"Skripsi ini membahas tentang pengaruh pemakaian Portland Composite Cement (PCC) terhadap ketahanan sulfat pada Self Compacting Concrete (SCC). Pada penelitian ini dilakukan uji kuat tekan, kuat tarik belah, kuat lentur dan permeabilitas pada metode perendaman air suling, air laut kadar sulfat 0.2%, larutan magnesium sulfat 5%, dan larutan magnesium sulfat 5% pasang surut pada umur 28, 42, dan 56 hari. Dari hasil penelitian didapatkan bahwa semakin besar kandungan sulfat dan semakin lama perendaman dalam sulfat, maka kekuatan beton yang diperoleh semakin menurun dan penetrasi semakin besar. Karena beton sensitif terhadap sulfat. Besar persentasi penurunan kuat tekan, kuat tarik belah, kuat lentur berurutan pada perendaman air laut sebesar 2.92%, 2.56%, -8.04%, pada larutan magnesium sulfat 5% sebesar 3.86%, 7.51%, -2.68%, pada larutan magnesium sulfat 5% sistem pasang surut sebesar 9.66%, 18.09%, 24.11%. Besar persentasi peningkatan penetrasi pada perendaman air laut sebesar 6.41%, dan pada perendaman larutan magnesium sulfat sebesar 6.41%.

---

The focus of this study discusses about the effect of using Portland Composite Cement (PCC) to the sulphate resistance of Self Compacting Concrete (SCC). On this research, some tests were done to determine the concrete?s compressive strength, splitting tensile strength, flexural strength and permeability of the immersion method of distilled water, sea water with 0.2% sulphate concentration, magnesium sulphate solution 5%, and tidal of magnesium sulfate solution 5% at 28, 42, and 56 days. The result showed that the larger the concentrate of sulphate and the longer the immersion of the concrete in sulphate solution, the strength of concrete obtained decreases and the concrete penetration increases. This happens because concrete is basically sensitive of sulphate. The reduction rate of compressive strength, splitting tensile strength, flexural strength respectively in sea water immersion for 2.92%, 2.56%, -8.04%, in the solution of magnesium sulphate are 5% of 3.86%, 7.51%, -2.68%, while in the solution of magnesium sulphate 5% with tidal of 9.66%, 18.09%, 24.11%. The increasing rate of the concrete penetration for the samples immersed in sea water is 6.41%, while the increasing rate for the samples immersed in solution of magnesium sulfate is 6.41%."

"Ketika beton berada dalam lingkungan air laut, tanah, dan kawasan industri dimana banyak terkandung sulfat, beton akan menjadi rentan terhadap serangan sulfat yang dapat mengurangi durabilitas beton akibat adanya disintegrasi material-material penyusun beton oleh sulfat. Bermacam-macam teknologi dikembangkan untuk mencegah serangan sulfat ini. Salah satunya adalah dengan pengembangan semen portland tipe II. Selain itu, dewasa ini dikembangkan juga beton pemadatan sendiri (self compacting concrete/SCC) yang memiliki flow ability yang tinggi yang dapat mengurangi permeabilitas beton yang merupakan salah satu faktor yang mempengaruhi kecepatan perusakan beton oleh sulfat. Namun demikian, seberapa besar ketahanan beton SCC yang menggunakan semen portland tipe II perlu dilakukan penelitian lebih lanjut. Penelitian ini dilakukan dengan cara membedakan metode perendaman beton. Setelah direndam dalam air suling selama 28 hari, beton akan direndam dalam empat kondisi, yaitu dalam air suling, dalam air laut, dalam larutan magnesium sulfat 5%, dan dalam larutan magnesium sulfat 5% dengan metode perendaman rendam angkat yang mengikuti perilaku pasang surut air laut selama 14 dan 28 hari. Pengujian yang dilakukan meliputi pengujian kuat tekan, kuat tarik belah, kuat lentur, dan permeabilitas. Hasil penelitian yang menunjukkan bahwa benda uji yang direndam dalam lingkungan yang mengandung sulfat menyebabkan penurunan kuat tekan sebesar 0,77%, kuat tarik belah sebesar 5,92%, dan kuat tarik lentur sebesar 8,26% untuk beton yang direndam dalam air laut, serta kuat tekan sebesar 16,93%, kuat tarik belah sebesar 11,58%, dan kuat tarik lentur sebesar 19,66% untuk benda uji yang direndam dalam magnesium sulfat. Pengkondisian rendam angkat memperbesar efek dari serangan sulfat sebesar 1,22% untuk kuat tekan, 0,6% untuk kuat tarik belah dan 5,3% untuk kuat tarik lentur. Selain itu, didapatkan pula bahwa tingkat kelolosan air bertambah sebesar 54,33% untuk beton yang direndam dalam air laut, 76,78% untuk beton yang direndam dalam magnesium sulfat, dan 107,46% untuk beton yang direndam dalam larutan magnesium sulfat dengan metode perendaman rendam angkat.

