"Penelitian ini adalah studi awal mengenai sel surya tersensitasi berbasis ZnO dengan zat pewarna organik. Tujuannya untuk mengetahui pengaruh dari tingkat pengisian dan besar kristalit TiO2 terhadap voltase DSSC. Hasil dari penelitian menunjukkan bahwa, besar kristalit berbanding terbalik dengan voltase yang dihasilkan. Semakin besar ukuran kristalit semakin kecil voltase yang dihasilkan dan sebaliknya semakin kecil ukuran kristalit semakin besar voltase yang dihasilkan. Sementara tingkat pengisian mempunyai pengaruh berbeda pada kristalit yang besar dan kristalit yang kecil. Selain itu, ukuran kristalit dan tingkat pengisian mempengaruh kestabilan layer oksida dan kemampuannya dalam menyerap molekul zat pewarna.

---

This research is an initial study about ZnO based dye sensitized solar cell (DSSC) with an organic dye. The purpose is to understand the effect of loading level and crystallite size to DSSC voltages.

The result of this research shows that, crystallite size is a contrary fraction with the voltages that produced by DSSC. The bigger size of crystallite the lower voltages outcome, on contrary the smaller size of crystallite the bigger voltages can be produced by DSSC. While loading level have a different affect in smaller and bigger crystallite. Afterwards, crystallite size and volume level affect the stability of the layer oxide and its ability to absorb dye molecules."

"Krisis iklim disebabkan oleh ketergantungan manusia akan energi berbahan dasar fosil berdampak pada peningkatan gas CO2 ke atmosfer bumi. Hal tersebut menyebabkan suhu rata-rata global meningkat dan berimplikasi pada bencana alam yang terjadi di seluruh dunia. Maka dari itu diperlukan energi alternatif yang ramah lingkungan dan dapat diperbaharui. Salah satu sumber energi alternatif itu adalah Dye Sensitized Solar Cell (DSSC) Berbasis N719. Pada pernelitian ini disusun perangkat DSSC dengan TiO2- nanotubes sebagai semikonduktor, ruthenium complex dye N719 sebagai fotosensitizer, Platina sebagai elektroda pembanding, dan elektrolit (I-/I3-). Preparasi TiO2-nanotubes dengan metode two-step anodization pada variasi waktu anodisasi 30, 60, 90, 180 menit. Material kemudian dikarakterisasi dengan SEM, XRD, FTIR, UV-VIS-DRS, dan potensiostat. Hasil penelitian tinggi tabung, dye loading, dan efisiensi DSSC pada variasi waktu anodisasi 30, 60, 90, 180 menit secara berurutan tinggi tabung sebesar 5,28 μm; 7,61 μm; 11,43 μm; 9,45 μm, dye loading sebesar 67,13 nmol/cm2; 125,44 nmol/cm2; 237,97 nmol/cm2; 207,91 nmol/cm2, dan persen efisiensi DSSC 1,72%; 2,13%; 3,32%; 3,03%. Hasil yang didapatkan menunjukkan nilai optimum persen efisiensi DSSC berbanding lurus dengan tinggi tabung dan dye loading TiO2-nanotubes.

---

Climate crisis caused by human need for fossil fuel energy have an impact on increasing CO2 emission gas into the atmosphere. More than that, disaster linked to the climate crisis has always been part of our Earth’s system but they are becoming more frequent and intense as the world warms due to an increase the Earth’s average temperature. Therefore we need alternative energy that can be renewed as well as environmentally friendly. One of the renewable and green energy is Dye-Sensitized Solar Cell (DSSC) based on dye N719. In this research, The DSSC device fabricated by TiO2-nanotubes as semoconductor, ruthenium complex dye N719 as photosensitizer, Platina (Pt) as counter electrode, and electrolyte solution (I-/I3-). The preparation of TiO2-nanotubes by two-step anodization method followed by anodization time treatment into four variations, these were in 30 minutes, 60 minutes, 90 minutes, and 180 minutes to get highly ordered length of TiO2-nanotubes. These materials were characterized by SEM, XRD, FTIR, UV-VIS- DRS, dan Electrochemical Work Station. The results of tube length, dye loading, and DSSCs efficiency at four variations of anodization time 30 minutes, 60 minutes, 90 minutes, and 180 minutes sequentially are tube length of 5,28 μm; 7,61 μm; 11,43 μm; 9,45 μm, dye loading of 67,13 nmol/cm2; 125,44 nmol/cm2; 237,97 nmol/cm2; 207,91 nmol/cm2, dan DSSC efficiency of 1,72%; 2,13%; 3,32%; 3,03%. The results show optimum value of DSSC efficiency directly proportional to tube length and dye loading of TiO2-nanotubes."

