"ABSTRAKPenelitian tentang kinetika pertumbuhan kristal barium heksaferit disubstitusi Mndan Ti dengan komposisi BaFe9.6Ti1.2Mn1.2O19 yang dibuat melalui proses pemaduan mekanik telah dilakukan. Ukuran kristal rata-rata BaFe9.6Ti1.2Mn1.2O19 didapat dengan metode Whole Powder Pattern Modeling (WPPM) pada software PM2K. Ukuran kristal bertambah secara bertahap dan akhirnya mencapai ukuran maksimum. Dari pemanasan isotermal, kinetika pertumbuhan kristal dapat dijelaskan oleh persamaan Avrami dengan energi aktivasi pertumbuhan kristal 𝑄 yang dihasilkan sebesar 51.76 kJ/mol.

---

ABSTRACTA study on the kinetics of crystal growth of barium hexaferrite substituted by Mn ? Ti with composition BaFe9.6Ti1.2Mn1.2O19 produced by mechanical alloying was carried out. The grain size of BaFe9.6Ti1.2Mn1.2O19 was estimated by the Whole Powder Pattern Modeling (WPPM) in PM2K software. The grain size increases gradually, and finally ceases to reach an ultimate value regardless of annealing time. From isothermal anneals, the grain growth kinetics can be described by Avrami?s equation and activation energy for grain growth Q has been determined to be 51,76 kJ/mol."

"ABSTRAKPada penelitian ini dilakukan pembuatan dan karakterisasi sampel Sn-xBi dan SnxBi-yAl sebanyak 10 sampel dengan variasi logam Bi dan Al dalam %berat yang berbeda menggunakan X-Ray Diffraction (XRD). Penentuan kapasitas panas sebagai fungsi temperatur Cp (T) dari material solder Sn-Bi dan Sn-Bi-Al menggunakan alat uji DSC pada rentang temperatur 30°C hingga 450oC dan laju 10 oC/menit. Hasil karakterisasi XRD selanjutnya diolah menggunakan aplikasi GSAS untuk mendapatkan informasi tentang struktur dan ukuran kristal, parameter kisi yang dimiliki terhadap pengaruh variasi Bi dan Al %berat, serta informasi lainnya yang dapat berpengaruh. Berdasarkan ukuran kristal pada paduan Sn-xBi diketahui bahwa semakin banyak penambahan logam Bi maka ukuran kristal Sn yang terbentuk akan semakin kecil.

---

ABSTRACT

In this research, manufacture and characterization of samples Sn and Sn-xBi-yAL as many as 10 samples with metal variation% Bi and Al in different weight using X-Ray Diffraction (XRD). Determination of the heat capacity as a function of temperature Cp (T) of the solder material of Sn-Bi and Sn-Bi-Al using a DSC test at 30oC to 450°C temperature range and a rate of 10 °C/min. XRD characterization results further processed using GSAS application to obtain information about the structure and size of the crystal, the lattice parameter of the effect of variation owned Bi and Al% by weight, as well as other information that can be influential. Based on the size of the crystals in the alloy Sn-xBi known that the more the addition of the metal Bi Sn formed crystal size will be smaller."

"Disertasi ini membahas karakterisasi produk blending antara monomer kristal cair kolesteril akrilat dengan monomer kristal cair metilfenilbenzoil akrilat yang difotopolimerisasi dengan teknik UV curing. Produk blending dan fotopolimerisasi hasil penelitian ini kemudian di uji serapannya dengan spektrofotometer ultraviolet-visibel. Monomer kristal cair kolesteril akrilat hasil dari reaksi esterifikasi Steglich antara kolesterol dengan prekursor akrilat menggunakan katalis N,N’-disikloheksilkarbodiimida (DCC) dan N,Ndimetilpiridin- 4-amina (DMAP). Monomer kristal cair metilfenilbenzoil akrilat merupakan hasil dari reaksi esterifikasi Steglich antara prekursor akrilat dan prekursor (S)-(+)-p-hidroksifenil-2-metil butanoat atau disebut juga (S)-(+)-2- HFM. Kedua monomer hasil esterifikasi tersebut kemudian dikarakterisasi menggunakan FTIR, 1H-NMR, dan 13C-NMR untuk penentuan struktur molekul; DSC untuk analisis termal, POM untuk tekstur kristal cair, dan XRD untuk kristalinitas. Oleh karena kedua monomer termasuk dalam kelompok kristal cair akrilat, maka hasil karakteriasi kedua monomer dengan FTIR menunjukkan puncak khas yang sama pada daerah 3000-2850 cm-1 yang merupakan daerah vibrasi rantai alifatik dan puncak pada daerah 1600,43 cm-1 yang menunjukkan gugus C=C dari akrilat. Selain itu terdapat juga puncak-puncak lainnya yang menjadi ciri khas masing-masing monomer. Tekstur monomer kristal cair kolesteril akrilat memperlihatkan tekstur oily streak pada suhu 81,28˚C sementara monomer kristal cair metilfenilbenzoil akrilat memperlihatkan tekstur schlieren pada 54,36oC. Proses blending kedua monomer menggunakan metode casting pelarut dan fotopolimerisasi menggunakan fotoinitiator 2-hidroksi-2-metil-1-fenilpropana (HMPP). Hasil GPC proses uv curing pada radiasi selama 15 dan 30 menit memberikan berat molekul (Mw) masing-masing 487.457 gram dan 463.279 gram. Struktur mikro produk fotopolimerisasi dengan SEM menunjukkan pola rantai polimer tipe side chain liquid crystalline polymers (SCLCPs). Serapan produk fotopolimerisasi dengan spektrofotometer ultraviolet-visibel menunjukkan bahwa fotopolimerisasi yang diradiasi selama 15 dan 30 menit memberikan serapan 0,116 dan 0,254 pada daerah panjang gelombang 363 nm dan 350 nm. Berdasarkan hasil penelitian ini, dengan demikian produk blending dan fotopolimerisasi kedua monomer menyerap pada panjang gelombang ultraviolet A (UVA).

