Hasil Pencarian  ::  Simpan CSV :: Kembali

"Mortar yang terbuat dari semen dan agregat halus dengan perbandingan 1:4, dimodifikasi dengan menambahkan abu sekam padi sebagai material subtitusi parsial yang menggantikan sejumlah proporsi agregat halus sebesar 10%, 20%, 30% dan 40% dari berat agregat halus. Serangkaian uji coba di laboratorium dilakukan untuk melihat pengaruhnya terhadap kuat tarik lentur, kuat tarik langsung dan susut mortar. Hasil evaluasi data hingga saat ini memberikan kesimpulan sebagai berikut : 1. Penggunaan abu sekam padi dalam campuran mortar mengakibatkan terjadinya penurunan kekuatan mortar. Semakin banyak penggunaan abu sekam padi semakin besar penurunan kekuatan mortar. 2. Penggunaan abu sekam padi pada campuran mortar menaikan susut kering mortar. Semakin banyak penggunaan abu sekam padi semakin besar penyusutan mortar.

---

The mortar used consists of 1 part cement and 4 parts of fine agreggate (sand) is modificated by rice husk ash as material subtitution partial of fine agreggate, with increasing of rice husk ash 10%, 20%, 30% and 40% of fine agreggate. Some trial mixes of mortar in laboratory were to find the influence about flexural strength, direct tensile strength and shrinkage of mortar.

The conclusions are:

1. The increase of rice husk ash in mortar can decrease the strength of mortar.

2. The increase of rice husk ash in mortar can increase the shrinkage of mortar."

"Pada penelitian ini dilakukan pengujian kuat tarik langsung, kuat tarik lentur, susut dan density dengan jumlah benda uji 250 buah.Pada penelitian ini dipakai 2 tipe Portland Composite Cement (PCC), Precious Slag Ball (PSB) dan Abu Sekam Padi (ASP) dengan komposisi campuran : 30% PCC (Portland Composite Cement) ? 30% ASP (Abu Sekam Padi) ? 40% PSB (Precious Slag Ball).Standar penelitian mengacu pada standar ASTM. Dari penelitian ini didapatkan kuat tarik langsung pada umur 28 hari sebesar 0.740 MPa untuk campuran PCC tipe 1 dan sebesar 0.641 MPa untuk campuran PCC tipe 2. Kuat tarik lentur pada umur 28 hari sebesar 1.750 MPa untuk campuran PCC tipe 1 dan sebesar 1.550 MPa untuk campuiran PCC tipe 2. Nilai susut sebesar 0.0092 untuk campuran PCC tipe 1 dan sebesar 0.0088 untuk campuran PCC tipe 2. Density Sebesar 1.579 gr/cm2 untuk campuran PCC tipe 1 dan sebesar 1.602 gr/cm2 untuk campuran tipe 2.

---

This research observing the tensile strength, flexural strength, length change and density of mortar cement done to 250 specimens.In this research two resources of Portland Composite Cement (PCC) produced by 2 industries were used in mortar mixing composed with Precious Slag Ball (PSB) and Rice Husk Ash (RHA) in proportion of 30% PCC; 30% RHA; 40% PSB. The terms used in this research relating to ASTM standards.The results from this research give value of tensile strength of 28 days type 1 and type 2 are 0.740 MPa and 0.641 MPa; Flexural strength of 28 days type 1 and type 2 are 1.750 MPa and 1.550 MPa; Shrinkage type 1 and type 2 are 0.0092 and 0.0088. Density type 1 and type 2 are 1.579 gr/cm2 and 1.602 gr/cm2."