"Sel surya tersensitasi zat warna (dye-sensitized solar cell, DSSC) merupakan perangkat yang dapat mengkonversi cahaya matahari menjadi arus listrik dengan menggunakan elektroda kerja berupa semikonduktor TiO2 yang dilapisi oleh zat warna dan kaca ITO (Indium Tin Oxide) sebagai elektroda counter. Lapisan tipis TiO2 dipreparasi di atas plat Ti dengan cara anodisasi dalam larutan NH4F dalam gliserol pada bias potensial 25 volt selama 4 jam dan dikalsinasi pada suhu 500°C selama 3 jam. Karakterisasi dengan SEM menunjukkan bahwa TiO2 yang terbentuk mempunyai morfologi nanotube dengan diameter tabung yang teratur, yaitu 40-60 nm. Karakterisasi dengan XRD dan DRS UV-Vis menunjukkan bahwa kristal TiO2 yang terbentuk berupa fasa anatase. Zat warna yang digunakan sebagai photosensitizer adalah zat warna alami cyanidin yang diekstrak dari buah black mulberry (Morus nigra L) dengan pelarut metanol:HCl (99:1). Karakterisasi cyanidin dengan UV-Vis menunjukkan serapan kuat paada panjang gelombang 513 nm. Cyanidin diadsorpsikan ke dalam TiO2 nanotube menggunakan metode elektroforesis, dengan variasi bias potensial dan waktu. Plat Ti/TiO2- nanotube/cyanidin dirangkai menjadi DSSC dengan larutan elektrolit Iˉ/I3ˉ dan kaca ITO. Nilai efisiensi konversi cahaya menjadi arus listrik tertinggi adalah 0,2678 % dan 0,2672%, ditunjukkan oleh plat Ti/TiO2-nanotube/cyanidin yang masing-masing dielektroforesis pada tegangan 20 volt selama 12 menit dan 25 volt selama 8 menit.

---

Dye-sensitized solar cell (DSSC) is a device that can convert the sunlight to electrical current, by employing dyes coated TiO2 semiconductor as working electrode and ITO (Indium Tin Oxide) glass as counter electrode. TiO2 thin film was prepared by anodization of Ti plate in NH4F/glycerol at potential 25 volt for 4 hours and then heated at 500°C for 3 hours. Characterization by SEM showed the TiO2 has a nanotube morphology having internal diameter of 40-60 nm. Characterization by XRD and DRS UV-Vis indicated that the TiO2 is in anatase crystal phase. Cyanidin, a natural dye, that was used as photo sensitizer was extracted from black mulberry fruit (Morus nigra L) in methanol:HCl (99:1) solvent. The extracted cyanidin showed a strong absorption at wavelength of 513 nm, which is suitable to absorb visible light. The cyanidin is coated into TiO2 nanotube by using electrophoresis method, at various bias potential and time. The Ti/TiO2-nanotube/cyanidin plate was assembled into DSSC using Iˉ/I3ˉ electrolyte solution and ITO glass. The highest efficiency values were 0.2678 % and 0.2672%, for Ti/TiO2-nanotube/cyanidin which were prepared by electrophoresis at 20 volt for 12 minutes and 25 volt for 8 minutes, respectively."

"ABSTRAKDSSC, dyes sensitized solar cell, dengan zat warna alami termasuk kurkumin memiliki efisiensi yang rendah karena masalah ketidakstabilan kromofor pada zat warna tersebut. Salah satu cara untuk meningkatkan efisiensi DSSC dengan meningkatkan kestabilan fotoanoda, yaitu dengan inkorporasi nanopartikel emas. Nanopartikel emas dapat meningkatkan photocurrent dikarenakan efek surface plasmon resonance yang mampu meningkatkan absorpsi fotoanoda terhadap cahaya tampak. Penelitian mengenai inkorporasi nanopartikel emas pada fotoanoda DSSC tersensitasi zat warna alami termasuk kurkumin masih kurang dipelajari. Tujuan dari penelitian ini adalah untuk mengetahui apakah inkorporasi nanopartikel emas dapat meningkatkan respon terhadap sinar tampak dan aktivitas photocurrent fotoanoda TiO2 tersensitasi kurkumin. Selain itu dimaksudkan juga untuk mengetahui apakah inkorporasi nanopartikel emas pada fotoanoda TiO2 tersensitasi kurkumin dapat meningkatkan efisiensi DSSC. Penelitian ini dimulai dengan sintesis dan persiapan bahan yang dibutuhkan untuk pembuatan fotoanoda. Fotoanoda yang digunakan adalah lapisan film TiO2 diatas kaca transparan yang konduktif kaca berlapis FTO, fluor doped Tin Oxide , yang disensitasi dengan kurkumin dan diinkorporasikan dengan nanopertikel emas. TiO2 dibuat dengan metoda Rapid Breakdown Anodization RBA , FTO dibuat dengan metode spray pyrolysis, dan nanopartikel emas disintesis dengan metode Turkevich. TiO2 dan kombinasi fotoanoda yang dibuat dikarakterisasi dengan SEM-EDX, UV-DRS, FTIR, dan XRD. Kombinasi empat fotoanoda yang dibuat yaitu FTO/TiO2, FTO/TiO2/Au, FTO/TiO2/Kurkumin dan FTO/TiO2/Au/ Kurkumin. FTO/TiO2 dibuat dengan metode doctor blade. Inkorporasi nanopartikel emas pada permukaan fotoanoda FTO/TiO2 dilakukan dengan metode elektroforesis. Hasil karakerisasi SEM-EDX mengkonfirmasi adanya nanopartikel emas yang telah terinkorporasi pada permukaan fotoanoda TiO2 dan distribusinya. Karaktersisasi FTIR mengkonfirmasi adanya interaksi antara kurkumin dan TiO2 setelah proses sensitasi. Untuk mempelajari dampak inkorporasi nanopartikel emas pada absorpsi dan aktivitas photocurrent fotoanoda TiO2 tersensitasi kurkumin pada cahaya tampak, dilakukan karakterisasi sifat optikal UV Vis dan UV DRS dan aktivitas photocurrent metode Multipulse Amperometry pada keempat fotoanoda yang telah dibuat. TiO2 hasil sintesis memiliki struktur anatase dengan ukuran 22.9 nm dan memiliki band gap sebesar 3.14 eV. FTO hasil sintesis memiliki sheet resistance rata rata sebesar 5.264 Ohm/sq dan Transmittans maksimum sebesar 84.2 . Nanopartikel emas hasil sintesis memiliki absorbansi maksimum pada panjang gelombang 536 nm. Absorpsi dan aktivitas photocurrent pada cahaya tampak dari FTO/TiO2/Au/kurkumin lebih baik dibandingkan FTO/TiO2/ Kurkumin. DSSC dengan fotoanoda FTO/TiO2/Au/Kurkumin ? = 0.07 memiliki efisiensi yang lebih besar dibandingkan FTO/TiO2/Kurkumin ? = 0.01 . Akhirnya untuk mengetahui apakah inkorporasi nanopartikel emas dapat meningkatkan efisiensi DSSC dengan fotoanoda TiO2 tersensitasi kurkumin, Fotoanoda FTO/TiO2/Kurkumin dan FTO/TiO2/Au/Kurkumin dirakit menjadi sistem DSSC dengan metode sandwich lalu dievaluasi efisiensinya dengan metode Linear Sweep Voltammetry dengan potensiostat. Hasil penelitian menunjukkan bahwa inkorporasi nanopartikel emas pada fotoanoda TiO2 tersensitasi kurkumin dapat meningkatkan aktivitas photocurrent, hal ini dikarenakan pengaruh surface plasmon resonance dari nanopartikel emas sehingga meningkatkan absorpsi fotoanoda TiO2 tersensitasi kurkumin pada cahaya tampak. Sementara itu kenaikan efisiensi yang signifikan juga diamati pada DSSC dengan fotoanoda yang diinkorporasikan dengan nanopartikel emas.

