Hasil Pencarian  ::  Simpan CSV :: Kembali

"Pengaruh perlakuan penuaan terhadap temperatur transformasi paduan ingat bentuk TiNi. Telah dilakukan penelitian temperatur transformasi paduan ingat bentuk TiNi akibat pertakuan penuaan. Paduan dengan komposisi Ti-50,04% at.Ni sebagai paduan ingat bentuk diberikan perlakuan perautan pada 1000°C selama 1 jam dan dicelupkan kedalam air kemudian dituakan pada temperatur 500 °C, 550 °C, 600 °C, 650 °C dan 700 °C selama 10 jam. Temperatur transformasi ditentukan dari pengukuran resistansi. Hasil pengamatan menunjukkan bahwa temperatur transformasi martensit mengalami kenaikan sekitar 4°C akibat proses penuaan pada 500°C selama 10 jam, tetapi penuaan dengan temperatur 500 °C - 700 °C selama 10 jam tidak menunjukkan perubahan yang berarti terhadap temperatur transformasi.

---

Effect of aging treatment on the transformation temperature of a TiNi shape memory alloy. Investigation of transformation temperature of a TiNi alloy due to aging treatment has been done. The shape memory alloy with Ti-50.04 % at.Ni composition was solution treated at 1000 °C for 1 hour and quenched in water, then aged in temperature 500 °C, 550 °C, 600 °C, 650 °C and 700 °C for 10 hours. Transformation temperature was measured using resistance measurement technique. The results of observation show that the martensitic transformation temperature increases about 4 °C after aging process at 500 °C for 10 hours, but in aging temperature 500 °C - 700 °C, there no significant change of the transformation temperature."

"Penelitian presipitasi pada paduan logam ingat bentuk (shape memory alloy) TiNi dan pengaruhnya terhadap temperatur transformasi, telah banyak dilakukan. Hasilnya antara lain menyatakan bahwa terbentuknya presipitat T13Ni4 dapat mengakibatkan paduan ingat bentuk TiNi peka terhadap perubahan temperatur laku panas, tetapi apabila presipitat tumbuh hingga mencapai fasa kesetimbangan, yaitu presipitat TiNi3, paduan ingat bentuk tidak menunjukan adanya fasa antara saat terjadi transformasi.Dalam penelitian ini, telah dilakukan penelitian pengaruh proses penuaan terhadap presipitasi dan temperatur transformasi ingat bentuk paduan Ti-50.04%at. Ni, dengan tujuan untuk mengetahui karakteristik presipitat dan temperatur paduan Ti-50,04%at.Ni yang dituakan pada tempertaur 550 °C selama 1, 2, 5, 10, 20 dan 30 jam, pengamatan dilakukan menggunakan beberapa metoda yaitu mikroskop optik, mikroskop elektron transmisi (Transmission Electron Microscope - TEM) dan metoda tahanan listrik four probe.Hasil penelitian menunjukan bahwa paduan Ti-50.04%at.Ni, akibat laku panas penuaan berfasa martensit dengan orientasi pelat yang acak. Presipitat yang terbentuk adalah TiNi3 yang tumbuh pada orientasi tertentu, yaitu sesuai dengan hubungan [2021]TmNi3 // [020]Matriks, sedangkan temperatur transformasi tidak menunjukan perubahan yang berarti sebagai akibat perlakuan penuaan.

---

Examination of precipitate of TiNi shape memory alloy on temperature transformation has been done by many scientists. They observed that Ti3Ni4 precipitate can affect the transformation temperature of the alloy by heat treatment. If precipitate grows into stability phase, i.e. TiNi3 phase, shape memory alloy failed to show intermediate phase. In this research work aging process on precipitation and transformation temperature of Ti-50.04%at.Ni shape memory alloy were carried out.

The aim was study the characteristics of precipitate and transformation temperature of Ti-50.04 %at.Ni alloy which were aged at 550 °C for 1, 2, 5, 10, 20 and 30 hours. The testing method use optical microscope, Transmission Electron Microscope (TEM) and four-probe electric resistance.

Experimental results show that Ti-50.04%at.Ni alloy, which were effected by aging treatment have martensite phase. This martensitic is arranged by fine-laths with random orientation. Type of precipitates observed is TiNi3 and they grow through fixed orientation, i.e. [2021]TiNi3 11 [020]Matrix. Furthermore in this study, the transformation temperature were not significantly affected by aging treatment."

"Paduan Aluminium 6201 adalah paduan yang khusus dipakai untuk kawat penghantar. Oleh karena lingkungan pemakaiannya seringkali menerima beban tarik yang cukup besar dan bersifat korosif, maka untuk memenuhi kriteria ini paduan tersebut harus diberikan perlakuan panas penguatan (precipitation hardening). Dalam penelitian ini proses perlakuan panas (artificial-aging) paduan Aluminium 6201 dilakukan pada temperatur antara 140°C-200°C dengan waktu "aging" selama 4 (empat) jam. Hasil pengamatan pengaruh temperatur aging terhadap kekuatan-tarik dan kekerasan menunjukkan, harga optimum terjadi pada temperatur "aging" antara 155°C-170°C. Sedangkan pengaruh temperatur "aging" terhadap laju korosi, menunjukkan laju terendah terjadi pada temperatur aging antara 140°C-155°C. Dari hasil pengamatan dengan "SEM-EDAX" menunjukkan bentuk korosi merupakan kombinasi antara "pitting" dan "intergranular" dan umumnya paduan Aluminium 6201 tidak tahan terhadap unsur Cl (chloride) yang terdapat didalam elektrolit disamping unsur yang lain seperti Si, Fe, Mn, Cu, dan Cr yang bersifat lebih katodik terhadap matrik aluminium. Sedang unsur Mg dan Zn bersifat lebih anodik. Hasil pengamatan dengan EPMA pada produk korosi menunjukkan makin tinggi temperatur "aging" makin banyak distribusi unsur paduan yang muncul ke permukaan sampel uji seperti Fe, Mg, Cu, Zn, Cl, K dan 0 yang berarti laju korosi maksimum lebih mungkin terjadi pada temperatur "aging" maksimum 200°C. "

"ABSTRAK Salah saiu proses Iaku panas pada A1 7050 adalah laku panas dengan kondisi 1emper T 7X. yang cianraranya Terdlri dar] T 73, T 7451 dan T 76. Kesemua proses laku panes ln! melibaikan Iaku panas penuaan ganda ( duplex aging ] _ Proses Inl akan memberikan perubcrhan pada strukiur mikro, yang mempengaruhl sifat dan karalderlstik can rnarenor. unrux nu cnramum penernim mengenal pengcuuh rempercrur dan waklu padaagrngrahap-2dser