"Sintesis membran nanokomposit PVA-Organoclay Tapanuli dilakukan dengan tahap sintesis organoclay Tapanuli dan sintesis nanokomposit PVAOrganoclay Tapanuli. Sintesis organoclay Tapanuli dilakukan dengan menginterkalasikan surfaktan HDTMABr ke dalam gallery clay melalui tahapan purifikasi, sintesis Na-MMT dan sintesis Organoclay Tapanuli, sedangkan pembuatan membran komposit melalui proses solvent casting. Pengaruh interkalasi surfaktan diamati dengan XRD dan FTIR. Dari karakterisasi XRD, diketahui bahwa interkalasi surfaktan ke dalam gallery clay meningkatkan nilai basal spacing organoclay Tapanuli dari 15.96 Å menjadi 18.81 Å. Nanokomposit dibuat dari PVA sebagai matriks dan organoclay Tapanuli - HDTMABr sebagai nanofiller. Karakterisasi yang dilakukan adalah XRD, FTIR, SEM, dan uji tarik. Dari hasil uji tarik diperoleh pada komposisi 3 wt % organoclay Tapanuli-HDTMABr merupakan hasil yang terbaik. Hal ini dibuktikan dengan nilai modulus tarik dan nilai kuat tarik yang paling tinggi dibandingkan dengan komposisi lainnya, dengan kenaikan masing-masing 162,3 % dan 13,55 %.

---

PVA - Organoclay Tapanuli nanocomposite membranes were syntesized through two steps, namely the organoclay Tapanuli intercalation process and the PVA - Organoclay Tapanuli nanocomposite syhthesis. The synthesis of organoclay Tapanuli was conducted by intercalating the HDTMABr surfactant into the clay gallery through purification, Na-MMT synthesis, and organoclay Tapanuli synthesis processes, while solvent casting technique was applied to produced the nanocmposite membranes. The effect of surfactant in the clay gallery was observed using XRD, and FTIR. The XRD results showed that, the surfactant was intercalate into the clay gallery and increased the basal spacing of organoclay Tapanuli from 15.96 Å to 18.81 Å. The nanocomposites were characterized using XRD, FTIR, and SEM, and tensile test was also carried out. The tensile test results showed that the 3 wt% organoclay Tapanuli - PVA was the best sample compared to other clay compositions. It was proved that the values of tensile modulus and tensile strength increased by 162,3 % and 13,55 % respectively."

"ABSTRAKDua tipe organoclay telah dapat disintesis dengan surfaktan yang berbedasebagai agen penginterkalasi. Surfaktan HDTMABr dan ODTMABr diinterkalasikanke dalam bentonit alam serta dilakukan karakterisasi dengan XRD, FT-IR, dan SEMEDS.Sebelumnya Na-bentonit disintesis kemudian dihitung nilai kapasitas tukarkation dengan metode tembaga amin sebesar 45,35 mek/100gram clay. Variasijumlah KTK digunakan untuk dapat melihat peningkatan besarnya basal spacingdengan difraksi sinar-X. Organoclay 1.0 KTK yang telah disintesis digunakansebagai adsorben fenol, katekol dan benzaldehida kemudian dilakukan pengukurandengan spektrofotometer UV. Perbedaan gugus yang melekat pada cincin benzenmempengaruhi kemampuannya untuk terserap pada bentonit. Dengan bertambahnyagugus hidroksi, maka semakin sulit untuk terserap oleh bentonit. Dan apabilasemakin nonpolar senyawa organik, akan semakin mudah terserap. Dengan semakinpanjang rantai alkil surfaktan, bentonit menjadi lebih hidrofobik sehingga menyeraplebih banyak senyawa nonpolar.

---

ABSTRACTTwo types of organoclay have been synthesized using different cationicsurfactants as intercalating agents. HDTMABr and ODTMABr are intercalated intothe interlayer space of sodium-clay. With the CEC value sodium-clay is about 45, 35mek/100gram clay using copper amine method. X-ray diffraction is used to study thecharacteristic of organoclay by its variation of CEC value. The resulting of 1,0 CECorganoclay are used to adsorb the organic molecules. UV spectra of this organicmolecule on filtrate reaction are further confirming adsorptions of both organoclay.The different groups which are binding on phenol, benzaldehide, and catechol havedifferent effect to organoclay. No polar organic molecules are the easier moleculewhich adsorbed on the interlayer clay. The longest alkyls chain surfactant will makemore hydrophobic clay furthermore it could adsorb no polar organic molecules."

