Hasil Pencarian  ::  Simpan CSV :: Kembali

"Pembuatan kopoli(stirena/butil akrilat/metil metakrilat) dilakukandengan metode polimerisasi emulsi. Ukuran dan distribusi partikel sangatmenentukan sifat polimer emulsi seperti sifat aliran dan kestabilan polimer.Tujuan penelitian ini adalah untuk mempelajari pengaruh jenis dankonsentrasi surfaktan, konsentrasi inisiator, dan teknik polimerisasi emulsiterhadap ukuran partikel dan distribusi ukuran partikel kopoli(stirena/butilakrilat/metil metakrilat). Surfaktan yang digunakan adalah sodium dodecylbenzene sulphonate (SOBS) dan sodium Iaury/ sulphate (SLS), inisiator yangdigunakan yaitu ammonium persulfat (APS), dan teknik polimerisasi yangdilakukan yaitu tek!fik semikontinyu, seeding 10%, dan batch. Kopolimeryang dihasilkan ditentukan solid content, viskositas, temperatur glass,spektrum IR, ukuran dan distribusi ukuran partikel. Penggunaan surfaktanSOBS memberikan hasil polimerisasi yang kurang sempurna. Padapengunaan surfaktan SLS, dengan meningkatnya konsentrasi SLS yangditambahkan memberikan hasil solid content yang meningkat, viskositaslarutan yang meningkat, dan ukuran partikel yang mengecil. Hasilpolimerisasi terbaik diperoleh pada penggunaan surfaktan SLS dengankonsentrasi 20 kali nilai critical micelle concentration (CMC), inisiator APSsebesar 1 %, dan teknik polimerisasi semikontinyu, dimana pada kondisi ini-dihasilkan solid content sebesar 39,6% (mendekati nilai solid content teoritis sebesar 40%), viskositas sebesar 15 mPas, diameter partikel sebesar 47,21nm, dan distribusi ukuran partikel yang monodispers"

"ABSTRAKPolimer telah menjadi bagian yang panting dalam teknologi kimla danbahan palimer mempunyai peranan panting dalam kahidupan sahari-hari.Untuk mamparluas aplikasi produk polimar yang talah ada, maka dilakukanusaha untuk mandapatkan polimar dangan sifat-sifat yang labih baik. Salahsatu usaha itu adalah dangan manambahkan bahan aditif. Bahan aditif yangditambahkan disini adalah antioksidan dangan tujuan agar bahan polimaryang diparolah akan mampunyai daya tahan tarhadap dagradasi yangdisababkan olah radikal babas yang tarbantuk akibat pamanasan, radiasi,akibat pangaruh logam ataupun oksidasi.Panalitian ini dilakukan untuk mambandingkan aktivitas antioksidanAnox® 20 dan Vanox® GT tarhadap dagradasi polipropilan. Hasil pangukuranOIT dangan DSC manunjukkan bahwa formulasi dangan Anox® 20mambarikan katahanan labih panjang dangan kisaran antara 1.08 - 2.41manit dibandingkan formulasi dangan Vanox® GT hanya mambari katahanandangan kisaran 1.42 - 1.90 manit. Hasil uji aging formulasi dangan Anox® 20tahan hingga 48 jam sadangkan formulasi dangan Vanox® GT tahan hanya24 jam. Uji MFR formulasi dangan Anox® 20 mambarikan nilai yang labihkacil dibandingkan dangan Vanox® GT. Untuk uji optis warna formulasidangan Vanox® GT mambarikan nilai Yellowness Index yang labih kacil dannilai Whiteness Index yang labih basar dibandingkan formulasi dangan Anox® 20. Pada formulasi dengan Anox® 20 setelah aging memberikanpenurunan nilai kuat tarik yang stabil dengan kisaran nilal antara 298 - 203kg/cm2, sedangkan untuk formulasi dengan konsentrasi Vanox® GT denganwaktu aging yang sangat pendek mengalami penurunan yang sangat tajam.Dari setiap pengujian yang dilakukan dalam penelitian ini diperoleh bahwaantioksidan Anox® 20 dengan jenis tetrakispropionat mempunyaikemampuan inhibisi terhadap oksidasi yang lebih baik dibanding denganantioksidan Vanox® GT yang berjenis isosianurat. Tetapi Vanox® GT memilikisatu keunggulan yaitu memberikan transparansi yang lebih baik ditinjau dari4uji warna. Dari analisis struktur dengan FTIR menunjukkan adanya prosesoksidasi yang ditunjukkan dari timbulnya spektrum gugus karbonii padabilangan gelombang v sebesar 1716.5 Cm""