"Sebagai negara agraris, Indonesia menghasilkan padi dalam jumlah besar setiap harinya. Selain itu, Indonesia sebagai negara berkembang menghasilkan limbah rumah tangga yang juga besar jumlahnya. Penelitian ini akan menggunakan abu sekam padi dari hasil pembakaran gabah padi dan limbah kertas sebagai admixture campuran mortar. Komposisi benda uji terdiri dari 4%, 8%, dan 12% abu sekam padi serta 10% kandungan kertas kering. Pengujian akan meliputi pengujian kuat tekan, kuat lentur, modulus elastisitas, susut, densitas, dan daya serap air. Mortar dengan kandungan abu sekam padi 4% memiliki kuat tekan tertinggi pada umur 28 hari."

"ABSTRAKDalam penelitian ini, peneliti menggunakan agregat halus untuk campuran mortar semen yang dicampurkan dengan bahan limbah berupa limbah adukan beton atau Concrete Sludge Waste (CSW) dan Abu Sekam Padi (RHA) yang dicampurkan dengan semen. Sifat mekanik yang diuji meliputi Kuat Tarik Langsung sebanyak 75 benda uji sesuai standar ASTM C 307-03, Kuat Tarik Lentur sebanyak 25 benda uji sesuai dengan standar ASTM C 78 - 02, Modulus Elastisitas sebanyak 25 benda uji sesuai standar ASTM C-580-02, dan Kuat Geser sebanyak 25 benda uji. Pada setiap pengujian memiliki variasi campuran yang berbeda-beda yang diberi kode CHWM 121 sampai CHWM 125. Pada pengujian Kuat Tarik Langsung nilai terbesarnya ada pada campuran CHWM 122 dengan nilai 5,52 MPa, sedangkan nilai terendahnya ada pada campuran CHWM 123 dengan nilai 2,40 MPa. Pada pengujian dan Modulus Elastisitas nilai terbesarnya ada pada campuran CHWM 121, sedangkan nilai terendahnya ada pada campuran CHWM 125. Pada pengujian Kuat Geser nilai terbesarnya ada pada campuran CHWM 121 dengan nilai 2,88 MPa, sedangkan nilai terendahnya ada pada campuran CHWM 123 dengan nilai 1,47 MPa.Dari pengujian Kuat Tarik Langsung disimpulkan bahwa campuran yang paling optimum untuk menahan Tegangan Tarik Langsung adalah campuran CHWM 122. Dari pengujian Kuat Tarik Lentur dan Modulus Elastisitas disimpulkan bahwa campuran yang paling optimum adalah CHWM 121. Dari pengujian Kuat Geser disimpulkan bahwa campuran yang paling optimum adalah CHWM 121.

---

ABSTRACTIn this study, researchers used a mixture of fine aggregate for cement mortar that is mixed with waste materials in the form of waste concrete or Concrete Sludge Waste (CSW) and Rice Husk Ash (RHA) is mixed with cement. Mechanical properties tested include Direct Tensile Strength as much as 75 specimens according to ASTM C 307-03, Flexural Strength Modulus of Ruptureas many as 25 test specimens in accordance with ASTM C 78-02, Modulus of Elasticity of 25 test specimens according to ASTM C-580-02 , and Shear of Strength much as 25 specimens. At each test has a variety of different mixtures are given a code CHWM CHWM 121 to 125. Direct Tensile of Strength on testing its greatest value is in the mixture CHWM 122 with a value of 5.52 MPa, while the lowest is in the mixture with a value of 2.40 CHWM 123 MPa. On Direct Tensile Strength testing and Modulus of Elasticity greatest value is in a mixture of CHWM 121, while the lowest is in the mixture CHWM 125. On Shear of Strength testing the greatest value is in the mixture CHWM 121 with a value of 2.88 MPa, while the lowest is in the mixture with a value of 1.47 CHWM 123 MPa.From Direct Tensile Strength testing concluded that the most optimum mix to hold Direct Tensile is a mixture of CHWM 122. On Shear of Strength testing and Modulus of Elasticity is concluded that the most optimum mix is CHWM 121. Shear of Strength tests concluded that the most optimum mix is CHWM 121."