"Membran selulosa asetat / organoclay-HDTMABr dibuat melalui dua tahap sintesis, yaitu sintesis organoclay dan sintesis membran. Sintesis organoclay meliputi tiga tahap, yaitu purifikasi karbonat, preparasi Na-Bentonit, dan sintesis organoclay-HDTMABr. Organoclay-HDTMABr disintesis menggunakan Na-Bentonit dan HDTMABr sebanyak 1 KTK dengan metode ultrasonik, dimana Na-Bentonit yang digunakan memiliki kapasitas tukar kation (KTK) sebesar 48,749 meq/100 gram bentonit. Pengujian XRD pada sampel organoclay menunjukkan interkalasi HDTMABr dapat meningkatkan basal spacing organoclay menjadi 18,80 Å dan 19,04 Å pada masing-masing sintesa dengan purifikasi dan tanpa purifikasi karbonat. Telah dilakukan variasi komposisi organoclay-HDTMABr 1 KTK (OCT-C16) yang ditambahkan pada biokomposit sebagai nanofiller. Hasil sintesis pada penelitian ini dikarakterisasi menggunakan FTIR. Dari kelima variasi komposisi OCT-C16 (0%, 1%, 3%, 5%, dan 7%) yang ditambahkan, variasi 7% OCT-C16 menghasilkan produk membran biokomposit yang paling keruh, paling lentur, dan tidak mudah robek.

---

Cellulose acetate / organoclay-HDTMABr membranes ware prepared ​​through two stages of synthesis, namely : the organoclay synthesis and membrane synthesis. Organoclay synthesis involved three stages : purification of carbonate, preparation of Na-bentonite, and synthesis of organoclay-HDTMABr. Organoclay-HDTMABr was synthesized with the amount of 1 CEC Na-Bentonite and HDTMABr using an ultrasonic method. The Na-Bentonite had a cation exchange capacity (CEC) of 48.749 meq/100 grams of bentonite. XRD measdurement result showed HDTMABr increased the basal spacing of organoclay to 18,80 Å and 19,04 Å for organoclay with carbonate purification and without carbonate purification respetively. The HDTMABr-organoclay (OCT-C16) was added to cellulose acetate as nanofiller with different compositions. The biocomposites obtained in this study, with the clay loading of 0%, 1%, 3%, 5%, and 7% were characterized by FTIR. It was observed that the addition of 7 % OCT-C16 into cellulose acetate membranes produced the most flexible, the most opaque, and most difficult torn membrane."

"Penelitian mengenai nanokomposit polimer telah menjadi penelitian yang banyak dilakukan dalam ilmu kimia polimer dan material selama belakangan ini. Telah berhasil dilakukan fabrikasi nanokomposit dengan matriks polipropilen dan lempung Pacitan sebagai nanofiller dengan menggunakan metode melt intercalation. Campuran terdiri dari polipropilen (PP), organoclay dari Pacitan (OCP), maleicanhydride (MA) dan diphenylamine (DPA). Struktur nanokomposit dikarakterisasi menggunakan X-ray diffractometer (XRD) dan transmission electron microscopy (TEM). Hasilnya menunjukkan terjadinya interkalasi clay Pacitan yang menyebabkan pelebaran jarak galeri lapisan silikat. Uji mekanik menunjukkan nanokomposit memiliki modulus tarik dan lentur lebih tinggi, tapi kekuatan tarik dan lentur lebih rendah dibandingkan PP-OCP0 dan harga literatur PP murni. Modulus tarik yang paling tinggi dimiliki oleh nanokomposit dengan kandungan organoclay sebanyak 7 wt%. Sifat termal PP-OCP0 dan PP-OCP7 diuji menggunakan alat Heat deflection temperature (HDT). Hasilnya menujukkan bahwa nilai HDT PP-OCP7 lebih rendah dari nilai HDT PP-OCP0.

---

The study of polymer nanocomposites has been an active research field in polymer chemistry and materials science for the past decade. Nanocomposites which consist of polypropylene as matrix and Pacitan clay nanofiller have been successfully prepared by a melt intercalation method. The compound consisted of polypropylene (PP), Pacitan organoclay (OCP), maleicanhydride (MA), and diphenylamine (DPA). The structure of nanocomposites was investigated using an X-ray diffractometer (XRD) and transmission electron microscopy (TEM). The results show that an intercalation of silicate layers was occurred. The intercalation caused the silicate layer distance expansed and PP was able to move into the gallery. The results of mechanical test show that the nanocomposites have higher tensile and flexural moduli, but lower tensile and flexural strengths compared to PP-OCP0 and theoretical value of pristine PP. The PP-OCP7 sample has best mechanical properties. Sample of PP-OCP0 and PP-OCP7 were thermal tested by using a heat deflection temperature (HDT) machine. The HDT results show that PP-OCP7 has a lower HDT value than the PP-OCP0."