"Ukuran partikel merupakan salah satu faktor yang menentukan sifat polimer emulsi. Polimer emulsi memiliki ukuran partikel antara 10 sampai dengan 1500 nm. Untuk aplikasi coating, dibutuhkan polimer emulsi dengan ukuran partikel yang kecil agar diperoleh hasil coating yang halus, kekuatan adhesi dan ketahanan terhadap air yang baik, serta kestabilan yang cukup lama. Penelitian ini bertujuan melihat pengaruh dari surfaktan natrium dodesil benzena sulfonat (SDBS) rantai lurus dan bercabang serta beberapa teknik polimerisasi emulsi terhadap ukuran partikel pada kopoli(stirena/butil akrilat/metil metakrilat) dengan menggunakan kombinasi surfaktan anionik dan nonionik (nonil fenol, EO10) dan inisiator ammonium persulfat.Hasil pengukuran DSC, solid content, IR, dan berat molekul relatif rata-rata menunjukkan bahwa terbentuk kopoli(stirena/butil akrilat/metil metakrilat). Surfaktan SDBS rantai bercabang menghasilkan ukuran partikel yang lebih kecil dibandingkan surfaktan SDBS rantai lurus tetapi grit yang terbentuk lebih banyak. Teknik batch dapat menghasilkan solid content tertinggi yaitu 38,73% saat menggunakan surfaktan SDBS rantai lurus dan 38,47% saat menggunakan surfaktan SDBS rantai bercabang. Teknik semi kontinyu secara umum menghasilkan viskositas yang tinggi yaitu 168,5 mPas saat menggunakan SDBS rantai lurus dan 128 mPas saat menggunakan SDBS rantai bercabang."

"Pembuatan kopolimer (stirena/butil akrilat/metil metakrilat) dilakukan dengan metode polimerisasi emulsi. Penelitian ini bertujuan untuk melihat pengaruh variasi inisiator dan teknik polimerisasi terhadap ukuran partikel pada kopolimerisasi emulsi stirena-butil akrilat-metil metakrilat. Inisiator yang digunakan adalah inisiator anorganik dan organik, yaitu ammonium persulfat (APS), hidrogen peroksida (H2O2), ters-butil hidroperoksida (TBHP), serta inisiator redoks (H2O2/asam askorbat). Teknik polimerisasi yang dilakukan adalah teknik batch dan semi kontinu. Kopolimer yang dihasilkan ditentukan kandungan padatan, viskositas, ukuran dan distribusi ukuran partikel, temperatur glass, IR dan berat molekulnya. Hasil kopolimerisasi emulsi bila menggunakan inisiator TBHP dan H2O2 kurang sempurna, oleh karena itu digunakan pasangan inisiator redoks H2O2/asam askorbat. Asam askorbat berfungsi sebagai pemicu dalam pembentukan radikal OH, sehingga polimer emulsi yang dihasilkan lebih sempurna. Semakin banyak inisiator yang ditambahkan, ukuran partikelnya pun akan semakin besar. Ukuran partikel yang dihasilkan akan mempengaruhi sifat-sifat polimer yang dihasilkan. Kata kunci : polimerisasi emulsi, inisiator, surfaktan, teknik polimerisasi."

"Chemical modification of maltodextrin DE(5-10) polymer fraction of sago strach (Metroxylon) with phosphoroxychloride as suspending agent: Based on a previous report,maltodextrin DE 5-10 polymer fraction did not stable as the suspending agent in aging for twelve week.Therefore to develop a stable maltodextrin DE 5-10 polymer fraction as suspending agent has to attemp by chemical modification.In this research chemical modification had been done with 0,25% POCI at ph9, and temperature 29 0C. The product was used as suspending agent 5%,10%and15% and paracetamol as a model.The results of suspension characteristic evaluation of both sedimentation volume,rate of solid redispersion,viscosity,pH and paracetamol concentration,showed the suspension quality with floculation system,stability of viscisity and pH,easiness to disperse,and the concentration of paracetamol confrom to phamarcope Indonesia 3 ed."

"Pembuatan polimer core-shell stirena-butil akrilat telah dicoba dengan metode polimerisasi emulsi. Pada penelitian ini telah berhasil disintesis polimer core-shell secara bertahap terhadap stirena (St) dan butil akrilat (BA). Teknik yang digunakan pada penelitian ini adalan teknik semikontinu. Konsentrasi surfaktan dibuat tetap yaitu sebesar 10 CMC. Konsentrasi inisiator juga dibuar tetap yaitu sebesar 1% baik umuk inisiator termal (APS) maupun inisiator redoks (H2O2-asam askorbat). Pada penelitian ini telah dipelajari pengaruh konsentrasi monomer terhadap ukuran dan distribusi ukuran partikel nomopolimer St maupun BA. Variasi konsentrasi St sebesar 20%, 25% dan 30% sedangkan BA Sebesar 17,33% dan 25%. Selain itu juga dipelajari penggunaan inisiator yang Iebin baik antara termal (APS) dan redoks (H2O2 dan asam askorbat). Optimalisasi nomopolimer digunakan untuk tahap selanjutnya yaitu polimerisasi core-shell.Polimerisasi stirena optimal didapat pada konsentrasi monomer 30% dengan menggunakan inisiator APS dimana didapat ukuran partikel sebesar 81,28 nm dan persen konversi sebesar 86,93%. Polimerisasi butil akrilat optimal didapat pada konsentrasi monomer 17,33% dengan menggunakan inisiator APS dimana didapat ukuran partikel sebesar 74,03 nm dan persen konversi sebesar 71 ,16%. Olen karena itu jenis inisiator yang akan dipakai pada polimerisasi core-shell adalah APS. Spektrum FTIR dan kurva DSC menunjukkan banwa telah terjadi polimerisasi momomer stirena menjadi polimer stirena. Spektrum FTIR dari polimer stirena nasil percobaan sesuai dengan referensi yang didapat dari literatur. Nilai Tg polimer stirena yang terbentuk sebesar 102,88°C juga tidak jauh berbeda dengan nilai Tg teoritis yang nilainya sebesar 100°c. Oleh sebab itu dapat dikatakan banvva polimerisasi stirena Sudan terjadi. Polimer core-shell yang didapat memiliki ukuran partikel 51,76 nm dan persen konversinya 47,04%."