"Menurut survey Badan Pusat Statistik di Indonesia diketahui telah terjadi pertumbuhan nilai konstruksi di Kalimantan Timur (lokasi baru Ibu Kota Negara) sebesar 6,60% dari tahun 2019-2020. Semakin tinggi nilai konstruksi maka semakin tinggi pula permintaan bahan bangunan, contohnya seperti mortar semen portland. Akan tetapi, terdapat dampak buruk dalam pemakaian semen portland yang secara terus-menerus yaitu terjadinya pemanasan global karena adanya emisi gas CO yang tinggi. Untuk mengurangi dampak buruk tersebut diperlukanlah bahan pengganti semen yang lebih ramah lingkungan seperti material geopolimer. Dalam pembentukan mortar geopolimer dibutuhkan bahan utama yang mengandung kadar Si dan Al yang tinggi seperti ASP dan zeolit, serta perlu adanya alkali aktivator seperti NaOH dan NaSiO yang berperan sebagai larutan pengikat unsur Si dan Al dalam reaksi geopolimerisasi. Ada perlakuan khusus pada studi ini untuk menjaga kualitas mortar geopolimer ASP-Zeolit yang terbentuk yaitu metode dengan oven di suhu 60°C selama 24 jam. Pada studi ini dilakukan pembentukan mortar geopolimer dengan lima variasi komposisi penyusun mortar geopolimer antara lain 100%ASP; 90%ASP-10%Zeolit; 70%ASP-30%Zeolit; 50%ASP-50%Zeolit; dan 100%Zeolit, untuk mengetahui pengaruh kadar prekursor terhadap nilai kuat tekan mortar tersebut serta membandingkan nilai kuat tekan mortar geopolimer dengan kuat tekan mortar semen portland. Hasil penelitian ini menunjukkan adanya kandungan Si yang tinggi dalam bahan penyusun mortar geopolimer akan meningkatkan nilai kuat tekannya seperti mortar geopolimer 100%ASP, tetapi nilai kuat tekan mortar geopolimer ASP-Zeolit masih dibawah nilai kuat tekan mortar semen portland.

---

According to a survey conducted by Indonesia's Central Statistics Agency, East Kalimantan (the new location for the State Capital of Indonesia) saw a 6,60% increase in construction value between 2019 and 2020. The higher the construction value, the higher the demand for building materials, such as portland cement mortar. However, there are negative impacts in the continuous use of portland cement which causes a global warming effect due to high CO2 gas emissions. To reduce these negative impacts, a more environmentally friendly cement substitute material, such as geopolymer material, is needed. In the formation of geopolymer mortar, the main ingredients that contain high levels of Si and Al are needed, such as RHA and zeolite, as well as the need for alkaline activators such as NaOH and Na2SiO3 which act as a binding solution for Si and Al elements in the geopolymerization reaction. There is special treatment in this study to maintain the quality of RHA-Zeolite geopolymer mortar that is formed namely curing oven at 60°C for 24 hours. In this study, geopolymer mortar was formed with five variations of geopolymer mortar composition, including 100% RHA; 90% RHA-10% Zeolite; 70% RHA-30% Zeolite; 50% RHA-50% Zeolite; and 100% Zeolite, to determine the effect of precursor content on the compressive strength of the mortar and to compare the compressive strength of this geopolymer mortar with the compressive strength of portland cement mortar. The results of this study indicate that a high Si content in the RHA-Zeolite geopolymer mortar will increase its compressive strength like 100% RHA geopolymer mortar, but the compressive strength of RHA-Zeolite geopolymer mortar is still below the compressive strength of portland cement mortar."

