Hasil Pencarian  ::  Simpan CSV :: Kembali

"Phase transformation studies have been carried out for pure iron and iron-carbon compounds of composition 0.1wt%C (low carbon), 0.4wt%C (hypo-eutectoid), and 0.8wt%C (nominal eutectoid) respectively. The samples were produced by powder metallurgy method. In this case Fe-C alloys were prepared by mixing both Fe and C powder prior to loading into a cylinder die and subsequently pressed using uniaxial force of 5 tons. The pressed samples (grain compact) were inserted into the quartz tube and air was evacuated by vacum to the level of 1.5x1 ff2mbar and then heated to 1100°C for 6 hours toward fully dense samples. Sintered samples were cooled in the furnace to room temperature. Results of OTA experiment indicated that ferromagnetic transition of pure iron taking place at temperature of 774°C and phase transformation of ferrite-austenite at temperature of 929°C. For 0.1wt%C alloy was occured pearlite-austenite transition at temperature of - 723°C with entalphy of formation of 17. 14J/g, and pro-eutectoid ferriteaustenite transition at temperature of 930°C. For 0.4wt%C alloy was occured entalphy of formation increasing of pearlite-austenite to 41.1 SJ/g. For nominal composition of 0.8wt%C was occured entalphy of formation increasing of pearlite-austenite to 72.0SJ/g at temperature of -723°C. From this study, it is found that the microstructure of pearlite consisted of ferrite and cementite in the lamelar structure. The volume fraction of pearlite consistently increased to -100% as the carbon content increased to the eutectoid composition."

"Saat ini, istilah komposit laminat pada umumnya hanya digunakan unuk menyebut komposit bermatrik polimer padahal material laminasi yang berbasis logam juga dapat disebut komposit laminasi (LMCs). Proses pembuatan komposit laminat hibrid Al/SiC-Al/Al2O3 dilakukan dengan metalurgi serbuk, dimana matrik aluminium dikuatkan dngan partikel SiC dan Al2O3. Metode ini memungkinkan komposit laminat hibrid dibuat seolah hanya satu lapisan namun dengan 2 jenis penguat yang berbeda. Metalurgi serbuk yang digunakan untuk membuat komposit laminat Al/SiC-Al/Al2O3 ini memiliki kelebihan seperti hasil yang mendekati ukuran sebenarnya, kehomogenen komposisi mikroskopik dan lebih murah secara biaya dibandingkan proses konvensional dengan casting. Pendekatan komposit isotropik digunakan untuk melakukan analisa awal terhadap komposit laminat hibrid. Sebelum digunakan sebagai penguat partikel SiC dan Al2O3 dilapisi dengan oksida logam melalui proses elektroless plating dari larutan elektrolit HNO3, Mg dan Al. Volum fraksi SiC dan Al2O3 divariasikan 10, 20, 30 dan 40%. Temperatur dan waktu tahan sintering dilakukan pada 500, 550, 600oC dan 2, 4, 6 jam untuk memperoleh kompaktibilitas komposit laminat optimum. Kompaktibilitas komposit laminat hibrid dikarakterisasi dari densitas, porositas dan modulus elastis komposit. Berdasarkan hasil pengujian HR-SEM, XRD, uji bending dan uji CTE, nilai sifat mekanik (modulus elastisitas) optimum dari komposit laminat hibrid Al/SiC-Al/Al2O3 diperoleh pada 40%Vf SiC/40%Vf Al2O3 temperatur sinter 600oC waktu tahan sinter 6 jam. Fenomena kegagalan antarmuka lapisan seperti retak, delaminasi dan kerusakan terjadi dan dipicu akibat ketidaksesuaian CTE antarlapisan.