---

When the concrete is subjected to sea water, soil, and industrial area where high amount of sulfate is contained, concrete will be susceptible to sulfate attack that will reduce its durability due to disintegration of the materials by sulfate. Various technologies are developed to prevent this sulfate attack. One of them is the the development of Portland cement type II. In addition, nowadays self compacting concrete (SCC) was also developed. SCC has high flow ability which can reduce the permeability of concrete, which is one of the factors that affect the rate of deterioration of concrete by sulfate attack. However, how much this SCC that use portland cement type II can resist sulfate attack need a further research. This research performed by differentiating the condition of immersion. After being immersed in tap water for 28 days, concrete will be immersed in four conditions: in tap water, sea water, 5% magnesium sulfate solution with full-mmersion, and 5% magnesium sulfate solution with drying-immersion cycle. The tests done on this research consist of compressive strength test, splitting tensile strength test, flexural strength test, and permeability test. The result of this research indicated that the specimens immersed in an sulfate-containing environment causes the decrease of compressive strength about 0,77%, splitting tensile strength about 5,92%, and flexural strength about 8,26% for concrete immersed in sea water and compressive strength about 16,93%, splitting tensile strength about 11,58%, and flexural strength about 19,66% for concrete immersed in magnesium sulfate. Drying-immersion cycle enlarge the effect of sulfate attack about 1,22% for compressive strength, 0,6% for splitting tensile strength, and 5,3% for flexural strength. In addition, it was also found that the permeability increased by 54,33% for concrete immersed in sea water, 76,78% for concrete immersed in magnesium sulfate, and 107,46% for concrete immersed in magnesium sulfate with drying-immersion cycle. "

"Serangan sulfat pada beton dalam jangka panjang dapat merusak ikatan antar material penyusun beton, sehingga mengurangi durabilitas beton. Salah satu teknologi praktis dalam pencegahan dampak serangan sulfat adalah penggunaan semen Portland tipe V. Selain itu, perkembangan teknologi beton berupa Self-Compacting Concrete (SCC) dapat meminimalisir jumlah void sehingga mengurangi difusi larutan sulfat. Tujuan dari penelitian ini adalah untuk mempelajari karakteristik SCC dengan semen Portland tipe V, dan mengetahui pengaruh serangan sulfat terhadap beton dengan semen Portland tipe V. Benda uji direndam pada air suling selama 28 hari, kemudian diperlakukan dengan beberapa variasi perendaman, yaitu menggunakan air suling, air laut, larutan magnesium sulfat 5%, dan perlakuan wetting-drying (rendam-angkat) pada larutan magnesium sulfat 5% selama 14 dan 28 hari. Peninjauan pengaruh sulfat terhadap beton dilakukan dengan pengujian kuat tekan, kuat tarik belah, kuat lentur, dan permeabilitas. Kekuatan tekan, tarik belah, dan lentur beton diukur pada umur ke-28, 42, dan 56 hari. Sementara permeabilitas diukur ketika beton berumur 42 hari. Hasil penelitian menunjukkan bahwa selama 28 hari, ketiga variasi perendaman menyebabkan penurunan kekuatan mekanis pada benda uji dibandingkan dengan benda uji yang direndam pada air suling. Akibat variasi perendaman air laut, presentase penurunan yang terjadi pada kekuatan tekan, tarik belah, dan tarik lentur masing-masing sebesar -7,23%, 3,37%, dan 1,68%. Sementara, akibat variasi perendaman larutan magnesium sulfat 5%, presentase penurunan pada kekuatan tekan, tarik belah, dan tarik lentur masing-masing sebesar -26,99%, -24,39%, dan 16,2%. Dan akibat perlakuan rendam-angkat pada larutan magnesium sulfat 5%, presentase penurunan pada kekuatan tekan, tarik belah, dan tarik lentur masing-masing sebesar -37,15%, -17,59%, dan 33,52%. Sementara, akibat perendaman dalam air laut, larutan magnesium sulfat, dan perlakuan rendam angkat pada magnesium sulfat, terjadi peningkatan penetrasi air pada uji permeabilitas, dengan presentase masing-masing sebesar -35,6%, 5,2%, dan 22,94%. Hasil yang didapat pada penelitian ini memerlukan penelitian lebih lanjut diakibatkan oleh kesalahan yang terjadi selama pembuatan benda uji.