"Penelitian awal mortar dengan campuran semen, abu sekam padi (ASP) dan precious slag ball (PSB) dengan perbandingan 30% PCC, 20% ASP dan 50% PSB di uji beberapa sifat mekanisnya yaitu kuat tarik langsung, kuat tarik lentur, susut dan density. Pengujian di lakukan dengan mengikuti standar pengujian Kuat Tarik Langsung ASTM-C-307-03, Kuat Lentur ASTM-C-348-02, Susut ASTM-C-490-00, Density ASTM-D-720-00. Dari penelitian diharapkan campuran ini dapat menghasilkan mortar dengan sifat mekanis yang memenuhi standar SNI atau ASTM.Nilai modulus kehalusan ASP adalah 0,754 dan PSB adalah 1,054, Akibat penambahan ASP dalam campuran nilai FAS yang di dapat tinggi yaitu lebih dari berat semen, hal ini disebabkan air yang dibutuhkan lebih banyak untuk mencapai konsistensi normal. Untuk semen tipe 1 (Tiga Roda) Campuran PCC dan PSB memiliki nilai kuat tarik langsung 3,6385 MPa ; kuat tarik lentur 13,992 MPa ; susut 0,0061% dan density 2,811 g/cm3. Campuran PCC ASP dan PSB memiliki nilai kuat tarik langsung 0,8975 MPa ; kuat tarik lentur 2,3625 MPa ; susut 0,0077% dan density 1,848 g/cm3. Untuk semen Tipe 2 (Holcim) Campuran PCC dan PSB memiliki nilai kuat tarik langsung 2,8667 MPa ; kuat tarik lentur 14,3166 MPa ; susut 0,0061% dan density 2,781 g/cm3 . Campuran PCC ASP dan PSB memiliki nilai kuat tarik langsung 0,8684MPa ; kuat tarik lentur 2,7882 MPa ; susut 0,0073% dan density 1,907 g/cm3.Mortar yang dihasilkan dengan menggunakan campuran PSB memiliki density tinggi sehingga nilai kuat tarik langsung dan tarik lentur lebih tinggi jika dihitung berdasarkan rumus yang ada di dalam SNI 03-2847-2002, sedangkan untuk mortar yang menggunakan campuran ASP dan PSB memiliki density lebih rendah dan dapat diklasifikasikan dalam mortar ringan dengan nilai 1,900 g/cm3 untuk itu menggunakan rumus perhitungan kuat tarik langsung dan tarik lentur untuk mortar ringan sesuai dengan SNI 03-2847-2002.

---

Initial studies with a mixture of mortar cement, rice husk ash (ASP) and precious slag ball (PSB) with a ratio of 30% PCC, 20% RHA and 50% PSB tested several mechanical properties of the direct tensile strength, flexural tensile strength, shrinkage and density. Tests done by following the testing standard ASTM Direct Tensile Strength C-307-03, Flexural Strength ASTM C-348-02, Shrinkage ASTM-C-490-00, Density ASTM D-720-00. This mixture of research is expected to produce mortar with mechanical properties that meet SNI or ASTM standards.

ASP fineness modulus value is 0.754 and the PSB is 1.054, a result of the addition of ASP in a mixture of values that FAS can be as high as more than the weight of cement, this is due to more water needed to achieve normal consistency. The first type of cement (Tiga Roda) mixture of PCC and the PSB has a value of direct tensile strength 3.6385 MPa; Flexural Tensile Strength 13.992 MPa; Shrinkage 0.0061% and Density 2.811 g/cm3. Mixture of PCC, ASP and the PSB has a value of direct tensile strength 0.8975 MPa; Flexural Tensile Strength 2.3625 MPa; Shrinkage 0.0077% and Density 1.848 g/cm3. For the second tipe of cement (Holcim) Mixed PCC and the PSB has a value of Direct Tensile Strength 2.8667 MPa; Flexural Tensile Strength 14.3166 MPa; Shrinkage 0.0061% and Density 2.781 g/cm3. Mixture of PCC, ASP and the PSB has a value of Direct Tensile Strength 0.8684 MPa; Flexural Tensile Strength 2.7882 MPa; Shrinkage 0.0073% and Density 1.907 g/cm3.