---

Recently, term of laminate composite most widely used only for polimer matrix composites. Laminated material base on metal called Laminates Matrix Composites (LMCs). The manufacturing process of Al/SiC-Al/Al2O3 hybrid laminated composites by powder metallurgy is reviewed. Matrix aluminum had reinforced by SiC-Al2O3 particulate. The methods available to form the hybrid laminated composites like a monolayer composites with different reinforcement. Powder metallurgy has been used for the fabrication of Al/SiC-Al/Al2O3 hybrid laminated composites and had many advantages such as near-net shaping, microscopic compositional homogeneity, and low cost compared with conventional processing using melting and casting methods. Particulate isotropic composite approach used in the formulation of cohesion elements are described initially. Before used as reinforcement, Particle SiC and Al2O3 coated by metal oxide obtained by electroless platting from electrolyte HNO3, Mg and Al. Volume fraction SiC and Al2O3 were varietied 10, 20, 30 and 40%. Temperature and holding time sintering conducted for 500, 550, 600oC and 2, 4, 6 hour to obtain optimatized compactibility of composite. The compatibility of hybrid laminate composite was characterized by investigation of density, porosity and elastic moduly. Based on investigations by HR-SEM, XRD, Bending Test and CTE concluded that the optimum mechanical properties of Al/SiC-Al/Al2O3 was obtained since 40%Vf SiC/40%Vf Al2O3 temperature sinter 600oC and holding time 6 hour. Interface phenomenon interlayer as cracking, delamination and fracture was occurred and triggered by mismatch CTE interlayer."

"Material Fe-M n-C telah banyak dikembangkan sebagai material mampu luruh untuk aplikasi penyangga pembuluh dalam satu dekade belakangan ini. Penggunaan biomaterial Fe-M n-C mampu menghindari tindakan pembedahan kembali setelah pembuluh jantung kembali normal setelah mengalami penyempitan, yaitu sekitar 6-12 bulan. Pengujian material Fe-M n-C dilakukan untuk mencari kelayakan kandidat biomaterial ini digunakan sebagai penyangga pembuluh yang mampu luruh. Material tersebut dibuat dengan cara pemaduan mekanik kemudian metalurgi serbuk. Hasil pengujian EDAX pada material akhir menunjukkan komposisi material yaitu Fe-24Mn-0.4C dan Fe-33Mn-0.3C. Hasil pengujian atomic absorption spectroscopy pada ektrak larutan kedua larutan menunjukkan kandungan logam pada ekstrak material Fe-24M n-0.4C lebih tinggi dari ekstrak material Fe-33M n-0.3C. Pada permukaan kedua material juga menunjukkan adanya pembentukan lapisan kalsium fosfor yang dapat memberikan tahanan antarmuka seperti data pada pengujian electrochemical impedance spectroscopy. Secara umum, hasil pengujian biokompatibilitas dengan metode sitotoksisitas pada kedua material menunjukkan nilai viabilitas sel yang lebih baik dari material SS 316 L. Secara keseluruhan, material Fe-24M n-0.4C dan material Fe-33M n-0.3C layak digunakan sebagai kandidat biomaterial.

---

Fe-M n-C materials has been developed as biodegradable material for coronary stent application in recent decades. The use of Fe-Mn-C biomaterials is able to avoid surgery after heart vessels returned to normal condition after a constriction, which is about 6-12 months. Material testing of Fe-M n-C alloy is performed to proving of feasibility that biomaterials candidate for biodegredable coronary stent. Fe-Mn-C biomaterials produce by mechanical alloying and powder metallurgy. EDAX test result shows that both material composition is Fe-24M n-0.4C and Fe-33Mn-0.3C. Atomic absorption spectroscopy (AAS) test result of solution extract of both materials shows that metal composition at solution extract of Fe-24M n-0.4C material higher than solution extract of Fe-33M n-0.4C material. On the surface of both materials shows that there is a Calsium/Phospor layer. Electrochemical impedance sp ectroscopy (EIS) test result shows that there is interface barrier on the surface, that cause by Calsium/Phospor layer. Generally, biocompatibility test result shows that the cell viability of both materials is higher than SS 316 L material. For all test result shows that both material, Fe-24M n-0.4C and Fe-33Mn-0.3C material can be used for biodegradable material candidate."