---

ABSTRACTDSSC, dyes sensitized solar cells, with natural dyes including curcumin have a low efficiency due to the chromophore instability of the dyestuff. One way to improve the efficiency of DSSC, by improving photoanode stability, is by incorporation of gold nanoparticles. The gold nanoparticles can increase the photocurrent due to the surface plasmon resonance effect which enhances the photoanode absorption to visible light. Research on the incorporation of gold nanoparticles in DSSC with natural dye sensitized photoanode including curcumin has not been extensively studied. The purpose of this study was to find out whether the incorporation of gold nanoparticles could improve the response to visible light and photocurrent activity of curcumin sensitized photoanode TiO2. It is also intended to find out whether the incorporation of gold nanoparticles in the curcumin sensitized photoanode TiO2 can improve the efficiency of DSSC. This research begins with the synthesis and preparation of materials required for the fabrication of photoanode. The photoanode that used is made by a layer of TiO2 film on a transparent conductive glass FTO coated glass, Fluorine doped Tin Oxide , which is sensitized with curcumin and incorporated with gold nanoparticles. TiO2 was prepared by Rapid Breakdown Anodization RBA method, FTO was made by spray pyrolysis method, and gold nanoparticles were synthesized by Turkevich rsquo s method. TiO2 and photoanode combinations that made were characterized by SEM EDX, UV DRS, FTIR, and XRD. The combination of four photoanode are FTO TiO2, FTO TiO2 Au, FTO TiO2 Curcumin and FTO TiO2 Au Curcumin. FTO TiO2 is made by doctor blade method. The incorporation of gold nanoparticles on photoanode FTO TiO2 surface is done by electrophoresis method. SEM EDX characterization results confirm the presence of gold nanoparticles that have been incorporated on the surface of the photoanode TiO2 and its distribution. FTIR confirms the interaction between curcumin and TiO2 after the sensitization process. To study the effect of incorporation of gold nanoparticles on photocurrent absorption and photocurrent activity of curcumin sensitized photoanode TiO2 under visible light, optical characterization UV Vis and UV DRS and photocurrent activity Multi Pulse Amperometry method is recorded on all four photoanode that were made. TiO2 has anatase structure with crystallite size 22.9 nm and has a band gap of 3.14 eV. FTO have an average sheet resistance of 5,264 Ohm sq and Transmittance maximum of 84.2 . Gold nanoparticles have a maximum absorbance at wavelength 536 nm. It is found that the absorption and photocurrent activity under visible light of photoanode FTO TiO2 Au Curcumin is better than FTO TiO2 Curcumin. DSSC with photoanode FTO TiO2 Au Curcumin 0.07 has greater efficiency than FTO TiO2 Curcumin 0.01 . Finally, to find out whether the incorporation of gold nanoparticles can improve the efficiency of DSSC with curcumin sensitized photoanode TiO2, Photoanode FTO TiO2 Curcumin and FTO TiO2 Au Curcumin are assembled into DSSC system by sandwich method and evaluated its efficiency by Linear Sweep Voltammetry method with potentiostat. The results showed that the incorporation of gold nanoparticles in the curcumin sensitized photoanode TiO2 increase the photocurrent activity, due to the influence of surface plasmon resonance from the gold nanoparticles thus increasing the absorption of curcumin sensitized photoanode TiO2 under visible light. Meanwhile significant efficiency improvements were also observed in the DSSC with photoanode incorporated with gold nanoparticles."