"Bentonit asal Tapanuli telah dimodifikasi menjadi organoclay dengan menggunakan surfaktan kationik ODTMABr sebagai agen penginterkalasi. Kemudian produk hasil modifikasi dikarakterisasi dengan XRD, FTIR, SEM¬EDS, dan TGA. Sebelum preparasi, dilakukan fraksinasi bentonit sehingga didapat Fraksi 2 yang kaya montmorillonite (MMT) yang kemudian diseragamkan kation bebasnya dengan Na+ (menjadi Na-MMT). Selanjutnya menggunakan tembaga amin, nilai KTK Na diperoleh sebesar 65,5mek/100gram Na-MMT. Variasi jumlah ODTMABr yang digunakan untuk preparasi organoclay adalah 1,0; 2,0; dan 2,5 KTK. Pengaruh penambahan ODTMABr terhadap basal spacing, diamati dengan XRD low angel, menunjukkan bahwa terjadi peningkatan basal spacing dari 17.36 Å untuk Na-MMT menjadi 21.03 Å, 20.72 Å, dan 18.39 Å untuk 1,0; 2,0; dan 2,5 KTK. Kemampuan adsorpsi organoclay 1.0 KTK yang telah diprerparasi digunakan sebagai adsorben untuk fenol dan dibandingkan dengan Fraksi 2 dan Na-MMT. Data yang diperoleh pada kurva isotherm adsorpsi menunjukkan bahwa organoclay lebih efektif dalam menyerap fenol dan proses penyerapannya mengikuti kurva isotherm adsorpsi Freundlich.Bentonite from Tapanuli has been modified into organoclay using cationic surfactant as an agent ODTMABr as intercalation agent. Then the products were characterized by XRD, FTIR, SEM-EDS, and TGA. Before perparation, bentonite fractionation was performed in order to get Fraction 2 which is rich with montmorillonite (MMT) phase, and then is cation-exchanged with Na+ (called Na-MMT). Furthermore, using a copper amine methode, its cation exchange capacity (CEC) value was determined as 65.5 mek/100gram Na-MMT. Variation of ODTMABr concentration used for the preparation of organoclay is 1.0; 2.0 and 2.5 CEC. The effect of the addition of ODTMABr to Na-MMT?s basal spacing, observed by low angel XRD, shows an increase in basal spacing of initially 17.36 Å for Na-MMT to 20.85 Å, 21.03 Å, and 18.02 Å for 1.0; 2.0; and 2.5 CEC. 1.0 CEC organoclay adsorption capacity was observed by using it as adsorbent for phenol and compared with the capacity of Fraction 2 and Na-MMT. Data obtained on the adsorption isotherm curve shows that the organoclay is more effective in adsorbing phenols and the adsorption process follows Freundlich adsorption isotherm curve."

"Bentonit asal Tasikmalaya dimodifikasi menjadi organoclay dengan menggunaan surfaktan non-ionik Triton X-100 sebagai agen penginterkalasi. Produk hasil modifikasi dikarakterisasi dengan XRD, FTIR, dan EDAX. Sebelum preparasi, dilakukan fraksinasi presipitasi bentonit dan didapat Fraksi 1 yang kaya montmorillonit (MMT) yang kemudian divariasikan kation penyeimbangnya dengan Na+ (menjadi Na-MMT) dan NH4+ (menjadi NH4-MMT). Kemudian nilai KTK Na diperoleh sebesar 66,5 meq/100 gram Na-MMT dengan menggunakan senyawa kompleks [Cu(en)2]2+, dan 65 meq/100 gram Na-MMT dengan menggunakan senyawa kompleks [Cu(NH3)4]2+. Variasi penambahan surfaktan Triton X-100 yang digunakan untuk preparasi organoclay 5360 ppm, 7490 ppm, dan 9630 ppm terhadap d-spacing diamati dengan XRD low angle menunjukkan bahwa terjadinya peningkatan d-spacing dari 15,10 Å untuk Na-MMT masing-masing menjadi 17,26 Å, 16,91 Å, dan 17,28 Å; 15,75 Å untuk MMT menjadi 16,24 A, 16,53 Å, dan 16,42 Å; 12,39 Å untuk NH4-MMT (dari Na-MMT) menjadi 15,02 Å, 14,99 Å, dan 14,88 Å; 12,47 Å untuk NH4-MMT (dari MMT) menjadi 15,11 Å, 14,88 Å, dan 15,07 Å. Data yang diperoleh menunjukkan bahwa d-spacing yang dihasilkan oleh organoclay dari Na-MMT lebih besar dibandingkan dengan organoclay lainnya, dan nilai % kenaikan d-spacing yang baik merupakan organoclay dari NH4-MMT (dari Na-MMT) maupun organoclay dari NH4-MMT (dari MMT).