"Dalam penelitian ini, komposisi tuangan dihasilkan oleh dapur krusibel tipe ciciuk, sedangkan cetakan yang digunakan adalah cetakan logam dengan standar JIS Z 2201 yang mana hasilnya berupa sampel tarik.Paduan tuang Al-Mg-Fe, dengan kadar Mg sebesar 5% dan kadar Fe divariasikan, ternyata menunjukkan peningkatan kekerasan dengan bertambahnya unsur Fe. Tetapi untuk kekuatan tarik menunjukkan hal sebaliknya dikarenakan cacat-cacat tuangan yang ditemui pada patahan hasil uji tarik. Sedangkan untuk regangan, menunjukkan penurunan bila kadar Fe bertambah dan spesifikasi sifat regangan terbaik dimiliki oleh komposisi dengan kadar Fe sebesar 0,5%.Sedangkan perlakuan panas yang dilakukan yaitu laku panas pelarutan 430ºC selama 12 jam serta laku panas penuaan 175ºC dengan waktu tahan divariasikan, ternyata tidak menunjukkan pengaruh yang begitu jelas pada panduan ini bila dibandingkan dengan variabel variasi unsur Fe. Untuk setiap komposisi kekerasan tertinggi umumnya dihasilkan oleh waktu tahan 4 jam untuk komposisi berkadar Fe 0,5 % dan 1,0% dengan mengalami kenaikan yang relatif kecil dari kondisi As cast yaitu 2,4% dan 4,2%. Sedangkan untuk komposisi berkadar Fe 1,5 % kekerasan tertinggi dihasilkan oleh waktu tahan 3 jam, juga dengan kenaikan yang relatif kecil dari kondisi as castnya yaitu sebesar 2,5&. Sehingga dapat disimpulkan, bahwa paduan ini bersifat non-heat treatable alloy."

"Saat ini kebutuhkan akan computer/laptop semakin meningkat. Laptop dengan performa tinggi akan menghasilkan energi yang besar sehingga akan membuat laptop panas. Untuk menghindari hal tersebut maka dibutuhkan sistem pendingin. Saat ini system pendingin pada laptop terbuat dari tembaga. Tembaga memiliki kekurangan dimana biaya yang mahal serta berat. Karena hal tersebut maka ditambahkan aluminium untuk memangkas biaya serta membuat sistem pendingin yang lebih ringan tanpa mengurangi secara signifikan konduktivitas termal yang dimiliki tembaga. Pada penilitian ini akan menjelaskan mengenai metode powder in sealed tube dengan variable berupa temperatur sintering yaitu 3000C, 4000C, dan 5000C. Sampe yang sudah difabrikasi akan dilakukan karakterisasi dengan menggunakan SEM dan EDS untuk melihat strukturmikro yang dihasilkan. Selain itu juga dilakukan pengujian densitas, porositas, kekerasan, dan konduktivitas termal. Dari hasil yang didapat menyatakan bahwa semakin tinggi temperature sintering yang dilakukan maka akan semakin tinggi pula densitas yang dimiliki sampel serta akan menurunkan porositas. Selain itu seiring bertambahnya temperatur sintering nilai kekerasan dan konduktivitas termal pada sampel akan semakin meningkat.

---

Currently the need for computers/laptops is increasing. Laptops with high performance will produce a lot of energy so that it will make the laptop hot. To avoid this, a cooling system is needed. Currently the cooling system on laptops is made of copper. Copper has the disadvantage of being expensive and heavy. Because of this, aluminum was added to cut costs and create a lighter cooling system without significantly reducing the thermal conductivity of copper. This research will explain about the powder in sealed tube method with variable sintering temperature, namely 3000C, 4000C, and 5000C. The fabricated samples will be characterized using SEM and EDS to see the resulting microstructure. In addition, density, porosity, hardness, and thermal conductivity tests were also carried out. From the results obtained, it is stated that the higher the sintering temperature, the higher the density of the sample and the lower the porosity. In addition, as the sintering temperature increases, the hardness and thermal conductivity of the sample will increase."