"[Dye Sensitized Solar Cell (DSSC) dalam konfigurasi tabung telah berhasil dibuat. DSSC dirakit menggunakan Inner Wall Conductive Glass Tube (IWCGT) yang mengandung SnO2-F (Fluorine Tin Oxide) sebagai lapisan konduktif. IWCGT dipreparasi menggunakan tehnik penguapan dan spray nebulizer, menghasilkan kaca transparan berpenghantar yang memiliki hambatan jenis antara 11-80 Ω/cm2.Sol TiO2 dilapiskan pada IWCGT dengan tehnik dip coating, dilanjutkan dengan kalsinasi pada suhu 500° C dan 550° C. Terhadap TiO2 hasil sintesis dilakukan karakterisasi menggunakan UV-Vis Diffuse Reflectance Spectrometry (DRS), Xray Diffraction (XRD), Fourier Transform Infra Red (FTIR) dan spektrofotometerRaman. Lapisan tipis yang diimobilisasi pada IWCGT dikarakterisasi menggunakan Field Emission Scanning Electron Microscope (FE-SEM) dan sistem elektrokimia. Berdasar spektrum UV-Vis dapat diketahui TiO2 yang dihasilkan memiliki energi celah (band gap) sebesar 3,01 dan 3,04 eV. Hasil pengukuran spektroskopi Raman dan XRD menunjukkan bahwa film yang dihasilkan didominasi oleh TiO2 dalam bentuk anatase dan mempunyai ukuran kristal sebesar 9,79 nm (kalsinasi pada suhu 500° C) dan 10,59 nm (kalsinasi pada suhu 550° C). Hasil FE-SEM menunjukkan bahwa lapisan TiO2 yang dipreparasi dengan bantuan template PEG memiliki ketebalan sebesar 496,56 nm. Sistem DSSC dalam konfigurasi tabung yang disiapkan dengan menggunakan TiO2 dan zat warna Rhodamin B, Klorofil dan campuran keduanya mampu menghasilkan efisiensi (η) antara 0,03 – 0,91%.;Dye Sensitized Solar Cell (DSSC) dalam konfigurasi tabung telah berhasil dibuat. DSSC dirakit menggunakan Inner Wall Conductive Glass Tube (IWCGT) yang mengandung SnO2-F (Fluorine Tin Oxide) sebagai lapisan konduktif. IWCGT dipreparasi menggunakan tehnik penguapan dan spray nebulizer, menghasilkan kaca transparan berpenghantar yang memiliki hambatan jenis antara 11-80 Ω/cm2.Sol TiO2 dilapiskan pada IWCGT dengan tehnik dip coating, dilanjutkan dengan kalsinasi pada suhu 500° C dan 550° C. Terhadap TiO2 hasil sintesis dilakukan karakterisasi menggunakan UV-Vis Diffuse Reflectance Spectrometry (DRS), Xray Diffraction (XRD), Fourier Transform Infra Red (FTIR) dan spektrofotometerRaman. Lapisan tipis yang diimobilisasi pada IWCGT dikarakterisasi menggunakan Field Emission Scanning Electron Microscope (FE-SEM) dan sistem elektrokimia. Berdasar spektrum UV-Vis dapat diketahui TiO2 yang dihasilkan memiliki energi celah (band gap) sebesar 3,01 dan 3,04 eV. Hasil pengukuran spektroskopi Raman dan XRD menunjukkan bahwa film yang dihasilkan didominasi oleh TiO2 dalam bentuk anatase dan mempunyai ukuran kristal sebesar 9,79 nm (kalsinasi pada suhu 500° C) dan 10,59 nm (kalsinasi pada suhu 550° C). Hasil FE-SEM menunjukkan bahwa lapisan TiO2 yang dipreparasi dengan bantuan template PEG memiliki ketebalan sebesar 496,56 nm. Sistem DSSC dalam konfigurasi tabung yang disiapkan dengan menggunakan TiO2 dan zat warna Rhodamin B, Klorofil dan campuran keduanya mampu menghasilkan efisiensi (η) antara 0,03 – 0,91%.

---

A dye sensitized solar cell (DSSC) having tube geometry has been successfully constructed. The DSSC employ an Inner Wall Conductive Glass Tube (IWCGT) containing SnO2-F (Fluorine Tin Oxide) as conductive layer, which was prepared by evaporation and spray nebulizer method. The IWGCT has a transparent

conductive oxide with high optical transmittance and low sheet resistance, that is 11-80 Ω/cm2. TiO2 film, immobilized on the IWCGT, was successfully prepared by a dip-coating technique from titania sol-gel, followed by heat treatment at 500° C and 550° C. The TiO2 was characterized by diffuse reflectance UV-Vis

spectroscopy and XRD, photoelectrochemical system (PES) and field emission scanning electron microscopy (FE-SEM). Characterization results indicated that the prepared TiO2 has band gap of 3,01 and 3,04 eV (DRS UV-Vis); predominantly by anatase phase (XRD and Raman); having crystallite size of