---

The dissertation discusses the characterizations of blending product from monomer liquid crystal cholesteryl acrylate and monomer liquid crystal of methylphenylbenzoyl acrylate photopolymerized by UV curing technique. The absorption of blending and photopolymerization products of this work was tested by using UV-Vis spectrophotometer. Cholesteryl acrylate was synthesized through Steglich esterification reaction between cholesterol with acrylic precursor with catalyst of N, N'-dicyclohexylcarbodiimide (DCC) and N, N-dimetilpiridin- 4-amine (DMAP). Monomer liquid crystal of methylphenylbenzoyl acrylate was synthesized by Steglich esterification reaction between acrylic precursors and precursors (S) - (+)-p-hydroxyphenyl-2-methyl butanoat or also known as (S) - (+)-2-HFM. The characterization of monomers was performed by using FTIR, 1HNMR and 13C-NMR for molecular structure; DSC for thermal analysis; POM for textures analysis; and XRD for crsytalinity. FTIR spectrum of the two monomers show typical peaks at 3000-2850 cm-1 for the aliphatic chain vibration, 1720 cm-1 for carbonyl group, and 1600.43 cm-1 for the group of acrylate C=C. The texture of cholesteryl acrylate shows an oily streak at temperature 81.28 ˚C and monomer methylphenylbenzoyl acrylate shows a schlieren texture at 54.36 0C. The blending process of the two monomers was performed by using solvent casting method and photopolymeirzation with UV curing technique by using photoinitiator of 2- hydroxy-2-methyl-1-phenyl-propan (HMPP). The molecular weight from the photopolymerization process with the radiation for 15 and 30 minutes Mw give the result of 487.457 and 463.279, respectively. Microstructure from SEM shows a type of side chain liquid crystalline polymers (SCLCPs). The photopolymerization product characterized by using UV-Vis spectrophotometer for 15 and 30 min of radiation gives wavelength at 363 nm and 350 nm, respectively. Based on the result of this research, it can be concluded that the blending product of the two monomers absorps a wavelength at ultraviolet A (UVA)."

"ABSTRAKPada penelitian ini dilaporkan investigasi mengenai efek dari eksposur faset kristal (001) TiO2 anatase terhadap aktivitas fotoelektrokatalitik dari fotoanoda yang terdiri dari film nanokomposit BiVO4/TiO2. Fotoanoda dibuat dengan mendeposisikan nanokomposit di atas permukaan kaca FTO melalui teknik doctor blade. Dalam penelitian ini, empat jenis morfologi TiO2 antase yaitu, nanospindel, nanocube, nanooctahedral, dan nanosheet disintesis melalui metode hidrotermal dengan penambahan directing agent yang berbeda. Selanjutnya, TiO2 hasil sintesis dikarakterisasi dengan menggunakan X-Ray Diffractometer (XRD), Transmission Electron Microscopy (TEM), Brunauer-Emmelt Tellers (BET), dan UV-Vis diffuse reflectance spectra (DRS). Berdasarkan hasil karakterisasi, puncak difraksi menunjukkan karakteristik untuk fase anatase murni dengan eksposure faset kristal (001) untuk nanospindel dan nanocube dan faset kristal (101) untuk nanocube dan nanooctahedral. Selain itu, respon fotoelektrokimia dari fotoanoda juga diukur menggunakan sistem 3 elektroda pada reaktor photocatalytic fuel cell (PFC) dan menghasilkan nilai densitas arus mencapai 0,0386 mA/cm2 untuk nanokomposit BiVO4/TiO2 nanosheet dan 0,0381 mA/cm2 untuk nanokomposit BiVO4/TiO2 nanospindle. Menggunakan sistem PFC ini, degradasi rhodamin B yang diperoleh adalah sebesar 23,15% untuk nanokomposit BiVO4/TiO2 nanosheet dan 30,58% untuk nanokomposit BiVO4/TiO2 nanospindle selama 3 jam reaksi.