Mortar is produced by using a mixture of PSB, has a high density so that the value of the direct tensile strength and flexural tensile higher if calculated on a formula that is in the SNI 03-2847-2002, while for the mortar using a mix of ASP and the PSB has a lower density and can be classified in the lightweight mortar with a value of 1.900 g/cm3 for it using a formula calculating the direct tensile strength and tensile bending to light mortar according to the SNI 03-2847-2002."

"ABSTRAKDalam penelitian ini penggunaan agregat halus untuk Campuran mortar semen digantikan dengan bahan limbah berupa abu sekam padi (ASP) dan Precious Slag Ball (PSB). kuat tarik langsung sebanyak 40 benda uji sesuai standar ASTM C 307-03, kuat tarik lentur sebanyak 70 benda uji sesuai standar ASTM C 580-02, susut sebanyak 10 benda uji sesuai standar ASTM C-490-04, density sebanyak 20 benda uji sesuai standar ASTM C 905-01. Dengan menggunakan semen PCC dari 2 industri berbeda dan dengan komposisi Campuran 30% PCC 70% PSB (Campuran 1) dan 30% PCC 15% ASP 55% PSB (Campuran 2) diperoleh kuat tarik langsung pada umur 28 hari sebesar 3.103 MPa dan 2.867 MPa untuk Campuran 1; serta 0,935 MPa dan 0.875 MPa untuk Campuran 2. Kuat tarik lentur umur 28 hari sebesar 12.87 MPa dan 13.99 MPa untuk Campuran1 serta 3.136 MPa dan 3.131 MPa untuk Campuran 2. Regangan susut untuk Campuran 1 sebesar 0,00607, 0,00607 dan Campuran 2 sebesar 0,00713, 0,00667. Nilai density Campuran 1 sebesar 2,652 gram/m3 dan 2,65793 gram/m3 serta untuk Campuran 2 sebesar, 1,67044 gram/m3 dan 1,69017 gram/m. Campuran mortar dapat digunakam sebagai plesteran dengan syarat shrinkage < 0.1% ( ASTM C-531); tarik langsung > 0.5 MPa (BS 4551:1980)

---

ABSTRACTIn this study the use of fine aggregate for cement mortar was replaced with waste material called rice husk ash (RHA) and Precious Slag Ball (PSB). Mechanical properties tested in the laboratory were tensile strength using 40 samples according to ASTM C 307-03, flexural strength using 70 samples acording to ASTM C 580-02, shrinkage using 10 samples acording to ASTM C 490-04, density using 20 samples according to ASTM C 905-01. The composition of mortar using cement PCC taken from 2 different industries with composition of mixture 30% PCC 70% PSB (Mixture 1) and 30% PCC 15% ASP 55% PSB (Mixture 2). The tensile strength of 28 days mixture 1 and mixture 2 are 3.103 MPa and 2.867 MPa, 0,935 MPa and 0.875 MPa; The flexural strength of 28 days mixture 1 and mixture 2 are 12.87 MPa and 13.99 MPa, 3.136 MPa and 3.131 MPa; The shrinkage mixture 1 and mixture 2 are 0,00607 and 0,00607, 0,00713 and 0,00667; Density of mixture 1 and mixture 2 are 2,652 gram/m3 and 2,65793 gram/m3, 1,67044 gram/m3 and 1,69017 3 gram/m. In my research, this mortar mixture can be used for plaster with the condition of shrinkage is below than 0.1% ( ASTM C-531); and tensile strangth above than 0.5 MPa (BS 4551:1980) "