9.79 nm (at 500° C calcinations) and 10.59 nm (at 550° C calcinations), and having 496,56 nm film thickness. By employing rhodamine B, chlorophyll and its mixture, as the dyes, the tubular DSSC reached efficiency (η) in the range of 0.03 to 0.91 %.;A dye sensitized solar cell (DSSC) having tube geometry has been successfully

constructed. The DSSC employ an Inner Wall Conductive Glass Tube (IWCGT)

containing SnO2-F (Fluorine Tin Oxide) as conductive layer, which was prepared

by evaporation and spray nebulizer method. The IWGCT has a transparent

conductive oxide with high optical transmittance and low sheet resistance, that is

11-80 Ω/cm2. TiO2 film, immobilized on the IWCGT, was successfully prepared

by a dip-coating technique from titania sol-gel, followed by heat treatment at

500° C and 550° C. The TiO2 was characterized by diffuse reflectance UV-Vis

spectroscopy and XRD, photoelectrochemical system (PES) and field emission

scanning electron microscopy (FE-SEM). Characterization results indicated that

the prepared TiO2 has band gap of 3,01 and 3,04 eV (DRS UV-Vis);

predominantly by anatase phase (XRD and Raman); having crystallite size of

9.79 nm (at 500° C calcinations) and 10.59 nm (at 550° C calcinations), and

having 496,56 nm film thickness. By employing rhodamine B, chlorophyll and its

mixture, as the dyes, the tubular DSSC reached efficiency (η) in the range of

0.03 to 0.91 %.;A dye sensitized solar cell (DSSC) having tube geometry has been successfully

constructed. The DSSC employ an Inner Wall Conductive Glass Tube (IWCGT)

containing SnO2-F (Fluorine Tin Oxide) as conductive layer, which was prepared

by evaporation and spray nebulizer method. The IWGCT has a transparent

conductive oxide with high optical transmittance and low sheet resistance, that is

11-80 Ω/cm2. TiO2 film, immobilized on the IWCGT, was successfully prepared

by a dip-coating technique from titania sol-gel, followed by heat treatment at

500° C and 550° C. The TiO2 was characterized by diffuse reflectance UV-Vis

spectroscopy and XRD, photoelectrochemical system (PES) and field emission

scanning electron microscopy (FE-SEM). Characterization results indicated that

the prepared TiO2 has band gap of 3,01 and 3,04 eV (DRS UV-Vis);

predominantly by anatase phase (XRD and Raman); having crystallite size of

9.79 nm (at 500° C calcinations) and 10.59 nm (at 550° C calcinations), and

having 496,56 nm film thickness. By employing rhodamine B, chlorophyll and its

mixture, as the dyes, the tubular DSSC reached efficiency (η) in the range of

0.03 to 0.91 %., A dye sensitized solar cell (DSSC) having tube geometry has been successfully

constructed. The DSSC employ an Inner Wall Conductive Glass Tube (IWCGT)

containing SnO2-F (Fluorine Tin Oxide) as conductive layer, which was prepared

by evaporation and spray nebulizer method. The IWGCT has a transparent

conductive oxide with high optical transmittance and low sheet resistance, that is

11-80 Ω/cm2. TiO2 film, immobilized on the IWCGT, was successfully prepared

by a dip-coating technique from titania sol-gel, followed by heat treatment at

500° C and 550° C. The TiO2 was characterized by diffuse reflectance UV-Vis

spectroscopy and XRD, photoelectrochemical system (PES) and field emission

scanning electron microscopy (FE-SEM). Characterization results indicated that

the prepared TiO2 has band gap of 3,01 and 3,04 eV (DRS UV-Vis);

predominantly by anatase phase (XRD and Raman); having crystallite size of

9.79 nm (at 500° C calcinations) and 10.59 nm (at 550° C calcinations), and

having 496,56 nm film thickness. By employing rhodamine B, chlorophyll and its

mixture, as the dyes, the tubular DSSC reached efficiency (η) in the range of

0.03 to 0.91 %.]"

"Dye-Sensitized Solar Cell (DSSC) telah menarik perhatian sebagai salah satu sumber energi alternatif yang terbarukan. Di daerah tropis, dimana cahaya matahari hampir tersedia sepanjang tahun, DSSC dapat menjadi sumber energi yang sangat berguna. Penelitian tentang DSSC telah dilakukan secara intensif oleh kelompok peneliti terutama di negara-negara maju. Saat ini, kami bekerja pada pembuatan DSSC dengan mensintesis TiO2 nanotube melalui proses anodisasi pada plat titanium dengan larutan elektrolit garam amonium florida dalam gliserol. Kemudian TiO2 nanotube dikarakterisasi dengan termal insitu XRD, UV-Vis DRS dan SEM, yang mengindikasikan terjadinya fase kristal anatase pada perlakuan panas suhu 400˚C. Film anatase yang terbentuk menunjukkan morfologi nanotube yang sangat teratur, dengan ketebalan film sekitar 1,6 μm. Nanotube memiliki rata-rata ketebalan dinding, diameter pori dan diameter luar sekitar 19 nm, 67 nm dan 105 nm. Kemudian zat warna alizarin yang berfungsi sebagai sensitizer dilekatkan pada TiO2 nanotube (TiO2-NT/alizarin) dengan metode elektroforesis. Ti/TiO2-NT/alizarin tersebut selanjutnya dirakit menjadi sel DSSC menggunakan iodium sebagai elektrolit dan film Pt pada kaca ITO sebagai elektroda counter. Hasil pengukuran menunjukkan bahwa rangkaian sel DSSC menghasilkan nilai efisiensi maksimum pada waktu anodisasi 4 jam dan waktu elektroforesis zat warna 12 menit.