---

ABSTRACTThis work reports an investigation on the effect of exposing (001) crystal facet of anatase TiO2 to photoelectrocatalytic activity of photoanode composed of TiO2/BiVO4 nanocomposite film. Here, the photoanode was fabricated by depositing the nanocomposite on the surface of FTO via doctor blade technique. In this study, four different types of anatase TiO2 morphologies, i. e. nanospindle, nanocube, nanooctahedra, and nanosheet were synthesized via hydrothermal method in the presence of various directing agents. Furthermore, the as-prepared TiO2 was characterized using X-Ray Diffractometer (XRD), Transmission Electron Microscopy (TEM), Brunauer-Emmelt-Tellers (BET), and UV-Vis diffuse reflectance spectra (DRS). Based on the result, the diffraction peaks revealed characteristic for the pure anatase phase with exposure (001) crystal facet for nanospindle and nanosheet and (101) crystal facet for nanocube and nanooctahedra. Additionally, photoelectrochemical response of the photoanode was also evaluated using a three-electrode system on the photocatalytic fuel cell (PFC) reactor and exhibited a significantly high current density value of 0.0386 mA/cm2 and 0.0381 mA/cm2 for TiO2 nanosheet/BiVO4 and TiO2 nanospindle/BiVO4 nanocomposite. Using this PFC system, the degradation of rhodamine B were obtained 23.15% and 30.58% for TiO2 nanosheet/BiVO4 and TiO2 nanospindle/BiVO4 nanocomposite for 3 hours reaction time. "

"We demonstrate, for the first time, the low voltage-driven electromechanical effects in liquid crystal clastomers (LCEs) swollen with low molecular weight liquid crystal (LMWLC). Thin film polydomain (POLY) and monodomain (MONO) LCEs were embedded in a well-known LMWLC, 4-n-pentyl 1-4 cyanobipheny 1 (5CB), and introducted between transparent indium tin oxide electrodes with 100 hm separation. Absorbing 5cb into poly and mono LCEs, shapes changes were obtained in these materials by application of a small voltage. That is, compared to unswollen LCEs, a dramatic-200 times decrease of the critical fields was found for eletromechanical effect in swollen LCEs. The response time when the field was switched on in both poly and mono is below 2s. The result expect the outstanding potential of swollen LCEs as a low powered devices and actuator (e.g artificial muscles)"

"ABSTRAKDalam penelitian ini telah dirancang instrumentasi yang diharapkan mampu mendeteksi keberadaan nyamuk kemudian mengusirnya secara otomatis. Rancangan yang dibuat terdiri dari tiga buah sub-rangkaian yang terdiri dari rangkaian receier, controller, dan transmitter. Rangkaian receiver yang dipergunakan untuk mendeteksi keberadaan nyamuk tersusun atas rangkaian microphone sebagai sensor suara, band pass filter sebagai penyaring frekuensi, dan amplifier sebagai penguat. Selanjutnya rangkain transmitter yang digunakan sebagai pengusir nyamuk terdiri dari rangkaian osilator kristal sebagai penghasil frekuensi osilasi yang stabil dan buzzer sebagai aktuator yang merubah besaran listrik menjadi besaran fisika berupa suara. Kemudian dibutuhkan rangkaian controller sebagai pengendali yang mengendalikan kerja alat agar dapat berfungsi secara otomatis, terdiri dari rangkaian komparator sebagai pembanding tegangan dan relay sebagai saklar listrik yang bertugas menjadi saklar osilator dengan catu daya. Alat ini akan bekerja menghasilkan frekuensi 39 kHz saat bagian receiver mendapatkan frekuensi pada rentang 300 ndash; 700 kHz. Alat ini diharapkan dapa menjadi solusi yang efektif dalam mengusir nyamuk di masa depan.

---

ABSTRAKIn this research has been designed instrumentation that is expected to detect the presence of mosquitoes and then drive it automatically. This designed instrumentation is consisted of three sub circuits with a series of each receivers, controllers, and transmitters. The series of receivers, that will be used to detect the presence of mosquitoes, composed of microphone series as sound sensors, band pass filters as frequency filters, and amplifiers as amplifiers. Furthermore, a series of transmitters, as mosquito repellent, consisted of crystal oscillator circuit as a stable oscillation frequency generator and buzzer as an actuator that converts electrical quantities into physical quantities of sound. Then, the controller circuit is needed to control the work of the tool in order to function automatically. it consisted of a comparator voltage circuit and relay as an electrical switch in charge of an oscillator switch with a power supply. This tool will work to generate frequency 39 kHz when the receiver gets frequency in the range 300 700 kHz. This tool is expected to be an effective solution in expelling mosquitoes in the future. "