hydrogen with catalytic decomposition of methane. Catalyst which is used in this research is multimetal catalyst, Ni-Cu-Al 3:2:1. Two experiment that had already done were twenty minutes and 355 minutes reactions. The highest conversion of methane is 70,16% and 74,29% hydrogen purity for twenty minutes reaction and yield carbon was 2,58 gram. For 355 minutes reaction, the conversion of methane decreasing from 76,15% to 46,06% and increase to 59,90%. After that, methane conversion relative stabil. After 355 minutes reaction , yield carbon was 17,25 gram."

"Penelitian dilakukan untuk melakukan uji kinerja reaktor katalis terstruktur pelat untuk produksi carbon nanotube dan hidrogen melalui reaksi dekomposisi katalitik metana. Katalis yang digunakan adalah katalis Ni-Cu-Al dengan perbandingan molar 2:1:1. Reaksi dekomposisi katalitik metana dilakukan pada suhu 700oC selama 5 jam, dengan variasi space time 0,0006; 0,0032; 0,006 gr min/mL. Hasil uji kinerja tertinggi didapatkan pada space time 0,006 gr min/mL dengan konversi metana tertinggi 83,01% , kemurnian hidrogen tertinggi 70,23% , dan yield karbon 2,5 gr/gr katalis. Carbon nanotube yang dihasilkan memiliki diameter dalam 7,5-15 nm dan berbentuk Y-junction.

---

AbstractThe purpose of this research is to test the performance of plate structured catalyst to produce carbon nanotube and hydrogen via catalytic decomposition of methane. In this research, catalyst of Ni-Cu-Al with the molar ratio by 2:1:1 was used. The decomposition reaction took place at 700oC temperature for 5 hours, using 0,0006; 0,0032; and 0,006 gr min/mL space time variations. The maximum performance space-time was 0,006 gr min/mL with 83,01% for the highest number of methane conversion, 70,23% for the highest number of hydrogen purity, and 2,5 gr C/ gr catalyst carbon yield. The carbon nanotubes produced from the research were Y-junction-shaped and have 7,5-15 nm inner diameter.;"

"Scale-up reaktor katalis terstruktur gauze untuk memperoleh 1 kg/hari nanokarbon dengan prinsip geometric similarity menghasilkan laju alir metana 140 L/h, diameter reaktor 8 cm, panjang reaktor 32 cm, diameter gauze 0,64 mm, jumlah mesh/inch 10, dan luas permukaan katalis 2938,982 cm 2. Penelitian ini bertujuan untuk memproduksi nanokarbon dan hidrogen dengan katalis terstruktur gauze melalui reaksi dekomposisi katalitik metana dengan katalis Ni-Cu-Al. Pada reaktor katalis terstruktur gauze ini dilakukan uji aktifitas selama 20 menit dan uji stabilitas selama 17 jam pada suhu 700°C. Untuk uji stabilitas dengan 20 L/jam metana, konversi metana tertinggi adalah 96,77% dan kemurnian hidrogen tertinggi adalah 97,46%. Yield karbon yang dihasilkan oleh 1,83 gram katalis adalah 170,36 gram karbon. Untuk uji aktivitas dengan laju alir metana 6 L/jam diperoleh konversi metana tertinggi adalah 76,1% dan kemurnian hidrogen tertinggi adalah 79,3%. Yield karbon yang dihasilkan oleh 1,81 gram katalis adalah 57,34 gram karbon. Dari hasil percobaan diperoleh bahwa kapasitas reaktor ini adalah 393,19 gram/hari.

---

Scale-up of gauze-type structural catalyst reactor to produce 1 kg/day nanocarbon by geometric similarity results in 140 L/h methane flow, 8 cm reactor diameter, 32 cm reactor length, 0,64 mm gauze diameter, 10 meshes/inch, and 2938,982 cm2 catalyst surface area. The purpose of this experiment is to produce nanocarbon and hydrogen by gauze-type structural catalyst through catalytic decomposition of methane with Ni-Cu-Al catalyst. Two experiment that have already done are stability test for 17 hours and activity test for 20 minutes at 700°C. In stability test with 20 L/h methane flow, the highest conversion of methane is 96,77% and the highest hydrogen purity is 97,46%. Yield carbon that produced by 1,83 gram catalyst is 170,36 gram carbon. In activity test with 6 L/h methane flow, the highest conversion of methane is 76,1% and the highest hydrogen purity is 79,3%. Yield carbon that produced by 1,81 gram catalyst is 57,34 gram carbon. From the experiment, the production capacity of the reactor is 393,19 gram C/day."