---

Sulfate attack on concrete in a long period of time breaks the bond between the former materials, so that it reduces durability of concrete. One of some practical technologies in mitigating the effect of sulfate attack is the use of type V Portland cement. Besides, the advancement of concrete technology, namely Self-Compacting Concrete (SCC) can reduce the diffusion of sulfate solution through the void because of its smaller amount of void. The objectives of this study are to examine the characteristic of SCC using type V Portland cement, and to study the effect of sulfate attack on type V Portland cement concrete. The concrete is treated with some methods of immersion: using tap water, sea water, 5% magnesium sulfate solution, and wetting-drying cycle on 5% magnesium sulfate solution during 14 and 28 days after being immersed during 28 days on tap water. Effect of sulfate attack on concrete reviewed by observing the compressive, splitting tensile, and flexural strength, also the permeability on each sample. The compressive, splitting tensile, and flexural strength of concrete observed on the 28th, 42nd, and 56th day. While, the permeability observed only on the age of 42 days. The result of this study shows that the immersion of samples in those three variation of immersion during 28 days results in the reduction of mechanical strength relative to the samples immersed in tap water. The rates of reduction on compressive, splitting tensile, and flexural strength due to the immersion in sea water, consecutively, are -7,23%, 3,37%, and 1,68%. While, due to the immersion in 5% magnesium sulfate solution, the rates of reduction on compressive, splitting tensile, and flexural strength, consecutively, are -26,99%, -24,39%, and 16,2%. And The rates of reduction on compressive, splitting tensile, and flexural strength due to wetting-drying cycle on 5% magnesium sulfate solution, consecutively, are -37,15%, -17,59%, and 33,52%. Otherwise, the immersion in sea water, magnesium sulfate solution, and wetting-drying cycle on magnesium sulfate solution results in the increase of water penetration level on the permeability test, by the rate of -35,6%, 5,2%, and 22,94%. The result of this research needs a more advanced research, due to the errors happen in the making of the samples."

"ABSTRAKKerusakan yang terjadi pada lantai beton di sekitar mesin produksi PT. FNG ( First National Glass Ware ), sangat menggangu kegiatan produksi yang dilakukan. Sehingga perlu dilakukan pemeriksaan mengenai sebab-sebab terjadinya kerusakan untuk didapat pemecahan mengenai masalah tersebut. Penelitian ini hanya bertujuan untuk mengevaluasi pengaruh oli (pelumas) yang dipakai pada mesin produksi di PT. FNG terhadap kemampuan ikat semen pada agregat kasar dan halus (kuat tekan beton). Metoda yang dilakukan dalam penelitian ini adalah dengan cara membandingkan hasil pengujian kuat tekan sampel beton yang dicampur oli pada temperatur 100 -- 115°C melalui proses hidrolisa, dengan beton normal yang tidak dicampur oli. Untuk pemeriksaan pengaruh di terhadap kuat tekan sampel beton dilakukan dengan difraksi sinar-x dan FTIR ( Fourier Transform Infrared ). Proses hidrolisa, pengujian kuat tekan, pemeriksaan dengan difraksi sinar-x dan FTIR masing-masing dilakukan di Laboratorium Kimia dan Bahan Fakultas Teknik Universitas Tarumanagara Jakarta, Laboratorium Bahan Fakultas Teknik Universitas Indonesia Depok, Pusat Penelitian Teknologi Mineral Bandung dan Laboratorium Kimia Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia Depok. Pengamatan yang dilakukan pada beton yang dicampur dengan oli melalui pengujian kuat tekan sampel beton menunjukkan adanya penurunan kuat tekan dari beton tersebut. Untuk beton yang dicampur dengan oli jenis Meditrans SAE40 terjadi penurunan sebesar 40 %, sedangkan jika oli yang digunakan adalah ELF Competition STX 15W50 terjadi penurunan sekitar 46%, dan jika oli yang di gunakan adalah Mesran 20W SAE20 terjadi penurunan sebesar 10%, dibandingkan dengan beton normal. Semua jenis di tersebut digunakan pada mesin diesel dan mesin produksi di PT. FNG. Pengamatan dengan difraksi sinar - x menunjukkan bahwa berkurangnya kekuatan dari beton tersebut karena adanya komponen kimia yang hilang dalam beton tersebut yaitu kalsium hidroksida, sehingga berakibat putusnya ikatan antara pasta semen dengan agregat. Pengamatan dengan FTIR juga menunjukkan bahwa oli yang digunakan setelah tercampur dengan beton pada temperatur 100 - 115 °C, tersebut terurai. Sehingga disimpulkan ada reaksi antara komponen kimia dalam beton dengan oli."

