Hasil Pencarian  ::  Simpan CSV :: Kembali

"Pipa elbow biasanya digunakan sebagai sambungan (fitting) ketika terjadi perubahan orientasi yang cukup ekstrim pada jalur pipa transmisi. Jalur pipa transmisi biasanya ditanam didalam tanah (underground) yang rentan terhadap korosi eksternal sehingga perlu dilakukan analisis keandalan. Analisis keandalan dilakukan dengan menggunakan simulasi Monte Carlo dengan terlebih dahulu mengukur pH, resistivitas tanah dan menghitung laju korosi eksternal. Keandalan pipa elbow pada segmen I adalah 39.56%, segmen II adalah 75.68%, dan segmen III adalah 99.99% Nilai resistivitas tanah pada segmen I berada pada level very corrosive (<500Ω-cm), segmen II berada pada level corrosive (500-1000 Ω-cm), dan segmen III berada pada level moderately corrosive (1000-2000 Ω-cm). Nilai pH berada pada rentang 5-7 untuk semua segmen. Laju korosi pipa elbow berkisar antara 0.029-0.765 mm/year, dan meningkat seiring penurunan nilai resistivitas tanah. Pengamatan struktur mikro menunjukkan ukuran butir pipa elbow adalah sebesar 16,5 µm. Hasil permodelan Autodesk Inventor memperlihatkan bahwa terjadi konsentrasi tegangan pada pipa sebesar 160 MPa , sementara itu hasil permodelan Caesar II.5.1 menunjukkan bahwa bending stress pada pipa elbowmerupakan stress paling tinggi (666-679 kg./sq. cm) pada saat kondisi operasi.

---

Elbow pipe is commonly used as fitting when pipeline shows an extreme change on its direction. Generally, transmission pipeline is buried underground which severe to external corrosion, thus reliability analysis is required. Reliability analysis was performed by using Monte Carlo simulation by first measured pH, soil resistivy and external corrosion rate. Reliability of elbow pipe at segment I was 39.56%, segment II was 75.68%, and segment III was 99.99%. Soil resistivity value at segment I was on very corrosive level (<500Ω-cm), while segement II was on corrosive level (500-1000 Ω-cm), and segment III was on moderately corrosive level (1000-2000 Ω-cm). pH value ranged from 5-7 for all segments. Corrosion rates ranged from 0.029-0.765 mm/year, and increased gradually as decreased of its soil resistivity value. Microstructure examination showed that grain size on elbow pipe was 16,5 µm. Autodesk Inventor modelling revealed that stress concentration was occured on innert side of elbow pipe as much as 160 MPa , while Caesar II.5.1 modelling showed that bending stress was the highest stress (666-679 kg./sq. cm) in operating condition."

"ABSTRAKJaringan pipa adalah salah satu sarana transportasi minyak dan gas yang paling aman dan ekonomis sehingga pipa tidak boleh mengalami kegagalan saat beroperasi. Pipa lurus dalam suatu pipeline adalah pipa dengan geometri yang paling sering dijumpai. Jalur pipa transmisi biasanya ditanam didalam tanah (underground) sehingga rentan terhadap korosi eksternal. Oleh karena itu perlu dilakukan analisis keandalan, terutama pada geometri lurus. Pengujian keandalandilakukan dengan menggunakan simulasi Monte Carlo. Untuk mengetahui pengaruh tanah terhadap laju korosi pipa maka dilakukan pengukuran pH , resistivitas tanah dan laju korosi pipa pada setiap segmen. Hasil dari pengukuran laju korosi pipa lurus kemudian dibandingkan dengan laju korosi pipa elbow.Pengamatan mikrostruktur dilakukan untuk mengetahui penyebab perbedaan laju korosi kedua jenis pipa tersebut. Untuk mengetahui kemungkinan terjadinya Stress Corrosion Cracking pada pipa lurus dilakukan permodelan menggunakan Autodesk Inventor. Nilai resistivitas tanah pada segmen I berada pada level very corrosive (<500Ω-cm), segmen II berada pada level corrosive (500-1000 Ω-cm),dan segmen II berada pada level moderately corrosive (1000-2000 Ω-cm). Nilai pH berada pada rentang 5-7 untuk semua segmen. Laju korosi pipa lurus meningkat seiring penurunan nilai resistivitas tanah, dengan range nilai antara 0.15-0.83 mm/year,. Pengamatan struktur mikro menunjukkan ukuran butir pipa lururs adalah sebesar 10.84 μm. Hasil permodelan Autodesk Inventor memperlihatkan bahwa terjadi konsentrasi tegangan pada pipa sebesar 122,2 Mpa. Keandalan pipa lurus pada segmen adalah 36.35%, segmen II adalah 56.03%, dansegmen III adalah 96.61%.