---

Dye-Sensitized Solar Cell (DSSC) has attracted attention as one of future renewable alternative energy source. In tropical area, where the solar light is almost available all the year, DSSC can be very useful. Research on DSSC has been conducted intensively by research groups mostly in advance countries. We recently start work on DSSC issue by employing highly ordered TiO2 nanotube, prepared by anodization of titanium metal sheet in the present of aqueous ammonium fluoride in glycerol. The prepared TiO2 nanotube was characterized by mean insitu thermal treatment XRD, UV-Vis DRS and SEM, which indicate the occurrence of anatase crystal phase upon heat treatment at 4000C. The formed anatase film showed morphology of highly ordered nanotube array, with about 1.6 μm film thickness, having average of wall thickness and internal diameter of 19 nm and 67 nm, respectively. The typical dyes sensitizer (e.g. alizarin) then was attached to the TiO2 nanotube (TiO2-NT/alizarin) by electrophoresis method. The Ti/TiO2-NT/alizarin then was assembled in typical DSSC, employing iodine as an electrolyte and Pt film supported on an ITO glass, as the counter electrode and light window as well. The measurement result indicates that the series of DSSC cells produce the maximum efficiency at 4 hours anodization and 12 minutes electrophoresis dye."

"Sel surya tersensitasi zat pewarna (dye-sensitized solar cell, DSSC) merupakan salah satu teknologi sel surya generasi ke 3 yang murah dan mudah proses manufakturnya. Akan tetapi, efisiensi konversi energi yang dihasilkan divais ini masih sangat kecil dibandingkan dengan sel surya generasi pertama. TiO2 nanopartikel merupakan jenis material semikonduktor yang biasa digunakan pada DSSC yang kualitasnya bergantung kepada ukuran butirnya. Ekstrak ketapang terbukti dapat berperan sebagai capping agent natural yang dapat mengurangi ukuran partikel dan kristalit TiO2 serta memperbaiki sifat fotokatalitik dan absorbansinya. Penambahan grafena oksida sebagai dopant juga dapat memperbaiki sifat fotokatalitik dari TiO2 agar dapat meningkatkan efisiensi konversi energi dari DSSC. Pada penelitian ini, sintesis organik dilakukan dengan variasi ekstrak buah ketapang dan dengan penambahan grafen oksida. Hasil penelitian memperlihatkan bahwa pada penambahan grafena oksida 0,0017% dan penggunaan ketapang pada konsentrasi 0,6 % memiliki peningkatan efisiensi konversi energi hingga 13,7%. Peningkatan efisiensi energi kini dapat dikaitkan dengan penggunaan ekstrak ketapang yang berperan sebagai capping agent pada saat proses sintesis dan penambahan grafen oksida dalam memperbaiki sifat fotokatalitiknya. Dengan demikian modifikasi green sintesis dengan ekstrak buah ketapang dan penambahan grafen oksida memiliki potensi yang besar dalam membangun proses manufaktur DSSC dengan konversi energi yang baik, murah serta ramah lingkungan

---

Dye sesnitized solar cell (DSSC) is one of the 3rd generation solar cell technologies that is cheap and easy to manufacture. However, the conversion energy efficiency produced is still very small compared to that of the first generation of solar cells. Titanium dioxide (TiO2) nanoparticles are a type of semikonduktor material commonly used in DSSC whose quality depends on the grain size. Almond extract is proven to act as a natural capping agent that can reduce the particle size and crystallite of TiO2 and improve its photocatalytic and absorbance properties. The addition of graphene as a dopant can also improve the photocatalytic properties of TiO2 in order to improve the energy conversion efficiency of DSSC. In this study, green synthesis was carried out using variations of almond extract and graphene oxide to improve photocatalytic properties and energy conversion. The result showed that the addition of graphene oxide of 0.0017% and 0.6% of almond extract increased energy conversion efficiency of up to 13.7%. The increase in energy eenergincy could be attributed to the use of almond extract which acts as a capping agent during the synthesis. Moreover, doping of graphene oxide improved its photocatalytic properties. Hence, green synthesis of TiO2 nanoparticles using almond extract media and the addition of graphene oxide has a great potential in fabrication of DSSC device with good energy conversion, cheap and environmentally friendly.