"ABSTRAKTulisan ini memuat hasil penelitian yang dilakukan di Fakultas Teknik Universitas Indonesia tentang peranan mikrosilika sebagai aditif mineral dalam meningkatkan ketahanan beton, dalam hal ini beton mutu sedang, terhadap lingkungan agresif yang mengandung garam sulfat, dalam rangka usaha untuk lebih mendayagunakan beton sebagai bahan bangunan di bawah tanah, terutama sehubungan dengan banyaknya rencana pembangungan infrastuktur bawah tanah di Jakarta. Ternyata penambahan mikrosilika dalam dosis yang tepat pada campuran beton dapat meningkatkan ketahanan beton terhadap agresi garam sulfat, sebagaimana disampaikan dalam kesimpulan penelitian di bagian akhir tulisan ini."

"Dampak lingkungan yang ditimbulkan oleh sektor konstruksi mulai pengoptimalan pemakaian material daur ulang, seperti penggunaan Ground Granulated Blast Furnace Slag (GGBFS). Penggunaannya pada mortar atau beton dalam kadar tertentu dapat menyerupai bahkan melebihi kekuatan dan ketahanan mortar atau beton yang menggunakan ordinary portland cement (OPC). Penggunaan GGBFS sebenarnya juga kerap digunakan sebagai pencampur tambahan pada semen portland, sehingga menghasilkan material komposit yang dinamakan Portland Composite Cement (PCC) yang sekarang ini sudah cukup pasaran. Di sisi lain, penggunaan serat sebagai material konstruksi juga menjadi salah satu alternatif untuk mengurangi penggunaan material, karena mampu meningkatkan kekuatan mekanis, terutama pada kuat tarik dan lentur. Pada penelitian ini dilakukan substitusi semen portland biasa (OPC) dengan PCC sebesar 100% dan GGBFS sebesar 50% pada mortar yang mengandung serat abaka dan serat rami. Variasi dilakukan uji mekanis seperti uji kuat tekan, uji kuat tarik belah, dan uji kuat lentur, serta uji fisis seperti uji permeabilitas, uji susut, dan uji absorpsi air. Hasil menunjukkan bahwa substitusi GGBFS dapat menghasilkan sifat mekanis dan fisis yang serupa dengan mortar yang hanya menggunakan semen OPC. Penambahan serat juga berdampak baik bagi sifat mekanis mortar, terutama pada kuat lenturnya.

---

The environmental impact caused by the construction sector has started to trigger the usage optimalization of recycled materials, such as the use of Ground Granulated Blast Furnace Slag (GGBFS). Its use in mortar or concrete in a certain way can resemble and even exceed the strength and durability of mortar or concrete using ordinary portland cement (OPC). The use of GGBFS is actually also often used as an additional mixer for portland cement, resulting in a composite material called Portland Composite Cement (PCC) which is currently quite on the market. On the other hand, the use of fiber as a construction material is also an alternative to reduce the use of materials, because it can increase the mechanical strength of mortar or concrete, especially in tensile and flexural strength. In this study, the substitution of ordinary portland cement (OPC) with 100% PCC and 50% GGBFS was carried out in a mortar containing abaca fiber and ramie fiber. Variations were carried out to mechanical tests such as compressive strength tests, split tensile strength tests, and flexural strength tests, as well as physical properties such as permeability tests, shrinkage tests, and water absorption tests. The results show that the GGBFS substitution can match the mechanical and physical properties of mortar using OPC. The addition of fibers also has a good impact on the mechanical properties of mortar, especially on its flexural strength."

"ABSTRAKMortar adalah campuran antara semen dengan pasir, mortar. Mortar digunakan sebagai bahan untuk pemasangan dinding, plesteran dan pondasi batukali atau pondasi lainnya. Semen sebagai perekat banyak type/jenis semen namun yang dijual (dipasarkan) adalagi semen yang disebut semen OPC (Ordinary Portland Cement) dalam kemasannya disebut type I, semen PCC ( Portland Composite Cement), semen PPC (Portland Puzzoland cement). Pembuatannya adalah membuat benda uji kubus mortar berukuran 5 cm x 5 cm x 5 cm dibuat 20 benda uji dari masing-masing type/jenis semen tersebut dengan perbandingan 1 banding 3 dan f.a.s 0,6 tetap. Pelaksanaan pengujian di laboratorium teknik sipil Politeknik Negeri Medan. Benda Uji tersebut di cetak sesuai dengan prosedur menggunakan acuan SNI 03 6825 2002 pelaksanaan di laboratorium teknik sipil, Setelah benda uji cukup umur 28 hari, di lakukan uji kuat tekan mortar masing masing uji dengan menggunakan alat test kuat tekan beton. Hasilnya diolah, rata rata dari masing masing variasi dicari standard deviasinya untuk menghitung kuat tekan karakteristik mutu mortarnya. Hasil dari pengujian kuat tekan karakteristik untuk semen type I 17 6,03 kg/cm2. Dari hasil pengujian dapat diambil kesimpulan yaitu untuk type semen PCC lebih baik kuat tekan karakteristik dibandingkan dari semen type OPC I, dan semen PPC."