"Evaluasi dan perbaikan desain scale-up reaktor katalis terstruktur gauze untuk memperoleh 1 kg/hari nanokarbon dengan prinsip geometric similarity. Menggunakan basis data scale up laju alir metana 140 L/h, diameter reaktor 8 cm, panjang reaktor 32 cm, diameter wire 0,64 mm, jumlah mesh/inch 10, dan luas permukaan katalis 2938,982 cm2. Penelitian ini bertujuan untuk memperbaiki desain reaktor dan sistem produksi pada reaktor dengan katalis terstruktur wire melalui reaksi dekomposisi katalitik metana dengan katalis Ni-Cu-Al untuk memproduksi nanokarbon dan hidrogen. Pada reaktor katalis terstruktur wire ini dilakukan uji kinerja selama 860 menit pada suhu 700_C. Konversi metana tertinggi adalah 41,66% dan kemurnian hidrogen tertinggi adalah 30,45%. Yield karbon yang dihasilkan oleh 4,71 gram katalis adalah 179,15 gram karbon.

---

Evaluation and improvement design of Scale-up of gauze-type structural catalyst reactor to produce 1 kg/day nanocarbon by geometric similarity. Seize on scale up data, 140 L/h methane flow, 8 cm reactor diameter, 32 cm reactor length, 0,64 mm wire diameter, 10 meshes/inch, and 2938,982 cm2 catalyst surface area. The purpose of this experiment is to improve reactor design and production system by gauze-type structural catalyst reactor through catalytic decomposition of methane with Ni-Cu-Al catalyst. Performance experiment that have already done during 860 minutes at 700_C are stability test for 17 hours and activity test for 20 minutes of gauze structural catalyst at 700_C. The highest conversion of methane is 41,66% and the highest hydrogen purity is 30,45%. Yield carbon that produced by 4,71 gram catalyst is 179,15 gram carbon."

"Reaktor terstruktur gauze digunakan sebagai solusi dari masalah yang ditemukan pada penggunaan reaktor fixed bed untuk reaksi dekomposisi katalitik metana. Reaktor terstruktur gauze memiliki beberapa kelebihan, yaitu memiliki pressure drop yang rendah dan konversi lebih tinggi. Pada penelitian ini, dilakukan pemodelan dan simulasi reaktor terstruktur gauze menggunakan Computational Fluid Dynamics yang mengacu pada kinetika Snoeck, 1997. Pemodelan hanya mempertimbangkan neraca massa dan momentum, di mana reaktor diasumsikan bersifat isotermal. Simulasi dilakukan dengan mengubah-ubah variabel proses seperti temperatur reaktor, komposisi masukkan, tekanan masukkan, dan kecepatan masuk. Melalui simulasi variasi proses, dapat diketahui pengaruh perubahan kondisi operasi terhadap kinerja reaktor, seperti pada kenaikan temperatur akan menyebabkan konversi reaktor semakin meningkat.

---

Gauze structured reactors are used as the solution of problems found in the use of fixed bed reactor for reaction of catalytic decompotition methane. Gauze structured reactor has several advantages, having a low pressure drop and higher conversion.

In this study, the modeling and simulation of structured gauze reactor using Computational Fluid Dynamics refers to the kinetic Snoeck, 1997. Modelling only consider the mass balance and momentum, where the reactor is assumed to be isothermal.

Simulations carried out by varying process variables such as reactor temperature, inlet composition, inlet pressure and inlet velocity. Through the simulation process variations, we can know the effect of changing operating conditions on reactor performance, such as the rise in temperature will cause the reactor conversion increases."