"Perkembangan telmologi yang lelah dicapai saai ini membaa! mamzsia membutuhlcan material yang memililri karakrerisiik yang baik secara ekonomis. Komposit merupakan salah satu marerial yang memiliki krireria seperri rersebut diaras. Material ltomposii merupakan maferial yang memiliki dua atau lebih lcomponen berbeda yang dilcombinasikan meiyadi marerial bam dengan si/at yang lebih balk. Metal Matrikskompsit merupakan salah satu jenis komposit yang mulai dikembanglfan di dalam indusfri. Paduan Al-SIC pada AMC membual material Al-SiC memiliki si/Ez! ringan karena memilild densilas yang rendah sesuai dengan matrilfs Al, kelruatan luluh Jung relalyqebih linggi dari AL kelferasan yang ringgi, ketahanan aus yang besar, kerangguhan _vang ringgi_ dan lcerahanan korosi yang balk.Pada penelilian pembuatan material metal matrilnr komposif Al-SiC menggunakan prioses meralurgi serbulc derzan kamposisi 82% serbuk Aluminum dan 18% Serbuk SiC dengan werllng agen! 1% Mg dan 1% Zinc .S'reara!e_ Bahan dimixing .velama 20 menit agar homogen dan dilanjutkan dengan proscs kompaksi dengan gaya relran sebesar 75000 M Kemudian dilakukan proses sinrering pada bakalan dengan remperatur simer 625°C Variabel yang digunakan adalah perbedaan waktu sintering yairu 30 menil, 60 menir, 90 menir, 120 menir, dan 150 menit. Serelah itu dilakukan pengujian swf mekanis pada marerial anrara lain pengulmran densilas dan porosiras marerial, pengujian kekerasan, pengujian lcelcuaran tekan, dan pengamaran sirukrur mikro marerial.Hasil pcnelirian yang didapar adalah sgfar mekanis maierial Hcekerasan dan kelcuafan rekan) meninglrar dari walcru sinier 30 menit hingga 120 menir. Hal ini disebalakan densitas material yang meninglcai dan porosiras yang berlrurang. Sedangkan pada wakru sinrer 150 menit si/'al melcanis material menuran lcarena densiras menurun dan jamiah porosiras bertambah."

"Perkembangan metalurgi serbuk besi untuk pembuatan komponen otomotif telah mendorong diciptakannya metode kompaksi hangat untuk mendapatkan bakalan dengan densitas yang tinggi. Penelitian ini hendak membandingkan beberapa karakteristik bakalan dan produk sintar hasil kornpaksf temperatur ruang, F50°C dan 25O°C dengan campuran serbuk yang relatif sederhana dan murah, yaitu_FeO hasil millscale, dan 0,5% grafit. Serbuk FeO, graffr, Zn stearate, dan glyserin dicampur dan diaduk; kemudian dikompaksi pada tiga variabel temperatur tersebut di atas pada tekanan 600 MPa, dengan waktu rahan 5 menit. Seluruh sampel disinter dalam atmosfir endogas pada temperatur H20”C selama 30 menit. Hasil penelitian menunjukkan bahwa makin tingginya temperatur kompaksi diikuti dengan peningkatan densitas dan kekuatan tekan bakalan; Serta peningkatan densitas, kekuatan tekan dan kekerasan prodak sinter. Porositas sinter ditemukan sernakin sedikit. Kompaksi hangar menyebabkan daerah kontak antar partfkef bakalan semakin Iuas, yang dibuktikan melalui pengujian fuas permukaan bakalan. Perubanan dimensi tidak menunjukkan kecenderungan tertentu meskipun perabahan total menunjukkan sampel mengalami pengembangan (sweiling). Dari perbandingan dua temperatur kampaksi 150°C dan 250°C, temperatur I50"C dinilai Iebih efisien karena selain lebih hemat biaya dan wakta pemanasan; beberapa karakteristik bakaian dan produk sinter dari kedua temperatur tersebat tidak berbeda jaun. Sedangkan antara kompaksi temperatur ruang dan ?50°C menunjukkan perbedaan yang berarti."