"Dalam penelitian ini meninjau penggunaan bahan limbah adukan beton siap pakai atau Concrete Sludge Waste (CSW) sebagai substitusi pasir untuk agregat halus dan penggunaan abu sekam padi Rice Husk Ash (RHA) sebagai substitusi perekat semen dalam campuran mortar yang diharapkan dapat dimanfaatkan dalam pembuatan paving block. CSW itu sendiri yaitu limbah sisa adukan beton yang sama sekali tidak terpakai dan menjadi suatu masalah bagi perusahaan produsen ready mix dalam hal tempat pembuangan akhirnya. Sifat mekanik campuran mortar yang diuji dengan total benda uji sebanyak 125 buah. Yang meliputi kuat tarik langsung 75 benda uji sesuai standar ASTM C 307-03, modulus elastisitas sebanyak 25 benda uji sesuai standar ASTM C 580-02, dan kuat geser sebanyak 25 benda uji. Pengujian sifat mekanis mortar dibagi kedalam 5 variasi campuran mortar dengan penambahan komposisi CSW sebanyak 30%,40%,50%,60%,70% untuk setiap masing-masing variasi campuran. Dalam pengujian ini didapatkan nilai kekuatan terbesar untuk campuran mortar dengan komposisi semen, agregat halus 1:3, yang terdiri dari 92% Semen, 8% RHA, 70% Pasir, 30% CSW mencapai nilai kuat tarik optimum sebesar 4.98 MPa, modulus elastistas sebesar 10299.224 MPa, dan nilai kuat geser sebesar 1.09 MPa.

---

In this research reviewed the use of waste material concrete ready mix or Concrete Sludge Waste (CSW) as a substitute sand for fine aggregate and the use of Rice Husk Ash (RHA) as a substitute for cement adhesive in the mix mortar that is expected to be utilized in the manufacture of paving blocks . CSW's own residual waste concrete that is completely unused and become a problem for ready mix manufacturers company in landfills. Mechanical properties of mortar mixtures were tested with a total 125 specimens. Which includes 75 direct tensile test specimens according to ASTM C 307-03, modulus of elasticity with 25 test specimens according to ASTM C 580-02, and the shear strength with 25 specimens.

Testing the mechanical properties of mortar mixtures were divided into five variations of the composition mortar with the addition of CSW as much as 30%, 40%, 50%, 60%, 70% for each variation of mixture. In this test the value obtained for the greatest strength of mortar mixed with the composition of cement, fine aggregate ratio 1:3, which consists of 92% cement, 8% RHA, 70% sand, 30% CSW getting optimum tensile strength value 4.98 MPa, modulus of elasticity 10299.224 MPa, and shear strength 1.09 MPa."

"ABSTRAK Penelitian ini bertujuan untuk membuat mortar menggunakan limbah kertas yang telah diproses sebelumnya untuk mendapatkan mortar yang ramah lingkungan dengan memaanfaatkan limbah namun tetap memiliki sifat mekanis dan fisik yang baik dimana kuat tekan melampaui 17.24 MPa dan densitasnya di bawah 1.8 gr/cm3 . Benda uji ditambahkan zat adiktif berupa fly ash dengan proporsi 4%, 8%, dan 12 % serta superplasticizer sebanyak 1% terhadap berat semen yang digunakan. Pengujian yang dilakukan adalah kuat tekan, kuat lentur, susut, modulus elastisitas, densitas, dan daya serap air. Penelitian ini akan merujuk pada ASTM C 873-94 dan ASTM C 78-94. Dari rata-rata hasil pengujian pada umur 28 hari, sampel dengan fly ash 8% memiliki nilai kuat tekan dan kuat lentur paling tinggi yaitu masing-masing sebesar 18.55 MPa dan 6.35 MPa. Susut terbesar terjadi pada sampel dengan penambahan fly ash sebesar 4% yaitu dengan nilai kumulatif sebesar 19.1%. Modulus elastisitas paling tinggi ada pada penambahan fly ash sebesar 12% yaitu dengan nilai rata-rata sebesar 3233.8 MPa. Densitas terbesar ada pada sampel dengan penambahan fly ash sebesar 12% yaitu dengan nilai rata-rata sebesar 1.78 gr/cm3. Dan untuk daya serap air paling rendah dimiliki oleh sampel dengan penambahan fly ash sebesar 12% yaitu dengan nilai rata-rata 11.59%.ABSTRAKThe purpose of this research is making mortar using waste paper that has passed its pretreatment in order to get green mortar using waste but still has good mechanical and physical characteristic which is the compressive strength should be above 17.24 MPa and the density should be below 1.8 gr/cm3. All samples have been added by fly ash with proportion 4%, 8%, and 12% and superplasticizer 1% based on cement mass. Tests that have been done are compressive strength, flexural strength, shrinkage, elastic modulus, density, and absorption. This research referred to ASTM C 873-94 and ASTM C 78-94. Average result at age 28 day, samples with addition 8% of fly ash have the highest score for compressive and flexural strength with each of them 18.55 Mpa and 6.35 MPa. The highest shrinkage happened on samples with addition 4% of fly ash with the cumulative result 19.1%. For elastic modulus, the highest score happened on samples with addition 12% of fly ash with the average result 3233.8 MPa. The highest score for density happened on samples with addition 12% of fly ash with the average result 1.78 gr/cm3. And for absorption, the lowest score happened on samples with addition 12% of fly ash with average result 11.59%."