---

ABSTRACTThe pipeline is one means of transportation of oil and gas are the most safe and economical so that the pipe should not fail during operation. Straight pipe in a pipeline is a pipe with the geometry of the most frequently encountered. Transmission pipelines are usually planted in the ground (underground) so susceptible to external corrosion. Therefore it is necessary for the reliability analysis, especially in a straight geometry. Reliability testing is done using Monte Carlo simulations. To determine the influence of soil on the rate of corrosion of pipes is carried out measurements of pH, soil resistivity and corrosion rate of pipes on each segment. Results of straight pipe corrosion rate measurements were then compared with the corrosion rate of elbow pipe. Microstructural observations performed to determine the cause of differences in the corrosion rate of the twotypes of pipe. To determine the possibility of Stress Corrosion Cracking in a straight pipe made from modeling using Autodesk Inventor. Soil resistivity values in the segment I was at the level very corrosive (<500Ω-cm), segment II at the level of corrosive (500-1000 Ω-cm), and segment II at the level of moderately corrosive (1000-2000 Ω-cm). PH value in the range 5-7 for all segments. Straight pipe corrosion rate increases with decrease in soil resistivity values, the values range between 0.15-0.83 mm / year,. Observation of the microstructure shows a grain size of the pipe lururs is 10.84 μm. Autodesk Inventor modeling results show that there are stress concentration on the pipe at 122.2 MPa. Reliability straight pipe segment was 36.35%, segment II is 56.03%, and segment III is 96.61%"

"Meningkatnya pengendara sepeda motor pada ruas-ruas jalan di kota-kota besar, khususnya Jakarta memberikan permasalahan baru bagi dunia transportasi. Kehadiran serta karakter fleksibel yang dimiliki sepeda motor di atas jalan membuat arus lalu lintas menjadi acak, kecelakaan meningkat, kendaraan lain pun harus lebih hati-hati dalam berkendara sehingga waktu perjalanan pun menjadi semakin kecil.Dari masalah-masalah yang muncul seperti itu maka timbul gagasan untuk membuat jalur yang khusus digunakan oleh pengendara sepeda motor yang tidak lain dimunculkan untuk meningkatkan kinerja ruas jalan. Melalui pengamatan dengan merekam arus lalu-lintas serta melakukan interpretasi data dari rekaman tersebut diperoleh hubungan antara kecepatan dan volume lalu-lintas pada kebutuhan jarak samping aman sepeda motor, yang tentu berpengaruh pada penentuan lebar jalur khusus sepeda motor yang digunakan.Pada kasus pengamatan segmen ruas Jalan Buncit Raya Pulo arah Pasar Minggu di kawasan Jakarta Selatan yang terdiri dari jalur cepat dan jalur lambat, hasil dari desain jalur khusus sepeda motor menaikkan kinerja jalur cepat pada jam sibuk dari Q/C 0,8 menjadi 0,75. Meskipun kinerja jalur lambat berubah dari nilai Q/C 0,48 menjadi 0,67, namun berdasarkan ketentuan IHCM 1997, Q/C 0,67 pada jam sibuk merupakan derajat kejenuhan yang baik karena tidak melebihi nilai standar derajat kejenuhan jam sibuk yaitu sebesar 0,75.

---

An increase of motorcycle rider in urban roads, especially in Jakarta, results transportation problems. Their flexibility and attendance in an urban road makes the traffic flows uncertain, accident increases, and it causes other vehicles drive more carefully and slowly so the travel time come longer than usual.Based on those problems, idea to make the traffic flows more convenient and comfort is facilitated in an exclusive motorcycle lane that used by motorcycle only. By observation of the traffic flow, interpretation data, and then analyzing them, derived speed-volume correlations considering to the demand of the safe side width of motorcycle obviously influences the design of motorcycle lane width.Research conducted in road segment of Jalan Buncit Raya Pulo to Pasar Minggu at South Jakarta, consisting of fast lane and slow lane, results that design of motorcycle lane can increase and repair the condition of traffic flow in fast lane on congested condition, Q/C value 0,8 decreases to 0,75. It means better than existing condition. Even though Q/C value 0,48 in slow lane increases to 0,67 on congested condition, based on IHCM 1997, it is not a bad Degree of Saturation (DS) because of below to Q/C standard value for congested condition, 0,75."