"

"Sel surya tersensitasi zat warna dye-sensitized solar cell, DSSC merupakan perangkat yang dapat mengkonversi sinar matahari menjadi arus listrik dengan menggunakan elektroda kerja berupa semikonduktor TiO2 yang dilapisizat warna dan kaca FTO Fluorine Tin Oxide sebagai elektroda counter. Lapisan tipis TiO2 dipreparasi pada plat Ti dengan cara anodisasi dalam larutan NH4F dalam gliserol pada bias potensial 25 volt selama 4 jam dan dikalsinasi pada suhu 450oC selama 2 jam. Karakterisasi menggunakan DRS UV-Vis dan FTIR menunjukkan bahwa TiO2 yang terbentuk berupa fasa anatase. Zat warna yang digunakan sebagai photosensitizer adalah zat warna alami yang diekstrak dari daun suji, wortel dan alga hijau-biru Spirulina platensis sebagai klorofil, '-karoten dan fikosianin. Optimasi dilakukan dengan memodifikasi klorofil dengan penambahan '-karoten dan fikosianin cocktail dyes dengan perbandingan 1:1 dan 1:2. Zat warna diadsorpsikan ke dalam TiO2-nanotube dengan metode elektroforesis pada bias potensial 20 volt selama 12 menit. Plat Ti/TiO2-nanotube/dyes dirangkai menjadi DSSC dengan larutan I-/I3- dan kaca FTO. Nilai efisiensi konversi cahaya menjadi arus listrik tertinggi ditunjukkan oleh plat Ti/TiO2-nanotube/cocktail dyes klorofil-fikosianin 1:1 sebesar 1.04926.

---

Dye sensitized solar cell DSSC is a device that can convert the sunlight to electrical current by employing dyes coated semiconductor as working electrode and FTO Fluorine Tin Oxide glass as counter electrode. TiO2 thin film was prepared by anodization of Ti plate in NH4F glycerol at potential 25 volt for 4 hours and heated at 450oC for 2 hours. Characterization by DRS UV Vis and FTIR showed that the TiO2 is in anatase crystal phase. Dye that was used as photosensitizer were natural dyes extracted from suji leaf, carrot and green blue algae Spirulina platensis as chlorophyll, carotene and phycocyanin. Optimization was done by modified the chlorophyll added by carotene and phycocyanin cocktail dyes with ratio 1 1 and 1 2. Dyes was coated into TiO2 nanotube by using electrophoresis method at 20 volt for 12 minutes. Ti TiO2 nanotube dyes was assembled into DSSC using I I3 electrolyte solution and FTO glass. The highest efficiency value was showed by Ti TiO2 nanotube cocktail dyes chlorophyll phycocyanin 1 1 was 1.04926."

"Dye Sensitized Solar Cell DSSC berbasis TiO2 merupakan tipe sel surya yang menarik perhatian karena proses fabrikasi yang mudah, biaya pembuatan yang murah, dan efisiensi yang menjanjikan. Dalam penelitian ini dilakukan fabrikasi DSSC menggunakan TiO2 nanotube yang disintesis dengan teknik Rapid Breakdown Anodization RBA dan Ultrafast Room Temperature Cristalization URTC . TiO2 kemudian dideposisikan pada substrat kaca Fluor Tin Oxide FTO menggunakan metode doctor blade, disensitasi dengan zat warna kurkumin, dan dirangkai sebagai elektroda kerja sel surya bersama elektroda counter berbasis karbon transparan yang disintesis menggunakan metode liquid-liquid interfacial system. Karakterisasi dilakukan dengan XRD, UV-VIS DRS, SEM, FTIR, Raman Spectroscopy, dan Potensiostat EDAQ. Hasil penelitian menunjukkan, metode URTC dapat merubah bentuk TiO2 amorf menjadi fasa kristalin anatase. Fotoaktivitas TiO2-URTC pada daerah UV sebesar 0,10 mA/cm2 pun tidak terlalu jauh dari fotoaktivitas TiO2-450C. Di sisi lain, elektroda counter karbon transparan FTO/Ct berhasil disintesis dan memberikan transimisi rata-rata 58,26 pada daerah sinar tampak dengan kemampuan elektrokatalitik lebih baik dari FTO. Uji kinerja DSSC dilakukan terhadap sel surya dengan rangkaian FTO/TiO2-URTC/kurkumin//FTO/Ct. Hasilnya menunjukkan bahwa DSSC ini memberikan efisiensi sebesar 0,467 pada penyinaran depan dan 0,262 pada penyinaran belakang. Nilai efisiensi tersebut tidak berbeda jauh dengan efisiensi DSSC dengan komponen FTO/TiO2-450C/kurkumin//FTO/Pt, yaitu 0,517 untuk penyinaran depan dan 0,356 untuk penyinaran belakang.

---

based Dye Sensitized Solar Cell DSSC is one of the most attractive solar cell, because of its easy fabrication, low cost, and relatively promising efficiency. In this research, we developed solar cell using TiO2 nanotube powder that was made by Rapid Breakdown Anodization RBA and Ultrafast Room Temperature Cristalization technique. The prepared TiO2 then was sensitized using curcumin dyes and utilized to construct DSSC using carbon transparent counter electrode prepared by liquid liquid interface system technique. Characterizations of the prepared materials were done by using XRD, SEM, UV Vis DRS, FTIR, Raman spectroscopy, and Electrochemical working station. The results indicate that by using URTC technique, the freshly prepared TiO2 was transformed to anatase crystalline phase. Furthermore, photoactivity of TiO2 ndash URTC in UV 0.10 mA cm2 just equal to that was being prepared by the conventional technique 0.12 mA cm2 . On the other hand, carbon transparent electrode FTO Ct was successfully prepared and gives 58.26 transparency in visible light region but having catalytic activity better than bare FTO. Furhermore, efficiency test of constructed DSSC FTO TiO2 URTC curcumin FTO Ct showed efficiency of 0.467 for front illumination and 0.262 for back illumination. This result is still lower, but not too far than conventional DSSC with components FTO TiO2 450C curcumin FTO Pt which gives 0.517 efficiency for front illumination and 0,356 for back illumination."