---

Bentonite of Tasikmalaya is modified into organoclay by using non-ionic surfactant Triton X-100 as an intercalation agent. The modified product is characterized with XRD, FTIR, and EDAX analysist. Leading to the preparation, the bentonite was fractionated to obtain the fraction 1 which is rich in montmorillonite (MMT). This fraction then modified using variation balancing cations. The cations variation are Na+ (as Na-MMT) and NH4+ (as NH4-MMT). The CEC of the Tasikmalaya bentonite obtained in the research is 66,5 meq/100 g clay with the Cu(en)22+ complex and 65 meq/100 g clay with the Cu(NH3)42+ complex. The Triton X-100 concentration used in the research was 5360 ppm, 7490 ppm, and 9630 ppm. The influence of Triton X-100 surfactant on the d-spacing of the clay was observed with low angle XRD. The result shows that d-spacing increase from 15,10 Å to 17,26, 16,91 Å, and 17,28 Å for Na-MMT; from 15,75 Å to 16,24 A, 16,53 Å, and 16,42 Å for MMT; from 12,39 Å to 15,02 Å, 14,99 Å, and 14,88 Å for NH4-MMT (of Na-MMT source) ; and from 12,47 Å to 15,11 Å, 14,88 Å, and 15,07 Å for NH4-MMT (from MMT source). The highest percentage of the d-spacing number was from both NH4-MMT (from Na-MMT and MMT source)."

"ABSTRAKBentonit asal Tapanuli telah dimodifikasi menjadi organoclay dengan menggunakan surfaktan alam rarasaponin sebagai agen penginterkalasi. Sintesis dilakukan dengan memvariasikan berat surfaktan, 0,5 gram, 1 gram dan 2 gram. Hasil diperoleh bahwa organoclay dengan 2 gram surfaktan memberikan kenaikan nilai basal spasing yang tinggi dari 15.1 menjadi 16.1 . Uji FTIR memperlihatkan penurunan drastis pada pita ikatan hidrogen dan spektra molekul H2O yang menandakan bahwa H2O yang berada pada interlayer tergantikan dengan rarasaponin. Uji ketahanan termal dilakukan hingga suhu 500 oC dan diperoleh hasil pada suhu 274 oC terjadi degradasi surfaktan. Kemampuan adsorpsi organoclay diuji dengan menggunakan zat pewarna rhodamin-B dengan variasi konsentrasi 0,3 ; 0,5 ; 0,8 dan 1 ppm. Hasil adsorpsi mengikuti isoterm Langmuir dengan kapasitas adsorpsi 1 mg/g dengan waktu optimal adsorpsi selama 30 menit.

---

ABSTRACTBentonite from Tapanuli has been modified into organoclay using natural surfactant rarasaponin as intercalation agent. Organoclay synthesis performed by varying the weight of surfactant, 0.5 gram, 1 gram and 2 gram. The results showed that 2 grams of organoclay with surfactant gives increase in basal spacing from 15.1 to 16.1 . FTIR test showed a drastic decrease in the band spectra of hydrogen bonds and H2O molecules indicating that H2O that located in interlayer replaced with rarasaponin Thermal endurance test carried out to a temperature of 500 oC and degradation of surfactant occurs in 274 oC. Organoclay adsorption capacity was tested using the dye rhodamine B with various concentrations of 0.3 0.5 0.8 and 1 ppm. Results adsorption follows the Langmuir isotherm with adsorption capacity 1 mg g with 30 minutes for optimal adsorption time. "