"Dekomposisi katalitik metana adalah salah satu alternatif untuk memproduksi hidrogen dan nanokarbon bermutu tinggi secara simultan. Nanokarbon banyak diaplikasikan dalam penyimpanan hidrogen, support katalis, alat penyimpan memory, penyimpanan emisi, dan industri polimer, sedangkan hidrogen dapat digunakan sebagai umpan pada sel bahan bakar (fuel cell) yang ramah lingkungan karena apabila dibakar tidak menghasilkan polutan. Masalah yang biasanya timbul dalam reaksi dekomposisi katalitik metana ini adalah terjadinya deaktivasi katalis akibat deposit karbon dan terjadinya pressure drop di dalam reaktor. Penelitian ini bertujuan menguji kinerja reaktor dengan katalis terstruktur untuk mengatasi pressure drop di dalam reaktor. Katalis Ni-Cu-Al dipreparasi dengan menggunakan metode sol-gel dengan perbandingan atomik 2:1:1. Katalis ini dilapisi pada kawat stainless steel yang telah dibentuk dengan metode dip coating. Reaksi dilakukan dengan mengalirkan metana ke dalam reaktor pada temperatur 650°C dan 700°C serta tekanan atmosferik. Produk gas dianalisis dengan menggunakan gas chromatography yang terpasang secara online dengan aliran keluar reaktor. Penggunaan katalis terstruktur pada dua temperatur berbeda ini dapat menghasilkan konversi metana hingga 87.55 % dan 94.87%. Produk dari reaksi dekomposisi katalitik metana berupa hidrogen memiliki kemurnian hingga 87.53% dan 95.14%. Karbon yang dihasilkan memiliki yield 28.45 dan 32.85 gr karbon/gr katalis untuk waktu reaksi 8.4 jam. Untuk reaksi selama 33 jam menghasilkan 201 gr karbon/gr katalis. Karakterisasi dengan menggunakan TEM menunjukkan karbon yang dihasilkan berbentuk nanotube dengan diameter 50-100. Pada reaktor dengan katalis terstruktur ini tidak terjadi pressure drop yang dapat mengakibatkan berakhirnya reaksi. Reaksi berakhir karena katalis sudah terdeaktivasi akibat tertutupnya permukaan katalis oleh deposit karbon. Lifetime katalis dapat mencapai 33 jam dan masih dapat berlanjut.

---

Methane decomposition is an alternative way to produce high quality carbon nanotubes (CNTs) and hydrogen simultaneously. CNTs can been used for various applications such as hydrogen storage, electronic device, composite materials, field emission source, and catalyst support. Hydrogen can be used as the future clean energy resource such as for fuel cells, which doesn't emit pollutants when combusted. The problem often found in methane catalytic decomposition is the presence of pressure drop. This problem is expected to be solved by designing a structured catalyst reactor.

In this experiment, Ni-Cu-Al catalyst is prepared by sol-gel method. Stainless steel wiremesh is coated with catalyst by dip coating method and put into a quartz tube reactor. The experiment was done at 650°C and 700°C with atmospheric pressure. Methane is fed into the reactor and decomposed by the catalyst. An online chromatograph is used to detect the gas products. The morphology of CNTs is characterized by TEM. The use of structured catalyst in these two different temperature gives conversion of methane up to 87.55 % and 94.87%. Hydrogen as the product has a purity of 87.53% dan 95.14% .

The carbon yields are 28.45 and 32.85 gr carbon / gr catalyst for 8.4 hours of reaction. For 33 hours of reaction, the yield becomes 201 gr carbon/ gr catalyst. TEM characterization shows that the diameter of CNTs are between 50-100 nm for both cases. Pressure drop isn't found in this structured catalyst reactor which could end the reaction. The reaction ends when the catalyst is deactivated due to carbon deposit on the catalyst. The lifetime of the catalyst can reach 33 hours and can still continue."

"Carbon foam merupakan material yang menjanjikan sebagai substrat katalis terstruktur karena keunggulan sifatnya yang memiliki luas permukaan yang besar serta pressure drop yang rendah. Penumbuhan nanokarbon pada carbon foam dapat menghasilkan luas permukaan yang jauh lebih besar untuk deposisi inti aktif katalis. Penumbuhan nanokarbon dilakukan melalui reaksi dekomposisi katalitik metana dengan katalis nikel pada suhu 500_C selama 5 jam. Katalis nikel dipreparasi menggunakan metode presipitasi. Precipitating agent yang digunakan adalah urea dan amonia. Deposisi katalis nikel dengan urea dilakukan selama 12 jam dan 24 jam, dengan loading masing-masing sebesar 0,0285 dan 0,0448 g Ni/g CF. Hasil deposisi katalis dikarakterisasi menggunakan SEM. Hasil SEM menunjukkan bahwa waktu deposisi yang lebih lama menghasilkan dispersi katalis yang lebih merata. Hasil penumbuhan nanokarbon pada carbon foam dikarakterisasi menggunakan SEM dan BET. Hasil SEM menunjukkan bahwa pertumbuhan nanokarbon belum optimal, sedangkan hasil BET menunjukkan peningkatan luas permukaan carbon foam sebesar 11,55 m2/g.