"Presious Slag Ball adalah limbah dari industry baja dan Abu Sekam Padi adalah hasil limbah pertanian. Kedua limbah ini belum dimanfaatkan secara optimal. Oleh sebab itu, dalam penelitian ini dilakukan usaha agar presious slag ball dan abu sekam padi dapat menjadi material yang memiliki nilai ekonomi pada mortar. Pada penelitian ini dilakukan pengujian kuat tarik langsung, kuat tarik lentur dan susut pada mortar. Dalam hal ini mortar menggunakan 2 (dua) tipe semen PCC yang berasal dari industri semen yang berbeda, yang kemudian dicampura dengan abu sekam padi dan presious slag ball dengan perbandingan 30% PCC : 25% ASP : 45% PSB. Standar penelitian ini mengacu pada standar ASTM. Dari penelitian ini dihasilkan nilai kuat tarik langsung mortar pada umur 28 hari berkisar antara 0.81-1.14 MPa untuk mortar dengan PCC type 1 dan 0.81-1.10 MPa untuk mortar dengan PCC tipe 2, kuat tarik lentur pada umur 28 hari berkisar antara 2.33-2.70 MPa untuk mortar dengan PCC tipe 1 dan 2.42-2.59 MPa untuk mortar dengan PCC tipe 2, dan nilai susut mortar PCC tipe 1 dan tipe 2 sebesar 0.0083 dan 0.0078. Pada penelitian ini, nilai kuat tarik langsung dan kuat tarik lentur yang menngunakan abu sekam padi yang lebih kecil serta nilai susut mortar yang lebih besar dibandingkan dengan mortar tanpa abu sekam padi.

---

Precious Slag Ball is a waste of metal industry and Rice Husk Ash is a waste of agricultural activity. Both of those wastes are currently not used optimally. Therefore, there is an effort to use precious slag ball and rice husk ash to be a valuable economic material on the mortar. This research concerning about tensile strength, flexural strength and length change of mortar. This mortar using portland composite cement (PCC) with 2 (two) type which produced by 2 industries mixing with rice husk ash (RHA) and precious slag ball (PSB) in proportion of 30% PCC: 25 % RHA : 45% PSB. This Research is based on the ASTM standard.

The results from this research give value of tensile strength when the mortar at 28 days is between 0.81-1.14 MPa for mortar with PCC type 1 and 0.81-1.10 MPa for mortar with PCC type 2, flexural strength of 28 days is between 2.33 -2.70 MPa for mortar with PCC type 1 and 2.42-2.59 MPa for mortar with PCC type 2, and Shrinkage for PCC type 1 and type 2 are 0.0083 and 0.0078. In this research, the tensile strength and flexural strength for mortar using RHA have smaller value and shrinkage have higher value than mortar without RHA."