"Sintesis membran selulosa asetat dilakukan melalui dua tahap yang meliputi: sintesis organoclay dan sintesis membran. Sedangkan, sintesis organoclay terdiri dari tiga tahapan yaitu purifikasi karbonat, sintesis Na-Bentonit dan sintesis organoclay-ODTMABr. Na-Bentonit dengan kapasitas tukar kation (KTK) 48,749 meq/100 gram bentonit yang diinterkalasi dengan 1 KTK surfaktan ODTMABr menghasilkan Organoclay Terinterkalasi (OCT). Pengaruh interkalasi diamati oleh XRD low angle yang menunjukkan adanya kenaikan nilai basal spacing dari Na-Bentonit ke OCT, baik tanpa maupun dengan purifikasi karbonat, masing-masing dari 15,31 Å ke 20,07 Å dan 15,66 Å ke 19,94 Å. Selulosa asetat (CA) dimodifikasi dengan penambahan nanofiller organoclay-ODTMABr (OCT-C18) dengan metode solvent casting. Karakterisasi yang dilakukan adalah XRD, FTIR, SEM, dan EDX. Pengamatan pengaruh komposisi berat OCT-C18 yang ditambahkan ke dalam larutan selulosa asetat menunjukkan bahwa membran dengan komposisi 7% wt memiliki warna yang paling keruh, secara fisik terasa paling lentur, dan tidak mudah robek.

---

Synthesis of cellulose acetate membranes through two stages which include organoclay synthesis and membrane synthesis. Meanwhile, organoclay synthesis consists of three phases that include carbonate purification, synthesis of Na-Bentonite and organoclay-ODTMABr synthesis. Na-bentonite by cation exchange capacity (CEC) 48.749 meq/100 grams of bentonite which intercalated with 1 CEC ODTMABr surfactant produce organoclay intercalated (OCT). Effect of intercalation was observed by low angle XRD which shows an increase value of basal spacing of Na-Bentonite to OCT, either without or with carbonate purification, respectively from 15.31 Å to 20.07 Å and 15.66 Å to 19.94 Å Å. Cellulose acetate (CA) modified with adding organoclay-ODTMABr (OCT-C18) nanofillers with a solvent casting method. XRD, FTIR, SEM, and EDX characterization was performed. Parameters measured influence of weight percent of OCT-C18 is added to a solution of cellulose acetate. Membrane with a composition of 7 wt% has the most opaque colors, the highest physical resilient, and the strongest (not easily torn)."

"Pembentukan nanokomposit OCT-C16/selulosa asetat- selulosa asetat butirat melalui dua tahapan sintesis, yaitu sintesis organoclay dan sintesis nanokomposit. Sebagai perbandingan, dalam penelitian ini juga disintesis nanokomposit selulosa asetat. Sintesis organoclay meliputi tiga tahapan yaitu purifikasi karbonat, sintesis Na-Bentonit Purifikasi dan sintesis organoclay- HDTMABr. Hasil karakterisasi dengan XRD pada sampel organoclay menunjukkan interkalasi pada surfaktan HDTMABr dapat meningkatkan basal spacing organoclay menjadi 19,7595 Å. Dalam sintesis nanokomposit selulosa asetat termodifikasi selulosa asetat butirat dilakukan penambahkan variasi persen berat organoclay-HDTMABr sebagai nanofiller sebanyak 0%, 1%, 3%, 5%, dan 7%. Pada sintesis selulosa asetat juga ditambahkan variasi persen berat organoclay- HDTMABr yang sama dengan nanokomposit selulosa asetat termodifikasi selulosa asetat butirat. Hasil sintesis dikarakterisasi dengan FTIR. Variasi dengan 7% organoclay- HDTMABr merupakan nanokomposit dengan produk paling keruh.

---

The formation of nanocomposite OCT-C16/cellulose acetate- cellulose acetate butyrate was carried out through two stages of synthesis, namely organoclay synthesis and cellulose acetate-cellulose acetate butyrate synthesis. As a comparison, in this study cellulose acetate nanocomposite was sythesized. Organoclay synthesis involves three steps, namely carbonate purification, synthesis of Na - Bentonite and intercalation HDTMABr surfactant. The XRD characterization on the samples showed that intercalation by HDTMABr surfactant can increase the basal spacing of organoclay up to 19.7595 Å.

In the synthesis of cellulose acetat-cellulose acetate butyrate nanocomposite variation of weight percent of organoclay as nanofiller as much as 0 %, 1 %, 3 %, 5 %, and 7 % was conducted. The similiar variation was applied in the synthesis of cellulose acetate- cellulose acetate butyrate The results of the synthesis were characterized by FTIR. Variation with 7 % organoclay nanocomposite - HDTMABr is the most turbid product."