---

Carbon foam is a promising material for structured catalyst support because it offers high surface area and low pressure drop. Growth of nanocarbon on carbon foam increasing accessible surface area of carbon foam to deposit catalyst particle. Growth of nanocarbon was done by catalytic decomposition of methane at 500_C. Reaction occurred in 5 hours. The catalyst used in this reaction is nickel which has been prepared by precipitation method, using urea and ammonia as precipitating agent. Deposition of nickel catalyst using urea as precipitation agent was carried out for 12 hours and 24 hours. Each deposition time produced different catalyst loading, which are 0.0285 and 0.0448 g Ni/g CF respectively. Products of deposition were characterized using SEM. SEM results showed that a longer deposition time produces a more uniform dispersion of catalysts. Product of nanocarbon growth on carbon foam was characterized using SEM and BET. SEM results showed a poor quality of nanocarbon grown on carbon foam, while the BET results showed an increasing surface area of 11.55 m2/g approximately."

"Dekomposisi katalitik metana adalah salah satu alternatif untuk memproduksi hidrogen dan nanokarbon bermutu tinggi secara simultan. Nanokarbon banyak diaplikasikan dalam penyimpanan hidrogen, support katalis, alat penyimpan memory, penyimpanan emisi, dan industri polimer, sedangkan hidrogen dapat digunakan sebagai umpan pada sel bahan bakar (fuel cell) yang ramah lingkungan karena apabila dibakar tidak menghasilkan polutan. Masalah yang biasanya timbul dalam reaksi dekomposisi katalitik metana ini adalah terjadinya deaktivasi katalis akibat deposit karbon dan terjadinya pressure drop di dalam reaktor. Penelitian ini bertujuan menguji kinerja reaktor dengan katalis terstruktur untuk mengatasi pressure drop di dalam reaktor. Katalis Ni/Cu/Al2O3 dipreparasi dengan menggunakan metode sol-gel. Katalis ini dilapisi pada kawat stainless steel yang telah dibentuk dengan metode dip coating. Reaksi dilakukan dengan mengalirkan metana ke dalam reaktor pada temperatur 650_C dan tekanan atmosferik. Produk gas dianalisis dengan menggunakan gas chromatography yang terpasang secara online dengan aliran keluar reaktor. Penggunaan katalis terstruktur ini dapat menghasilkan konversi metana hingga 59,57 %. Produk dari reaksi dekomposisi katalitik metana berupa hidrogen memiliki kemurnian hingga 99,32 %. Karbon yang dihasilkan memiliki yield 56,89 gr karbon/gr katalis. Karakterisasi dengan menggunakan TEM menunjukkan karbon yang dihasilkan berbentuk nanotube dengan diameter 30-50 nm dan ketebalan dinding 10- 20 nm. Pada reaktor dengan katalis terstruktur ini tidak terjadi pressure drop yang dapat mengakibatkan berakhirnya reaksi. Reaksi berakhir karena katalis sudah terdeaktivasi akibat tertutupnya permukaan katalis oleh deposit karbon. Lifetime katalis dapat mencapai 1340 menit atau 22,33 jam.

---

Methane decomposition is alternative way to produce high quality carbon nanotubes (CNTs) and hydrogen simultaneously. CNTs have been used for many applications such as hydrogen storage, electronic device, composite materials, field emission source, and catalyst support. Hydrogen can be used as clean energy sorce in the future. The solid CNTs products simultaneously produced make the catalyst deactive rapidly through blocking the active pores of catalyst or encapsulating the whole catalyst particle. Besides that, the CNTs products usually block the flow of methane and cause pressure drop. To solve that problem, reactor with structured catalyst is used in this research. Ni/Cu/Al2O3 catalyst was prepared by sol-gel method. Stainless steel gauze was coated with catalyst by dip coating method and was put in quartz reactor with 16 mm diameter. The experiment was done at 650 _C and atmospheric pressure. Methane (20 ml/min) was fed into the reactor and decomposed by the catalyst. An online chromatograph was used to detect the gas product. The morphologies of CNTs were characterized by using TEM. The using of structured catalyst in this experiment can give conversion of methane up to 59.57 % and yield carbon 56.89 gr carbon/gr catalyst. The hydrogen which is produced from reaction has high purity up to 99.32 %. TEM characterization shows carbon produced from this experiment has nanotubes morphologies with 30-50 nm diameter and 10-20 wall thickness. There was no pressure drop that happen in this experiment and the catalyst lifetime reach 1340 minutes or 22.33 hours."