"Ukuran partikel merupakan salah satu faktor yang menentukan sifat polimer emulsi. Untuk aplikasi coating, dibutuhkan polimer emulsi dengan ukuran partikel yang kecil agar diperoleh hasil coating yang halus, kekuatan adhesi dan ketahanan terhadap air yang baik, serta kestabilan yang cukup lama. Penelitian ini bertujuan melihat pengaruh dari surfaktan natrium dodesil benzena sulfonat (SDBS) rantai bercabang serta beberapa teknik polimerisasi emulsi terhadap ukuran partikel kopoli(stirena/butil akrilat/metil metakrilat) dengan menggunakan kombinasi surfaktan anionik dan nonionik (nonil fenol, EO|U) serta inisiator ammonium persulfat.Hasil pengukuran DSC, solid content, dan IR menunjukkan bahwa terbentuk kopoli (stirena/butil akrilat/metil metakrilat). Dari hasil yang diperoleh, dapat dilihat bahwa terbentuk grit yang banyak. Teknik batch dapat menghasilkan solid content tertinggi yaitu 38,47%. Teknik semi kontinyu secara umum menghasilkan viskositas yang tinggi yaitu 128 mPas. Surfaktan SDBS rantai bercabang secara umum menghasilkan polimer emulsi dengan ukuran partikel yang kecil tetapi grit yang terbentuk lebih banyak. Banyaknya persen seeding monomer dan inisiator yang ditambahkan ke dalam initial charge mempengaruhi ukuran partikel polimer emulsi yang terbenluk, dan jumlah inti yang dihasilkan."

"Variasi konsentrasi monomer metil metakrilat (MMA), surfaktan natrium lauril sulfat (SLS) dan inisiator ammonium persulfat (APS) dilakukan untuk mengetahui pengaruh terhadap ukuran pertikel, persen konversi dan indeks polidispersitas dan menghasilkan ukuran pertikel polimer 100-200 nm. Terjadinya polimer MMA dibuktikan dengan spektrum IR dan nilai Tg. Nilai Tg homopolimer yang diperoleh sebesar 100,070C. Kenaikan monomer, insiator APS dan surfaktan akan menaikkan persen konversi dan indeks polidispersitas.Konsentrasi surfaktan yang kecil dengan kenaikan konsentrasi inisiator APS dan MMA maka akan memperbesar ukuran pertikel. Pengaruh kenaikan konsentrasi monomer dan inisator pada konsentrasi maksimum, maka ukuran partikel yang diperoleh sebesar 100,2 nm, PDI 0,717 dan persen konversi 89,5%. Variasi surfaktan SLS terkecil sampai 1 CMC diperoleh ukuran pertikel 96,27 nm, PDI 0,074 serta persen konversi sebesar 96,27%. Ukuran pertikel terbesar yang dihasilkan berukuran 116,8 nm dengan PDI 0,153 dan persen konversi 95,08%."

"Pada penelitian ini telah dilakukan optimasi homopolimer butil akrilat dengan proses polimerisasi emulsi yang bertujuan untuk mempelajari pengaruh variasi konsentrasi surfaktan sodium lauryl sulfate (SLS) dan inisiator ammonium peroxodisulfate (APS) serta variasi teknik polimerisasi yang terdiri dari teknik semikontinu, teknik batch, dan teknik seeding 10% dengan waktu feeding 5 jam. Homopolimer yang dihasilkan kemudian ditentukan solid content, indeks viskositas, ukuran dan distribusi ukuran partikel, temperature glass, dan spektrum IR. Homopolimer ini selanjutnya dapat digunakan sebagai shell dalam polimer core-shell yang menimbulkan efek warna. Peningkatan konsentrasi surfaktan dan konsentrasi inisiator menghasilkan solid content yang semakin meningkat dan ukuran partikel yang cenderung menurun. Kondisi optimum yang diperoleh pada penggunaan konsentrasi surfaktan 0,5 CMC, konsentrasi inisiator 1%, melalui teknik semikontinu dengan persen konversi sebesar 97,21%, ukuran partikel 104,4 nm dan bersifat monodispers."