"Dye-Sensitized Solar Cell (DSSC) merupakan sumber energi alternatif yang sangat menjanjikan. Salah satu komponen penting DSSC adalah fotoanoda yaitu berupa bahan TiO2 yang disensitasi dengan zat warna. Pada penelitian kali ini, TiO2 Nanorod telah berhasil disintesis dengan menggunakan metode hidrotermal menggunakan Ti(OBu)4 sebagai prekursor Ti dan dilanjutkan dengan perlakuan panas (kalsinasi) pada variasi suhu (tanpa kalsinasi, 500ºC, 700ºC, 800ºC, dan 950ºC). Berdasarkan hasil karakterisasi SEM-EDX, bentuk morfologi nanorod belum nampak pada sampel TiO2 (tanpa kalsinasi), untuk sampel TiO2 (dengan suhu kalsinasi 700ºC) sudah mulai nampak terbentuk morfologi nanorod tetapi belum sempurna dan untuk sampel TiO2 (dengan suhu kalsinasi 950ºC) sudah terbentuk morfologi nanorod secara jelas dengan diameter lubang rod yang bervariasi yaitu sebesar 223.8 nm, 277.8 nm, 322.0 nm, dan 326.3 nm. Hasil analisis FTIR menunjukkan bahwa pada suhu kalsinasi semakin tinggi maka puncak serapan pada daerah yang khas untuk gugus fungsi hidroksil semakin rendah nilai serapannya, mengindikasikan semakin berkurangnya keberadaan residu gugus OH bebas. Sedangkan, hasil dari analisis XRD didapatkan hasil bahwa sampel tanpa kalsinasi menunjukkan keberadaan fasa anatase dan rutile dengan ukuran kristalit sebesar 11.34 nm. Sampel TiO2 Nanorod dengan perlakuan panas pada suhu kalsinasi 500ºdidominasi oleh keberadaan fasa kristal rutile, memiliki ukuran kristalit sebesar 20.98 nm. Semakin besar suhu kalsinasi diamati semakin didominasi oleh fasa rutile, dan ukuran kristalitnya menjadi semakin besar, berturut-turut sampel TiO2 Nanorod (dengan suhu kalsinasi 700º, 800ºC dan 950ºC) sebesar 22.14 nm, 39.45 nm, 46.76 nm. Hasil karakterisasi dengan menggunakan Spektrofotometri UV-DRS didapatkan hasil semakin besar suhu kalsinasi maka nilai energi band gap semakin kecil. Nilai band gap yang dihasilkan berada pada rentang anatase dan rutile. TiO2 Nanorod (tanpa kalsinasi) memiliki nilai band gap sebesar 3.06 eV, sedangkan untuk TiO2 Nanorod (dengan suhu kalsinasi 500ºC, 700ºC, 800ºC dan 950ºC sebesar 3.05 eV, 3.04 eV, 3.03 eV, dan 3.03 eV.

---

Dye-sensitized solar cell (DSSC) is a very promising source of alternative energy. One of the key components of the DSSC is photoanoda, which is associated with the TiO2 content. In this research, nanorod TiO2 has been successfully synthesized using the hydrothermal method, by using Ti(OBu)4 as a precursor of Ti, and followed by thermal treatment (calcination) at various temperature (without calcination, 500ºC, 700ºC, 800ºC, and 950ºC). Based on SEM-EDX characterization, TiO2 samples the sample (without calcination) showed no clear formation of nanorod morphology. In the other hand, the TiO2 sample which was heated at 700ºC, started showing the nanorod morphology and a clear nanorod morphology was observed in the TiO2 sample which has heated at 950ºC. The diameter of the rood produced was 223.8 nm, 277.8 nm, 322.0 nm, and 326.3 nm, respectively. The FTIR analysis showed that the peak absorption attributed to the OH group decreased when with more high temperature treatment exposed to the TiO2 samples. The XRD analysis of uncalcinated sample indicated the formation of slightly anatase and more predominantly by rutile, which has a crystallite size of 11.34 nm. It was observed that with more higher temperatures, TiO2 Nanorod samples were predominated by rutile crystal phase. In addition the higher calcination temperatures resulted bigger crystallite size these are the calcination temperature of 500ºC, 700ºC, 800ºC, and 950oC resulted crystallite size of 20.98 nm, 22.14 nm, 39.45 nm, and 46.76 nm, respectively. The characterization results using UV-DRS spectrophotometry showed that the greater the calcination temperature, the smaller the band gap energy value. The resulting band gap values are in the anatase and rutile ranges. TiO2 Nanorod (without calcination) has a band gap value of 3.06 eV, while for TiO2 Nanorod (with calcination temperatures of 500ºC, 700ºC, 800ºC and 950ºC of 3.05 eV, 3.04 eV, 3.03 eV and 3.03 eV."