"Pembuatan Carbon nanotube (CNT)sangat sulit dan mahal untuk dilakukan dalam skala industri. Oleh karena itu, pada penelitian ini reaktor dari skala laboratorium dimodelkan untuk menurunkan resiko kegagalan scale-up. Persamaan yang diperoleh dari penelitian kinetika dikombinasikan dengan prinsip peristiwa perpindahan menggunakan program Computational Fluid Dynamics (CFD) yaitu, COMSOL Multiphysics sehingga didapatkan sebuah model reaktor. Model disimulasikan dengan variasi space-time untuk melihat pengaruh parameter-parameter tersebut terhadap suhu dan produksi CNT. Hasil simulasi menunjukan pola aliran fluida, profil suhu, konsentrasi, dan konversi sebagai fungsi jarak dan waktu. Pola aliran fluida dipengaruhi tekanan dan faktor friksi dengan dinding dan pelat;sedangkan profil suhu dipengaruhi oleh reaksi, panas furnace dan kontak dengan lingkungan. Konversi metana meningkat akibat peningkatan space-time (9%). Berdasarkan hasil simulasi didapatkan konversi metana tertinggi pada space-time 0,006 gr.min/ml.

---

Production Carbon nanotubes (CNTs) are expensive and hard to do in industrial scale. Therefore, in this research the laboratorium scale reactor is being modeled to reduce the scale-risk of failure. The equations obtained from kinetic studies combined with the principle of transport phenomenon using Computational Fluid Dynamics (CFD) program Multiphysics to obtain a reactor model. Model simulated with space-time variation to study the effect of that parameter on the reactor temperature and CNT production.

The results obtained from the simulation are fluid flow pattern, temperature, consertration and conversion profile as a function of time and distance. The fluid flow pattern affected by pressure drop and friction factor between wall and plates. Meanwhile, the temperature profile is affected due to the reaction, heat from the furnace and contact with environment. Conversion of methane increased due to enhancement in space-time (9%). The greatest conversion of methane on space-time 0.006 gr.min/ml."

"Reaksi dekomposisi katalitik metana dipercaya dapat menghasilkan hidrogen dengan tingkat kemurnian yang tinggi, sehingga dapat langsung dimanfaatkan untuk aplikasi fuel cell tanpa proses purifikasi. Namun demikian, jumlah hidrogen per mol metana yang didapatkan dari reaksi ini masih lebih rendah daripada jumlah hidrogen per mol metana yang didapatkan dari reaksi reformasi kukus metana. Oleh karena itu, pengembangan reaksi ini difokuskan untuk menghasilkan produk karbon bernilai tinggi, seperti karbon nanotube, untuk meningkatkan nilai ekonomi dari reaksi dekomposisi metana ini. Bagaimanapun, untuk memperoleh nanokarbon yang berkualitas tinggi tidaklah mudah, karena memerlukan temperatur reaksi yang tinggi untuk mentransformasi katalis dalam bentuk quasi liquid. Penambahan logam transisi sebagai structural promoter dan oksida logam sebagai textural promoter pada katalis dapat menghasilkan katalis berfasa quasi liquid pada temperatur yang lebih rendah. Namun demikian, penambahan jenis textural promoter yang berbeda menghasilkan tipe nanokarbon yang berbeda. Pada penelitian ini, pengaruh dari textural promoter pada katalis terhadap yield karbon dievaluasi dengan melakukan reaksi dekomposisi katalitik metana pada temperatur 650 _ menggunakan katalis berbasis Ni-Cu dengan variasi textural promoter (MgO, SiO2, a n d A l2O3). Karakter katalis dievaluasi dengan analisa XRD sedangkan morfologi produk nanokarbon dievaluasi denagn analisa TEM. Hasil dari analisa XRD menunjukkan bahwa textural promoter mempengaruhi karakter kristalografik katalis. Karakter kristalografik ini selanjutnya mempengaruhi kualitas dan kuantitas produk nanokarbon. Yield karbon paling banyak diperoleh dengan menggunakan katalis bertextural promoter MgO, sedangkan kualitas karbon paling baik diperoleh dengan menggunakan katalis bertextural promoter Al2O3."